NAVFAC MO-307
September 1992
SN 0525-LP-542-3100
FOREWORD
Corrosion of shore and waterfront facilities is a common and serious problem.
Naval shore establishment losses to corrosion are estimated at over one-half billion dollars annually. Corrosion related costs and the adverse impact on mission readiness are
of increasing concern. Additionally a corrosion leak in a POL tank or pipeline could be
very expensive for cleanup and could effect the mission adversely. Action to control corrosion or to repair corrosion damage are among the most frequent reasons for performing maintenance on shore and waterfront facilities.
Additional information or suggestions that will improve this manual are invited
and should be submitted through appropriate channels to the Naval Facilities Engineering Command, (Attention: Code 1632), 200 Stovall Street, Alexandria, VA 22332-2300.
This publication has been reviewed in accordance with the Secretary of the Navy
Instruction 5600.16A and is certified as an official publication of the Naval Facilities Engineering Command.
E. R. HAMM
CAPTAIN, CEC, U. S. Navy
Assistant Commander for
Public Works Centers and Departments
ABSTRACT
The purpose of this manual is to serve as a technical guide for both Naval and
civilian personnel in identifying existing or potential corrosion problems, determining
the proper corrective actions, and implementing the corrective actions. As corrosion
and corrosion control are affected by both original design and construction and maintenance, information is presented regarding all methods for reducing corrosion even
though the information is primarily oriented toward maintenance and repair.
This manual describes the mechanisms of corrosion, the types of corrosion commonly experienced in naval shore facilities and waterfront structures, the methods that
can be used to control corrosion and methods for implementing an effective corrosion
control program. This manual emphasizes methods for determining the most cost effective means of controlling corrosion and practical application of corrosion control to typical problems encountered in the Naval shore establishment.
iii
Table of Contents
1.
l-l
1.1 INTRODUCTION
1.2 PURPOSE
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
1-1
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
1-1
. . . . . . . . . . . . . . . . . . . . . . . . . . . . .
1-1
. . . . . . . . . . . . . . 1-1
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
1-2
1-2
1.5.4 Safety . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
1-2
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
1-3
2-1
3-1
3.3.2
3.4
3.5
vii
3.6
3.7
3.8
3.9
3-66
4-1
4.1
4.2
4-1
. . . . . . . . . . . . . . . . . . . . . . . . . . . 4-7
. . . . . . . . . . . . . . . . . . . . . . . . . . . 4-8
4.3.4 Pitting . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
4.3.5 Concentration Cell Corrosion
4.3.6 Dealloying
4-11
. . . . . . . . . . . . . . . . . . . . 4-13
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
4-15
4-16
. . . . . . . . . . . . . . . . . . . . . . 4-18
4-20
4-21
. . . . . . . . . . . . . . . . . . . . . . . . .
4-22
5.
5.1
viii
6-1
6.1
6-1
6.2
ATMOSPHERIC EXPOSURE
6.
6.2.1 Electrolyte
. . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
6-1
6-1
6.3
. . . . . . . . . . . . . 6-2
6.2.3
6.2.4
SUBMERGED EXPOSURE
6.3.1 Electrolyte
. . . . . . . . . . . 6-2
. . . . . . . . . . . . . . . . . . . . . . . . 6-3
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
6-3
. . . . . . . . . . . . . 6-4
. . . . . . . . . . . 6-4
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
6-5
. . . . . . . . . . . . . 6-5
. . . . . . . . . . . 6-6
UNDERGROUND . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6-6
6.5.1 Electrolyte
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
6-7
. . . . . . . . . . . . . 6-7
7-1
7.1.1 Scope
7.1.2
7.2
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7-1
. . . . . . . . . . . 7-1
7-1
. . . . . . . . . . . . . . . . . . . . . . . . . . . . 7-1
. . . . . . . . . . . . . . . . . . . . . . . . . 7-1
. . . . . . . . 7-2
7-6
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
7-6
7-7
. . . . . . . . . 7-8
7-22
. . . . . . . . . . . . . . . . . . . . . . . . . . .
7-23
7.7.2 Roller . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
7-24
7.7.3 Spray
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7-24
. . . . . . . . . . . . . . . . 7-27
7-31
. . . . . . . . . . . . . . . . . . . . . . . .
7-31
7-31
7-32
7-33
. . . . . . . . . . . . . . . . . .
7-33
7-33
7-33
7.10.1 Compatibilities . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
7-33
7-34
7-34
7.11.2 Piping . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
7-34
7-35
7.11.4 Antenna and Other Tall Towers and Supporting Equipment . . . 7-35
7.12 PAINTING GALVANIZED SURFACES . . . . . . . . . . . . . . . . . 7-35
7.13 PAINTING ALUMINUM AND OTHER NONFERROUS METALS
7-35
7.14 PAINTINGSAFETY . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
7-35
7-36
. . . . . . . . . . . . . . . . . . . . . . . . .
7-36
7-36
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
xi
7-36
8-1
8.
8.1
8.2
. . . . . . . . . . 8-1
. . . . . . . . . . . . . . . . . 8-1
. . . . . . . . . . . . . . . . . . . . . . . . . 8-1
. . . . . . . . . . . . . 8-2
. . . . . . . . . . . . . . . . . . . . . . . 8-2
. . . . . . . . . . . . . . . . . . . . . . . . . . . . 8-5
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8-7
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8-8
9.1
9-1
Definition . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9-1
9.1.2
Classification . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9-1
9.1.3
9.1.4
9.1.5
Laboratory Tests . . . . . . . . . . . . . . . . . . . . . . . . . . . .
9.1.6
9.1.7
9.1.8
Polymerization
9-2
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9-3
xii
9-4
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
9-4
9-12
9-13
. . . . . . . . . . . . . . . . . . . . . .
9-16
. . . . . . . . . . . . . . . . . . . . . . . . .
9-20
9-21
9-24
9-30
9.2.11 Polystyrene . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
9-32
9.2.5
. . . . . . . . . . . . . 9-35
. . . . . . . . . . . . . . . . . . . . . . . . . . . .
9-36
. . . . . . . . . . . . . . . . . .
9-43
9-43
9-46
. . . . . . . . . . . . . . . . . . . . . . . . . . .
9-48
9-50
9-53
9.4
9.3.8 Silicones . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
9-54
9-57
9-57
9-61
9-69
. . . . . . . . . . . . . . . . .
9-70
xiii
10-1
10.1 INTRODUCTION . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
10-1
. . . . . . . . . . . . . 10-1
. . . . . . . . . . . . . . . . . . . .
10-1
10-2
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
10-2
. . . . . . . . . . . . . . . . . . . . . . . . . . .
10-2
10-2
. . . . . . . . . . . . . . . . . . . . . .
10-3
10-3
. . . . . . . . . . . . . . . . 10-4
. . . . . . . . . . . 10-5
. . . . . . . . . . . . . . . . . . .
10-8
11-1
11.1 INTRODUCTION . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
11-1
. . . . . . . . . . . . . . . . . . . . . . . . .
11-1
11-1
11-1
xiv
11-1
. . . . . . . . . . . . . . .
11-2
11-2
. . . . . . . . . . . . . . . . . . . . .
11-2
11-7
. . . . . . . . . . . . . . . . . . . . .
11-10
. . . . . . . . . . . . . . . . 11-10
. . . . . . . . . . . . . . . . . . . 11-10
. . . . . . . . . . . . . . . . . . 11-10
. . . . . . . . . . . . . . . . . . 11-12
12-1
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
12-1
12.2 BIBLIOGRAPHY . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
12-1
12.1 REFERENCES
APPENDIX A
APPENDIX B
APPENDIX C
A-1
B-1
C-1
Index-1
INDEX
xv
FIGURES
Figure No.
Page
Title
3-1
3-2
3-2
3-8
3-3
3-10
3-4
3-11
3-5
3-13
3-6
3-14
3-7
3-14
3-8
3-15
3-9
3-19
3-10
3-20
3-11
3-22
3-12
3-23
3-13
3-26
3-14
3-27
3-15
3-31
3-16
3-33
3-17
3-35
3-18
3-38
xvi
FIGURES
Figure No.
3-19
Title
Page
3-41
3-43
3-45
3-22
3-46
3-23
3-47
3-50
3-51
3-52
3-53
3-28
3-54
3-29
3-55
3-59
3-60
3-32
3-63
3-33
3-64
3-34
3-65
3-35
3-68
3-69
3-20
3-21
3-24
3-25
3-26
3-27
3-30
3-31
3-36
xvii
FIGURES
Figure No.
Page
Title
3-70
3-71
3-72
3-73
4-1
Electrochemical Cell
4-1
4-2
Galvanic Cell
4-8
4-3
4-11
4-4
4-11
4-5
4-22
6-1
6-23
6-2
6-24
6-3
6-24
6-4
Tie-Rod Corrosion
6-25
6-5
6-25
6-6
Protective Jacket
6-26
6-7
6-27
6-8
6-27
6-9
6-28
6-10
6-28
6-11
6-29
6-12
6-13
6-30
6-14
6-31
3-37
3-38
3-39
3-40
xviii
FIGURES
Figure No.
Page
Title
6-15
6-31
6-16
6-32
6-17
6-32
10-1
10-3
10-2
10-6
10-3
10-7
10-4
10-8
10-5
10-9
xix
TABLES
Table No.
Page
Title
4-1
4-10
6-1
6-8
6-2
Submerged Structures
6-10
6-3
Waterside Piping
6-14
6-4
Underground Structures
6-17
10-1
10-4
10-5
10-2
xx
needlessly eliminate all corrosion. Through an economic and mission analysis, a proper
balance can be maintained between the potential impact of corrosion and the cost to
prevent it.
1.5.1 Cost. It has been estimated that the direct cost of corrosion in the U.S. exceeds $70,000,000 per year with about 25% of these costs being avoidable. It has been
estimated that the total annual cost of corrosion within the naval shore establishment exceeds $1,000,000 and that equipment and facilities with a value of over $6,000,000,000
are at risk from corrosion. It is important that a maximum value be obtained from the
application of corrosion control measures as the limited available funds for maintenance and repair of facilities must be effectively applied to meeting critical mission
requirements. It is also important that corrosion control be considered during the
design and construction of new facilities or during major additions and repairs to existing facilities. It is often significantly less costly to eliminate those features that contribute to corrosion and to use corrosion resistant materials than to correct the problem
once construction is complete. In other cases, corrosion control must be carefully considered for application to facilities that have exceeded their original design life, but
must be operated for extended periods due to long lead times and limited funds for new
construction. In these cases, corrosion control measures that are not cost effective must
be applied simply to maintain the ability to provide Fleet support.
1.5.2 Mission. The mission of the Naval Facilities Engineering Command is to
serve as the Navys expert for: Facilities, Public Works, Environment Ashore, and
Seabees. As part of the mission, NAVFAC is assigned as the construction agent for the
Navy. Many of the facilities constructed by Naval Facilities Engineering Command are
at risk from corrosion and failure of a facility can adversely affect Fleet readiness. This
is particularly true for facilities such as utility systems, waterfront structures, and aviation operational facilities where there is a direct interface between the facility and the
Fleet.
1.5.3 Readiness. Corrosion can adversely affect Fleet readiness. A fuel line
that is shut down due to leaks can interrupt the flow of vital fuel to ships or aircraft as effectively as enemy action. In many cases, redundant systems are provided to insure an
uninterrupted ability to provide Fleet support. In these cases, redundancy can be
reduced if one or more of the sections of a facility is out of service for the repair of corrosion damage. In addition, corroded systems are more prone to unexpected failure due
to wind, wave, earthquake, or enemy action. Nearly all of this corrosion can be anticipated, detected, and effectively controlled.
1.5.4 Safety. Corrosion can have a significant effect on the safety of the operations performed by the Naval Facilities Engineering Command. Aside from the obvious
dangers from structural collapse and leakage of hazardous or flammable materials, corrosion can cause more insidious problems. Corroded systems are more prone to failure
1-2
from other causes as described above. Corrosion products can also contaminate fuel
and water supplies causing health and operational problems. Corrosion of safety systems can also render them unable to perform their required function when needed.
