TALAT Lecture 3704: Deep Drawing
TALAT Lecture 3704: Deep Drawing
Deep Drawing
15 pages, 16 figures
Advanced Level
prepared by
K. Siegert and S. Wagner, Institut für Umformtechnik, Universität Stuttgart
Objectives:
Prerequisites:
Table of Contents
TALAT 3704 2
3704.01 Definitions and Fundamentals of the Deep Drawing Process
Deep drawing is one of the most important processes for forming sheets metal parts. It is
used widely for mass production of hollow shapes in the packing industry, automotive
industry etc.. According to the definition in DIN 8584, deep drawing is the tensile-
compressive forming of a sheet blank (or, depending on the material, also of foils or
plates) to a hollow body open on one side or the forming of a pre-drawn hollow shape
into another with a smaller cross-section without an intentional change in the sheet
thickness, see Figure 3704.01.01. The process limitations are laid out by the conditions
required to transmit the force into the forming zone. The drawing force necessary for the
forming is transmitted from the punch to the work-piece base and from there to the
forming zone in the flange. The resulting limiting deformation in the force application
zone has nothing to do with the depletion of the forming capacity of the material in the
forming zone. The process limits are reached when the largest applied drawing force
cannot be transmitted to the forming zone in the flange. From this condition, one can
derive the characteristic behaviour of deep drawing, that a number of forming steps can
be carried out consecutively without an intermediate annealing step. Subdividing the
whole process into a number of drawing steps has the advantage that the tensile force
acting at the force application zone can be reduced. Most special processes which have
been developed, make use of this fact [1].
alu
Definition of Deep Drawing 3704.01.01
Training in Aluminium Application Technologies
TALAT 3704 3
Classification of the Deep Drawing Process
According to DIN 8584 deep drawing processes are classified as outlined in Figure
3704.01.02
Based on the type of force application, the deep drawing processes can be divided into
three methods:
Generally, only the first two methods are used, deep drawing with active energy being of
no practical importance [1].
The general terms and definitions of deep drawing with a blankholder are illustrated in
Figure 3704.01.03. The deformation in the flange is a result of tangential compressive
stresses and radial tensile stresses, when the sheet blank with diameter Do is drawn
through the die to a cup with the punch diameter do. The blankholder force FN prevents
the formation of folds. The stress due to the blankholder pressure is small compared to
the radial and tangential stresses.
TALAT 3704 4
Deep Drawing with Blankholder
FN FSt FN FN FN
FSt
blankholder
drawing punch
blank
d0
drawing ring (die)
s0
rm rSt
flange
body
D0 dm base
Da
Starting diameter of blank D0 Punch edge radius rSt
Punch diameter d0 Die diameter dm
Sheet thickness of blank s0 Die radius rm
Punch force FSt Drawing gap Uz
Blankholder force FN Momentary flange diameter Da
Source: IFU Stuttgart
alu
Forming zone
Bending zone
alu
TALAT 3704 5
Stress Zones during Deep Drawing
During the drawing process the cup can be divided into four characteristic zones, see
Figure 3704.01.04, with different state of stress and deformation:
− The blankholder force FN prevents folds of „type 1“.
− The forming zone is the sheet material between the flange outer edge (D = f(h)) and
the outlet of the material to be formed from the drawing ring radius („die shoulder“)
− The surface area of the drawn part is about the same as that of the starting blank.
Consequently, the sheet thickness remains almost constant.
− The base of the drawn part is formed on the same principles that apply to mechanical
drawing.
During the deep drawing of cylindrical cups, the parts of the blank under the
blankholder are subjected to a radial tensile stress and a tangential compressive stress,
see Figure 3704.01.05. A minimum normal stress must be applied in order to prevent
buckling of the sheet (folds of „type 1“). This normal stress, however, also affects the
friction between the blankholder and sheet as well as between sheet and drawing ring.
Generally, a higher normal stress, i.e., a higher blankholder force, leads to higher
frictional forces [2].
FST
FN
dO
2
D σr
2
dα σt
dx S σI+dσI
+σ σt dα
σr 2 dα
Kfi
0 DO
Kfa σn RO= 2
−σ σt X
DO
R= 2
alu
TALAT 3704 6
Force-Displacement Curve during Deep Drawing
During the deep drawing process, the drawing force increases from zero up to a
maximum value and then falls down again to zero, see Figure 3704.01.06. The base is
first formed in a manner similar to the stretch forming process and then the actual
drawing process follows.
Ftot max
h* hmax
h
alu
D0
FN
Base tearing
d0 FN
FN
Folds
As illustrated in Figure 3704.01.07 the process limits depend on the properties of the
sheet material, on the lubricant, on the tool geometry and the forming parameters. The
upper process limit is determined by the formation of tears. The lower limit is
TALAT 3704 7
determined by the tendency to build folds. These two failure criteria then determine the
limits of the process. The limiting draw ratio ßomax is a measure of the process limit
due to tearing. The limiting draw ratio can be increased by minimising the punch force
and by increasing the tearing factor. Calculations and experiments have shown that
during deep drawing, the ratio do/so has an influence on the limiting draw ratio. The
limiting draw ratio decreases with increasing ratio do/so. The higher the coefficient of
friction under the blankholder, the larger is the decrease of ßomax with an increasing
do/so ratio [2].
