for
the fabrication of continuous fiber-reinforced polymer composite laminate test panels used in the
generation of mechanical properties and (2) an approach for the validation of composite
fabrication processes used during the certification of composite aircraft structure. These
guidelines were prepared by a team of industry experts that have extensive experience generating
material specifications, processing of composite materials, qualification program management,
and design allowables development.
Guidelines are given based on processes and sound engineering practices currently used within
the aerospace industry. This report is intended to advance the work that has been done through
previous Federal Aviation Administration (FAA) programs, such as the Advanced General
Aviation Transport Experiment (AGATE). These programs have established a methodology for
developing statistical-based databases and their standardization.
The guidelines found in this document should not be viewed as policy or as the single acceptable
method for composite laminate fabrication. They are meant to be a documentation or current
knowledge and application of sound engineering principles to the composite laminate fabrication
process. It is envisioned that these guidelines would be used to develop:
process specifications,
work instructions (planning),
sections within material specifications, and
certification and qualification test plans.
An important theme found within these guidelines is the importance of clearly documenting the
procedures used to fabricate laminates. The ability to consistently repeat the fabrication process
at a later date is necessary to minimize the variability in composite material test data and
production parts. This can only be accomplished if the fabrication instructions are accurately
documented.
This document can also be used to develop an industry approach so that the following goals can
be achieved:
Greatly reduce the number of material and process specifications for identical composite
material systems.
Develop property databases that uniquely define a given material.
The terminology process specification will be used throughout this report for the instructions and controls used
in test panel fabrication. However, only part of the processing information needs to be contained in a process
specification, alternatively, some may appear in other documentation.
1
Establish material batch testing and process monitoring sufficient to minimize variability
and preclude property changes over time.
Reduce costs through common documentation and shared databases of basic material
properties.
This document complements the recommendations and guidance for composite prepreg material
specifications found in reference 1.
1.2 BACKGROUND.
Steady growth in the use of composites has continued in transport aircraft and rotorcraft.
General aviation has emerged recently with the growth of new composite aircraft and composite
material applications in primary structures. Several new composite aircraft are undergoing the
certification process. Many more aircraft are currently undergoing the design and development
processes that take advantage of composite materials for primary structure applications. With
this growth of composite applications, certification issues have emerged with respect to the
philosophy of quality control and quality assurance methods needed to guarantee a safe and
consistent material supply.
The material properties of a composite are manufactured into the structure as part of the
fabrication process (process intensive material). Therefore, it is essential that material and
process specifications used to produce composite materials contain sufficient information to
ensure that critical parameters in the fabrication process are identified to facilitate production and
adherence to standards in the final engineered part. Due to the wide variety of composite aircraft
structures now emerging for certification, control of the materials is rapidly becoming a vital
issue with respect to the overall assurance of safety.
In recent years, the aerospace industry, the National Aeronautics and Space Administration, and
the FAA have worked together to develop a cost-effective method of qualifying composite
material systems by sharing material qualification databases such as MIL-HDBK-17 and
AGATE. By using shared databases, a manufacturer can select an approved composite material
system to fabricate parts and validate with a smaller subset of testing for a specific application.
For materials to be accepted into these shared databases, the raw materials are required to be
manufactured in accordance with a material specification which imposes control of key
characteristics (physical, chemical, and mechanical properties) and be processed in accordance
with a process specification that controls key characteristics (processing parameters).
1.3 CERTIFICATION PROCESS.
The objective of the composite aircraft structure certification process is to validate that the
design meets the applicable configuration requirements. In this context, the design validation
process (to establish by proof) is accomplished through verification (to prove by evidence) and
qualification (to define attributes or characteristics) of the materials, processes, and analysis
tools. Verification is simply to prove by evidence, usually by test data, that the proposed design
is acceptable. Material qualification is the verifying of a materials attributes and
characterizations, which are typically determined through testing.
2
A widely acknowledged validation process used within the composite aircraft industry for the
substantiation of composite structure is called the building block approach. This approach uses
analysis and associated tests of increasing structural complexity [2]. The building block
approach is integrated with supporting technologies and design considerations. Refer to MIL-
HDBK-17F, Volume 3, Chapter 4 for a complete description of the building block approach.
Key elements supporting the building block approach are the material and process specifications.
The material and process specifications are interwoven throughout the certification and
validation process. Material specifications are used to define the materials attributes and to
define the qualification characterization tests. Materials used within the building block tests are
purchased in accordance with a material specification. The material specification is used for
procurement of production material. This ensures the delivered materials are of the same quality
and performance standards used in the certification validation process. Process specifications
define and control the processes used for the conversion of materials into structural parts. It is
widely accepted that the performance properties of composite laminates are directly determined
by the specific process used for their fabrication. It is critical that the test specimens fabricated
through the various levels of the building block approach use the same process, which is
representative of the one that will be used in the fabrication of production aircraft and rotorcraft.
Material qualification is a key element of the validation process, which occurs during the coupon
level of the building block approach. It is during qualification that the composite material is
fully defined and characterized. Qualification tests are planned and conducted to
establish key material attributes,
establish material performance properties, and
verify material characteristics will work in the intended application.
The objective in defining material attributes is to establish the material property limits.
Examples of attributes in which limits are set include
resin content,
fiber areal weight,
cured per ply thickness, and
fiber volume.
These attributes define the material and control its resulting performance properties. Other
attributes that are often overlooked are related to the physical structure of the material, which
affects processing characteristics. Example attributes of this type include
fiber-sizing level and type,
level of impregnation,
resin impregnation method (hot-melt film or solution),
width tolerance, and
backing material selection.
3
Performance properties are established, or made stable, through statistically significant amounts
of testing. It is imperative that the materials natural variability is captured at this time. The
objective is not to meet a desired level of performance, but rather, establish the true performance
range of the material. Mechanical properties are typically thought of as the only performance
properties.
There are other performance-related properties that have a direct bearing on the more familiar
mechanical properties, which include tack or handling characteristics, kinetic behavior,
rheological behavior, sensitivity to ambient moisture and temperature (out-time effects), effect of
freezer storage, and resistance to fluids and solvents. Multiple material batches (typically three)
are tested to establish the material variability. Results obtained from these tests are used to
establish minimum and maximum values within the material specification.
2. PROCESS SPECIFICATION GUIDELINES.
The objective of process specifications is to provide a means by which engineering requirements
and procedures can be documented and communicated to the various organizations involved in
the fabrication of composite laminates. The intent is to flow down and specify any regulatory or
engineering requirements and procedures that are necessary for the fabrication process. It is
imperative that the process specifications be clear and complete to ensure that the resulting
laminates are consistent in quality.
For the purpose of this report, the term process specifications refers to documents such as
process specifications, material specifications, planning, work instructions, or test plans. The
guidelines found in the following sections can be applied to any of the above documents. These
guidelines have been found to be helpful in the fabrication of continuous fiber-reinforced
polymer composite test laminates but should not be viewed as the only means of control for a
particular application.
The guidelines for the fabrication of continuous fiber-reinforced polymer composite test
laminates are divided into the following sections:
Work Instructions
Personnel
Materials
Equipment Description
Facility Description
Tooling
Panel Lamination
Panel Acceptance
Process Monitoring
2.1 WORK INSTRUCTIONS.
Work instructions (also referred to as planning) contain the requirements and procedures to be
used in the fabrication process. Detailed step-by-step work instructions in conjunction with
4
process specifications have been found to be a successful approach for the fabrication of
repeatable quality laminates. Process specifications define the engineering requirements while
the work instructions convert the engineering requirements into detailed step-by-step process
instructions.
The level of detail contained within the work instructions is subjective and varies from
organization to organization. While the level of detail can vary, it should always be sufficient to
ensure clear communication of the procedures. Many instructions are best communicated
through sketches or figures. Provisions should also be made within the work instructions for the
recording of relevant observations, data, and quality assurance stamps.
2.2 PERSONNEL.
Highly skilled technicians are needed to produce quality laminates. Fabricators are encouraged
to establish a comprehensive training program for technicians directly involved with the
fabrication of composite test panels. Both written and practical proficiency tests are
recommended for the training program. Fabrication of test panels and production parts by
trained technicians increases the probability of fabricating high quality and repeatable test
panels. The quality of the laminates has a direct bearing on program cost (elimination of rework
due to poor quality laminates) and optimum structural performance (establishment of design
allowables).
Table 1 lists suggested factors to be addressed in the selection of fabrication personnel.
TABLE 1. RECOMMENDED PERSONNEL SELECTION FACTORS
Experience
Inspection personnel, ratio to manufacturing personnel
Level of training
Personnel status identified (qualified or unqualified)
It is strongly recommended that a mentoring relationship be established between the companys
technicians and engineering personnel. This mentoring relationship is best if the flow of
knowledge is in both directions.
2.3 MATERIALS.
All materials (and their sources) required for the fabrication procedures and requirements
relevant to the materials should be listed within the process specifications. The listing includes
both consumable and structural materials. In cases where equivalent materials may be used,
specific alternate materials should be explicitly stated.
Materials that can come in contact with the composite prepreg should be evaluated to verify they
do not contaminate the prepreg material. It should be verified that all materials that have the
potential to become a foreign object within the laminate can be detected by nondestructive
inspection (NDI) methods that will be used for the inspection of production parts.