1.5.5 Corrosivity of Environment. As the majority of Naval Shore Facilities are
located in marine or industrial environments, the corrosivity of the environment at most
activities is significantly greater than average. Commercial equipment is normally
produced to be resistant to conditions of average severity and additional protection may
be necessary when the equipment is used at a site with increased corrosivity. This is particularly true for tropical marine and industrial marine sites.
1.5.6 Environmental Contamination. Environmental contamination from leaking fuel and hazardous material poses a significant environmental concern. The cost to
handle hazardous materials that leak from corroded facilities usually exceeds the costs
associated with the control of the corrosion responsible for the leak. In addition, operating facilities, such as power plants, which have a potential for adverse environmental impact, can be adversely affected by corrosion. The impact of corrosion on operating
conditions can cause increased emissions of pollutants. In some cases, the products of
corrosion themselves are hazardous and corrosion must be controlled to prevent direct
environmental damage.
1.5.7 Manpower. Corrosion control can also reduce manpower requirements. It
is usually a more effective use of manpower to control corrosion than to correct corrosion damage. For example, inspection and maintenance of a cathodic protection system on a 5-mile section of fuel pipeline can be performed on a routine basis using
approximately 24 man hours per year. Over 200 man hours are usually required to
repair a single leak in such a system even without considering environmental cleanup
and an unprotected pipeline can experience several leaks per year. In addition, corrosion control can be performed on a planned basis so that available manpower can be
effectively used.
1-3
2-1
3-1
A flowchart of the economic analysis process is shown in Figure 3-1. This analysis
process consists of six consecutive steps with the performance of the sensitivity analysis
providing feedback to reiterate the process. All six steps must be performed to prepare
a thorough and objective analysis.
Figure 3-1
Six Steps of Economic Analysis
Step 1. Define the Objective.
The objective statement defines the purpose of the analysis. For example, provide
corrosion control for a sheet of steel piling seawall for the lowest life cycle cost. The
statement should be unbiased, well defined, and incorporate a measurable standard of
performance. The objective statement example is unbiased because no specific method
of corrosion control is stipulated. The statement is well defined because it states the
desired outcome, corrosion control, of the project. Finally, the objective statement incorporates a measurable standard of performance by selecting an alternative based on
the life cycle cost proposal with the least associated cost.
Step 2. Generate Alternatives.
After the objective statement is defined, all feasible alternatives should be generated
that will meet that objective. For example:
1. Provide no corrosion prevention or control.
2. Coat the seawall.
3. Provide cathodic protection and coat the seawall.
3-2
3-3
1. Sunk Costs. Sunk costs are costs that have already been spent, such as
research and development and previous acquisition of an asset. These costs occur
before the decision point (time of analysis) and are irretrievable. Sunk costs do not effect the outcome of the decision and are not considered in the economic analysis.
2. One-Time Costs. One-time costs are costs that occur at one point in
time. Maintenance and operation costs that vary over an extended period of time
(economic life) are also considered one-time costs. Examples are acquisition costs, research and development costs (after the decision point), varying maintenance costs, and
the terminal or salvage values of assets at the end of their economic lives.
3. Recurring Annual Costs. Recurring annual costs are equal costs that
occur annually, over an extended period of time (economic life). Personnel, operating,
and maintenance costs are examples of recurring annual costs.
3-4
NAVFAC P-442 (Ref 3) specifies four types of benefits: (1) Direct cost savings,
(2) efficiency/productivity increases, (3) other quantifiable output measures, and (4)
non-quantifiable output measures.
A thorough treatment of benefit documentation can be found in Reference 3 (NAVFAC P-442, Chapter 4).
Step 5. Compare Costs and Benefits and Rank Alternatives.
After the present value costs and benefits are determined, a comparison of the
alternatives should be produced. Alternatives should be ranked based on economic
desirability.
Step 6. Perform Sensitivity Analysis.
Following the ranking of alternatives, a sensitivity analysis should be performed
to determine the consequences of varying the cost estimates and assumptions. The sen3-5
sitivity analysis gives credibility to the final results and provides feedback within the
economic process (see Figure 3-1). It further refines the assumptions and indicates that
values are sensitive to change. In this way, the decision maker can be certain that all
relevant information has been considered. A thorough treatment of sensitivity analysis
can be found in Reference 3 (NAVFAC P-442, Chapter 7).
3.3 MAINTENANCE AND OPERATION. Justification of recurring maintenance and
operation costs requires an economic analysis. Some costs can be directly measured and
are more easily quantified using the economic process. Examples include the costs of
acquisition and recurring maintenance. Some costs can not be measured directly and
are more difficult to quantify, but still require documentation. These include the costs
of increased maintenance resulting from uncontrolled corrosion, costs associated with
the loss of material and cleanup of spills, and the cost of initial overdesign.
3.3.1 Costs of Increased Maintenance Resulting From Uncontrolled Corrosion.
Costs of uncontrolled corrosion must, eventually, include direct loss of a facility and/or
replacement of the facility. Maintenance and repair costs due to increasing leakage
over time, must also be considered. Although estimates can be made, it is difficult to
predict precisely when a facility will fail or when leaks will occur.
3.3.2 Costs Associated With Loss of Material and Cleanup of Spills.
Costs associated with spills are assumed to be high and should be included in the
analysis as additional information. Several predictions must be made to determine the
costs associated with the loss of material and cleanup of spills: (1) Forecast the timing
and frequency of spills, (2) predict how much material will be lost, and (3) estimate the
value of the lost material.
These costs can not be ignored. Costs associated with hazardous spills are the
most difficult to quantify risk and uncertainty are evident when estimating a cost value
for human life or the environment. There exists some methods of risk analysis to
analyze these costs. Risk analysis is covered briefly in Reference 3 (Chapter 7).
3.3.3 Cost of Initial Overdesign. Overdesign refers to increasing construction
costs to prevent corrosion losses. The selection of corrosion-resistant metal, or the use
of additional metal thickness to compensate for corrosion loss, are two examples of overdesign. Preventing unnecessary overdesign requires trade-off analysis between the cost
of corrosion control versus the costs incurred when no prevention or control is practiced. One way to accomplish this is to evaluate all feasible alternatives and select the
least costly alternative.
3.4 CORROSION PREVENTION AND CONTROL FOR PIPELINES
3-6
3-7
8. Costs of labor and materials increase (or decrease) with the general inflation rate.
Cost of fuel, however, requires special treatment when determining the value lost (disbenefit) from a pipeline leak. Otherwise, this analysis requires no special treatment of
inflation.
Cost/Benefit Analysis
Alternative 1. Continue repairs on existing line.
Cost to repair leaks: at $25,000 each (number of leaks increase exponentially)
Terminal value: $24,000
Figure 3-2
Cash Flow Diagram - Continue Repairs on Existing Line.
The Cash Flow Diagram Represents the Magnitudes and Timing of Costs and
Benefits for the Entire Economic Life of an Alternative
3-8
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
18
19
20
21
22
23
24
25
25
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Replacement
Terminal value
25,000
50,000
50,000
75,000
75,000
100,000
125,000
150,000
175,000
225,000
275,000
325,000
375,000
425,000
500,000
575,000
650,000
725,000
825,000
925,000
1,025,000
1,125,000
1,250,000
1,375,000
960,000
(24,000)
0.909
0.826
0.751
0.683
0.621
0.564
0.513
0.467
0.424
0.386
0.350
0.319
0.290
0.263
0.239
0.218
0.198
0.180
0.164
0.149
0.135
0.123
0.112
0.102
0.092
0.092
$ 22,725
41,300
37,550
51,225
46,575
56,400
64,125
70,050
74,200
86,850
96,250
103,675
108,750
111,775
119,500
125,350
128,700
130,500
135,300
137,825
138,375
138,375
140,000
140,250
88,320
(2,208)
$2,391,737
Total Net Present Value Cost:
Uniform Annual Cost:
$2,391,737/9.077 = $ 263,494
3-9
3.5
3.5
3.5
3.5
3.5
3.5
3.5
3.5
10
3.5
$38,000
$ 3,500
$12,000
11
3.5
12
3.5
13
3.5
14
3.5
15
3.5
Figure 5-3
Cash Flow Diagram - Retrofit Cathodic Protection
on Existing Line
Alternative 2 (economic life - 15 years)
Amount
Project
Year(s)
0
1-15
15
Cost
Element
Installation
Maintenance
Rehabilitation
One-Time
Recurring
Discount
Factor
Discounted
Cost
$3,500
1.000
7.606
0.239
$38,000
26,621
2,868
$38,000
12,000
3-10
15.5
$960,000
$ 25,000 each (number of leaks increase exponentially)
$ 24,000
10
11
12
13
14
15 16
17
18
50
50
19
20
21
22
23
24
25
25 25
75 75
100
125
150
175
225
Figure 3-4
Cash Flow Diagram - Replacement of Existing Line
Alternative 3 (economic life - 25 years)
Amount
Project
Year(s)
0
0
1-14
15
16
17
18
19
20
21
22
23
24
25
Cost
Element
Installation
Terminal value
None
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Repair leaks
Discount
Factor
Discounted
Cost
$960,000
(24,000)
1.000
1.000
$960,000
(24,000)
25,000
25,000
50,000
50,000
75,000
75,000
100,000
125,000
150,000
175,000
225,000
0.239
0.218
0.198
0.180
0.164
0.149
0.135
0.123
0.112
0.102
0.092
One-Time
Recurring
5,975
5,450
9,900
9,000
12,300
11,175
13,500
15,375
16,800
17,850
20,700
$1,074,025
Total Net Present Value Cost:
Uniform Annual Cost: $1,074.025/9.077 = $ 118,324
3-11
$2,391,737
$ ,263,494
$ 67,489
$ 8,873
$1,074,025
$ 118,324
3-12
The dominant cost factors for each alternative are represented by the steepest curve.
These are as follows:
Alternative 1 - Repair Costs
Alternative 2 - Installation Cost
Alternative 3 - Installation Cost
Figure 3-5
Determination of the Dominant Cost Factor
Alternative 1 - Continue Repairs
3-13
Figure 3-6
Determination of the Dominant Cost Factor
Alternative 2 - Cathodic Protection
Figure 3-7
Determination of the Dominant Cost Factor
Alternative 3 - Replacement
3-14
First Stage: Repair cost is the dominant cost factor for Alternative 1, as
illustrated in Figure 3-5. A method of sensitivity analysis is applied by
varying the cost of repairs and determining if this variation changes the
ranking of alternatives. The first stage compares the uniform annual costs
of Alternative 1 and Alternative 3 with the uniform annual cost of
Alternative 2 as the repair costs are varied. It is tested to see if and when
lowering the repair costs will result in equal uniform annual costs of
Alternative 1 or Alternative 3 with those of Alternative 2. Figure 3-8
graphs the uniform annual cost of each alternative as the repair cost is
varied. The uniform annual cost is used because the three alternatives
have differing economic lives. As the repair cost is varied from $0 to
$50,000. Alternative 2 remains the economic choice. Varying the repair
cost changes the ranking of Alternatives 1 and 3 only when the repair cost
falls below $9,803. This suggests that the ranking of alternatives is
insensitive to variation in the repair cost.
Figure 3-8
Sensitivity Analysis
Vary Repair Costs - All Alternatives
3-15
Second Stage. Installation cost is the dominant cost factor for Alternatives
2 as illustrated in Figure 3-6. To test the sensitivity of varying the
installation cost of cathodic protection on the existing line, a break-even
analysis is used. The variable X is substituted into the equations that were
originally used to estimate the uniform annual costs of Alternatives 1 and
3. X represents the installation cost of cathodic protection on the existing
line. These equations are set equal to the uniform annual cost of the least
costly alternative (Alternative 2). Solving the equations for X determines
the minimum installation cost of cathodic protection required for the
uniform annual cost of Alternative 2 to be equivalent with Alternatives 1
and 3. At a higher cost than X, Alternative 2 will no longer be the most
economical alternative. The following example illustrates this process:
3-16
$118,324
$118,324
$118,324
$899,972
$899,972
$870,483
3-17
Assumptions
1. The maximum economic life of an elevated water storage tank is 25 years. It is
assumed that a salvage value of $45,000 will be remitted when the tank is replaced.
