Contouring, Finishing, and Polishing Anterior Composites
Contouring, Finishing, and Polishing Anterior Composites
CONTINUING EDUCATION
ESTHETICS
RESTORATIVE IMPLANTS
polishing requires the use of a sequential series of nishing and polishing burs, discs, strips, and pastes. Following the proper sequence of materials ensures the long-term health and polishability of restorations. If a part of this process if skipped, the tooth will often be left rough and susceptible to plaque and staining. Either multi-uted carbides or ne diamonds for gross contouring can be used to begin nishing the restoration.
Discs
Composites
The ability to achieve a good nish and polish on anterior composites is determined by two very important factorsaccess to the right materials and the artistic ability of the dentist. Having access to the right materials, however,
K. WILLIAM MOPPER, DDS, MS
Private Practice Glenview, Illinois
In terms of color stability and polishability, in the authors opinion microll is the only composite material that really stands the test of time. A microll must be used as the nal layer in order to obtain the best polish, surface smoothness, and long-term wear resistance. Nanohybrids or nanolls can also be used to replace the enamel layer in composite restorations. These materials initially provide a relatively good surface smoothness and high shine. Over time, however, nanoll composites lose their luster and are less wear-resistant than microll composites.8 Microhybrids are the least polishable of the three main composite types. Used as an anterior enamel layer, microhybrids rapidly lose polish and are more susceptible to staining. To achieve a beautiful, long-lasting polish, a microll composite must be used as the nal layer.
Polishing Materials
Discs can be used for the contouring of all tooth surfaces as well as bulk reduction of excess material. Discs will help contour and finish curved surfaces such as labial proximal line angles, lingual marginal ridges, cervical areas, incisal edges, shaping and finishing of incisal corners, plus finishing and polishing of labial surfaces. They are also excellent for contouring and finishing of posterior marginal ridge areas, and for lingual and buccal surfaces.
Where do polishers best t into a practices current procedures? One- or twostep polishers can certainly be used when polishing composite restorations quickly. But, if the goal is to achieve the best long-term polish, then it is more desirable to use a comprehensive polishing system.
62
INSIDE
ESTHETICS
into the tooth surface, eliminating the white line and raised margins. MediumThe medium grit should be used to continue smoothing the restoration surface. Medium grits remove any remaining imperfections and marks. FineThis part of the grit sequence is where polish really starts to shine through. The ne grit helps remove the smallest imperfections while adding a nice luster to the restoration. SuperneThe superne grit further renes the surface smoothness attainable to create a highly polished restoration.
Diamond Strips
The author is an advocate of the fourgrit disc sequence, which is designed to gradually reduce the amount of roughness caused by initial abrasion until a smooth glossy tooth surface is achieved. To provide maximum control for the operator, composite nishing should be done under low-speed/high-torque (speed from 0 rpm to 30,000 rpms). CoarseThe coarse grit is the stiffest of all the discs. This grit is used in conjunction with multi-uted nishing burs for gross contouring and shaping. When used with pressure, the coarse disc makes it easy to blend the composite
Diamond strips help start the interproximal finishing process while maintaining the integrity of the interproximal contact. A larger-grit (45-m strip) should be used for interproximal stripping of natural teeth or for gross removal of material, and smaller grits (15 m and 30 m) should be used to start interproximal polishing. Strips should be used to contour and polish interproximal areas. Use of a high-quality strip will remove tenacious stains and create a high polish at the interproximal without damaging the soft tissue. It is important that the strip is
thin and will stay intact as it is drawn through the interproximal contact areas. Aluminum-oxide cups should be used to polish gingival margins, achieve labial characterization and anatomy, and effectively reach areas such as the gingival third and the gingival margins of anterior teeth. Aluminum-oxide points should be used to create labial grooves in veneers, to nish and polish occlusal surfaces of posterior teeth, and on lingual surfaces of anterior teeth. An aluminum-oxide polishing paste should be used as the last step in the nishing and polishing process. Polishing paste with felt discs and points can be
Aluminum Oxide
FIG. 1
FIG. 2
FIG. 3
FIG. 4
FIG. 5
FIG. 6
FIG. 7
FIG. 8
FIG. 9
FIG. 10
FIG.11
FIG. 12
FIG. 13
FIG. 14
FIG.15
SCULPTING AND CONTOURING, REFINEMENT AND FINISHING (1.) Class III restoration preoperative view (note the long bevel). (2.) Lingual view of the preparation. (3.) Application of Renamel NANO Shade A1 (Cosmedent, www.cosmedent.com) using Cosmedents 8A Composite Polishing Instrument. (4.) Lingual sculpting and shaping of Renamel NANO using Cosmedents IPCT Composite Polishing Instrument. (5.) Addition of a small amount of Renamel NANO to blend onto the long bevel. This completed the block-out of shine-through and acted as an opaquer. (6.) Addition of the nano-hybrid composite is complete. Notice there is still enough room to apply Renamel Microll (Cosmedent). (7. AND 8.) Sculpting and contouring of Renamel Microll to proper shape and contour. (9.) A Brasseler ET-9 bur was used for for labial reduction. (10.) A Brasseler 0S-1 bur was used for lingual reduction. (11.) A Brasseler 8392-016 bur was used to rene the lingual and labial embrasure spaces. (12. THROUGH 15.) A disc system (FlexiDisc System by Cosmedent) from coarse to superne was used to achieve a high polish and invisibly blend composite into the tooth structure. Note the high ex and resilience of the discs.
