Stone Waste in India For Concrete With Value Creation Opportunities
Stone Waste in India For Concrete With Value Creation Opportunities
I. INTRODUCTION Marble/granite/kotastone has been commonly used as a building material since the ancient times. The industrys disposal of the marble/granite/kotastone powder material, consisting of very fine powder, today constitutes one of the environmental problems around the world. Marble / Granite blocks are cut into smaller blocks in order to give them the desired smooth shape. During the cutting process about 25% the original marble mass is lost in the form of dust. This mixture of slurry coming out during cutting is called stone waste. Use of stone waste in various engineering applications can solve the problem of disposal of stone waste and other purposes. Stone waste can be used in concrete to improve its strength and other durability factors. Stone waste can be used as a partial replacement of cement or replacement of fine aggregate and as a supplementary addition to achieve different properties of concrete. The use of the replacement materials offer cost reduction, energy savings, arguably superior products, and fewer hazards in the environment. Concrete is a composite construction material composed of cement, aggregate (generally a coarse aggregate made of gravels or crushed rocks such as limestone, or granite, plus a fine aggregate such as sand), water, and/or admixtures. Concrete is made by mixing: Cement, water, course fine aggregates and admixtures (if required). The objectives are to mix these materials traditionally to make concrete that is easy to: Transport, place, compact, finish and to give a strong and durable product. The proportionate quantity of each material (i.e. Cement, water and aggregates) affects the properties of hardened concrete. In the building industry, Marble/Granite has been commonly used for various purposes like flooring, cladding etc., as a building material since the ancient times. Marble/Granite stone industry generates both solid waste and stone slurry. Whereas solid waste results from the rejects at the mine sites or at the processing units, stone slurry is a semi
113
ISSN: 2278-621X
liquid substance consisting of particles originating from the sawing and the polishing processes and water used to cool and lubricate the sawing and polishing machines. During the process of cutting, in that original stone waste / Granite mass is lost by 25% in the form of dust. Therefore the scientific and industrial community must commit towards more sustainable practices. So it is necessary to dispose the stone waste / Granite waste quickly and use in the construction industry. II. EXPERIMENTAL MATERIALS 2.1 Materials 2.1.1 Stone waste The principle waste coming in the stone industry is stone itself, specifically in the forms of overburden, screening residual, stone fragments. Stone wastes are generated as a waste during the process of cutting and polishing. It is estimated that 175 million tons of quarrying waste are produced each year, and although a portion of this waste may be utilized on-site, such as for excavation pit refill or berm construction, The disposals of these waste materials acquire large land areas and remain scattered all around, spoiling the aesthetic of the entire region. It is very difficult to find a use for all scrap stone and fines produced. Stone waste can be used in concrete to improve its strength and other durability factors. Stone waste can be used as a partial replacement of cement or as a partial replacement of fine aggregates and as supplementary addition to achieve different properties of concrete.
Figure: 1. Stone waste Source: Uma Marble, GIDC, Vallabh Vidyanagar, Anand, Gujarat TABLE1 PROPERTIES OF STONE WASTE
Constituent
Value (%)
SiO2 36.96 Al2O3 0.49 Fe2O3 3.40 CaO 28.60 MgO 6.08 SO3 0.15 LOI 22.16 TOTAL 97.78 Source: GEO TEST HOUSE, Gorwa estate Baroda 2.1.2 Cement (OPC) The most common cement used is an Ordinary Portland Cement (OPC). The Ordinary Portland Cement of 53 grades (SANGHI cement OPC) conforming to IS: 8112-1989 is being used. Many tests were conducted on cement; some of them are consistency tests, setting tests, soundness tests, etc.
114
ISSN: 2278-621X
Sr. No.
1 2 3
Physical properties of SANGHI OPC 53cement Specific gravity Standard consistency (%) Initial setting time (hours, min) Final setting time (hours, min) Compressive strength N/mm2 at 28 days
2.1.3 Aggregate Aggregates are the important constituents in concrete. They give body to the concrete, reduce shrinkage and effect economy. One of the most important factors for producing workable concrete is a good gradation of aggregates. Good grading implies that a sample fraction of aggregates in required proportion such that the sample contains minimum voids. Samples of the well graded aggregate containing minimum voids require minimum paste to fill up the voids in the aggregates. Minimum paste means less quantity of cement and less water, which are further mean increased economy, higher strength, lower shrinkage and greater durability. 2.1.4 Coarse Aggregate The fractions from 20 mm to 4.75 mm are used as coarse aggregate. The Coarse Aggregates from crushed Basalt rock, conforming to IS: 383 is being used. The Flakiness and Elongation Index were maintained well below 15%.
115
ISSN: 2278-621X
Figure: 4 Grit
2.1.5 Fine aggregate Those fractions from 4.75 mm to 150 microns are termed as fine aggregate. The river sand and crushed sand are used in combination as fine aggregate conforming to the requirements of IS: 383. The river sand is washed and screen, to eliminate deleterious materials and oversize particles.