2. The predicted frequency of coating repairs required on the existing water storage
tank without cathodic protection is once every 2 years. The predicted frequency of coating replacement is once every 6 years. The tank will be replaced in the 18th year of the
analysis, when it is 25 years old. These predictions are based on historical data and technical expertise.
3. The predicted frequency of coating repairs required on the existing water storage
tank retrofitted with cathodic protection is once every 7 years. Continued maintenance
and protection is assumed. Thus, coating and tank replacement is not required during
the analysis period. This prediction is based on historical data and technical expertise.
4. To compute present values, a 10% discount rate is assumed.
5. Labor and materials costs increase (or decrease) with the general inflation rate.
This analysis requires no special treatment of inflation.
Cost/Benefit Analysis
Alternative 1 - Continue repairs and coatings of existing tank/no cathodic protection.
Cost of coating repairs: $15,000 each (every 2 years/between
coatings)
$70,000 each (every 6 years)
Cost of coating:
Cost of new installation:
Water storage tank:
Initial coating:
Terminal value:
$650,000
+ 70,000
$720,000
3-18
15
15
Repair Costs ($K)
70
Coating Costs ($K)
10 11
12
15
15
Repair Costs ($K)
70
Coating
costs
($K)
13
14
15
16
17
18
15
15
Repair Costs ($K)
70
Coating Costs ($K)
720
Installation
Costs
($K)
Figure 3-9
Cash Flow Diagram - Continue Repairs and Coatings of
Existing Tank/No Cathodic Protection
Alternative 1 (economic life - 18 years)
Amount
Project
Year(s)
0
2
4
6
8
10
12
14
16
18
18
Cost
Element
One-Time
Coating
Repair
Repair
Coating
Repair
Repair
Coating
Repair
Repair
Installation
Terminal Value
$ 70,000
15,000
15,000
70,000
15,000
15,000
70,000
15,000
15,000
720,000
(45,000)
Recurring
Discount
Factor
Discounted
Cost
1.000
0.826
0.683
0.564
0.467
0.386
0.319
0.263
0.218
0.180
0.180
$ 70,000
12,390
10,245
39,480
7,005
5,790
22,330
3,945
3,270
129,600
(8,100)
$295,955
Total Net Present Cost:
Uniform Annual Cost : $295,955/8.201 = $ 36,088
3-19
0 1 2 3 4 5 6
7 8 9 10 11 12 13
7 7 7 7 7 7
7 7 7 7
Maintenance
Maintenance
Costs ($K)
22
Costs ($K)
Repair and
Maintenance
135
Costs ($K)
Coating and
Retrofitting
Costs ($K)
14
15
16
17
18
19
20
7
7
7
7
7
7
Maintenance Costs ($K)
22
Repair and
Maintenance
Costs ($K)
22
Repair and
Maintenance
Costs ($K)
Figure 3-10
Cash Flow Diagram - Continue Repairs and Coatings of
Existing Tank/Retrofitting Cathodic Protection
Alternative 2 (economic life - 21 years)
Amount
Project
Year(s)
Cost
Element
0
0
1-21
7
14
21
Coating
Retrofit
Maintenance
Repair
Repair
Repair
One-Time
Recurring
$70,000
65,000
7,000
15,000
15,000
15,000
Discount
Factor
Discounted
Cost
1.000
1.000
8.649
0.513
0.263
0.135
$ 70,000
65,000
60,543
7,695
3,945
2,025
3-20
21
$295,955
$36,088
$209,208
$24,189
Objective: To provide corrosion control for the 100,000 ft exterior steel surface of a
water storage tank. This water storage tank is located on the Pacific Coast.
Alternatives
1. Continue applying a three-coat alkyd coating system.
2. Continue applying a three-coat epoxy coating system.
This list is not exhaustive. All feasible alternatives should be examined that will meet
the objective. For clarity of demonstration, only two alternatives will be considered in
this example.
Assumptions
1. Although the physical life of an elevated water storage tank is 40 years, due to constraints of discounting factors, a maximum economic life of 25 years will be assumed. In
reality, it may take longer than 40 years for the tank to be replaced. Thus, replacement
is not included in this analysis. To facilitate the analysis process, the economic lives
used are 24 years for the alkyd coating system and 20 years for the epoxy coating system.
This allows the ending year of the final coating application of each alternative to match
the ending analysis year.
3-21
2. The predicted frequency for recoating required for a three-coat alkyd coating
system, is once every 6 years. This prediction is based on historical data and technical
expertise.
3. The predicted frequency for recoating required for a three-coat epoxy coating
system, is once every 10 years. This prediction is based on historical data and technical
expertise.
4. To compute present values, a 10% discount rate is assumed.
5. Costs of labor and materials increase (or decrease) with the general inflation
rate. This analysis requires no special treatment of inflation.
Cost/Benefit Analysis
Alternative 1. Continue applying a three-coat alkyd coating system
Cost of applying a three-coat alkyd coating system:
Surface preparation (commercial blast):
Paint material:
Paint application:
Total
$ 0.60/ft or
2
+ 0 . 0 8 / f t or
2
+0.45/ft or
2
$ 1.13/ft or
$ 60,000
+ 8,000
+45,000
$113,000
Figure 3-11
Cash Flow Diagram - Continue Applying a Three-Coat Alkyd Coating System
3-22
Cost
Element
0
O-24
6
12
18
24
One-Time
Coating
Maintenance
Coating
Coating
Coating
Coating
Recurring
Discount
Factor
Discounted
Cost
1.000
8.985
0.564
0.319
0.180
0.102
$113,000
27,404
63,732
36,047
20,340
11,526
$113,000
$3,050
113,000
113,000
113,000
113,000
$272,049
$272,049/8.985 = $ 30,278
$ 0.80/ft or
2
+ 0.11/ft or
2
+0.60/ft or
2
$ 1.51/ft or
$ 80,000
+ 11,000
+60,000
$151,000
151
10 11
12 13
14 15
16
$2,250
+ 1,100
$3,350
17
18
19
Figure 3-12
Cash Flow Diagram - Continue Applying an Epoxy Coating System
20
151
$260,307
$260,307/8.985 = $ 28,971
Objective: To provide corrosion control for the 100,000 ft exterior steel surface of a
water storage tank. The tanks cannot be abrasively blasted because of local restrictions,
and it will be necessary to prepare the steel surface for painting by power wire brushing.
Using wire brushing to prepare the surface shortens the service lives of the coating systems. The service lives of the alkyd and epoxy systems are expected to be 5 and 6 years,
respectively.
3-24
Alternatives
1. Continue applying a three-coat alkyd coating system.
2. Continue applying a three-coat epoxy coating system.
This list is not exhaustive. All feasible alternatives should be examined that will meet
the objective. For clarity of demonstration, only two alternatives will be considered in
this example.
Assumptions
1. The physical life of an elevated water storage tank is 25 years. To facilitate the
analysis process, the economic lives used are 25 years for this alkyd coating system and
24 years for the epoxy coating system. This allows the ending year of the final coating
application of each alternative to match the ending analysis year.
2. The predicted frequency for recoating required for a three-coat alkyd coating
system, is once every 5 years. This prediction is based on historical data and technical
expertise.
3. The predicted frequency for recoating required for an epoxy coating system is
once every 6 years. This prediction is based on historical data and technical expertise.
4. To compute present values, a 10% discount rate is assumed.
5. Costs of labor and materials increase (or decrease) with the general inflation
rate. This analysis requires no special treatment of inflation.
Cost/Benefit Analysis
Alternative 1. Continue applying a three-coat alkyd coating system
Cost of applying a three-coat alkyd coating system:
Surface preparation (power wire brushing):
Paint material:
Paint application:
Total:
3-25
$ 0.50/ft or $ 50,000
2
+ 0.08/ft or + 8,000
2
+ 0 . 4 5 / f t o r +45,000
2
$ 1.03/ft or $ 103,000
$0.225/ft x 10,000 ft =
2
2
0.080/ft x 10,000 ft =
Total:
$2,250
+800
$3,050
Figure 3-13
Cash Flow Diagram - Continue Applying a Three-Coat Alkyd Coating System
Alternative 1 (economic life - 25 years)
Amount
Project
Year(s)
Cost
Element
0
0-25
5
10
20
25
Coating
Maintenance
Coating
Coating
Coating
Coating
One-Time
Recurring
$103,000
$3,050
103,000
103,000
103,000
103,000
3-26
Discount
Factor
Discounted
Cost
1.000
9.077
0.621
0.386
0.149
0.092
$103,000
27,685
63,963
39,758
15,347
9,476
$283,846
$283,846/9.077 = $ 31,271
$ 0.50/ft or
2
+0.11/ft or
2
+0.60/ft or
2
$1.21/ft or
$50,000
+ 11,000
+ 60,000
$121,000
0 1 2 3 4 5 6 7 8 9
$0.225/ft x 10,000 ft =
2
2
0.110/ft x 10,000 ft =
Total
$2,250
+ 1,100
$3,350
10 11 12 13 14 15 16 17 18 19 20 21 22
23 24
121
121
121
121
Figure 3-14
Cash Flow Diagram - Continue Applying a Three-Coat Epoxy Coating System
Alternative 2 (economic life - 24 years)
Project
Year(s)
0
0-24
6
12
18
24
Cost
Element
Coating
Maintenance
Coating
Coating
Coating
Coating
Amount
One-Time
Recurring
$121,000
$3,350
121,000
121,000
121,000
121,000
3-27
Discount
Factor
Discounted
Cost
1.000
8.985
0.564
0.319
0.180
0.102
$121,000
30,100
68,244
38,599
21,780
12,342
$292,065
$292,065/9.077 = $ 32,506
3-28
1:
2:
3:
4:
Economic Life
7 years
9 years
9 years
10 years
Alternative
Alternative
Alternative
Alternative
1:
2:
3:
4:
12 years
15 years
15 years
16 years
2. Maintenance painting will be performed when required and that the tower will
be coated again at the end of the economic life of the coating system.
3. Environmental regulations require that abrasive from blasting be disposed of as
hazardous waste. It is assumed that the disposal of abrasive at the site increases the
total cost of coating and maintenance painting by a factor of two. This is a conservative
estimate.
4. The disposal of abrasive from blasting in the shop increases the total cost of
coating and maintenance painting by a factor of 1-1/4. The cost is less than abrasive disposal at the site because an enclosed system is used and the abrasive is recycled several
times before final disposal.
5. To compute present values, a 10% discount rate is assumed.
6. Costs of labor and materials increase (or decrease) with the general inflation
rate. This analysis requires no special treatment of inflation.
Cost/Benefit Analysis
Alternative 1. Coat at the site after the tower is erected (inorganic zinc primer).
The surface is prepared with conventional abrasive blasting and coated with an inorganic zinc primer, an intermediate coat of epoxy-polyamide, and a finish coat of
aliphatic polyurethane.
Cost to coat at the site after the tower is erected:
Surface preparation (conventional blasting)
2
3-29
$0.40/ft x 10,000 ft =
2
2
$0.07/ft x 10,000 ft =
2
$2.77/ft
$4,000
+ 700
$27,700
x 2
$55,400
$3,000
+ 110
$3,110
$3.00/ft x 1,000 ft =
2
2
$0.11/ft x 1,000 ft =
2
$3.11/ft
3-30
2
$6,220
4 5 6
10
11
12
6.2
Maintenance
Painting ($K)
55.4
Coating
Costs ($K)
55.4
Coating
Costs ($K)
Figure 3-13
Cash Flow Diagram - Coated at the Site After the
Tower is Erected (inorganic zinc primer)
Alternative 1 (economic life - 12 years)
Amount
Project
Year(s)
Cost
Element
0
7
12
Coating
Maintenance
Coating
One-Time
Recurring
$55,400
6,220
55,400
3-31
Discount
Factor
Discounted
Cost
1.000
0.513
0.319
$55,400
3,191
17,673
$76,264
$76,264/6.814 = $11,192
Alternative 2. Coated at the site after the tower is erected (zinc rich epoxy primer).