5
Prepreg materials should be inspected upon receipt by the purchaser, per the material
specification. Test methods, types of tests required, sampling requirements, criteria (acceptance
value), and retest provisions should be clearly defined. Supplier certification records should be
reviewed and maintained with the laminate process instructions. Material that does not meet the
established quality requirements should not be processed into test panels.
Prepreg material freezer storage conditions (temperature) and shelf life limits should be defined
(controlled in the material specification). Most prepreg resins require a storage temperature of
0F or lower. Freezer storage life can be from 6 to 18 months, with 12 months the most
common. Procedures for the disposition of out-of-date material also need to be defined. This
could include shelf life extension based on the performance of reinspection tests.
Ambient working life (sometimes called out-time) limits should be defined. The time period
should be associated with a defined temperature and relative humidity range. This time period
should have been determined during the material qualification test program.
Within the industry, two approaches are used in defining ambient working life. The first
approach refers to the ambient working life as out-time. Out-time begins when the prepreg is
removed from freezer storage and ends when the cure cycle begins. Depending on the resin, out-
time will typically be from 10 to 30 days. The second approach is to divide the ambient working
life into two sections: handling life and staging life. Handling life begins when the prepreg is
removed from the freezer and ends with placement of the prepreg onto the tool. The staging life
begins at placement of the ply on the tool and ends when the cure cycle begins.
Definition of the ambient environment is critical to producing quality parts and avoidance of
scrapped material and parts. Figure 1 is an example schematic of the relationship between
prepreg storage life, handling life, and staging life.
Date of
Manufacture
(Impregnation)
Out of
Storage
End of
Storage
Life
Prepreg Laid-
up on a Tool
or Mold
Part
Cure
Storage Life
(function of
storage
temperature)
Handling Life*
(function of
factory
environment)
Staging Life**
(function of
factory
environment)
Out-Time
*a.k.a. application, assembly, or work life
**a.k.a. mechanical or tool life
FIGURE 1. PREPREG STORAGE AND OUT-TIME LIFE RELATIONSHIP
6
Resins are typically perishable at ambient temperatures, i.e., they continue to react. This
continuing reaction could, in time, reduce the resin kinetics and flow characteristics of the
material, thus affecting producibility and properties.
Prepreg handling properties are a function of temperature. Too high a temperature and the
material will be too tacky, making it difficult to position and handle the plies. Too low a
temperature and the material will be stiff and again difficult to work with.
Some resins are susceptible to moisture in that the absorbed water inhibits cure kinetics.
Therefore, controlling the relative humidity is important for ensuring the resin will obtain an
optimal cure. High humidity will also increase the tack of the material. Prepreg materials with
high tack have been shown to trap air and moisture between the plies, resulting in porosity in the
laminates.
Complete records should be maintained that document traceability of the fiber, resin, adhesive,
prepreg, and laminates. These records should also document the total shelf life and out-time of
the prepreg and adhesive materials up to the time of panel cure. Provisions should be made
within the work instructions to record material batch and roll numbers and ambient out-time at
the time of collation and cure.
2.4 EQUIPMENT DESCRIPTION.
All equipment needed to perform the fabrication process with necessary requirements should be
listed in the process instructions. Sources for the equipment should also be listed. Calibration
and certification requirements should be defined. Equipment requiring calibration and
certification typically includes ovens, autoclaves, thermocouples, vacuum gages, and ply-
warming devices (e.g., hot-air guns). Provisions should be made within the process specification
to record the last date of calibration (as applicable) and equipment serial number.
2.5 FACILITY DESCRIPTION.
Collation (lay-up) of plies should be performed in a clean room. The clean room is an
environmentally controlled facility where, in addition to the control and monitoring of
temperature, humidity, air pressure, air distribution, and air velocity, conditions are established
to minimize the introduction, generation, and retention of airborne particles [3]. Good
housekeeping procedures should be followed along with controlling the temperature, humidity,
and airborne particles. A complete clean room discussion can be found in reference 3.
Additional information on manufacturing facility controls can be found in reference 4.
Prepreg handling and curing characteristics are sensitive to both temperature and humidity and,
therefore, it is critical to control and monitor temperature and humidity within the lay-up area.
The temperature and humidity requirements should align with the materials ambient out-time
requirements. A typical clean room temperature/humidity environmental requirement envelope
is shown in figure 2.
7
0
10
20
30
40
50
60
70
80
60 65 70 75 80
Temperature (F)
R
e
l
a
t
i
v
e
H
u
m
i
d
i
t
y
(
%
)
OPERATING
CONDITIONS
FIGURE 2. TYPICAL CLEAN ROOM TEMPERATURE/HUMIDITY REQUIREMENTS
The control of airborne particles is essential to maintaining a clean environment for the
fabrication of composite laminates. Airborne particles are controlled through the use of filters,
restricting dirty operations, and the establishment of positive pressure within the clean room.
Filtration of the air is recommended to not only ensure clean air is introduced into the clean
room, but also to clean particles from the air that were generated within the clean room. ISO
14644-1 Class 9 is recommended as the minimum level of filtration for a clean room [5]. The
following actions also help to minimize the generation of airborne particles:
Clean work areas on a regular basis and inspect for potential foreign objects.
Do not allow mold releases or other silicone-containing materials into the room.
Do not allow sanding, machining, or any other operation that generates dirt, dust, or other
debris in the room.
Do not allow an air tool to be used without special precautions against contaminating
parts with oil suspended in most shop air.
The inclusion of a positive-pressure ventilation system in the lay-up room is an effective method
of preventing the introduction of airborne particles from other parts of the facility, such as
machine shops.
8
Table 2 presents a checklist of items to consider when specifying requirements for a clean room.
TABLE 2. RECOMMENDED CLEAN ROOM REQUIREMENTS CHECKLIST
Limit access by other equipment (gas powered fork lifts)
Limit access by non-lay-up personnel
Air flow through the room
Equipment for monitoring environmental control
No Contamination by other processes (chemical processing, painting, and sanding)
Treatments and cleanliness of floors
Humidity (minimum and maximum)
Temperature (minimum and maximum)
Isolation from other contaminates
Lay-up area status (approved, unapproved)
Lighting (lumens)
Particulate count
Pressure (positive)
Proximity to staging area and autoclaves
Vacuum hose status (approved, unapproved)
Treatment and cleanliness of walls
Provisions should be made within the work instructions to record the temperature and humidity
at the time of ply collation.
2.6 TOOLING.
For the fabrication of flat test panels, typically, tooling consists of a base plate and a caul plate.
They should be designed for the defined process conditions (e.g., cure temperature and pressure).
Surface finish and flatness requirements should be defined (as applicable). All tools should be
clearly identified. Tool storage conditions that ensure the tools are not damaged over time need
to be defined.
A heat survey should be performed on all tools. The survey should verify the tool can meet
required heat-up rates and that the temperature is uniform throughout the tool surfaces.
Thermocouples should be placed at the coldest and hottest locations.
A method for accurately positioning the plies is required. It is imperative that the ply orientation
is within the engineering requirements, as strength and modulus properties are sensitive to
orientation. A method must be used that allows for transfer of the tool zero direction to the panel
and then to the machining equipment. Scribe lines on the tool and thin metal strips embedded
along one edge of the panel are two methods that have been successfully used.
9
Detailed tool preparation procedures are necessary. Areas to cover include tool inspection,
verification that all tooling details are available and in good working condition, mold release
application procedure (acceptable mold releases should be listed in the materials section), and
tool clean-up procedures. See table 3 for a checklist of tooling control items.
TABLE 3. RECOMMENDED TOOLING CONTROL CHECKLIST
Method of cleaning, solvents, cleaning cloths
Mold release agents
Tool heat survey results (location of coldest and hottest thermocouples)
Scribe marking
Template inspection intervals
Template surface conditions
Template material
Templates, number of
Tool heat-up rate
Tool inspection intervals
Tool surface conditions
Tool, method of moving, transportation
Tooling condition (mold release applied, and no mold release)
Tooling configuration (flat, vertical)
Tooling status identified (approved, unapproved)
Tooling storage conditions and locations
Tooling, expansion and contraction rate
Tooling material
Location and number of vacuum ports
Orientation rosette
Tool repair procedures
Tool inspection intervals
2.7 PANEL LAMINATION.
2.7.1 Lay-Up of Plies.
Frozen prepreg in sealed containers must be warmed to room temperature prior to opening to
prevent condensation from getting onto the prepreg. The length of time required to warm the
prepreg to ambient temperature is a function of the roll size; the larger the roll, the longer the
thaw time. Small rolls (5 to 10 pounds) can reach room temperature in 2 to 3 hours, while 30- to
50-pound rolls can take over 6 hours.
Plies should be cut on surfaces specifically dedicated to cutting plies. Plies should not be
trimmed or cut on the tool to ensure the tool or underlying plies are not damaged. If trimming of
10
plies on the tool is required, a clean metal shim should be placed between the prepreg and tool
surface. Individual plies should be identified and marked at the time of cutting.
The plies are collated onto the tool as defined in the detailed work instructions. Care should be
taken to accurately align the plies with respect to the tool zero-degree reference direction. See
reference 6 for a description of the reference bar method used to maintain ply alignment through
the panel fabrication and subsequent specimen machining operations. Prior to collation, the plies
are inspected for visual defects. Damaged plies are repaired or replaced as applicable. Plies are
debulked (compacted with vacuum pressure) as applicable. After each ply is collated and the
backing paper is removed, its surface is inspected for foreign objects.
The panel is bagged for cure as specified in the detailed work instructions. The panel should be
clearly marked to ensure traceability.