Property
Coarse Aggregate 20 mm 10 mm down down 7.54 3.19 2.76 1741 2.69 1711
116
ISSN: 2278-621X
1.20
1.83
1.35
2.1.6 Water Water is an important ingredient of concrete as it actually participates in the chemical reaction with cement. Since it helps to from the strength giving cement gel, the quantity and quality of water are required to be looked into very carefully. III. DESIGN MIX A mix M25 grade was designed as per Indian Standard method (IS 10262-2009) and the same was used to prepare the test samples. The design mix proportion is done in Table 4.
TABLE-4 DESIGN MIX PROPORTION FOR (M25 MIX)
W (Lit)
C (Kg/m3)
F.A. (Kg/m3)
C.A. (Kg/m3)
479 485.75 1197.03 By Weight, 191.60 [gms] 0.40 1 1.01 2.50 By Volume, [m3] W= Water, C= cement, F.A. = Fine Aggregate, C.A. = Coarse Aggregate
TABLE-5 CONCRETE DESIGN MIX (M25 MIX) PROPORTIONS
Sr. No.
Concrete Design Mix Proportion C.T. W/C ratio C 1.00 0.90 0.80 0.70 0.60 0.50 F.A. 1.01 1.01 1.01 1.01 1.01 1.01 C.A. 2.50 2.50 2.50 2.50 2.50 2.50 S.W. 0.10 0.20 0.30 0.40 0.50
1 2 3 4 5 6
A0 A1 A2 A3 A4 A5
C.T.= Concrete Type, C= cement, F.A. = Fine Aggregate, C.A. = Coarse Aggregate, S.W. = Stone waste IV EXPERIMENTAL SET UP
TABLE-6 DESIGN MIX PROPORTION FOR VARIOUS CONCRETE
Sr. No. 1 2 3 4 5 6
Concrete Type A0 A1 A2 A3 A4 A5
OPC cement Replacement with Stone waste Standard Concrete 10% replacement 20% replacement 30% replacement 40% replacement 50% replacement
117
ISSN: 2278-621X
V. EXPERIMENTAL METHODOLOGY The evaluation of stone waste for use as a replacement of OPC cement material begins with the concrete testing. Concrete contains OPC cement, water, fine aggregate, coarse aggregate and grit. With the control concrete, i.e. 10%, 20%, 30%, 40%, and 50% of the OPC cement is replaced with stone waste ,the data from the stone waste is compared with data from a standard concrete without stone waste. Three cube samples were cast on the mould of size 150*150*150 mm for each 1:1.01:2.50 concrete mix with partial replacement of OPC cement with a w/c ratio as 0.40 were also cast. After about 24 h the specimens were de-moulded and water curing was continued till the respective specimens were tested after 7,14 and 28 days for compressive strength test. 5.1 Compressive strength Compressive strength tests were performed on compression testing machine using cube samples. Three samples per batch were tested with the average strength values reported in this paper. The loading rate on the cube is 35 N/mm2 per min. The comparative studies were made on their characteristics for concrete mix ratio of 1:1.01:2.50 with partial replacement of cement with stone waste as 10%, 20%, 30%, 40% and 50%.
Figure: 6 Setup of Compression Strength Testing Machine TABLE -7 COMPRESSIVE STRENGTH OF CUBES (150X150X150) FOR M25 MIX AT 7, 14, 28 DAYS
Concrete Type
A0 A1 A2 A3 A4 A5
118
ISSN: 2278-621X
Figure: 7 % Replacement of stone waste V/S Compressive Strength (N/mm2) of Concrete for M25 mix at 7, 14 and 28 days
V. ECONOMIC FEASABILITY
TABLE- 8 COSTS OF MATERIALS
Sr. No. 1 2 3 4
Materials Cement (SANGHI OPC 53 grade) Fine aggregate (Regional ) Coarse aggregate (Regional ) Stone waste
TABLE - 9 TOTAL COST OF MATERIALS FOR M25 DESIGNE MIX CONCRETE (1:1.01:2.50) PER m3 C. T. A0 A1 A2 A3 A4 A5 Consumption of Design Mix Proportions For M25 Concrete (1:1.01:2.50) C F.A. C.A. S.W. 479.00 485.75 718.22 431.10 485.75 718.22 47.90 383.20 485.75 718.22 95.80 335.50 485.75 718.22 143.70 287.40 485.75 718.22 191.60 239.50 485.75 718.22 239.50 Total Cost /m3 4135.12 3838.14 3541.16 3244.18 2947.20 2650.22 % Cost change 0 -7.18 -14.36 -21.54 -28.72 -35.90
C.T. = Concrete Types, C= Cement, F.A. = Fine Aggregate, C.A. = Coarse Aggregate, S.W. =Stone waste VI. CONCLUSION Based on limited experimental investigations concerning the compressive strength of concrete, the following observations are made regarding the resistance of partially replaced stone waste: (a) Compressive strength increase when replacement with stone waste percentage increases when compare to traditional concrete. (b) From this test, replacement of OPC cement with this stone waste material provides maximum compressive strength at 30% replacement.