The surface is prepared with conventional abrasive blasting and coated with a zinc
rich epoxy primer, an intermediate coat of epoxy-polyamide, and a finish coat of
aliphatic polyurethane.
Cost to coat at the site after the tower is erected:
Surface preparation (conventional blasting)
2
2
$ 1.20/ft x 10,000 ft = $12,000
Labor, equipment, related costs
Primer (zinc rich epoxy)
Labor, equipment, related costs
Material costs
$56,200
2
2
$3.00/ft x 1,000 ft = $3,000
2
2
$0.15/ft x 1,000 ft = $ 150
2
$3,150
$3.15/ft
3-32
$ 6,300
10
11
12
13
14
15
6.3
Maintenance
Painting Costs
($K)
56.2
Coating
Costs ($K)
56.2
Coating
Costs ($K)
Figure 3-16
Cash Flow Diagram - Coated at the Site After the
Tower is Erected (zinc rich epoxy primer)
Alternative 2 (economic life - 15 years)
Amount
Project
Year(s)
Cost
Element
0
9
15
Coating
Maintenance
Coating
One-Time
Recurring
$56,200
6,300
56,200
3-33
Discount
Factor
Discounted
Cost
1.000
0.424
0.239
$56,200
2,671
13,432
$72,303
$72,303/7.606 = $ 9,506
Alternative 3. Coated at the site before the tower is erected (inorganic zinc primer).
The surface is prepared with conventional abrasive blasting and coated with an
inorganic zinc primer, an intermediate coat of epoxy-polyamide, and a finish coat of
aliphatic polyurethane.
Cost to coat at the site before the tower is erected:
Surface preparation (conventional blasting)
2
2
$0.60/ft x 10,000 ft = $6,000
Labor, equipment, related costs
Primer (inorganic zinc)
Labor, equipment, related costs
Material costs
x 2
$30,400
$3,000
+ 110
$3,110
x 2
$6,220
3-34
x
Total cost to recoat
2
$55,400
30.4
Coating
Costs ($K)
55.4
Coating
Costs ($K)
Figure 3-17
Cash Flow Diagram - Coated at the Site Before the Tower
is Erected (inorganic zinc primer)
3-35
Amount
Project
Year(s)
Cost
Element
0
9
15
Coating
Maintenance
Coating
One-Time
Recurring
$30,400
6,220
55,400
Discount
Factor
Discounted
Cost
1.000
0.424
0.239
$30,400
2,637
13,241
$46,278
$46,278/7.606 = $ 6,084
Alternative 4. Coat in a shop before the tower is erected (inorganic zinc primer).
The surface is prepared with centrifugal abrasive blasting and coated with an
inorganic zinc primer, an intermediate coat of epoxy-polyamide, and a finish coat of
aliphatic polyurethane.
Cost to coat:
Surface preparation (white metal blasting)
2
2
$0.50/ft x 10,000 ft = $5,000
Labor, equipment, related costs
Primer (inorganic zinc)
Labor, equipment, related costs
Material costs
3-36
x 1.25
$13,875
$3,000
+ 110
$3,110
x 2
$ 6,220
3-37
x 2
$55,400
Figure 3-18
Cash Flow Diagram - Coated in a Shop Before the
Tower is Erected (inorganic zinc primer)
Alternative 4 (economic life - 16 years)
Amount
Project
Year(s)
Cost
Element
One-Time
0
10
16
Coating
Maintenance
Coating
$13,875
6,220
55,400
Recurring
3-38
Discount
Factor
Discounted
Cost
1.000
0.386
0.218
$13,875
2,401
12,077
$28,353
$20,353/7.824 = $ 3,624
= $76,264
= $11,192
Alternative 2. Coat at the site after the tower is erected (zinc rich epoxy primer)
Net present value
Uniform annual cost
= $72,303
= $9,506
Alternative 3. Coat at the site before the tower is erected (inorganic zinc primer)
Net present value
Uniform annual cost
= $46,278
= $ 6,084
Alternative 4. Coat in a shop before the tower is erected (inorganic zinc primer)
Net present value
Uniform annual cost
= $28,353
= $ 3,624
A comparison of the uniform annual costs suggest that Alternative 4 is the life
cycle cost proposal with the least associated cost.
3.7 CORROSION PREVENTION AND CONTROL FOR STEEL PIPING UNDER A
PIER
Example 6. Steel Piping Under a Pier.
Objective: Provide corrosion control for the steel piping located under a Pacific coast
2
pier. The piping is 3 inches in diameter and 1,200 feet long (surface area = 942 ft ).
Alternatives
1. Blast cleaning and applying an epoxy polymer coating.
2. Application of petroleum paste and tape.
This list is not exhaustive. All feasible alternatives should be examined that will meet
the objective. For clarity of demonstration, only two alternatives will be considered in
this example.
3-39
Assumptions
1. The maintenance painting requirement and economic life of the steel piping
varies depending on the alternative selected.
Maintenance Painting Required
Economic Life
Alternative 1: 2 years
Alternative 2: 3 years
Alternative 1: 4 years
Alternative 2: 9 years
3-40
x 2
$3,138
x 2
$ 510
Replacement Cost
Cost to install new steel piping:
Labor, equipment, related costs
Material costs
$7.00/ft x 1,200 ft
$1.00/ft x 1,200 ft
= $8,400
= $1,200
Figure 3-19
Cash Flow Diagram - Blast Cleaning and Application
of an Epoxy Polymer Coating
3-41
Amount
Cost
Element
Project
Year(s)
Coating
Maintenance
Coating
Coating
One-Time
Recurring
$ 3,138
510
14,800
3,138
Discount
Factor
Discounted
Cost
1.000
0.826
0.683
0.683
$ 3,138
421
10,108
2,143
$15,810
$15,810/3.170 = $ 4,987
$ 0 . 7 0 / f t x 942 ft = $ 659
1 2
4 5
0.33
3.6
Coating
Costs ($K)
0.33
Maintenance Costs
($K)
18.4
Replacement and
Coating Costs
($K)
Figure 3-20
Cash Flow Diagram - Tape and Application
of a Petroleum Paste
Alternative 2 (economic life - 9 years)
Amount
Project
Year(s)
0
3
6
9
9
Cost
Element
One-Time
Coating
Maintenance
Maintenance
Replacement
Coating
$ 3,673
334
334
14,800
3,673
Recurring
Discount
Factor
Discounted
Cost
1.000
0.751
0.564
0.424
0.424
$ 3,673
251
188
6,275
1,557
$11,944
$11,944/5.759 = $ 2,074
3-44
Cost/Benefit Analysis
Alternative 1. Provide no corrosion prevention or control
Cost of new installation:
Cost of replacement:
Terminal value (year 15):
Salvage value
Cost to remove existing seawall:
Terminal value:
$20,000
-8,000
$12,000
$20/ft x 1,000 ft =
$8/ft x 1,000 ft =
Terminal
Value ($K)
12
0
2 3
10
11
12
13
375
Installation
Cost ($K)
14
15
375
Installation
Cost ($K)
Figure 3-21
Cash Flow Diagram - Provide No Corrosion
Prevention or Control
Alternative 1 (economic life - 15 years)
Amount
Project
Year(s)
Cost
Element
One-Time
0
15
15
Installation
Replacement
Terminal
$375,000
375,000
(12,000)
Recurring
Discount
Factor
1.000
0.239
0.239
Cost of replacement:
Cost of seawall:
Cost of coating:
$375/ft x 1,000 ft =
$50/ft x 1,000 ft =
$425/ft
$375,000
$50,000
$425,000
0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20
425 Installation
Cost ($K)
Replacement
Cost ($K)
Figure 3-22
Cash Flow Diagram - Coat the Seawall
Alternative 2 (economic life - 20 years)
Amount
Project
Year(s)
0
20
20
Cost
Element
Installation
Replacement
Salvage
One-Time
Recurring
$425,000
425,000
(12,000)
Discount
Factor
Discounted
Cost
1.000
0.149
0.149
$425,000
63,325
(1,788)
$486,537
Total Net Present Value Cost:
$486,537/8.514 = $ 57,145
Uniform Annual Cost:
3-46
425
$5/ft x 1,000 ft =
$ 5,000
455
Installation
Costs ($K)
Figure 3-23
Cash Flow Diagram - Provide Cathodic Protection
and Coat the Seawall
Alternative 3 (economic life - 25 years)
Amount
Project
Year(s)
Cost
Element
0
1-25
Installation
Maintenance
One-Time
Recurring
Discount
Factor
5,000
1.000
9.077
$455,000
Discounted
Cost
$455,000
45,385
3-47
3-48
Assumptions
1. The economic life of the seawall varies depending on the alternative selected:
a.
b.
c.
d.
2. A salvage value of $20/ft or $20,000 will be remitted when the seawall is replaced.
3. Mechanical repair of the existing seawall will extend the economic life 10 years.
Replacement will then be necessary.
4. Mechanical repair of the existing seawall and intertidal coating will extend the
economic life 15 years. Replacement will then be necessary.
5. Mechanical repair of the existing seawall, intertidal coatings, and installing cathodic
protection will extend the economic life indefinitely.
6. To compute present values, a 10% discount rate is assumed.
7. Costs of labor and materials increase (or decrease) with the general inflation rate.
This analysis requires no special treatment of inflation.