Thermocouples should be placed such that the panel temperature can be directly measured. The
thermocouples should be placed against the prepreg to ensure the material is heated to the
specified temperatures. At least two thermocouples should be used for each panel. If the panel
is large, 4 to 6 thermocouples are recommended. In cases where the tool contains embedded
thermocouples, a heat survey should be performed to validate that the embedded thermocouples
are an accurate measurement of the panel temperature.
2.7.2 Cure Cycle.
The panel is cured to the applicable cure cycle. Prior to cure, a leak check should be performed
on the vacuum bag. All leaks should be repaired before performing the cure cycle. Leaks
through the tool can create as serious problems as leaks around the edges of the bag. The cure
cycle should define heat-up rate, temperature range, time, vacuum, pressure, and cool-down rate.
Although oven temperature is sometimes used, ideally, the cure time and temperature should be
controlled by the slowest (lagging) thermocouple in the cure run. Temperature, vacuum, and
pressure should be recorded as a function of time for the complete cure cycle.
2.7.3 Panel Identification.
Each panel should be marked with a unique identification number. This identification number
will provide traceability to the requesting document, prepreg batch number, cure cycle, and test
type. Lines can also be drawn at an angle across the laminate surface to aid in identifying
specimen location within the panel.
2.8 INSPECTION AND PROCESS MONITORING.
This section defines the recommended examinations, inspections, and tests to be performed in
order to verify that the processes, as well as the equipment, specified by the engineering
requirements are followed. Each inspection or examination given in this section should be tied
directly to a requirement specified by the process instructions.
11
2.8.1 Responsibility for Inspection.
Organizations or personnel responsible for the performance of the inspections and process
monitoring examinations should be identified. When personnel other than quality assurance
inspectors are given the responsibility to perform inspection, they must be trained in the
performance of quality assurance tasks and must be supported with complete documentation on
the required inspection process.
2.8.2 Panel Inspection.
After cure, it is strongly recommended that the panel be inspected to ensure all engineering
requirements have been met prior to machining test specimens. Inspections or tests are
performed on each panel to verify they are acceptable for submission to the machining step.
They include panel thickness, surface flatness, completeness of cure, and NDI for internal
defects and embedded materials. Test panels that fail to meet these requirements will result in
test data that is not representative of the material.
The tests recommended in this section are not necessarily applicable to production parts (though
they are often used for developmental parts and first part qualification). They are used to verify
that the panel is acceptable for further testing and are required to provide a complete database.
The panel should be visually inspected for surface defects that could be sources for premature
test failures. If possible, specimens should be machined from areas outside of these defects.
Panel density and resin content (fiber volume) should also be determined. This requires that
small samples (1/2 by 1/2 inch) be machined from the panel.
Panel thickness is verified at a number of locations. The measurement locations should be
equally spaced (within reason) around the panel. The actual thickness is converted to a per ply
thickness by dividing the average measured thickness by the number of plies. The panel should
not be tested if it fails to meet the required per ply thickness. The thickness data can also be
interrogated to determine degree of flatness. Again, failure to meet engineering thickness
requirements, results in the panel not being tested.
Each panel should be nondestructively inspected for internal defects, such as porosity, foreign
objects, or delaminations. NDI standards should be fabricated as early as possible within the
certification process. These NDI standards consist of panels fabricated with known defects so
that the nondestructive methods and criteria can be calibrated relative to defect severity and
panel thickness. It is imperative that NDI indications (such as sound loss for ultrasonic through
transmission) be tied to a known physical defect type, location, and size. See SAE ARP 5605 for
guidance in the fabrication of solid laminate NDI references and SAE ARP 5606 for guidance in
the fabrication of honeycomb sandwich NDI standards [7 and 8].
Completeness of cure can be verified by measuring the glass transition temperature (Tg) and in
some cases degree of cure using differential scanning calorimetry (DSC).
Ply lay-up orientation can be verified by polishing an edge for examination under a microscope
(20 to 50X).
12
All records should be reviewed to verify the panels were fabricated in compliance with the
engineering requirements. The records should include material batch/lot traceability, panel
identification, cure cycle parameters, and ply count.
Machining diagrams should be developed for each panel and included in the detail work
instructions. The type of machining equipment used to machine the panels into specimens is
recorded along with cutting tool type, speeds, and feed rates. After machining, the specimens are
inspected for damaged edges and dimensionally inspected. Specimens failing to meet
engineering requirements should be replaced.
Table 4 is a list of items to control for the machining of test specimens.
TABLE 4. RECOMMENDED ITEMS TO BE CONTROLLED FOR MACHINING
Use of and type of coolant
Marking of trim lines
Type of tools for trimming, hole drilling
Tools for control of cutting surfaces
Tools, inspection intervals
Method for transferring the 0 direction to each specimen
2.8.3 Monitoring Procedures.
The following areas should be reviewed and monitoring procedures instituted.
EquipmentAll equipment requirements requiring verification should be listed for
inspection. Calibration frequency is also defined.
MaterialsAll material requirements requiring verification should be listed for
inspection. This would include freezer storage temperature, storage life, out-time life at
time of collation and cure, performance of receiving inspection tests, use of approved
consumable materials, and batch numbers.
FacilitiesAll facility requirements requiring verification should be listed for inspection.
This would include clean room temperature and humidity and cleaning schedule.
ToolingAll tooling requirements requiring verification should be listed for inspection.
This would include performance of heat surveys to document temperature uniformity
during the cure cycle, performance of tool visual inspections, and monitoring of storage
conditions.
2.8.4 Documentation.
All information required to be recorded and reported should be listed. The time span all process
records should be retained is also specified. A period of 7 years is recommended.
13
2.8.5 Test Methods.
All test methods specified within the process instructions should be listed. The preferred
practice is to reference industry test method specifications or standards such as those published
by ASTM. Exceptions to standard methods should be clearly documented.
3. PRODUCIBILITY VALIDATION GUIDELINES.
Certification and qualification test programs typically concentrate on the validation of
mechanical properties and allowables. Of equal importance is the validation of processing
parameters and part producibility. This section presents recommended producibility validation
guidelines, which address (1) verification of material attributes that affect producibility and (2)
qualification and verification of fabricator processes to ensure the part meets the expected
properties.
3.1 PRODUCIBILITY QUALIFICATION TESTS.
An important element of the material qualification effort is the verification of the materials
producibility. During the material qualification test program, thin flat constant thickness test
panels are used to develop material performance properties, i.e., strength and stiffness. It is the
inherent characteristics, or attributes, of the prepreg that govern the materials producibility.
Some of the material attributes that influence producibility are tack, level of impregnation, resin
flow properties, and surface texture.
In addition to validating the influence of prepreg attributes, scale-up effects on producibility
must also be addressed during the qualification process. The fabrication of constant thickness
flat panels does not fully demonstrate the materials ability (or inability) to be fabricated into
large-scale production laminates. These scale-up effects could include laminate thickness, part
area, internal ply drop off features, and in the case of sandwich structure, core density, ramp
angle, and prepreg surface characteristics. Due to their nature, the performance of mechanical
property tests obtained from flat test panels does not assess the impact of processing scale-up
effects. But these effects can have a major impact on producibility of large-scale components
and thus the structural performance of the component.
There typically exists a need for a panel design that will discriminate these material attributes
and their ability or robustness to accommodate scale-up effects. This panel can then be
fabricated as part of the qualification test program. The objective of the Discriminator Panel is
to distinguish one material from another similar (or like) material by exposing their differences
as related to producibility. The difference in material attributes is often quantified by the amount
of porosity within the Discriminator Panel. For example, significant porosity may occur when
the material is used to fabricate complex, contoured components even though small test panels
made with the same material were void-free. In many cases, prepreg materials suitable for
fabrication of monolithic laminates will not produce high-quality honeycomb sandwich panels.
Therefore, the Discriminator Panel needs to be representative of the intended application. It
must be representative in thickness and contour and contain ply drop off features representative
of the proposed component designs. It must be fabricated with procedures representative of
14
production methods (e.g., do not use hand layup for the panel when the production method is
automated tape laying).
Instead of fabricating a Discriminator Panel, an actual part can be fabricated to address prepreg
material processing attributes. This allows a direct evaluation of scale-up effects. The down
side to using an actual part is that the performance of any evaluation is tied to tool availability. It
is rare that a part is designed, and applicable tooling is available, when the material qualification
program is being performed. Material selection decisions are typically made prior to the start of
the design process.
Tests typically performed on the Discriminator Panel could include NDI and thickness, glass
transition temperature, degree of cure, and mechanical property tests.
The Discriminator Panel can also be used in conjunction with test panels to assess the impact of
processing or material changes. In cases where there is the need to assess a change in
impregnation processing parameters, the Discriminator Panel often will be more discerning to
the changes than mechanical properties from test panels.
3.2 FABRICATOR QUALIFICATION.
During many building block certification efforts, the initial fabrication of coupon test panels,
elements, and components is performed at a different location or fabricator than the production
components. This could result in material property values that are not representative of those
produced by the full-scale production facility. It is recommended that the part fabricators also be
qualified as part of the certification process. The fabricator qualification consists of three
elements: (1) verification of coupon performance property equivalency, (2) verification of
component structural equivalency, and (3) verification of engineering compliance. Each of these
elements is discussed below.