66
INSIDE
ESTHETICS
from the facial aspect. A realistic tooth form should be developed before the pre-contouring phase begins. Now it is time to apply the correct technique during the nal phases of the restoration. The best nishing and polishing technique depends on the type of restoration the dentist is presented with. When polishing a Class IV restoration, for instance, the dentist should rely mainly on discs. However, cups and points will help develop more realistic characterization when polishing a veneer. A step-by-step guide to polishing on various restorations is outlined below.
YOUR PRODUCT RESOURCE
used to bring out the nal beautiful polish of composites, metals, porcelain, or natural dentition after prophylaxis. Before finishing and polishing, the dentist must conceptualize the desired end result. The dentist will not have to work as hard to obtain lifelike results if the restoration is pre-contoured to the correct shape and form before polishing. Many practitioners lose the shape of the restoration because of a lack of attention to the material application phase. Many dentists have a tendency to over-bulk the composite, and end up losing the intended shape. It is much easier to obtain the desired result if the composite is initially placed into the correct anatomical form and only slightly over-contour
Step 3: Action
Step 2: Conceptualization
www.dentalaegis.com/products
Composite Finishing and Polishing
Handpiece
Finishing and polishing should be achieved with a low-speed, high-torque handpiece, typically anywhere from 7,000 rpm to 30,000 rpm. A high-speed handpiece may be used to pre-contour, but using anything over 30,000 rpm during nishing and polishing is too high. Low-speed, high-torque is preferable, because it gives the operator complete control.
Starting with a coarse disc or a carbidenishing bur, the restoration can be completely contoured moving from restorative material to tooth surface, similar to burnishing metal. This can be done in a wet or dry eld. The material
should be extended well past the long bevel, and the dentist should not come back to the beveled margin. The nal restoration should be feather-edged onto the tooth surface past the beveled margin. If done properly, any white line or raised margin will completely disappear. At this stage, the disc should be exed for maximum nishing potential.
FIG. 16
FIG. 17
FIG. 18
FIG. 19
FIG. 20
FIG.21
FIG. 22
FIG. 23
FIG. 24
FIG. 25
FIG. 26
FIG. 27
FIG. 28
FIG.29
FINAL POLISHING (16.) Gingival torquing opened the contact to start the interproximal nishing. (17. AND 18.) Use of both wide and narrow superne diamond nishing strips (Cosmedents FlexiDiamond Strips). Running these strips once or twice through the contact will smooth the contact area. (19.) This view shows that there is still more nishing and polishing to be done to further rene the embrasure space. (20.) Further renement of the mesiallabial line angle to further rene embrasure space and create symmetry of both centrals. Here, the use of the medium-grit (FlexiDisc) is preferred. (21.) Continuing the polishing with a ne disc. (22.) Polishing with a superne disc. (23.) Polishing the lingual surface with diamond polishers (Cosmedents nanohybrid composite polishers). (24.) Polishing the lingual surface with a superne cup. (25.) Finishing and characterizing the labial surface with a superne point. (26.) Application of an aluminum-oxide polishing paste (Enamelize, Cosmedent) with a felt buff (FlexiBuff, Cosmedent). (27.) Polishing the lingual surface with Enamelize and Felt FlexiPoint (Cosmedent). (28.) This is the incisal view of the nished restoration. Note the symmetry of the labial surfaces, the contour at the embrasures surfaces, the contact, and the beautiful blend of the polished material into the tooth surface. (29.) Labial view of the nished restoration.
68
INSIDE
ESTHETICS
Although this is a small diameter, the 3/8 disc can be exed to gain access to hardto-reach areas. The gingival half of the restoration can be polished nicely using exible cups, but rubber must be kept off the occlusal and incisal margins. If Class V restoration invades the proximal surfaces, the diamond strips and aluminum oxide strips should be used in the narrow width for polishing these surfaces. An aluminum-oxide polishing paste with felt discs and points is recommended for the nal polish. and down the tooth surface. Blunting off sharp edges on a green stone prior to characterizing prevents scarring and over-characterization. After a grooved surface has been developed, augmenting with rubber points highlights the grooves. Polishing the surface is completed with ne and then superne polishing discs. To polish the interproximal surfaces, diamond and aluminum-oxide strips are used as previously described. For the nal polish, an aluminum-oxide polishing paste with felt discs and points is used.