Cost/Benefit Analysis
Alternative 1. Mechanical repair of the existing seawall (no corrosion prevention or
control)
Cost to repair:
Cost of replacement:
Terminal value (year 10):
Salvage value:
Cost to remove existing seawall:
3-49
Terminal
Value ($K)
12
65
Repair
costs
($K)
375
Replacement
Costs ($K)
Figure 3-24
Cash Flow Diagram - Mechanical Repair of Existing Seawall
(no corrosion prevention or control)
Alternative 1 (economic life - 10 years)
Amount
Project
Year(s)
0
10
10
Cost
Element
Mechanical
Repair
Replacement
Terminal Value
One-Time
Recurring
$ 65,000
375,000
(12,000)
Discount
Factor
Discounted
Cost
1.000
0.386
0.386
$205,118
Total Net Present Value Cost:
$205,118/6.145 = $ 33,380
Uniform Annual Cost:
3-50
$375/ft x 1,000 ft =
+50/ft x 1,000 ft =
$425/ft
$375,000
+ 50,000
$425,000
Figure 3-25
Cash Flow Diagram - Mechanical Repair of Existing Seawall (coat only)
Alternative 2 (economic life - 15 years)
Amount
Project
Year(s)
0
0
15
15
Cost
Element
Mechanical
Repair
Intertidal
Coating
Replacement
Terminal Value
One-Time
Recurring
Discount
Factor
1.000
$ 65,000
15,000
425,000
(12,000)
1.000
0.239
0.239
Discounted
Cost
$ 65,000
15,000
101,575
(2,868)
3-51
Cost to repair:
Cost to coat intertidal:
Cost of retrofitting cathodic
protection on the seawall:
Cost of annual maintenance
(cathodic protection):
Figure 3-26
Cash Flow Diagram - Mechanical Repair
of Existing Seawall (coat and cathodic protection)
Amount
Project
Year(s)
0
0
0
l-25
Cost
Element
Mechanical
Repair
Intertidal
Coating
Retrofit
Maintenance
One-Time
Recurring
Discount
Factor
Discounted
Cost
$ 65,000
1.000
$ 65,000
15,000
30,000
1.000
1.000
9.077
15,000
30,000
45,385
5,000
$155,385
Total Net Present Value Cost:
$155,385/9.077 = $ 17,118
Uniform Annual Cost:
3-52
Cost of replacement:
Terminal value (year 15):
Salvage value:
Cost to remove existing seawall:
Terminal
Value ($K)
12
10
11
12
13
375
Replacement
Costs ($K)
14
15
375
Replacement
Costs ($K)
Figure 3-27
Cash Flow Diagram - Replace the Seawall
(no corrosion prevention or control)
Alternative 4 (economic life - 15 years)
Amount
Project
Year(s)
0
0
15
15
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
One-Time
Recurring
$375,000
(12,000)
375,000
(12,000
Discount
Factor
Discounted
Cost
1.000
1.000
0.239
0.239
$375,000
(12,000)
89,625
(12,000)
$449,757
Total Net Present Value Cost:
$449,757/7.606 = $ 59,132
Uniform Annual Cost:
3-53
1 2 3 4
425
Replacement
Costs ($K)
10
11
12
13
14
15
16
17
18 19
0
0
20
20
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
20
Replacement 425
Costs ($K)
Figure 3-28
Cash Flow Diagram - Replace the Seawall (coat only)
Project
Year(s)
12
One-Time
Recurring
$425,000
(12,000)
425,000
(12,000)
Discount
Factor
Discounted
Cost
1.000
1.000
0.149
0.149
$425,000
(12,000)
63,325
(1,788)
$474,537
Total Net Present Value Cost:
$474,537/8.514 = $ 55,736
Uniform Annual Cost:
3-54
12 Terminal
Value ($K)
1 2 3 4 5 6 7 8 9 10 11
12 13 14 15 16 17 18 19 20 21 22 23 24 25
455 Replacement
Costs ($K)
Figure 3-29
Cash Flow Diagram - Replace the Seawall
(coat and cathodic protection)
Alternative 6 (economic life - 25 years)
Amount
Project
Year(s)
0
0
1-25
Cost
Element
Replacement
Terminal Value
Maintenance
One-Time
Recurring
$455,000
(12,000)
5,000
Discount
Factor
Discounted
Cost
1.000
$455,000
(12,000)
45,385
9.077
$488,385
Total Net Present Value Cost:
$488,385/9.077 = $ 53,805
Uniform Annual Cost:
3-55
3-56
3-57
Cost/Benefit Analysis
Alternative 1. Hollow core wood interior with steel exterior doors
Doors to be replaced annually = 75 doors
Cost of installation (per door):
Materials (per door)
$ 300.00
+ 100.00
$ 400.00
(a) Door
(b) Frame
4.00
$ 26.41/hr
x
2hrs
$ 52.82
$ 26.41/hr
x
9 hrs
$ 237.69
4.00
$ 26.41/hr
x 1 h r
$ 26.41
$ 724.92
339
$ 724.92
75
x
$54,369.00
3-58
0 1 2 3 4 5 6 7 8
9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25
54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.3 54.5 54.3
Replacement Costs ($K)
Figure 3-30
Cash Flow Diagram - Hollow Core Wood Interior,
Steel Exterior Doors
Alternative 1 (economic life - 25 years)
Amount
Project
Year(s)
Cost
Element
1-25
Replacement
One-Time
Recurring
Discount
Factor
$54,369
9.077
Discounted
Cost
$493,507
$ 300.00
+125.00
$ 425.00
$ 26.41/hr
3-59
x
9 hrs
$ 237.69
$ 662.69
339
$ 662.69
x
47
$31,146.00
Figure 3-31
Cash Flow Diagram - Fiberglass Gelcoat Balsa
Wooden Core Exterior Doors
Alternative 2
Amount
Project
Year(s)
Cost
Element
1-25
Replacement
One-Time
Recurring
Discount
Factor
$31,146
9.077
Discounted
Cost
$282,712
$282,712
Total Net Present Value Cost:
$282,712/9.077 = $ 31,146
Uniform Annual Cost:
3-60
3-61
$ 210,795
295
x
$ 62,184,525
3-62
Cost/Benefit Analysis
Alternative 1 - Galvanized steel rain gutters
Cost to replace rain gutters (includes downspouts):
Installation costs: $0.70/ft x 70 ft x 100 houses = $ 4,900
Material costs: $1.30/ft x 70 ft x 100 houses = + 9,100
$2.00/ft
$ 14,000
Cost of maintenance painting: $30/house x 100 houses = $3,000
0
3
3
3
Paint Costs ($K)
17 Replacement
Cost ($K)
17 Replacement
Costs ($K)
Figure 3-32
Cash Flow Diagram - Galvanized Steel Rain Gutters
Alternative 1 (economic life - 8 years)
Amount
Project
Year(s)
Cost
Element
Replacement
Paint
Paint
Paint
Paint
Replacement
Paint
One-Time
Recurring
$14,000
3,000
3,000
3,000
3,000
14,000
3,000
3-63
Discount
Factor
Discounted
Cost
1.000
1.000
0.826
0.683
0.564
0.467
0.467
$14,000
3,000
2,478
2,049
1,692
6,538
1,401
$31,158
$31,158/5.335 = $ 5,840
10
11
16.8
Replacement
Costs ($K)
12
16.8
Replacement
Costs ($K)
Figure 3-33
Cash Flow Diagram - Plastic Rain Gutters
Alternative 2 (economic life - 12 years)
Amount
Project
Year(s)
Cost
Element
One-Time
0
12
Replacement
Replacement
$16,800
16,800
Recurring
Discount
Factor
1.000
0.319
Discounted
Cost
$16,800
5,359
$22,159
Total Net Present Value Cost:
Uniform Annual Cost:
$22,159/6.814 = $ 3,252
3-64
18.2
Replacement
Costs ($K)
18.2
Replacement
Costs ($K)
Figure 3-34
Cash Flow Diagram - Aluminum Rain Gutters
Alternative 3 (economic life - 10 years)
Amount
Project
Year(s)
Cost
Element
0
10
Replacement
Replacement
One-Time
Recurring
$18,200
18,200
Discount
Factor
Discounted
Cost
1.000
0.386
$18,200
7,025
3-65
3-66
2. At the end of the economic life, the entire fence will be replaced.
3. When the existing fence is replaced, there is a removal cost of
$0.15/ft x 1,200 ft = $180 fence and that the removal produces no salvage value.
4. To compute present values, a 10% discount rate is assumed.
5. Costs of labor and materials increase (or decrease) with the general inflation
rate. This analysis requires no special treatment of inflation.
Cost/Benefit Analysis
Alternative 1. Galvanized steel chain link fence in a tropical marine environment.
Cost to replace fence:
Installation costs $1.25/ft x 1,200 ft = $1,500
Material costs $1.50/ft x 1,200 ft = $1,800
$2.75/ft
$3,300
$ 0
3-67
Amount
Project
Year(s)
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
One-Time
Recurring
$3,300
180
3,300
180
3-68
Discount
Factor
Discounted
Cost
1.000
1.000
0.751
0.751
$3,300
180
2,478
135
$6,093
$6,093/2.487 = $2,450
0.18
3.7
3.7
Replacement Costs ($K)
Figure 3-36
Cash Flow Diagram - Vinyl-Coated Steel
Chain Link Fence (tropical marine environment)
Alternative 2 (economic life - 6 years)
Amount
Project
Year(s)
0
0
3
3
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
One-Time
Recurring
$3,720
180
3,720
180
3-69
Discount
Factor
Discounted
Cost
1.000
1.000
0.564
0.564
$3,720
180
2,098
101
$6,099
$6,099/4.355 = $1,400
$ 0
$ 180
$180
0.18
3.3
3.3
Replacement Costs ($K)
Figure 3-37
Cash Flow Diagram - Galvanized Steel
Chain Link Fence (temperate marine environment)
Alternative 1 (economic life - 7 years)
Amount
Project
Year(s)
0
0
7
7
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
One-Time
Recurring
$3,300
180
3,300
180
3-70
Discount
Factor
Discounted
Cost
1.000
1.000
0.513
0.513
$3,300
180
1,693
92
$5,265
$5,265/4.868 = $1,082
0.18
$
0
$ 180
$ 180
0.18
3.7
Replacement
Costs ($K)
3.7
Replacement
Costs ($K)
Figure 3-38
Cash Flow Diagram - Vinyl-Coated Steel
Chain Link Fence (temperate marine environment)
Alternative 2 (economic life - 10 years)
Amount
One-Time
Terminal Value
Recurring
$3,720
180
3,720
180
3-71
Discount
Factor
Discounted
Cost
1.000
1.000
0.386
0.386
$3,720
180
1,436
69
$5,405
$5,405/6.145 = $ 880
0.18
$ 0
$ 180
$ 180
3.3
10
0.18
11
12
13
14
15
3.3
Figure 3-39
Cash Flow Diagram - Galvanized Steel Chain Link Fence
in a Rural (non-marine) Environment
Alternative 1 (economic life - 15 years)
Amount
Project
Year(s)
0
0
15
15
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
Recurring
One-Time
$3,300
180
3,300
180
3-72
1.000
1.000
0.239
0.239
$3,300
180
789
43
$4,312
$4,312/7.606 = $ 567
$ 0
$ 180
$ 180
1 2 3 4 5 6 7 8 9 10 11
I
12 13 14 15 16 17 18 19 20 21 22 23 24 25
Replacement Costs ($K)
3.7
3.7
Figure 3-40
Cash Flow Diagram - Vinyl-Coated Chain Link Fence in a
Rural (non-marine) Environment
Alternative 2 (economic life - 25 years)
Amount
Project
Year(s)
0
0
25
25
Cost
Element
Replacement
Terminal Value
Replacement
Terminal Value
0.18
One-Time
Recurring
$3,720
180
3,720
180
3-73
Discount
Factor
Discounted
Cost
1.000
1.000
0.092
0.092
$3,720
180
342
17
$4,259
$4,259/9.077 = $ 469
3-74
Figure 4-1
Electrochemical Cell
4-l
Anode. In an electrochemical cell, the anode is the site where electrons are
produced through the chemical activity of the metal. The anode is the area where metal
loss occurs. The metal loses electrons and migrates from the metal surface through the
environment. The electrons remain in the metal but are free to move about in response
to voltage gradients.
Cathode. The cathode in an electrochemical cell is the site where electrons
are consumed. For each electron that is produced at an anodic site, an electron must be
consumed at a cathodic site. No metal loss occurs at sites that are totally cathodic.
Electron Path. In order for electrons to flow from the anodic sites to
cathodic sites, the electrons migrate through a metallic path. This migration occurs due
to a voltage difference between the anodic and cathodic reactions. Electrons can move
easily only through metals and some non-metals such as graphite. Electrons from
electrochemical reactions cannot move through insulating materials such as most plastics nor can they directly enter water or air. In some cases, the electron path is the corroding metal itself, in other cases, the electron path is through an external electrical
path.
Electrolyte. Electrolytes are solutions that can conduct electrical currents
through the movement of charged chemical constituents called ions. Positive and negative ions are present in equal amounts. Positive ions tend to migrate away from anodic
areas and toward cathodic areas. Negative ions tend to migrate away from cathodic
areas and towards anodic areas.
Anodic Reactions. Metal loss at anodic sites in an electrochemical cell occurs when
the metal atoms give up one or more electrons and move into the electrolyte as positively charged ions.
Typical Reactions. The generic chemical formula for this metal loss at
anodic sites is:
M
where:
>
M +
4-2
This type of chemical reaction is called oxidation even though it does not directly involve oxygen but only results in an increase in positive charge on the atom undergoing
oxidation.
More than one electron can be lost in the reaction as in the case for iron where the
most common anodic reaction is:
F
>
F e
+ +
2 e
where:
F e = metallic iron
F e
+ +
Correlation Between Current Flow and Weight Loss. For each specific
anodic reaction a characteristic number of electrons are produced in the reaction of one
metal ions. Thus, all other things being equal, the metal loss is proportional to the number of electrons that are produced. As the electrons produced migrate to cathodic areas
through the electron path, the metal loss is proportional to the current flow. In cases
where more positively charged ions are produced, more electrons flow for a given number of corroding metal atoms but the current flow remains proportional to the metal
loss.