3.2.1 Performance Property Equivalency.
Performance property equivalency is verified by the fabrication and testing of test panels. The
purpose of this is to validate that their processes yield properties, which are from the same
statistical population as the qualification and allowables data. The process of validating the
material properties for an alternate process or facility is termed equivalency testing (see
references 1 and 6). An audit to verify the compliance with the process specification
requirements is also recommended as part of the fabricator qualification process.
3.2.2 Component Structural Equivalency.
Verification of component structural equivalency can only be accomplished by the destructive
testing of a full-scale component. This is not the same as testing an element specimen or
subcomponent. As a rule, the design of elements and subcomponents includes provisions for
load introduction that would not be a part of the production design. In addition, the tooling
concepts are not always identical between test parts and production parts. Therefore, it is
typically necessary to destructively inspect a part fabricated with production tooling and
processes.
15
The objectives for performing a destructive inspection on a part are to
verify the performance properties established during coupon- and element-level testing
(qualification and allowables) are the same in the component.
quantify internal (hidden) defects or indications detected by NDI, i.e., validate NDI
methods.
validate laminate physical properties (resin content and thickness).
verify fiber path continuity within joints and complicated geometries (typically features
that cannot be verified through a Discriminator Panel or by NDI).
A typical geometric feature that can only be evaluated by a destructive inspection is a cocured
joint. Cocured joint quality is strongly dependent on the tooling approach and design features. It
is only through the fabrication of full-scale hardware with the actual production tooling that
cocured joint strength can be evaluated. Another design feature that is difficult to evaluate
without the assistance of a destruct article is the honeycomb sandwich panel where foaming
adhesive is used to splice honeycomb core to solid structure (such as ribs or spars). In many
cases, the foaming adhesive will migrate from the core to spar bond line into the skin to spar
bond line. This migration is detrimental to bond line strength and almost impossible to detect by
standard NDI techniques. It is only through destructive inspection that it can be verified that the
processing techniques imposed to prevent foaming adhesive migration actually work.
The fabrication of a destruct article provides a great opportunity to access the impact of
anticipated manufacturing defects on structural performance. Known defects can be placed
within the destruct article during fabrication. NDI procedures can then be validated through the
detection and identification of these known defects. Element test specimens can then be
machined from the article such that the test section contains the known defects. The impact of
the defect on structural performance can then be determined. Data of this nature is very valuable
to the material review board disposition process. In some cases, the defect can be repaired prior
to testing. Typical defects to include within the destruct article include:
Delaminations
Wrinkles or ply waviness
Thickness variation
Tool mark off (resin ridge or surface wrinkle)
Porosity or voids
Foreign inclusions
The destructive inspection process typically includes:
Full dimensional inspection
NDI
16
Section cuts through areas indicted by the NDI and areas of complex geometry and layup,
and bonded or cocured joint regions
Excising coupons for mechanical property testing
Coupons typically excised include glass transition temperature, degree of cure as determined by
DSC, resin content, short beam strength, compression strength, open hole tension or compression
strength, and flexural strength. If possible, element or joint specimens should also be excised for
testing.
Prior to the performance of any mechanical property coupon or element tests, it is critical that the
pass/fail criteria be established. These criteria must be tied to the analysis approach and
allowables used to design the part and also must account for part configuration effects. Thought
must be given to what action will be taken if the criteria are not met. Do not go into these tests
without thinking through the benefits and consequences of these tests. Selection of which tests
to perform is also a critical element of this process.
If other fabrication techniques, such as bonding or mechanical fastening, are used, they should
also be verified. The development of requirements for those additional fabrication techniques is
beyond the scope of this document but should be included in the destructive inspection process.
Destructive inspections should be performed on part families. A typical part family might be all
cocured assemblies and another might be all honeycomb sandwich assemblies. A destructive
inspection is typically performed on one part that is representative of a given process, design,
and tooling approach. The destructive inspection is repeated for each major change in tooling,
design, alternate materials, fabricator location (or company), or process. A Discriminator Panel
can be used to assess minor material and process changes. The destructive inspection does not
have to be performed on the first assembly (component) produced, but it should be performed
such that the results are evaluated prior to the assembly of the component on the first aircraft
assembled.
3.2.3 Engineering Compliance.
The final step in the producibility validation process is to verify that the as-produced parts
comply with engineering drawings and specifications. This can be accomplished through a First
Article Inspection (FAI). The objective of the FAI is to verify that everything has come together
(specifications, tooling, process instructions, process parameters, and design details) to produce a
conforming part. The FAI is a physical examination of the part to verify engineering design (fit,
form, and function, e.g., as fabricated weight, finish, physical interfaces, and workmanship).
This is normally accomplished by NDI in conjunction with an expanded dimensional inspection
and a through audit of the fabrication records. The FAI should expand the types, number, and
locations of physical measurements beyond those identified as key characteristics. Each part
type should go through the FAI process.
17
4. REFERENCES.
1. McCarvill, W., Ward, S., Bogucki, G., and Tomblin, J., Guidelines and Recommended
Criteria for the Development of a Material Specification For Carbon Fiber/Epoxy
Unidirectional Prepregs, DOT/FAA/AR-02/109, March 2003.
2. MIL-HDBK-17, Composite Materials Handbook.
3. Cseke, Jr., Peter, Introduction to Establishing Air Force Clean Facilities for Composite
Processing, Department of the Air force, Air Force Research Laboratory (Hill Air Force
Base, Utah).
4. AC 21-26, Quality Control for the Manufacture of Composite Structure, Department of
Transportation, Federal Aviation Administration.
5. ISO 14644-1, Cleanrooms and Associated Controlled EnvironmentsPart 1:
Classification of Air Cleanliness, British Standards Institution on ERC Specs and
Standards, March 2001.
6. Tomblin, J.S., Ng, Y.C., and Raju, K.S., Material Qualification and Equivalency for
Polymer Matrix Composite Material Systems, DOT/FAA/AR-00/47, April 2001.
7. ARP 5605, Solid Composite Laminate NDI Reference Standards, SAE International,
400 Commonwealth Drive, Warrendale, PA 15096-0001.
8. ARP 5606, Composite Honeycomb NDI Reference Standards, SAE International, 400
Commonwealth Drive, Warrendale, PA 15096-0001.
Related Information
AIR 4938, Composite and Bonded Structure Technician/Specialist Training Document, SAE
International, 400 Commonwealth Drive, Warrendale, PA 15096-0001.
AIR 5278, Composite and Bonded Structure Engineer: Training Document, SAE International,
400 Commonwealth Drive, Warrendale, PA 15096-0001.
AIR 5279, Composite and Bonded Structure Inspector: Training Document, SAE
International, 400 Commonwealth Drive, Warrendale, PA 15096-0001.
ARP 5089, Composite Repair NDT/NDI Handbook, SAE International, 400 Commonwealth
Drive, Warrendale, PA 15096-0001.
ASTM C 274, Standard Terminology of Structural Sandwich Constructions, ASTM
International, 100 Barr Harbor Drive, West Conshohocken, PA 19429-2959.
ASTM D 3878, Standard Terminology for Composite Materials, ASTM International, 100
Barr Harbor Drive, West Conshohocken, PA 19429-2959.
18
ASTM D 3993, Standard Terminology Relating to Fabric Defects, ASTM International, 100
Barr Harbor Drive, West Conshohocken, PA 19429-2959.
ASTM D 5687, Standard Guide for Preparation of Flat Composite Panels with Processing
Guidelines for Specimen Preparation, ASTM International, 100 Barr Harbor Drive, West
Conshohocken, PA 19429-2959.
ASTM D 6507, Standard Practice for Fiber-Reinforced Orientation Codes for Composite
Materials, ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19429-2959.
ASTM E 1309, Standard Guide for Identification of Fiber-Reinforced Polymer-Matrix
Composite Materials in Databases, ASTM International, 100 Barr Harbor Drive, West
Conshohocken, PA 19429-2959.
ASTM E 1434, Standard Guide for Recording Mechanical Test Data of Fiber-Reinforced
Polymer-Matrix Composite Materials in Databases, ASTM International, 100 Barr Harbor
Drive, West Conshohocken, PA 19429-2959.
ASTM E 1471, Standard Guide for Identification of Fibers, Fillers, and Core Materials in
Computerized Property Databases, ASTM International, 100 Barr Harbor Drive, West
Conshohocken, PA 19429-2959.
MIL-STD-961, Department of Defense Standard Practice Defense Specification.
George Lubin, ed., Handbook of Composites (Van Norstrand Reinhold Company, 1982).
ASTM D 123, Standard Terminology Relating to Textiles, ASTM International, 100 Barr
Harbor Drive, West Conshohocken, PA 19429-2959.
ASTM E 473, Standard Terminology Relating to Thermal Analysis, ASTM International, 100
Barr Harbor Drive, West Conshohocken, PA 19429-2959.
ASTM D 883, Standard Terminology Relating to Plastics, ASTM International, 100 Barr
Harbor Drive, West Conshohocken, PA 19429-2959.
ASTM D 907, Standard Terminology of Adhesives, ASTM International, 100 Barr Harbor
Drive, West Conshohocken, PA 19429-2959.
SACMA SRM 10, SACMA Recommended Method for Fiber Volume, Percent Resin Volume
and Calculated Average Cured Ply Thickness of Plied Laminates, Suppliers of Advanced
Composite Materials Association.
19
5. GLOSSARY.
This glossary is a compilation of terms with their definitions used within this report and of
general interest. Definitions for this glossary were obtained from a variety of sources, which are
noted at the end of the definition. Refer to MIL-HDBK-17 for a more complete listing of terms
and their definitions.