The different grit sizesmedium, ne, and superneshould be continued through in succession. An enamel-like luster rapidly appears. The interproximal process should be started with diamond strips to maintain the integrity of the contact. One or two times through the interproximal should be sufficient, followed with the ne-superne aluminum oxide strip on dry surface until no resistance is felt, and a smooth surface is apparent. For the nal polish, an aluminum oxide polishing paste with felt discs and points should be used. This is the step that really brings out the amazing nal polish.
TABLE 2
Quick Tips
Aluminum-oxide discs, rubber cups and points, and an aluminum-oxide polishing paste are used to obtain the best polish on a microfill composite.10 Diamond or aluminum-oxide discs, and aluminum-oxide or diamond polishing points, cups, and wheels are used to achieve the best polish on a nanofill restoration, followed with an aluminum-oxide polishing paste. The best polish on a microhybrid restoration is obtained by starting with aluminum-oxide finishing discs, followed with diamond-impregnated cups, points, and wheels. Maximum polish is achieved with the use of a diamond polishing paste, followed by the use of an aluminumoxide polishing paste with felt wheels and felt points.
Class V
On occlusal or incisal margins, 5/8 or 1/2 coarse disc should be used past the long bevel. Discs are always preferred on exposed margins. To start nishing from restoration to tooth surface, a coarse disc is used, followed by medium and then ne; nishing with the superne disc to achieve maximum polish. The 3/8 disc should be used at the gingival margin.
V1 Girl AD pro for Polish Article 4/1/11 12:42 PM Page 1
The coarse disc or contouring bur is used to start contouring and nishing. The coarse and medium discs can be used to complete the contouring of the veneer. It is desirable to maintain the character and anatomy placed in the facial surface. This cannot be done with discs, but cups and points are very useful for this purpose. To characterize, the cup is placed at on the tooth surface, exed slightly, and run with pressure up
Excessive staining is removed in the usual fashion. A small amount of aluminum-oxide polishing paste is then applied to each surface and polish. To remove interproximal staining, each interproximal should be packed with polishing paste, and a wide, ne/superne polishing strip is used to polish the surface.
BAR CODE:
Scan the bar code below with your camera phones Bar Code reader.
*You can download a bar code reader from iTunes or BlackBerry .
URL:
navigator.insidedentistry.net/0322web
The proper contouring, nishing, and polishing of anterior restorations is a key component to the long-term success of bonded restorations. This article outlines the importance of three different phases in the nishing and polishing process. First, the appropriate restorative materials, from composites to polishers, must be carefully selected to help get the job done right. Then, the dentist must conceptualize the desired end result, and set up the restoration accordingly. And, nally, the proper finishing and polishing technique must be executed in order to achieve maximum restorative success. For a clinical example of the technique described, the author provides a complete case pictured in Figure 1 through Figure 29.
Disclosure
The author is part owner of Cosmedent.
Conclusion
4. Ikeda M, Martin K, Nikaido T, Foxton RM, et al. Effect of surface characteristics on adherence of S. mutans biofilms to indirect resin composites. Dent Mater J. 2007;26(6):915-923. 5. Kantorski KZ, Scotti R, Valandro LF, et al. Adherence of Streptococcus mutans to uncoated and saliva-coated glass-ceramics and composites. Gen Dent. 2008:56(7)740-747. 6. Mopper KW. Lets talk composites! Dent Today. 2008;27(10):120-122. 7. Craig RG, Ward ML (eds). Restorative Dental Materials. Mosby, St. Louis, 1997,p263. 8. Barucci-Pster N, Gohring TN. Subjective and objective perceptions of specular gloss and surface roughness of esthetic resin composites before and after artificial aging. Am J Dent. 2009;22(2):102-110. 9. Takanashi E, Kishikawa R, Ikeda M, et al. Inuence of abrasive particle size on surface properties of owable composites. Dent Mater J. 2008:27(6):780-786. 10. Cenci MS, Venturini D, Pereira-Cenci T, et al. The effect of polishing techniques and time on the surface characteristics and sealing ability of resin composite restorations after oneyear storage. Oper Dent. 2008;33(2):169-176.
WEB ENTRY:
InsideDentalProducts.com
This softtissue diode laser has presets for more than 30 clinical procedures, a wireless foot pedal, and a touch-screen monitor. US retail value: $7,495.
* Contest is open only to dentists practicing in North America.
References
1. Jefferies SR. Abrasive nishing and polishing in restorative dentistry: a state-of-the-art review. Dent Clin North Am. 2007;51(2):379-397. 2. Turkun LS, Turkun M. The effect of one-step polishing system on the surface roughness of three esthetic resin composite materials. Oper Dent. 2004;29(2):203-211. 3. Mopper KW. How do composite resins stand the test of time? Dent Today. 2004;23(5):74-79.
Spreading Smiles