Cathodic Reactions. The electrons that are produced at anodic sites are consumed
at cathodic sites. The type of chemical reactions that consume electrons are called
reduction and have the generic chemical formula:
+
where:
e
+
>
> R
4-3
e
+
Where:
>
e = electron
o
H = hydrogen atom
In most cases, the hydrogen atoms combine in pairs to form hydrogen gas (H2), which is
often visible as bubbles on the metal surface.
Reactions in Neutral and Alkaline Solutions. In alkaline solutions, there
are few hydrogen ions. In such solutions, other cathodic reactions predominate. The
most common cathodic reaction in such solutions is the reduction of water. The formula for this reaction is:
2 H2 O + O2 + 4 e
> 4 OH
In this reaction, two water molecules combine with one oxygen molecule and four
electrons to form four hydroxyl (OH ) ions. This reaction requires oxygen and proceeds
rapidly when the oxygen content of the environment is high. The production of hydroxyl
ions makes the solution in the area of the cathodes more alkaline. Although this is the
most common cathodic reaction in seawater or other alkaline environments, other reactions can and will occur, particularly if the amount of dissolved oxygen is reduced.
Overall Reactions. The generic formula for the overall electrochemical reaction is:
M
>
M +
In this formula, the electrons, which are exchanged in equal amounts, are not noted.
Reaction Rates. Most metals tend to corrode in any environment where moisture
is present. However, the rate of corrosion can often be controlled to acceptable levels.
As electrochemical reactions depend on electron production at the anode, electron conduction through the electron path and electron combination at the cathode, the rate of
reaction can be controlled by controlling the reactions at either the anodes or cathodes
or by increasing the resistance to the flow of electrons through the electron path.
4-4
The site where the electrochemical activity is most limited controls the overall
reaction rate.
Polarization. In electrochemical reactions, chemical activity at or near the metal
surface can have a significant effect on the reaction rates. These reactions often limit
the flow of current in the reactions and result in polarization, or resistance to flow of current across the metal-electrolyte interface.
Formation of Films. The buildup of reaction products is a common cause
of polarization. Metal ions buildup at anodic sites and make the formation of more
metal ions more difficult. Similar buildup of reaction products, such as hydrogen gas or
hydroxyl ions, at cathodic areas inhibit further reactions there. This reduction of reaction rates due to the buildup of reaction products is common in many chemical reactions and is called the law of mass action. The law of mass action states that in a
generic reaction such as:
M
>
M +
That an excess of materials, which appear on the left of the arrow, will increase the reaction rate whereas an excess of the materials on the right will decrease the reaction rate.
In many environments, polarization at the cathode due to the buildup of hydroxyl
ions is a common limiting factor in the rate of corrosion. Under flow conditions,
polarization if commonly reduced as the materials causing polarization are rapidly carried away.
Passivity. In some cases the surface of a metal is naturally covered by a film
of reaction products. Stainless steels and titanium alloys are resistant to corrosion in
many environments due to the presence of such passive films. In the case of stainless
steel and titanium, these films are oxides and are naturally formed during the manufacture of the materials. This film causes a high level of polarization and can result in excellent resistance to corrosion. In some environments, however, these passive films can
break down and result in localized attack.
Supply of Reactants. Polarization can also be caused by limiting the amount
of materials required for reactions that are available at the metal surface. An example
of this type of polarization occurs in the typical cathodic reaction in alkaline or neutral
solutions:
2
H2 O + O2 + 4 e
> 4 OH
4-5
In this case, the availability of oxygen can limit the reaction rate. The availability of
oxygen can be affected by both the amount of oxygen dissolved in the electrolyte and by
the velocity of flow that provides a continuous source of water that is rich in oxygen.
Seawater as an Electrolyte. Seawater is an excellent electrolyte. The presence
of a large amount of dissolved salts, sodium chloride (NaCl), that are ionized make it an
excellent conductor. The chloride ions is particularly aggressive as it causes a breakdown of passivity. The chloride ion is also particularly aggressive as most chloride compounds are highly soluble, which limits the formation of polarizing anodic films.
Seawater also usually contains enough dissolved oxygen for reducing water to be the
prevalent cathodic reaction in most cases.
4.3 FORMS OF CORROSION. Although there is only one fundamental mechanism of
corrosion, the electrochemical cell, there are several forms of attack that can occur.
Each form of attack has a specific arrangement of anodes and cathodes and the corrosion which occurs has a specific location and pattern. Each form of corrosion can be
effectively controlled during design if it is anticipated. By understanding the various
forms of corrosion, the conditions under which they occur, and how they are quantified,
they can each be addressed and controlled.
4.3.1 Immunity. The first form of corrosion described is the lack of attack, or
immunity. This can result from the action of two basic mechanism. Corrosion test
measurements that are used to measure very low corrosion rates must be used to
validate that corrosion activity is completely absent.
Definition. Immunity is the lack of measurable attack on a metal when
exposed to operational environments.
Mechanism. Immunity can result from two basic mechanisms. In the first
case, the energy content of the metal is lower (more stable) than any of the corrosion
products that could possibly form. Such metals are commonly found in nature as metals
that indicates the stability of the metallic state for these elements. Corrosion of such
metals where an increase of energy is required will not take place naturally just as a ball
will not roll uphill unless pushed. In the second case, there is an energy tendency for the
metal to corrode, but corrosion activity is prevented by the presence of a highly stable
passive film. Not only must this film be stable in the environment, but it must be able to
repair itself by reaction with the environment if it is damaged.
Examples. Gold and platinum are examples of metals that are normally
immune in a wide variety of environments due to the low energy content of their metallic state. Titanium and some highly alloyed materials, such as the complex nickelchromium-molybdenum alloy Hastelloy C-276, have an extremely stable passive film
that will repair itself when damaged.
4-6
then exposed for a specific period of time, re-cleaned and re-weighed. The amount of
metal loss as measured by the weight loss is used to calculate the loss in thickness of the
metal assuming that the corrosion was absolutely uniform. In some cases this is further
verified by thickness measurements. These results are commonly expressed in Mils per
Year or Microns per Year. It must be remembered that these rates are usually calculated from weight loss rather than thickness loss and are only valid if the attack was
uniform. The maximum error of this measurement is theoretically a factor of two if the
rule that attack can be no greater than twice the average rate at any given point is
properly applied.
4.3.3 Galvanic Corrosion. When two different metals are electrically connected
in an electrolyte, the electrochemical cell formed is called a galvanic cell. This is one of
the original forms of electrochemical cell that was discovered and was used to produce
direct current electricity in a battery. The dry cell batteries in common use today use
the galvanic corrosion of zinc as an anode in conjunction with graphite as a cathode to
produce useful electric current. Galvanic corrosion is a similar but undesirable for of
electrochemical action.
Definition. Galvanic corrosion is corrosion that is caused or accelerated
through the electrical coupling of two or more dissimilar metals that are both immersed
in an electrolyte.
Mechanism. As shown in Figure 4-2, galvanic corrosion is caused by
classical electrochemical activity. The more active metal acts as an anode. The less active metal acts as a cathode. The rate of attack on the anode is usually controlled by the
activity of the cathode or the resistance of the external circuit.
Figure 4-2
Galvanic Cell
4-8
The Galvanic Series. The activity of most metals and alloys has been
determined both experimentally and through practical experience. In a galvanic series,
the metals are listed in order of their activity, usually with the most active metals listed
higher in the series. A galvanic series for common metals in seawater is given in Table
4-1. In this series, when coupled with a metal lower in the series, a metal will suffer accelerated attack. The ordering of materials in the galvanic series for a wide variety of
environments such as fresh water and soils closely follows their ordering in the galvanic
series for seawater.
Galvanic Corrosion Rates. The rate at which galvanic corrosion proceeds
can be controlled by the rate of activity at either the anode or the cathode or by electrical resistance of the electron path. The driving force for the reaction is the potential difference between the anode and cathode. This is a function of their separation in the
galvanic series. Metals that are close to each other in the galvanic series will suffer less
attack than widely separated metals, all other factors remain equal.
In common situations in many environments the limiting factor is the activity at the
cathode. Corrosion at the anode will usually occur as fast as the reaction as the cathode
can consume the electrons produced at the anode. The relative exposed areas of anodic
and cathodic metals in a galvanic cell is a very important factor in the rate at which galvanic corrosion will attack the anodic material. If, as in Figure 4-3, the exposed anodic
area is large with respect to the exposed cathodic area, the attack at the anode is limited
by the ability of the electrons produced at the anode to be consumed at the small
cathode. However, if as in Figure 4-4, the exposed cathodic area is large with respect to
the exposed anodic area, the electrons produced in the anodic reaction are easily consumed over the large cathode and the activity is concentrated in a small anodic area.
Thus, when the anode is small with respect to the cathode, the most severe attack will
occur. The application of protective coatings can affect the effective areas of metals in
galvanic cells. If the anode is coated and the cathode is left bare, the effective cathode/
anode areas are large and rapid attack can occur at the anode.
Examples. When two or more dissimilar metals are electrically connected
and immersed in an electrolyte, galvanic corrosion will occur. As nearly every structure
or piece of equipment is constructed of more than one metal, galvanic corrosion is likely
to occur. Ships hulls are severely affected by the electrical coupling with their bronze
propellers unless corrective action is taken. Aluminum alloys are particularly susceptible to galvanic attack due to their high activity. If isolated, the performance of many of
the aluminum alloys is satisfactory, but galvanic corrosion can cause rapid attack, particularly when adverse area ratios are encountered.
Stray electrical currents can also result in what is essentially galvanic corrosion.
This is particularly severe where direct currents are involved but can also occur with alternating current. Where the (positive) current leaves the metal and enters the
4-9
Table 4-1
Galvanic Series in Seawater
Most Active
Least Active
Magnesium
Zinc
Galvanized Steel (New)
Aluminum Alloy 7000 Series
Aluminum Alloy 6000 Series
Pure Aluminum (99 + %)
Aluminum Alloy 3000 Series
Aluminum Alloy 2000 Series
Aluminum Alloy 5000 Series
Mild Steel
Alloy Steel
Cast Iron
Monel Alloy 400 (Active)
Stainless Steel 410 (Active)
Stainless Steel 430 (Active)
Solder (60% Pb - 40% Sn)
Stainless Steel 304 (Active)
Stainless Steel 316 (Active)
Stainless Steel Alloy 20-Cb (Active)
Lead
Tin
Muntz Metal
Manganese Bronze
Naval Brass
Nickel (Active)
Yellow Brass
Admiralty Brass
Aluminum Bronze
Red Brass
Copper
Silicon Bronze
Nickel Silver
Cupro-Nickel 90-10
Cupro-Nickel 80-20
Cupro-Nickel 70-30
G-Bronze
M-Bronze
Nickel (Passive)
Silver Solder
Monel (Passive)
Stainless Steel 410 (Passive)
Stainless Steel 430 (Passive)
Stainless Steel 316 (Active)
Stainless Steel 304 (Passive)
Stainless Steel Alloy 20-Cb (Passive)
Silver
Inconel 625
Hastelloy C
Titanium
Graphite
Gold
Platinum
4-10
electrolyte it does so through an anodic reaction. For alternating currents, the current
reverses during each cycle. The anodic activity is periodic and partially counteracted
while the surfaces are cathodic.
Appearance. Galvanic corrosion can take many forms on the anodic
surfaces. It can either be uniform or non-uniform. Very high galvanic corrosion activity
can be accompanied with the formation of gas bubbles on both the anodes and the
cathodes.
Small Anode
Large Cathode
Small Cathode
Large Anode
Figure 4-4
Adverse Area Relationship
Figure 4-3
Benign Area Relationship
4.3.5 Concentration Cell Corrosion. As mentioned above, a difference in environment between sites on a single metal can also result in increased electrochemical
activity. This difference in environment can be due to non-uniform deposits or fouling
on the surface, or, more commonly, built in features which create significant difference
in environment. Crevices at joints are the most common cause of these built in environmental differences. This form of concentration cell corrosion called crevice corrosion
is often the most difficult form of corrosion to avoid in design and also is one of the
most common causes of failure of marine equipment.
Definition. Concentration cell corrosion is corrosion that is accelerated
by differences in environment between separated areas on a single metal.