119
ISSN: 2278-621X
(c) People approach to the stone waste in concrete will be more and more as it will strengthen the building at economical cost. (d) Environmental effects of wastes and disposal problems of waste can be reduced through this research and make the environment green. (e) It will reduce the wastage and solve dumping problem of the industry. VII. ACKNOWLEDGMENTS The Authors thankfully acknowledge to Dr.C.L.Patel, Chairman, Charutar Vidya Mandal, Er.V.M.Patel, Hon.Jt. Secretary, Charutar Vidya Mandal, Mr. Yatinbhai Desai, Jay Maharaj construction, Dr.B.K.Shah, Associate Professor, Structural Engineering Department, B.V.M. Engineering College, Vallabh Vidyanagar, Gujarat, India for their motivations and infrastructural support to carry out this research. REFERENCES
[1] [2] [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] [14] [15] [16] [17] [18] Abrar Awol Using Marble Waste Powder in Cement And Concrete Production March 2011 Azza I. Kandil and Tarek H. Selim Characteristics of the Marble Industry In Egypt Bahar Demirel The Effect of the Using Waste Marble Dust as Fine Sand on the Mechanical Properties of the Concrete International Journal of the Physical Sciences Vol. 5(9), Pp. 1372-1380, 18 August, 2010 Baboo Rai, Khan Naushad H, Abhishek Kr, Tabin Rushad S, Duggal S.K Influence Of Marble Powder/Granules in Concrete Mix International Journal of Civil and Structural Engineering Volume 1, No 4, 2011 IS: 8112-1989, Specifications for 43-Grade Portland cement, Bureau of Indian Standards, New Delhi, India. IS: 383-1970, Specifications for coarse and fine aggregates from natural sources for concrete, Bureau of Indian Standards, New Delhi, India. IS: 10262-1982, Recommended guidelines for concrete mix design, Bureau of Indian Standards, New Delhi, India. IS: 1199-1959, Indian standard methods of sampling and analysis of concrete, Bureau of Indian Standards, New Delhi, India. IS: 516-1959, Indian standard code of practice- methods of test for strength of concrete, Bureau of Indian Standards, New Delhi, India. Elham Khalilzadeh Shirazi Reusing of Stone Waste in Various Industrial Activities 2011 2nd International Conference on Environmental Science and Development IPCBEE Vol.4 (2011) Hanifi Binici, Hasan Kaplan and Salih Yilmaz Influence of Marble and Limestone Dusts as Additives on Scientific Research and Essay Vol. 2 (9) ISSN 1992-2248 Accepted 6 August M. Shahul Hameed And A. S. S. Sekar Properties Of Green Concrete Containing Quarry Rock Dust And Marble Sludge Powder As Fine Aggregate Arpn Journal of Engineering and Applied Sciences Vol. 4, No. 4, June 2009 M. Belachia And H. Hebhoub Use of the Marble Wastes in the Hydraulic Concrete 6th International Advanced Technologies Symposium (IATS11), 16-18 May 2011, Elaz, Turkey Mamta B. Rajgor , Prof. Jayeshkumar Pitroda A Study of Utilization Aspect of Stone Waste in Indian Context International Global research analysis, Volume : 2 Issue : 1 Jan 2013 ISSN No 2277 8160, PP 50-54 Nutan c patel , Prof. Jayeshkumar Pitroda A Technical study on querying and processing of marble & its waste Incorporating with concrete International Journal Global Research analysis (GRA) Volume: 2 Issue: 2 Feb 2013, ISSN: 2277-8160 Nutan c patel , Amit Raval, Prof. Jayeshkumar Pitroda Marble Waste : opportunities for development of low cost concrete International Journal Global Research analysis (GRA) Volume: 2 Issue: 2 Feb 2013, ISSN: 2277-8160 Prof. P.A. Seriously, Ataur Rahman B, Rakesh D. Gupta Partial Replacement Of Cement With Marble Dust Powder International Journal of Advanced Engineering Research and Studies April-June, 2012 Prof. J R Pitroda, Dr L B Zala, Dr F S Umrigar (2012), Hypo Sludge Management: Opportunities For Developing Low Cost Concrete With Glass Fibres International Journal Global Research Analysis, (GRA), Volume: 1, Issue: 7, Dec 2012, ISSN No 2277 8160, pp-5658. Prof. Jayeshkumar Pitroda, Dr. L.B.Zala, Dr.F.S.Umrigar (2012), Experimental Investigations on Partial Replacement of Cement with Fly Ash in Design Mix Concrete International Journal of Advanced Engineering Technology,IJAET/Vol.III/ Issue IV/Oct.-Dec., 2012/126-129 Prof. Jayeshkumar Pitroda, Dr. L.B.Zala, Dr.F.S.Umrigar (2013), Innovative Use of Paper Industry Waste (Hypo Sludge) in Design Mix Concrete International Journal of Advanced Engineering Technology, IJAET / Vol. IV/ Issue I / Jan.-March., 2013 / 31-35 Rania Hamza, Salah El-Haggar, Safwan Khedr Utilization of Marble And Granite Waste in Concrete Bricks 2011 International Conference on Environment And Bioscience IPCBEE Vol.21 (2011)
120
ISSN: 2278-621X