Autoclave, na closed vessel for conducting a chemical reaction or other operation under
pressure and heat (Handbook of Composites).
B Stage, nan intermediate stage in the reaction of a thermosetting resin in which the material
softens when heated and swells when in contact with certain liquids but does not entirely fuse or
dissolve. Materials are usually procured to this stage to facilitate handling and processing prior
to final cure. See also C Stage (MIL-HDBK-17).
bag, vthe process of enclosing the ply layers within a flexible container. See also vacuum bag
(ASTM D 5687).
baseplate, na flat plate on which a laminate is laid up. See also mold (ASTM D 5687).
bleeder, ncloth that allows matrix to flow into it for the purpose of removing excess matrix
from the laminate. Net resin prepreg systems do not require the use of bleeder materials (ASTM
D 5687).
braided fabric, na cloth constructed by a braiding process (ASTM D 3878).
breather, ncloth which allows even gas flow over the layup surface. The breather also helps
minimize bag punctures by protecting the bag from sharp points (ASTM D 5687).
Discussion: Typically within the bagging layup sequence, the breather material is a
mixture of materials. The layer closest to the laminate is a lightweight glass fabric, such
as Style 120, in order to minimize mark off on the laminate. The remaining layers are
materials selected for their ability to transport gasses under pressure and elevated
temperature. Typical materials are heavy weight glasses such as Style 1000 or synthetic
nonwoven materials.
breather string, na glass string connected from the laminate to a breather in the bagging lay-up.
It provides a path for gasses to be transferred from the laminate while minimizing matrix flow
(ASTM D 5687).
broadgoods, nprepreg material (fabric or unidirectional) where the width is greater than 24
inches. See also tape.
C Stage, nthe final stage of the curing reaction of a thermosetting resin in which the material
has become practically infusible and insoluble. See also B Stage (MIL-HDBK-17).
caul plate, na flat plate used to provide a flat surface to the top of the laminate during laminate
consolidation or cure (ASTM D 3878).
20
CFRCode of Federal Regulations.
cloth, na piece of textile fabric containing woven reinforcement without a load transferring
matrix (ASTM D 5687).
composite material, na substance consisting of two or more materials, insoluble in one
another, which are combined to form a useful engineering material possessing certain properties
not possessed by the constituents. Composites are subdivided into classes on the basis of the
form of the structural constituents; Laminar: Composed of layer or laminar constituents;
Particular: The dispersed phase consists of fibers; Flake: The dispersed phase consists of flat
flakes; Skeletal: Composed of a continuous skeletal matrix filled by a second material (ASTM D
3878 and Handbook of Composites).
consolidation, vthe process of forming individual plies into one solid composite laminate. For
polymeric based composite materials, consolidation is the compaction of the plies under pressure
at elevated temperature until the polymer matrix material is cured.
cure, vto change the physical properties of a polymer by chemical reaction, which may be by
condensation, polymerization, or vulcanization; usually accomplished by the action of heat and
catalyst, alone or in combination, with or without pressure (ASTM D 907).
cured ply thickness (CPT), nthe theoretical thickness of an individual ply, which is a function
of the fiber areal weight, resin content, fiber density, and resin density.
Discussion: cured per ply thickness is determined from the fiber areal weight, fiber
volume, and fiber density:
FV
FAW
CPT
f
25400
=
Where:
CPT is theoretical cured ply thickness (inches)
FAW is fiber areal weight (g/m
2
)
25400 is a units conversion factor
f
is the fiber density (g/cc)
FV is fiber volume (fraction, e.g., 0.61)
Or cured per ply thickness can also be determined from the fiber areal weight, resin
content, fiber density, and resin density:
( )
(
(
+ =
RC
RC FAW
CPT
r f
1
1
25400
21
Where:
CPT is theoretical cured ply thickness (inches)
FAW is fiber areal weight (g/m
2
)
25400 is a units conversion factor
f
is the fiber density (g/cc)
r
is the resin density (g/cc)
RC is resin weight content (fraction, e.g., 0.33)
The actual cured ply thickness is determined by measuring the laminate thickness and
dividing it by the number of plies (see SACMA SRM 10).
Fiber volume and resin content are related by the fiber and resin densities:
(
(
(
=
1
1
1
r f
f
RC RC
RC
FV
Where:
FV is fiber volume (fraction, e.g., 0.61)
f
is the fiber density (g/cc)
r
is the resin density (g/cc)
RC is resin weight content (fraction, e.g., 0.33)
dam, na solid material (such as silicone rubber, steel, or aluminum) used in the lay-up to
contain the matrix material within defined boundaries during laminate consolidation (ASTM D
5687).
DARDesignated Airworthiness Representative. FAA designees authorized to conduct
conformity inspections on behalf of the FAA.
debulk, vprocess of decreasing voids between lamina before laminate consolidation through
use of vacuum or by mechanical means. Lamina can be debulked at ambient or elevated
temperature (ASTM D 5687).
degree of cure (), nin thermoset polymers, the quantity of heat of reaction of the unreacted
resin remaining after a reaction (cure cycle) compared to the total available quantity of heat of
reaction expended by the complete reaction (cure) of a reacted resin.
Discussion: The degree of cure of a laminate can be obtained from differential scanning
calorimetry (DSC) data. In order to obtain the degree of cure of a laminate, the baseline
or total heat of reaction released by the complete curing of the resin (or prepreg) must
first be obtained. This total heat of reaction is determined from the DSC curve. It is
important to obtain the total heat of reaction from a sample that is of the same resin
content as the laminate in question. This is typically accomplished by testing a sample of
22
the prepreg used to fabricate the laminate. The laminate in question is then tested to
determine the partial heat of reaction. The DSC heating rate used to determine the
baseline heat of reaction and partial heat of reaction must be the same. Typically a
heating rate of 10C per minute is used. The degree of cure is calculated as follows:
|
|
.
|
\
|
= 100 100
T
P
H
H
Where:
is the percent degree of cure (ranges from 0% to 100% with 100% being
fully cured)
H
P
is the heat of reaction released by the partially cured sample (laminate in
question) expressed in Joules
H
T
is the total heat of reaction released by the uncured resin expressed in
Joules (baseline)
Resin formulations commonly used in the aerospace industry rarely reach a degree of
cure of 100%. Values of 95% to 98% are common. It should be noted that determining
degree of cure by DSC is not considered the most repeatable test and is best limited to
research investigations and not used as a production test. Depending on the
circumstances, measurement of the glass transition temperature may be the best method
to determine if a laminate is fully cured.
DERDesignated Engineering Representative. FAA designees authorized to approve
engineering data.
differential scanning calorimetry (DSC), na technique in which the temperature difference
between the substance and a reference material is measured as a function of temperature while
the substance and reference material are subjected to a controlled-temperature program (ASTM
E 473).
DMIRDesignated Manufacturing Inspection Representative. FAA designees authorized to
conduct conformity inspections on behalf of the FAA.
end, nin fabric, an individual warp yarn (single or ply) or cord (ASTM D 123).
ETDElevated Temperature Dry.
ETWElevated Temperature Wet.
FAAFederal Aviation Administration.
fabric, nin textiles, a planar structure consisting of yarns or fibers (ASTM D 123).
23
FEP, nfluorinated ethylenepropylene.
Discussion: fluorinated ethylenepropylene is a fluorocarbon polymer commonly known
by its DuPont trade name Teflon
FEP.
fiber, nin textiles, a generic term for any one of the various types of matter that form the basic
elements of a textile and that is characterized by having a length at least 100 times its diameter
(ASTM D 123).
fiber areal weight (FAW), nthe weight per area of the fiber reinforcement within a composite,
expressed as grams per square meter or ounces per square yard. See also prepreg areal weight.
fiber content, nthe amount of fiber present in a composite expressed either as a percent by
weight or percent by volume. This is sometimes stated as a fraction, that is, fiber volume
fraction (ASTM D 3878).
fiber volume fraction (FV or V
f
), nsee fiber content (ASTM D 3878).
filament, na fibrous form of matter with an aspect ratio >10 and an effective diameter <1 mm
(ASTM D 3878).
fill, nin a woven fabric, (1) the yarn running from selvage to selvage at right angles to the
warp and (2) fiber inserted by the shuttle during weaving also designated as filling (ASTM D
3878, MIL-HDBK-17, and ASTM D 5687).
flip/flop, vthe process of alternating plies through an angle orientation of 180 during laminate
lay-up. This practice is commonly used if the material of the same width as the laminate has a
recurring flaw. The process changes the location of the flaw so that it does not unduly affect the
laminate structure (ASTM D 5687).
glass transition, nthe reversible change in an amorphous polymer or in amorphous regions of a
partially crystalline polymer from (or to) a viscous or rubbery condition to (or from) a hard and
relatively brittle one (MIL-HDBK-17).
Discussion: The glass transition generally occurs over a relatively narrow temperature
region and is similar to the solidification of a liquid to a glassy state; it is not a phase
transition. Not only do hardness and brittleness undergo rapid changes in this
temperature region but other properties, such as thermal expansibility and specific heat,
also change rapidly. This phenomenon has been called second order transition, rubber
transition, and rubbery transition. The word transformation has also been used instead of
transition. Where more than one amorphous transition occurs in a polymer, the one
associated with segmental motions of the polymer backbone chain or accompanied by the
largest change in properties is usually considered to be the glass transition
(ASTM D 883).
glass transition temperature (Tg), nthe approximate midpoint of the temperature range over
which the glass transition takes place (MIL-HDBK-17).