Mechanism. Any situation that creates a difference in environment
between areas on a single metal can cause concentration cell attack. The basic
mechanism is essentially the same as in galvanic corrosion but in the case of concentration cell corrosion the driving force is the difference in potential between a single metal
exposed to different environments rather than the difference in potential between two
different metals exposed to a single environment. The rates of attack experienced in
concentration cell corrosion are affected by relative anode/cathode areas in the same
manner as in galvanic corrosion. In crevice corrosion, the resistance of the electrolyte
to the flow of ions can also be a significant factor in limiting attack in deep tight crevices.
Oxygen Concentration Cells. Dissolved oxygen has a significant
effect on the corrosion of many metals. This is particularly true for alloys such as stainless steels where the corrosion resistance of the alloy is dependent upon abundant
oxygen for the stability and self-repair of protective films. Oxygen is also an active participant in the most predominant cathodic reaction in many environments. The oxygen
content of the electrolyte inside a crevice is usually low as oxygen is consumed by both
corrosion and biological activity and replacement of oxygen inside the crevice is limited.
The crevice can be formed by metal-to-metal contact, by contact of a metal with a nonmetal or under deposits of debris or fouling.
For a metal with a passive film, the metal tends to become active within the crevice
where the lack of oxygen causes the passive film to be less stable and less easily
repaired. The resulting active/passive cell has substantial driving potential as noted on
the galvanic series. The anodic area within the crevice is normally small with respect to
the cathodic area outside the crevice and with this adverse area ratio, the corrosion inside the crevice can be very rapid. Once initiated, crevice corrosion can also be accelerated by the formation of aggressive chemical compounds within the crevice which
further accelerates the attack within the crevice. In the case of stainless steels, the
chromium and nickel chlorides which are formed are very acidic and crevice corrosion
can be very rapid once initiated.
4-13
Oxygen concentration cell corrosion can also occur on metals which do not have
passive films. In this case, the difference in oxygen content makes the area with low
oxygen content predominantly anodic with respect to more highly oxygenated areas.
The reason for this is due to the effect of the law of mass action on the predominant
cathodic reaction in neutral and alkaline environments. This reaction is:
2 H2 O
O2 + 4 e
> 4 OH
The law of mass action indicates that, where the oxygen content is high, the cathodic
reaction will occur more readily than when the oxygen content is low. Thus areas where
the oxygen content is low will not be as effective a cathode, anodic reactions will
predominate and the area will act as an anode. Where the oxygen content is high, the
cathodic reactions will predominate and the area will act as a cathode. Thus, the area inside a crevice will be anodic with respect to the area outside and the same process as
described above for active/passive oxygen concentration cells will occur.
Oxygen concentration cell crevice corrosion is particularly insidious. First, many
material are susceptible to this form of attack that have otherwise excellent performance in marine environments. Second, the attack often occurs deep inside crevices in
sealed areas, in joints, and in fasteners where a very small amount of corrosion can
result in a serious failure. Third, as it occurs deep within the crevice, it is difficult to
detect. Crevice corrosion of this type often remains hidden until revealed by failure.
Metal Ion Concentration Cells. Differences in concentration of
other dissolved materials. In metal ion concentration cells the difference in concentration of metal ions, usually those formed during the corrosion process, cause accelerated
corrosion. In crevices or other protected areas, the metal ions produced by corrosion
build up to high concentrations. In boldly exposed areas the concentration of these ions
is lower due to diffusion and natural flushing of the surfaces. As in the case of oxygen
concentration cells, this form of attack is governed by the law of mass action. In this
case, it is the anodic reaction that is affected. In the anodic reaction:
M
>
M + e
a buildup of metal ions inhibits the reaction. In areas where the anodic reaction is inhibited, cathodic reactions predominate and those areas become cathodes. In areas
where the relative content of metal ions is low, the reaction can proceed freely and
those areas tend to become anodic. In metal ion concentration cell attack, it is the areas
outside the crevices which are anodic. Thus, in metal ion concentration cell attack, corrosion is concentrated just inside or at the entrance to the crevice. In most configurations, the area outside the crevices is much larger than that inside. Thus the
anode/cathode area is more favorable than in oxygen concentration cell attack and the
acceleration of attack is less severe.
4-14
normal handling. Single phase material, where the alloy constituents are well mixed,
are often less susceptible to this form of attack than alloys where phases of largely different composition are present. In many alloys, heat treatments have been developed
specifically to make the alloy more homogeneous and less susceptible to dealloying.
Examples. The dezincification of brass and the graphitization of cast iron
are common examples of dealloying.
Appearance. In dealloying, the size and shape of the original component is
often retained. The remaining constituent is often a different color than the original
alloy and the depth and location of attack can be easily identified by this color change.
Dealloying can either occur over the entire surface (layering) or localized in pits (plug
type).
Significant Measurements. Weight loss is not a significant measurement
of the impact of dealloying. The depth of attack must be measured by sectioning and
microscopic examination. The impact of dealloying on the strength of the material can
be assessed through mechanical testing. In many cases, the depth of attack is self-limiting, particularly in the plug type of attack but the limiting depth is significant, often in
the order of 1/4 inch. The fact that there is a limiting depth is significant only for very
thick walled sections.
4.3.7 Intergranular Corrosion. Just as most engineering metals are mixtures of
one or more metals, they consist of large numbers of individual metal crystals called
grains that are joined together at their surfaces or grain boundaries. As there can be differences in composition at or adjacent to these grain boundaries, selective corrosion can
occur at these sites.
Definition. Intergranular corrosion is a selective attack of a metal at or
adjacent to grain boundaries.
Mechanism. There are three mechanisms that have been identified as
causing intergranular corrosion in various situations.
1. The first mechanism is the selective attack of grain boundary material
due to its high energy content. Metal crystals form in an ordered arrangement of atoms
because this ordered arrangement has a lower energy content than a disordered arrangement. Grain boundaries are highly disordered as they are at the boundaries of crystals
which, although they are internally ordered, have random orientation with respect to
each other. The disordered grain boundary is often 10 to 100 atoms wide and these
atoms have a higher energy than the surrounding atoms. Higher energy material can be
more chemically active than lower energy material and thus, the grain boundary
material can be anodic with respect to the surrounding grains. When this occurs, the
4-16
anodic area is small and the cathodic area is large, thus, rapid attack can occur. The
result is that the individual grains are no longer joined with the strong grain boundary
glue and disintegrate leaving a powdery residue and rough grainy surface.
2. A second mechanism is selective attack of grain boundary material that
has a different composition from the surrounding grains. When metals crystallize from
the molten state, the crystals tend to be more pure than the molten material. This is because the pure metal crystals are more ordered and have a lower energy content than if
they contained large amounts of impurities. In some cases, most of the impurities are
concentrated at the grain boundaries. When the composition of this impure material
causes it to be more anodic than the surrounding grains, rapid attack can occur with
results similar to those described above. When the composition of the impure grain
boundary material causes it to be more cathodic than the surrounding grains, the
favorable anode/cathode area ratio makes this situation relatively innocuous. Contamination of grain boundaries can sometimes also occur after manufacture. Mercury
on aluminum can penetrate and contaminate the grain boundaries and cause subsequent intergranular attack. This is why mercury and mercury compounds are
prohibited aboard aluminum ships or on aircraft.
3. A third mechanism is selective attack adjacent to the grain boundaries
due to the local depletion of an alloying element. This form of attack can occur in many
stainless steels. It is called sensitization. Many stainless steels rely on a combination of
nickel and chromium for their corrosion resistance. As both nickel and chromium are
expensive, they are added only in amounts necessary to obtain the necessary corrosion
resistance. Another element, which is commonly present in ail steels, is carbon. In
stainless steels, carbon atoms tend to concentrate at the grain boundaries as an impurity
during solidification. Chromium carbides can form adjacent to the grain boundaries
during welding and heat treatment. When these compounds form, the chromium is
removed from the alloy adjacent to the grain boundaries and the resulting alloy does not
have enough chromium content to remain passive. Again, there is a very unfavorable
anode/cathode area ratio and rapid attack can occur. Three different methods are used
to avoid this type of attack in stainless steels during welding or other heating.
a. The first method to avoid sensitization is through heat treatment. At
high temperatures (above 1,800F), chromium carbides are unstable and will redissolve
if they have formed. At low temperatures, (below 1,000F) the chromium and carbon
atoms cannot move and formation of chromium carbides is prevented. Formation of
the chromium carbides is a problem primarily in the ranges of 1,100 to 1,600F. When
welding stainless steel, some area adjacent to the weld is likely to reach this temperature
range long enough to form amounts of chromium carbides. When this occurs, or when
the alloy is otherwise sensitized, it should be heated to temperatures above 1,800F to
redissolve the carbides, then rapidly cooled to below 1,000F to avoid carbide formation.
4-17
4-18
Mechanism. Even after many years of intensive study, the exact mechanism
of stress corrosion cracking remains a matter of extensive disagreement and study. It is
commonly attributed to the rupture of protective films at the tips of pits or pre-existing
cracks due to the applied stress. In many cases, the materials appear to be totally resistant to corrosion in a given environment until stresses are applied. They then crack
catastrophically without any sign of other corrosion attack.
Examples. Many materials, particularly high strength materials, are
susceptible to stress corrosion cracking when exposed to a specific environment. For example, cold worked brass, which is found in ammunition cartridges, is susceptible to
stress corrosion cracking when exposed to an environment containing ammonia. In
chloride containing environments, titanium alloys, aluminum alloys, and high strength
stainless steels are susceptible and specific alloys, which are resistant to stress corrosion
cracking, should be used. The stresses required to initiate and propagate cracking are
often low and many failures occur due to residual stresses rather than applied stress.
Appearance. Stress corrosion cracking must be evaluated using microscopic
examination of the cracked sections. The cracking is often branched. Stress corrosion
cracking can occur in the presence of other forms of corrosion attack or without the
presence of other visible attack.
Significant Measurements. In general, alloys known to be susceptible to
stress corrosion cracking should be avoided. In some cases, special heat treatments can
minimize the susceptibility to stress corrosion cracking. Many tests have been
developed to test the susceptibility of metals to stress corrosion cracking. All of these
combine mechanical loading, often in the presence of a pre-existing crack, and exposure
to the specific environment of interest. For alloys with limited sensitivity to stress corrosion cracking, critical stresses can be defined below which stress corrosion will not
occur. The structural analysis and manufacturing processes required to accommodate
these critical stress criteria are often very complex and the use of highly resistant
materials is recommended.
4.3.9 Hydrogen Embrittlement. Hydrogen can enter most metals. Due to the
small size of the hydrogen atom, it can migrate through the metal structure and cause a
loss of ductility similar to that experienced in stress corrosion cracking.
Definition. Hydrogen embrittlement is the severe loss of ductility of a
metal when hydrogen has been introduced into the metal structure.
Mechanism. Hydrogen atoms can enter a metal either from hydrogen gas,
usually at elevated temperatures, or from atomic hydrogen that is electrolytically
formed on its surface. This hydrogen can either reduce the energy required for forming
cracks under stress or can accumulate at areas of high stress, such as crack tips, and
4-19
cause pressure, which directly assists crack propagation. High strength materials in
general are the most susceptible to hydrogen embrittlement. Hydrogen can be formed
electrolytically during electroplating, during welding when hydrogen is present in the
electrode material, in the electrode coating, in the shielding gas, or simply as moisture
on the metal surface, or when excessive cathodic protection is applied (potentials more
negative than minus 1.2 volts are normally required for significant hydrogen formation
by cathodic protection.)
Examples. Ferritic and martensitic (magnetic) steels, particularly those
with a yield strength in excess of 130 ksi, are particularly prone to hydrogen embrittlement. Austenitic (non-magnetic) stainless steels are less susceptible. When hydrogen
pickup is suspected, such as in electroplating or welding, the hydrogen can be removed
by baking at 200 to 300F. Hydrogen pickup during welding is normally prevented by
using low hydrogen electrodes and mild preheating to remove water from the surfaces
being welded.
