Performance-Related Product Specification Tensar Triax Tx160 Geogrid
Performance-Related Product Specification Tensar Triax Tx160 Geogrid
11
General
The geogrid is manufactured in accordance with a management system Tensar TriAx Geogrid which complies with the requirements of BS EN ISO 9001:2008. The geogrid is manufactured from a punched polypropylene sheet, which is then oriented in three equilateral directions so that the resulting ribs of the triangular apertures have a high degree of molecular orientation which continues through the mass of the integral node. The properties contributing to the performance of a mechanically stabilised layer are:
Geometrical
Rib pitch (mm) Mid-rib depth (mm) Mid-rib width (mm) Nodal thickness (mm) Rib shape Aperture shape Open area aspect ratio (%)(11)
Longitudinal
40 -
Diagonal
40 1.8 1.1
Transverse General
1.5 1.3 3.1 rectangular triangular >85 90 390 >0.75 45550
Mechanical
Junction efficiency (%) (1,9) Aperture stability (N.mm/deg @ 500 N.mm) (2,9) Isotropic stiffness ratio (3,8) Mean radial secant modulus at low strain (kN/m @ 0.5% strain)(3,10)
Durability
Resistance Resistance Resistance Resistance of to to to chemical degradation(4) weathering(5) oxidation installation damage(6) 96% 98% 90% >87%
1/2
TN/PR_Triax_TX_160/25.08.11
Notes Load transfer capability determined in accordance with GRI-GG2 and GRI-GG1 and expressed as a percentage of ultimate tensile strength. In-plane torsional rigidity measured in accordance with U.S. Army Corps of Engineers Methodology for measurement of Torsional Rigidity, (Kinney, T.C. Aperture stability Modulus ref 3, 3.1.2000). Stiffness, (secant modulus), is determined in a test conducted in any in-plane direction and which records the maximum and minimum radial values when tested in accordance with ISO 10319:1996 Resistance to loss of ultimate load capacity when subjected to chemically aggressive environments in accordance with testing to EN12960 as part of a durability assessment in accordance with ISO13434:1999 7.3 Resistance to loss of ultimate load capacity when subjected to ultra-violet light and weathering in accordance with testing to EN12224 as part of a durability assessment in accordance with ISO13434:1999 7.2 Resistance to loss of radial stiffness when subjected to the effects of installation from a graded engineering fill. The procedure is in accordance with BS 8006:1995 and the radial stiffness is derived as in Note 3. All geometrical and durability values are quoted as typical. Declared as the ratio between the minimum and maximum value on a sample at the 95% confidence limit. Declared at 95% confidence limit. Declared at mean standard deviation Determination of the open area aspect ratio of a geogrid, Tensar International Ref QTC004, 2011
Determination of the suitability of any information or material for the use contemplated or the manner of use is the sole responsibility of the user.Tensar is a registered
2/2