24
Discussion: The glass transition temperature can be determined readily only by
observing the temperature at which a significant change takes place in a specific
electrical, mechanical, or other physical property. Moreover, the observed temperature
can vary significantly depending on the specific property chosen for observation and on
details of the experimental technique (for example, rate of heating and frequency). Three
common methods for determining Tg are Thermal Mechanical Analysis, Differential
Scanning Calorimetry, or Dynamic Mechanical Analysis.
knit, va textile process that interlocks, in a specific pattern loop, by means of needles or wires
(ASTM D 3878).
knitted fabric, na cloth constructed by a knitting process (ASTM D 3878).
lamina, na subunit of a laminate consisting of one or more adjacent plies of the same material
with identical orientation (ASTM D 3878).
laminate, nany fiber or fabric-reinforced composite consisting of lamina (plies) with one or
more orientations with respect to some reference direction (ASTM D 3878).
lamination, vsee consolidation.
laminate coordinate axes, na set of coordinate axes, usually right-handed Cartesian, used as a
reference in describing the directional properties and geometrical structure of the laminate.
Usually the x-axis and the y-axes lie in the plane of the laminate, and the x-axis is the reference
axis from which ply angle is measured (ASTM D 3878).
laminate principal axis, nthe laminate coordinate axis that coincides with the direction of
maximum in plane Youngs modulus (ASTM D 3878).
lay-up, n(1) the stack of plies in specified sequence and orientation before cure or
consolidation; (2) the complete stack of plies, bagging material, and so on before cure or
consolidation; and (3) a description of the component materials, geometry, and so on of a
laminate (ASTM D 3878).
lay up, vto stack plies of material in specified sequence and orientation (ASTM D 3878).
lay-up code, na designation system for abbreviating the stacking sequence of laminated
composites (ASTM D 3878).
mandrel, na form, fixture, or male mold used as the base for production of a part in processes
such as lay-up or filament winding (ASTM D 3878).
material form, nthe contour, arrangement, and structure of an unconsolidated composite
material, especially with regard to the geometry and nature of the reinforcement. Factors
considered part of the material form include, but are not limited to, reinforcement length (for
discontinuous reinforcements), tow size or count, fabric areal weight, fabric style, reinforcement
content, and ply thickness (ASTM D 3878).
25
matrix, nthe continuous constituent of a composite material, which surrounds or engulfs
embedded filler or reinforcement (ASTM D 3878).
matrix content, nthe amount of matrix present in a composite expressed either as a percent by
weight or percent by volume. Standard practice is to specify matrix content as weight percent
(ASTM D 3878).
MIDOManufacturing Inspection District Office for the FAA.
MOLMaterial Operational Limit.
mold, nthe support structure that holds the laminate or lay-up during laminate consolidation
process (ASTM D 5687).
MRBMaterial Review Board.
NISTNational Institute of Standards and Technology.
nondestructive inspection (NDI), v to identify and measure abnormal conditions within a
laminate without degrading or impairing the utility of the laminate.
nonperforated FEP, na nonporous fluorinated ethylenepropylene film used as a release film in
the bagging lay-up.
Discussion: fluorinated ethylenepropylene is a fluorocarbon polymer commonly known
by its DuPont trade name Teflon
FEP.
nonperforated TFE, na nonporous tetrafluoroethylene film used as a release film in the
bagging lay-up (ASTM D 5687).
Discussion: tetrafluoroethylene is a fluorocarbon polymer commonly known by its
DuPont trade name Teflon
TFE.
nonporous TFE-coated cloth, na cloth coated with tetrafluoroethylene used as a release
material in the bagging process (ASTM D 5687).
nonwoven fabric, na cloth constructed by bonding or interlocking, or both (but not
interlacing), fiber by any combination of mechanical, chemical, thermal, or solvent means
(ASTM D 3878).
panel, na uniformly contoured composite laminate, typically flat (ASTM D 5687).
peel ply, na cloth with release capabilities, usually used in conjunction with laminates
requiring secondary bonding (ASTM D 5687).
perforated FEP, na porous fluorinated ethylenepropylene film used in the bagging process that
allows gasses or excess matrix materials to escape (flow) from a laminate during consolidation
while protecting the laminate from physical bonding to other items such as caul plates.
26
perforated TFE, na porous tetrafluoroethylene film used in the bagging process that allows
gasses or excess matrix materials to escape (flow) from a laminate during consolidation while
protecting the laminate from physical bonding to other items such as caul plates (ASTM D
5687).
plied yarn, na yarn formed by twisting together two or more single yarns in one operation
(ASTM D 3878).
ply, nin laminar composites, the constituent single layer as used in fabricating or occurring
within a composite structure (ASTM D 3878).
ply coordinate axes, na set of Cartesian coordinates, two of which lie within the plane of the
ply, one axis of which is parallel to the principal fiber direction and the other axis perpendicular
to the principal fiber direction (the third axis is through the plys thickness) (ASTM D 3878).
ply count, nin laminated composite materials, the number of plies or lamina used to construct
the composite (ASTM D 3878).
ply orientation, nthe acute angle (theta) including 90 between a reference direction and the
ply principal axis. The ply orientation is positive if measured counterclockwise from the
reference direction and negative if measured clockwise (ASTM D 3878).
ply principal axis, nthe ply coordinate axis that coincides with the direction of maximum in
plane Youngs modulus. For balance weave fabric, either warp or fill direction may be chosen
(ASTM D 3878).
polymer, nan organic material composed of molecules characterized by the repetition of one or
more types of monomeric units (MIL-HDBK-17).
polymerization, na chemical reaction in which the molecules of a monomer(s) are linked
together in repeating units to form larger molecules (ASTM D 907).
porosity, na condition of trapped pockets of air, gas, or vacuum within a solid material, usually
expressed as a percentage of the total nonsolid volume to the total volume (solid plus nonsolid)
of a unit quantity of material (MIL-HDBK-17).
porous TFE-coated cloth, na porous cloth coated with tetrafluoroethylene used in the bagging
process that allows gasses or excess matrix materials to escape (flow) from a laminate during
consolidation. It differs from perforated TFE in that it gives a textured surface to the laminate
(ASTM D 5687).
prepreg, na ready to mold or cure fibrous reinforcement impregnated with a polymeric matrix.
Its form may be sheet, tape, or tow. For thermosetting matrices, it has been partially cured to a
controlled viscosity called B stage (ASTM D 3878 and MIL-HDBK-17).
prepreg areal weight (PAW), nthe weight per area of the prepreg composite material,
expressed as pounds per square foot or the inverse square feet per pound. Used as a conversion
factor to convert prepreg area to prepreg weight. See also fiber areal weight.
27
Discussion: Prepreg areal weight is a function of resin content and fiber areal weight:
RC
FAW
PAW
=
1
Where:
PAW is prepreg areal weight (g/m
2
)
FAW is fiber areal weight (g/m
2
)
RC is resin weight content (fraction, e.g., 0.33)
To convert g/m
2
to lb/ft
2
multiply by 204.81 x 10
-6
.
reinforcement, nin a composite material, the discrete constituent of a composite material,
either fiber or particle, which is contained within the continuous matrix (ASTM D 3878).
resin, na solid or pseudosolid organic material, often of high molecular weight, which exhibits
a tendency to flow when subjected to stress, usually has a high softening or melting range, and
usually fractures conchoidally (ASTM D 3878).
resin content (RC), nsee matrix content (ASTM D 3878).
sealant, na high-temperature material used to seal the edges of a vacuum bag to a base plate
during consolidation (ASTM D 5687).
selvage, nthe woven edge portion of a fabric parallel to the warp (ASTM D 3878).
single yarn, nan end in which each filament follows the same twist (ASTM D 3878).
stacking sequence, nthe arrangement of ply orientations and material components in a
laminate specified with respect to some reference direction (ASTM D 3878).
staggered, adjthe description of ply placement where the joints are not positioned in the same
in-plane location through some specified thickness of the laminate (ASTM D 5687).
tape, nprepreg material (typically unidirectional material) equal to or less than 24 inches in
width. Also see broadgoods.
textile, na general term applied to fibers and organized assemblies of fibers with sufficient
integrity to retain the organization (ASTM D 3878).
thermoplastic, na plastic that repeatedly can be softened by heating and hardened by cooling
through a temperature range characteristic of the plastic, and that in the softened state can be
shaped by flow into articles by molding or extrusion for example (ASTM D 883).
thermoset, na class of polymers that, when cured using heat, chemical, or other means,
changes into a substantially infusible and insoluble material (ASTM D 3878).
28
tow, nin fibrous composites, a continuous, ordered assembly of essentially parallel, collimated
filaments, normally without twist and of continuous filaments (ASTM D 3878).
traveler, na coupon with the same nominal thickness and, preferably, width as the test
specimen, made of the same material, and processed similarly to the specimen except usually
without tabs or gages. The traveler is used to measure mass changes during environmental
conditioning when it is impractical to measure these changes on the actual specimen (ASTM D
5687).
traveler panel, n(aka witness panel) a panel that is subjected to the same conditions as a part or
group of parts to allow destructive testing to verify processing.
unidirectional, nany fiber-reinforced composite with all the fibers aligned in a single direction.
