Interseal 670HS is a low VOC, two component, high build, high solids, surface tolerant, epoxy coating suitable for use in both maintenance and new construction. Excellent anti-corrosive protection with minimal surface preparation even when applied over hand prepared rusty steel. Can be used on bridges, offshore splashzones and sub sea structures, ballast tanks and is certified to ANSI / NSF Standard 61.
Interseal 670HS is a low VOC, two component, high build, high solids, surface tolerant, epoxy coating suitable for use in both maintenance and new construction. Excellent anti-corrosive protection with minimal surface preparation even when applied over hand prepared rusty steel. Can be used on bridges, offshore splashzones and sub sea structures, ballast tanks and is certified to ANSI / NSF Standard 61.
Interseal 670HS is a low VOC, two component, high build, high solids, surface tolerant, epoxy coating suitable for use in both maintenance and new construction. Excellent anti-corrosive protection with minimal surface preparation even when applied over hand prepared rusty steel. Can be used on bridges, offshore splashzones and sub sea structures, ballast tanks and is certified to ANSI / NSF Standard 61.
Interseal 670HS is a low VOC, two component, high build, high solids, surface tolerant, epoxy coating suitable for use in both maintenance and new construction. Excellent anti-corrosive protection with minimal surface preparation even when applied over hand prepared rusty steel. Can be used on bridges, offshore splashzones and sub sea structures, ballast tanks and is certified to ANSI / NSF Standard 61.
Can be applied over abrasive blasted, hydroblasted or
mechanically cleaned surfaces
Available in a range of colours as well as aluminium
Suitable for application temperatures from
-5C (23F) to 40C (104F)
Compatible with cathodic protection
Interseal 670HS is certified to ANSI/NSF standard 61
As a high build epoxy it is suitable for a variety of new construction applications including immersion, as a deck coating or for structural steel. Excellent anti-corrosive protection with minimal surface preparation even when applied over hand prepared rusty steel makes Interseal 670HS perfect for maintenance too. Interseal 670HS One product, multiple uses
www.international-pc.com [email protected] and and all product names mentioned in this publication are trademarks of, or licensed to, AkzoNobel. AKZONOBEL 2009. International Protective Coatings has used its best endeavours to ensure that the information contained in this publication is correct at the time of printing. Please contact your local International Protective Coatings representative if you have any questions. Unless otherwise agreed by us in writing, any contract to purchase products referred to in this brochure and any advice which we give in connection with the supply of products are subject to our standard conditions of sale. Interseal
670HS is a low VOC, two component, high build, high solids, surface tolerant, epoxy coating suitable for use in both maintenance and new construction. Interseal 670HS is suitable for application to a wide variety of substrates including hand prepared rusted steel, abrasive blast cleaned and hydroblasted steel, and a wide range of intact, aged coatings. Anti-Corrosive Protection Interseal 670HS provides excellent anti-corrosive protection in industrial and offshore environments for both atmospheric exposure and immersion service. Immersion Environments Interseal 670HS can be used on bridges, offshore splashzones and sub sea structures, ballast tanks and is certified to ANSI/NSF Standard 61 for use in drinking water tanks. Certification is for tanks greater than 100 gallons (378 litres), for pipes six inches (15cm) in diameter or greater, and valves which are two inches (5cm) in diameter or greater. Chromascan Interseal 670HS is available in a range of colours via the Chromascan remote colour tinting system. This means that project shades and specific site colour requirements can be met rapidly and in low volume requirements when required. Colour Aluminium and a selected range of colours via Chromascan Volume Solids 82% Film 100-200m (4-8mils) dry Mix Ratio 5.67:1 by volume Temperature Touch Dry Min Recoat Min Recoat with with Self Recommended Topcoat 10C (50F) 8 hours 32 hours 20 hours 15C (59F) 7 hours 26 hours 14 hours 25C (77F) 5 hours 18 hours 10 hours 40C (104F) 2 hours 6 hours 4 hours VOCs 240g/lt EPA Method 24 112g/kg EU Solvent Emissions Directive (Council Directive 1999/13/EC) Technical Information For curing at low temperatures, an alternative curing agent is available. Please consult product datasheet. RESULTS Pull-Off Adhesion ISO 4624 1 x 100m (4 mils) dft Interseal 670HS applied Typically 7Mpa (1015psi) Adhesion directly to Sa2.5 (SSPC-SP10) blasted steel. Abrasion Resistance ASTM D4060b 1 x 125m (5mils) dft Interseal 670HS applied Average of 259mg weight loss per 1000 cycles using directly to Sa2.5 (SSPC-SP10) blasted steel. CS17 wheels and a 1Kg loading Impact Resistance ASTM D2794 1 x 125m (5 mils) dft Interseal 670HS applied Direct impact resistance typically 4.17 Joules directly to Sa2.5 (SSPC-SP10) blasted steel Cathodic Protection ASTM G8 2 x 225m (9 mils) dft Interseal 670HS applied Typically less than 3mm disbondment following 30 directly to Sa2.5 (SSPC-SP10) blasted steel days exposure. Salt Spray ISO 7253 1 x 200m (8 mils) Interseal 670HS applied No film defects and an average of 1mm rust creep directly to Sa2.5 (SSPC-SP10) blasted steel at the scribe after 3000 hours exposure Prohesion Cycling ASTM G85 1 x 200m (8 mils) Interseal 670HS applied No film defects and an average of 1mm rust creep at directly to Sa2.5 (SSPC-SP10) blasted steel the scribe after 3000 hours exposure Immersion ISO 2812 1 x 150m (6 mils) dft Interseal 670HS applied No film defects after 1 year exposure directly to Sa2.5 (SSPC-SP10) blasted steel Constant Condensation ISO 6270 1 x 200m (8mils) dft Interseal 670HS applied No film defects after 4200 hours exposure directly to Sa2.5 (SSPC-SP10) blasted steel Test Data REFERENCE DETAILS TEST TYPE The above performance data has been compiled based on present experience of in-service product performance and upon performance data obtained under laboratory test conditions. Actual performance of the product will depend upon the conditions in which the product is used. Interseal 670HS provides excellent anti-corrosive protection A N 0 2 8 0 1 _ 1 4 1 2 0 9 G 2 _ 6 7 0 H S _ U K 0 1 / 1 0