Figure 3704.01.08 illustrates the limits of the blankholder force for a fuel tank shell; an
upper limit due to the formation of tears and a lower limit due to the formation of folds
of „type 1“. The working range for faultless parts lies between these limits. The upper
limit is also determined by the maximum blankholder force which can be delivered by
the pressing machine [3].
800
working range
Blankholder Force FN
Working Range
600
for Good Parts
400
wrinkles
200
Contacting
Point necessary
0 40 80 120 160 200 drawing depth
Punch Distance h
Source: IfU Stuttgart
alu
TALAT 3704 8
Use of Nitrogen Pressure Springs for Deep Drawing
Pressing ram
Die
Blankholder Work-piece
Drawing punch
Nitrogen spring
Compensating tank
Press table
alu
In forming of steel sheets the useful deformation capacity is extended well beyond the
uniform elongation into the range of fracture elongation (necking). When forming
aluminium sheet metal parts deformation should be confined to the region of uniform
elongation and the region of necking should be avoided. For aluminium alloys it is
important to work with prototype tools to determine the feasibility of drawing as well as
the springback effect. In addition, it is helpful to ascertain the tolerances which can be
attained by altering the tools. Some general recommendations should be remembered
when designing press tools for the successful drawing of aluminium parts, see Figure
3704.01.10. Special attention should be given to the subject of lubrication. The
aluminium industry offers aluminium sheets with a wide range of surface morphologies,
including sheet surfaces with spark eroded textures (EDT) which allow a good
distribution of lubricant, thus making it possible to obtain better performances with
acceptable surfaces for difficult forming operations [Ref. 5 and TALAT Lecture 3702].
TALAT 3704 9
Aluminium Optimised Construction of Deep
Drawing Machines
Direct Re-Drawing
To obtain larger drawing ratios direct re-drawing is necessary. The principle scheme is
shown in Figure 3704.02.01. The trace of stresses in the forming zone is qualitatively
the same as in the first draw. Contrary to the first draw, however, the conical shape of
the drawing ring makes it possible to apply a normal force to the sheet even without a
blankholder. This normal force then presses the work-piece against the drawing ring.
di-1
s0
αz
di
rz rst
uz
dz
alu
TALAT 3704 10
Reverse Re-Drawing
During reverse re-drawing, the first draw is combined with an additional drawing step,
whereby the reverse re-drawing punch works opposite to the working direction of the
first draw punch. One has to differentiate between reverse re-drawing without a ring and
the tool oriented reverse re-drawing (see Figure 3704.02.02). A main advantage of
reverse re-drawing over conventional direct re-drawing is the reduced amount of
bending over the die curvature. Normally, both first draw and reverse re-drawing are
carried out together in one working step. The combination of both draws means that one
operational step can be eliminated. In the case of a stepped tool one transport stroke is
also eliminated. For this forming process, however, a larger punch stroke or, depending
on the tool construction, even a triple acting press may be required.
Reverse Redrawing
Punch for first draw = drawing ring for redraw
Blankholder for first draw
alu
As opposed to the hydromechanical drawing process without a membrane, the fluid cell
process works with a polyurethane membrane. The rigid drawing die is replaced by a
"hydraulic cushion" closed on all sides, see Figure 3704.03.01. The top side which
presses against the forming die, consists of the membrane. During the working stroke of
the punch the force is transmitted through the active medium onto the membrane and
finally through the membrane to the blank, pressing it both against the punch as well as
against the blankholder. This eliminates the formation of folds of „type 1“ and frictional
forces can act between punch and the drawing part. Thus frictional forces can be
TALAT 3704 11
transmitted between punch and workpiece, thereby displacing the normal failure zone
from the exit of the punch bottom radius further onto the rib of the drawn part, i.e. to a
location with a higher flow stress. The limiting draw ratio as well as the form and
dimensional precision which can be obtained depend on the control of pressure in the
active medium.
Source: ABB
alu
The fluid cell drawing process has been applied especially in the aircraft industry for
producing components with relatively small drawing depths. Another interesting
application, in use during the last few years, is the fabrication of prototypes in the
automobile industry. Figure 3704.03.02 shows a machine with equipment and work-
piece removal station as well as a sectional view illustrating the drawing process. The
forming movement of the tool of conventional presses is replaced by the supply of
pressurised oil from an external hydraulic aggregate. Using extremely high forming
pressures, it is even possible to form materials which are otherwise difficult to form.
TALAT 3704 12
Press cylinder Membrane Medium Forming part
under pressure
Blank
Pressure Forming
medium inlet pad
Horizontal frame
Trough
Tool
Source: ABB
Schematic View Showing the Principle of a
alu
3704.03.02
Training in Aluminium Application Technologies Fluid Cell Press
Source: ABB
alu
A Wheel-house Fabricated by the Fluid Cell Process 3704.03.03
Training in Aluminium Application Technologies
TALAT 3704 13
Hydromechanical Deep Drawing
Another sheet metal drawing process which has particular merits for forming aluminium
is the hydromechanical deep drawing process. As opposed to conventional deep drawing
with rigid tools, the work-piece is pressed into a bottom tool filled with liquid, instead
of a rigid die. The principle is explained in Figure 3704.03.04.
alu
With hydromechanical deep drawing it is possible to form flat sheet blanks or preformed
sheets to hollow bodies of various complex geometries. With this process it is also
possible to produce shapes with tapered bodies in a single step, which would otherwise
require several drawing steps in a conventional deep drawing process. Further
advantages are: better form and dimensional precision, a higher drawing ratio, reduced
residual stresses and the production of parts with undamaged surfaces.