Both prepreg material and consolidated laminates can be described as being unidirectional.
vacuum bag, na low gas permeable material used to enclose and seal the lay-up during a
consolidation or debulking cycle (ASTM D 5687).
vacuum couple, nthe mechanical connection that seals the vacuum source to the lay-up during
a consolidation or debulking cycle (ASTM D 5687).
vitrification, nthe point during polymerization where the Tg of the polymer rises above the
temperature of cure.
void, nany pocket of enclosed gas or air within a composite (ASTM D 3878).
void content, nthe volume percentage of voids in a composite (ASTM D 3878).
warp, n(1) the yarn running lengthwise in a woven fabric; (2) a group of yarns in long lengths
and approximately parallel, put on beams or warp reels for further textile processing including
weaving, knitting, twisting, dyeing, and so forth (ASTM D 3878).
warp surface, nthe ply surface that shows the larger area of warp tows with respect to fill tows
(ASTM D 3878).
warp surface nesting, vprocess of laying up fabric plies in an alternating pattern where the
warp surface is placed up and then for the next ply the warp surface is placed down, thus nesting
the plies.
weave, vinterlaces, in a specific pattern, strands or yarns orientated in two or more directions
in a planar textile process (ASTM D 3878).
woven fabric, n a cloth constructed by a weaving process (ASTM D 3878).
yarn, nin fibrous composites, a continuous, ordered assembly of essentially parallel,
collimated filaments, normally with twist, and either discontinuous or continuous filaments
(ASTM D 3878).
29/30
APPENDIX AEXAMPLE PROCESS SPECIFICATION
The appendix contains an example process specification for the fabrication of carbon fiber-
reinforced epoxy composite test laminates. The example specification is based on the format
defined in MIL-STD-961 as shown below.
1.0 Scope
2.0 Applicable Documents
3.0 Requirements
3.1 Personnel
3.2 Required Materials
3.3 Required Equipment
3.4 Facilities
3.5 Tooling
3.6 Required Procedures
4.0 Quality Assurance
4.1 Responsibility for Inspection
4.2 Inspection
4.3 Documentation
4.4 Test Methods
5.0 Notes
It should be noted that this format is not the only acceptable format and is provided as an
acceptable format widely used in industry. The format defined by SAE is also widely used
within industry.
While the example specification contains specific requirements, it is not implied that the
specified requirements are the only acceptable requirements for the fabrication of quality
composite laminates. Many requirements are a function of the specific material being processed,
e.g., cure temperature and time. The requirements do not identify objective values for many
requirements in this example; however, the more requirements that include objective values, the
better the control.
As a rule, composite laminate fabrication process specifications are not stand-alone documents.
They will reference companion specifications for processes that warrant process specifications in
their own right. An example process that warrants its own specification is nondestructive
inspection. The example process specification contains references to companion (or sub tier)
specifications, and since it is an example, the companion specifications do not exist.
A-1
Example Process Specification for the
Fabrication and Acceptance of Carbon Fiber Reinforced
Epoxy Composite Test Laminates
1.0 SCOPE
1.1 This specification establishes the requirements and procedures for the fabrication
and acceptance of carbon fiber reinforced composite test laminates. Laminates
processed in accordance with this specification are used in the qualification of
new materials, establishment of mechanical property equivalency, or batch
acceptance.
2.0 APPLICABLE DOCUMENTS
2.1 The following documents form a part of this specification to the extent specified.
ASTM D 792Density and Specific Gravity (Relative Density) of Plastics by
Displacement
ASTM D 3171Constituent Content of Composite Materials
SACMA SRM 10SACMA Recommended Method for Fiber Volume, percent
Resin Volume and Calculated Average Cured Ply Thickness of Plied Laminates
SACMA SRM 18SACMA Recommended Method for Glass Transition
Temperature (Tg) Determination by DMA of Oriented FiberResin Composites
3.0 REQUIREMENTS
3.1 Personnel
Fabrication of composite laminates shall be performed by qualified personnel who
have passed both written and practical proficiency tests and possess the skills and
job knowledge necessary to ensure acceptable workmanship.
3.2 Required Materials
This section lists the approved specific materials needed to perform the operations
specified within this specification along with the specific trade names and
sources.
3.2.1 Material Listing
a) Prepreg Test Material
b) Film Adhesive
c) Mold Release AgentsBulk Liquid Wipe-On
d) Release FilmNonporous Fluorinated Ethylene Propylene (FEP)
e) Release FilmNonporous Teflon-Coated Glass Fabric
A-2
f) Release Fabric (Mold release coated)
g) Peel PlyNylon Fabric (uncoated)
h) Peel PlyPolyester Fabric (uncoated)
i) Dam MaterialsSealant Tape
j) Dam MaterialsCork
k) Pressure Sensitive TapeGeneral Purpose
l) Pressure Sensitive TapeTeflon Film
m) Pressure Sensitive TapeNonporous Teflon-Coated Glass Fabric
n) Pressure Sensitive TapeDouble Sided
o) BleederGlass Fabric (style 120 and 7781)
p) BreatherPolyester Nonwoven
q) Nylon Vacuum Bag Film
r) Vacuum Bag Sealant Tape
s) Wiping MaterialsCotton Cloth Wipers
t) Wiping MaterialsCheesecloth, Cotton, Bleached
u) Wiping MaterialsPaper and Synthetic Nonwoven Wipers
v) Synthetic Gloves
w) Barrier Hand Creams
3.2.2 Material Requirements
3.2.2.1 All prepreg and adhesive materials are required to have passed their applicable
receiving inspection requirements as defined in the material specification and
have been released for use.
3.2.2.2 Prepreg and adhesive materials that are frozen shall be warmed to ambient
temperature for a minimum of two hours. Large rolls (in excess of 25 pounds)
can require up to six hours to reach ambient temperature The materials are
considered to be at ambient temperature when there are no traces of moisture or
condensation on the outside of the polyethylene storage bag. During ply collation
the prepreg and adhesive material shall be stored at ambient temperature in the
environmentally controlled lay-up room in sealed polyethylene storage bags.
3.2.2.3 Splices are prohibited unless authorized by the requesting engineering documents.
3.2.2.4 Gaps between adjacent pieces of prepreg in the same layer and parallel to the
fibers shall be kept to a minimum and shall not exceed 0.100 inches. Edge splice
overlaps shall not exceed 0.030 inches. Edge splices of consecutive plies of the
same orientation shall not be located directly over each other. They shall be
staggered by at least 2.0 inches.
3.2.2.5 Prepreg plies containing defects shall be replaced.
3.2.2.6 Prepreg storage life and ambient exposure time shall be recorded and monitored
to ensure compliance with the ambient working life requirements established in
the applicable material specification.
3.2.2.7 Prepreg plies shall be handled in a manner to prevent damage.
A-3
3.2.2.8 Mold releases are not to be applied within the ply collation room or area.
3.3 Required Equipment
3.3.1 Equipment Listing
a) Vacuum source and supply (minimum of 22 inches of mercury)
b) Tool plate (also called base plate)
c) Caul Plate
d) Thermocouples
e) Reference bar (metal)
f) Cutting tools (knives or automated cutting system)
g) Work tables
h) Vacuum PortsThrough The Bag Fittings
i) Autoclave
j) Air Circulating Oven
3.3.1 Equipment Requirements
3.3.1.1 The autoclave shall be capable of holding the base plate with bagged lay-up. The
autoclave shall be able to provide the required vacuum, pressure, and heat. The
control system shall be calibrated on a defined schedule.
3.3.1.2 The oven shall be capable of holding the base plate with bagged lay-up. The oven
shall be able to provide the required vacuum and heat. The control system shall
be calibrated on a defined schedule.
3.3.1.3 Ensure the cutting system blade is sharp and working correctly. The prepreg
material should not be distorted when being cut. If the material is being distorted,
then the cutting blade is to be replaced.
3.4 Facilities Control
3.4.1 Collation and bagging of the laminate shall be performed in a controlled
environment in accordance with a company process specification.
3.4.2 Airborne particles are to be kept at a minimum within the controlled lay-up
environment. Filters are to be used within the air circulation system and are to be
replaced on a defined schedule that ensures they perform as required. The floor
shall be sweep twice during a work shift. All work surfaces are to be dusted at the
same time the floors are swept.
3.5 Tooling
3.5.1 Base plate and caul plates shall be either aluminum or steel with a roughness of
125 RMS or less. The base plate should have a minimum thickness of 0.25 inches
and a maximum thickness of 0.50 inches with a flatness tolerance of 0.002 inches.
A-4
The caul plate should have a minimum thickness of 0.125 inches and a maximum
thickness of 0.25 inches with a flatness tolerance of 0.002 inches.
3.5.2 Metal reference bar shall be either aluminum or steel with a thickness equal or
greater than the composite lay-up.
3.6 Required Procedures
3.6.1 Process Instructions
3.6.1.1 A detailed sequential fabrication procedure shall be generated for the fabrication
of each item. The fabrication procedure shall contain inspection buy-off
sequences in accordance with Section 4.2. The fabrication procedures shall
contain provisions for the recording of the following information: material batch
number, material date of manufacture, material cumulative ambient out time at
time of cure, date of collation and cure, general observations of the prepreg
material handling characteristics, tool identification number, type and method of
applying tool mold release, technician identity, and environmental conditions
within the lay-up room during ply collation.
3.6.2 Tool Preparation
3.6.2.1 Mold release shall be applied to all new reference bars, base plates and caul
plates. Reapply the mold release if during its use panels begin to stick. Apply the
mold release in accordance with the manufactures instructions. Apply a light
coating of air-dry release agent to the tools before each lay-up operation. This
coating is to be uniform, smooth, and free of streaks. A solid FEP release film
may be placed on the tool surface in lieu of applying the air-dry release agent.
Inspect the tools for gouges and imperfections that could transfer to the composite
laminate. Repair the defects before using the tool.
THIS PROCESS SHALL NOT BE PERFORMED WITHIN THE LAYUP
ROOM.
3.6.3 Material Preparation
3.6.3.1 Cut the required plies using an automated digital numerically controlled ply
cutting system or by hand using templates. Record the prepreg ambient out-time
at the time of ply cutting. Identify each ply.
3.6.4 Lay-up Procedure
3.6.4.1 Collate the prepreg plies in the sequence and orientation as specified in the
process instructions. Take care to align the ply orientation to the reference edge
tool bar. Use templates, laser projection devises, or overlays to assist in the
collation process. Proper ply orientation is essential to generating quality test
data.
A-5
3.6.4.2 Smooth the ply by hand or with a squeegee or roller. Remove the backing paper
(or poly as applicable). Retain the backing paper for ply count verification after
collation. Visually inspect the ply for foreign objects. Remove any foreign
objects. Notate on the process instructions completion of the ply collation.
3.6.4.3 Continue with collation of the remaining plies. Take care to not trap air between
subsequent plies by tacking the ply at one edge then working the ply down
towards the opposite edge. Vacuum debulk the laminate stack every 4 plies.
Debulk the prepreg as follows:
a) Place a layer of porous release material over the prepreg plies. Extend the
layer beyond the boundaries of the laminate.
b) Place at least one layer of dry glass cloth or synthetic breather over the porous
release material. Extend to the vacuum ports.
c) Place a nylon vacuum bag, sealed with vacuum bag sealant tape, over the
laminate. A vacuum-debulking box may be used in lieu of the nylon vacuum
bag.
d) Apply vacuum (22 to 29 inches of mercury) to the laminate for a maximum of
ten minutes.
e) Remove vacuum debulking materials and continue ply collation.
3.6.4.4 After the last ply has been collated, place a glass yarn (string) along the edges of
the laminate (except for the edge with the reference bar). Extend the glass yarn
far enough to reach the area between where the edge dam will be located and the
vacuum bag sealant tape.
3.6.4.5 Place the edge dam around the three remaining edges of the ply stack-up. Make
sure the dam is in contact with the ply stack-up edge. Place one layer of FEP
release film over the laminate. Extend the film beyond the dams. Seal the release
film to the top of the edge dam.
3.6.4.6 Apply the caul plate on top of the release film. The caul plate should fit inside the
edge dams.
3.6.4.7 Place dry fiberglass cloth or synthetic breather over the caul plate. Extend the
breather material to just inside where the vacuum bag sealant tape will be located.
Make sure the breather material covers the glass yarn from 3.5.4.4.
3.6.4.8 Prepare two dry fiberglass cloth vacuum port pads for inclusion into the bagging
material stack-up. The vacuum port pads should be roughly 4 by 4 inches and
four to six plies thick. Place the two vacuum pad ports on top of the breather
material at opposite corners of the base plate. Place the bottom portion of the
vacuum port on the port pads.
A-6
3.6.4.9 Place vacuum bag sealant tape around the periphery of the lay-up. Do not remove
the paper release layer from the sealant tape at this time.
3.6.4.10 Place a nylon vacuum bag over the top of the entire lay-up. Extend the bag
beyond the perimeter of the vacuum bag sealant tape. Tack the bag to top of the
vacuum bag sealant tape on one side of the lay-up. Pull the bag tight and seal to
the top of the remaining vacuum bag sealant tape sealing the vacuum bag on all
four sides.
3.6.4.11 Attach the upper portion of the vacuum port to the lower portion by cutting a hole
through the bagging film directly over the bottom portion at both locations.
Attach a static vacuum gage at one of the ports and a vacuum line to the other
vacuum port and slowly evacuate the bagged lay-up, making sure there are no
wrinkles in the bagging film. Once the vacuum stabilizes at a minimum of 20
inches of mercury, perform a leak check.
3.6.4.12 Perform the leak check as follows:
a) Pull 20 to 29 inches of mercury vacuum,
b) Isolate the system, wait two minutes and record the initial vacuum level,
c) Wait two additional minutes and record the change (drop) in vacuum,
d) Acceptable leakage rate is less than 1.0 inches of mercury two minutes,
e) If the leakage rate is 1.0 inches of mercury or greater in two minutes, locate
the leak and repair as required,
f) Repeat the leak check, until the acceptable leakage rate is achieved.
3.6.4.13 Transport the bagged assembly to the autoclave for cure.
3.6.5 Cure Procedure
3.6.5.1 Autoclave cure the panel as follows:
a) Place bagged assembly in the autoclave.
b) Hook up thermocouples and vacuum lines. Remove the static gage and hook
up both vacuum ports. One line will be an active line, while the second line
will function as the static line.
c) Pull 20 to 29 inches of mercury on the bagged assembly.
d) Perform the leak check of 3.6.4.12.
e) Increase the autoclave pressure to 80 5 psi. When the pressure reaches 25
psi, vent the vacuum to atmosphere.
A-7
f) When the pressure reaches 75 psi, increase the temperature to 350 10F at
1 to 5F per minute. Begin the hold when the coldest thermocouple reaches
340F. Hold at 350 10F for 120 to 140 minutes based on the coldest
thermocouple in the autoclave run.
g) At the end of the hold at 350 10F for 120 to 140 minutes, cool to 150F in
no less than 35 minutes.
h) Remove the assembly from the autoclave for unbagging.
3.6.5.2 Record the following information:
a) Cure serial number
b) Autoclave identification
c) Material (material specification and product name)
d) Batch and roll number
e) Cure date
3.6.6 Panel Identification
3.6.6.1 Identify each panel with its unique identification number.
3.6.7 Inspection
3.6.7.1 Inspect each panel as defined in Table 1.
Table 1 - Panel Inspection Requirements
Inspection Test Sample Size
Number of
Samples
Test Method
Cured Per Ply Thickness Entire Panel 10 locations 4.4.1
Glass Transition
Temperature
0.50 by 2.0 in. Two 4.4.2
Resin Content 0.5 by 0.5 in. Three 4.4.3
Density 0.5 by 0.5 in. Three 4.4.4
3.6.7.2 Inspection requirements shall be as defined in the applicable material
specification. Panels failing to meet the applicable requirements shall not be
tested.
3.6.7.2 Nondestructively inspect each panel by Through Transmission Ultrasonics (TTU)
in accordance with company procedures.
A-8
3.6.8 Machining
3.6.8.1 Machine the panel into test specimens as specified in the Engineering
documentation.
4.0 QUALITY ASSURANCE
4.1 Responsibility for Inspection
The Quality Assurance Organization has the responsibility to ensure that the
quality requirements specified in this specification are met. Quality Assurance
shall verify that the fabrication of the composite is performed by qualified
technicians.
4.2 Inspection
Quality Assurance shall perform the necessary inspections to verify the following
procedures are performed in compliance with this specification.
4.2.1 Monitoring ProceduresEquipment
4.2.1.1 Quality Assurance shall survey ovens, autoclaves, freezers, and nondestructive
inspection equipment monthly to assure proper calibration procedures have been
performed.
4.2.1 Monitoring ProceduresMaterials
4.2.2.1 Quality Assurance shall verify that the following requirements are met:
a) Only properly qualified prepreg materials are used in the fabrication
b) The plies are collated in the orientation specified in the engineering
requirements document,
c) Splices and gaps within a ply are in accordance with 3.2.2.3 and 3.2.2.4,
d) The prepreg material is warmed to room temperature prior to the opening of
the storage container in accordance with 3.2.2.2
e) The lay-up does not contain any visible foreign material contamination, and
f) The material ambient out-time is recorded in accordance with 3.2.2.6.
4.2.3 Monitoring ProceduresFacilities
4.2.3.1 Quality Assurance shall verify that the lay-up room is in accordance with 3.4.
4.2.4 Monitoring ProceduresTooling
A-9
4.2.1.1 Quality Assurance shall verify that the tooling complies with the requirements of
3.5.
4.3 Documentation
4.3.1 Quality Assurance shall monitor and maintain records on the following
information.
a) Prepreg batch and roll number
b) Prepreg cumulative freezer storage life and cumulative ambient out-time
c) Cure cycle information of 3.6.5.2
d) Inspection results of 3.6.7
4.4 Test Methods
4.4.1 Cured Per Ply ThicknessDetermine cured per ply thickness in accordance with
SACMA SRM 10.
4.4.2 Glass Transition TemperatureDetermine glass transition temperature in
accordance with SACMA SRM 18.
4.4.3 Resin ContentDetermine laminate resin content in accordance with ASTM D
3171.
4.4.4 DensityDetermine laminate density in accordance with ASTM D 792.
5.0 NOTES
None.
A-10
APPENDIX BTYPICAL PROCESSING PARAMETER TOLERANCES
Parameter Typical Application Tolerance
temperature cure temperature 10F
pressure autoclave pressure during
cure cycle
5 psig
time length of cure -0, + 15 minutes
vacuum vacuum level during cure
cycle
2 inches of Hg
angle ply orientation 2
B-1/B-2