Appearance. Other than catastrophic failure by cracking, there is often no
visible evidence of hydrogen embrittlement. In extreme cases, where hydrogen gas bubbles are formed inside the metal, shinny internal blisters are visible at the fracture surface.
Significant Measurements. Analysis of the metal for untrained hydrogen
can be used to verify hydrogen embrittlement if heating subsequent to failure has not
driven off the hydrogen gas. Due to the difficulty in verifying this form of attack, it is
often blamed for other forms of cracking failure, often when simple overload is the actual cause of failure.
4.3.10 Corrosion Fatigue. Many materials will exhibit a substantial reduction in
fatigue life when exposed to a corrosive environment. In some cases, the reduction is
severe, in other cases it is less dramatic, but only a very few materials show a fatigue
resistance in a corrosive environments as great as that in dry air.
Definition. Corrosion fatigue is the reduced ability of a metal to withstand
repeated stress when exposed to the combined action of stress and a corrosive environment as compared to the effects of stress alone.
Mechanism. Fatigue resistance can be reduced by corrosion activity in
many ways. In materials that are susceptible to stress corrosion, fatigue resistance is
probably lowered by the rapid propagation of fatigue cracks after they reach the size required for stress corrosion cracking. In materials not susceptible to stress corrosion
cracking, corrosion probably enhances crack propagation through direct attack at the
crack tips, or by the formation of stress risers such as pits. Corrosion fatigue is usually
4-20
more severe at low cycling frequency where the longer time to failure allows more corrosion activity to occur.
Examples. High strength steels are susceptible to substantial reduction in
fatigue resistance in many environments. The endurance limit (stress below which
fatigue failure will not occur) is often reduced by a factor of ten from that measured in
air. Cathodic protection can increase the resistance of steels to corrosion fatigue, but
care must be taken not to overprotect them as hydrogen embrittlement would then
occur. Titanium alloys, which are not subject to stress corrosion cracking, are particularly resistant to corrosion fatigue as are some of the more corrosion resistance nickel alloys, such as Inconel 625 and Inconel 718. Copper alloys and stainless steels are also
susceptible to corrosion fatigue with a reduction of one-half in their endurance limit
being common.
Appearance. Corrosion fatigue gives a fracture surface similar to ordinary
fatigue except that in some cases, corrosion products are present in the outer sections of
the cracks.
Significant Measurements. In the simplest corrosion fatigue test, the
electrolyte is simply dripped over the surface of a rotating beam fatigue test specimen.
In more sophisticated tests, flat specimens are stressed as cantilever beams and only tensile stresses are induced on the surface exposed to the corrosive environment. When
cyclic loading is a factor in design, fatigue data from tests that include the corrosive environment must be used.
4.3.11 Erosion Corrosion. When water flows over a metal surface at high
velocity, corrosion can be greatly increased over that encountered at low flow velocities.
Definition. Corrosion accelerated by the high velocity flow of a liquid, or a
suspension of solid particles in a liquid is known as erosion corrosion.
Mechanism. Flow can increase corrosion in two ways. First, at relatively
low velocities, materials, such as oxygen which are required for the corrosion process,
are supplied in greater amounts and the metal ions produced are removed from the sites
of attack. Thus both the anodic and the cathodic reactions are enhanced and corrosion
is increased. Second, at higher velocities, protective films that give many metals their
corrosion resistance can be stripped from the surface. This effect is enhanced by the
presence of suspended solids in the fluid and by turbulent flow conditions.
Examples. Erosion corrosion is commonly encountered in pipes, pumps,
and valves. Conditions that enhance the effect of velocity are sudden changes in the
diameter or direction of flow in pipes, a discontinuity such as a poorly fitting gasket or
flange in an otherwise smooth surface, or an improperly used valve such as a gate valve
4-21
used as a throttling valve, which causes localized high velocity and induces turbulence
downstream. For materials that are protected by passive films there is often a limiting
flow velocity above which the film will be stripped from the surface even under laminar
flow conditions and rapid corrosion will occur.
Appearance. Erosion corrosion usually causes characteristic horseshoe
shaped pits shaped as shown in Figure 4-5. It is often localized in the areas where turbulence are induced.
Figure 4-5
Horseshoe-Shaped Pits Created by Erosion Corrosion
Significant Measurements. Limiting flow velocities are often established
for common piping materials, primarily based on a combination of experience and testing. For very high velocities such as those experienced in pumps and propellers, impingement tests where a high velocity jet of water impinges on the metal surface have been
developed for erosion corrosion testing. In most cases, only those materials that have
shown actual experience or actual component tests should be used when high velocity
flow is anticipated.
4.3.12 Cavitation Corrosion. Under high velocity flow conditions, particularly
when the flow is turbulent, areas of high and low pressure will be induced. In areas of
low pressure, gas and vapor bubbles will be produced. When these bubbles move to an
area of higher pressure, they collapse and their implosion creates a pressure wave that
can remove protective films and cause increased corrosion.
Definition. Cavitation corrosion is corrosion that is enhanced through the
formation and collapse of gas or vapor bubbles at or near the metal surface.
4-22
4-24
5-1
In the second method, an alternative source of direct electrical current, usually a rectifier that converts alternating current to direct current, is used to provide the required
electrical current. In this system, the electrical circuit is completed through an inert
anode material that is not consumed in the process. Section 10 manual covers the application of cathodic protection for corrosion control in detail.
5.5 MODIFY THE OPERATING ENVIRONMENT. Another method of corrosion control often neglected is modifying the operating environment. Using a selective backfill
around a buried structure, using corrosion inhibitors in power plant or in engine cooling
systems, and modifying structures to provide adequate drainage are all examples of the
use of this method of corrosion control. Although best employed during the design
stage, in some cases, actions taken to correct corrosion problems through modifying the
environment can be taken after a system is built. Careful identification and characterization of corrosion problems will often reveal opportunities for changing the environment to control corrosion. Identification and characterization of corrosion
problems is covered in detail in Chapter 11.
5-2
steels and copper alloys are also used. In most facilities, several metals are used in combinations. The resultant galvanic corrosion can be significant. As opposed to galvanic
corrosion in immersion service, the active area of the galvanic couple in atmospheric exposures is limited to the interface between the coupled metals and the areas just adjacent to the interface, thus the area ratios are roughly equal in most cases.
Protective coatings is the most widely used method of corrosion control in
atmospheric environments. If the structure design is proper, protective coatings can
give excellent service in most atmospheric environments. Proper design for the successful use of protective coatings includes easy inspection, surface preparation, and coating
application as well as avoiding crevices and sharp edges.
Metallic coatings are also used to control corrosion in atmospheric exposures. Hotdipped zinc coated (galvanized) steel is the most common example of metallic coated
metal used in atmospheric exposures.
6.2.3 Structural Features That Lead to Corrosion. Structural features that lead
to adverse corrosion in atmospheric exposures are features that trap and hold moisture
or debris. Features of this type of corrosion are shown in Figure 6-1 along with suggested alternative designs and corrective modifications.
Features that inhibit the successful use of protective coatings can also cause
unnecessary corrosion in atmospheric service.
Galvanic corrosion is usually encountered at joints in atmospheric service and can
be due either to coupling of dissimilar metal components, using incompatible fastener
materials, or both.
6.2.4 Examples of Corrosion and Means for Control. The following are examples of corrosion problems usually encountered and suggested methods for preventing or avoiding such problems illustrate the various structural features that can lead to
attack and offer suggested means for controlling corrosion in atmospheric environments. Table 6-1 contains additional examples of atmospheric corrosion and means for
its control.
Galvanic Corrosion. In Figure 6-2, several examples of galvanic corrosion in atmospheric exposures are given. In the uppermost example, two basic problems exist. The
first problem is the direct bi-metallic activity between aluminum and brass and between
aluminum and steel. The second problem is with the contamination of the aluminum
surfaces with corrosion products from the brass that also accelerates the attack of the
aluminum. In this case, the problem could have been avoided at the design stage by
using aluminum angle iron supports and either a welded joint or by using stainless steel
fasteners with a sealant at the interface between the support angle and the aluminum
6-2
cover. After construction, the problem could be addressed by replacing the brass fasteners with stainless steel, cleaning the brass corrosion products from the aluminum by
sandblasting, and applying a sealant between the angle iron and the aluminum cover. It
is clear from this example that corrosion is much easier to avoid in the design stage than
to correct through modification after construction.
In the middle example a similar problem exists. In this case, either stainless steel
or aluminum nails should be used.
Galvanic corrosion of the steel gutter in the bottom example can be controlled by
using a material at the joint between the copper and steel. This would exclude moisture
from the area where the two metals are adjacent. Either a mastic type coating or sealant
would perform adequately provided that the surfaces were properly cleaned. At the
design stage, using an all copper system, an all steel (coated) system, or a non-metallic
gutter and downspout would have been cost effective.
Effect of Sharp Corners on Paint. Figure 6-3 illustrates how paint draws thin at a
sharp corner. Such features can lead to the rapid local failure of protective coatings.
Good designs avoid such features, but if they are found after construction, they must be
ground to a generous radius and recoated.
6.3 SUBMERGED EXPOSURE. When metals are exposed directly to water or other
liquid electrolytes, corrosion is usually more rapid than in atmospheric exposures. The
surfaces are continually wet and any electrochemical cells that become active remain active. Galvanic corrosion is often severe in submerged environments as the presence of a
bulk electrolyte allows the galvanic currents to affect a large surface area. The effect of
adverse anode to cathode area ratios is much more pronounced than in atmospheric environments.
In submerged exposures more methods of corrosion control are applicable than in
atmospheric exposures. In addition to using protective coatings, cathodic protection can
also be used in many cases.
6.3.1 Electrolyte. Even pure water can serve as an electrolyte and allow corrosion to proceed. In general, electrolytes that are more conductive are more corrosive.
Other factors, such as the composition of the dissolved salts in the solution, the acidity
or alkalinity of the solution (pH), the types and amounts of dissolved gasses, and the
temperature of the environment can also effect corrosion of submerged surfaces.
Seawater is an excellent electrical conductor and contains large amounts of chloride ion,
which is particularly corrosive.
6.3.2 Commonly Used Materials. Steel, primarily due to its low cost and ease of
fabrication, is widely used in submerged service at Navy activities. In nearly all in6-3
steel in waterfront structures, protective coatings can be used in the atmospheric zone
and in the intertidal zone. The coating in the intertidal zone will reduce the attack just
below low tide by covering the cathodic intertidal zone. Cathodic protection can effectively prevent corrosion in the submerged zone and is particularly effective when used
with a factory applied coating on the piling. It is, however, usually more cost effective to
cathodically protect an existing bare steel structure in the continually immersed zone
than to attempt to coat the structure using expensive underwater coatings.
Figure 6-6 shows a method for repairing a damaged piling. Great care must be
taken to insure that the lower seal is completely effective in isolating the inside of the
jacketed area from the area outside. Unless complete isolation is achieved, a concentration cell will form and result in accelerated attack of the piling at the bottom of the jacket. A similar effect can occur when a concrete jacket is used for damage repair. In these
cases, it is advisable to use the jacket as a means for controlling corrosion in the intertidal zone and to provide protection in the submerged zone. Using cathodic protection
will control corrosion in the continuously submerged zone and prevent concentration
cell attack at the poorly isolated jackets.
6.4 WATERSIDE (PIPING)
6.4.1 Electrolyte. As described above, water is the most common electrolyte
responsible for corrosion. Even pure water can be corrosive. In fuel systems, water can
collect a low points in the system and, particularly where microbial action leads to an increase in corrosivity of the water, accelerated corrosion can occur. In some cases, the
corrosivity of the liquids in the systems can be reduced by adding corrosion inhibitors.
6.4.2 Commonly Used Materials. Steel is the most common material for piping
systems. Cast iron is also used in pipes, valves, and pumps. Copper alloys are used for
small diameter piping systems and in heat exchanger tubes.
As the amounts of materials used are often less in submerged service than in atmospheric service, more costly corrosion resistant materials can be considered for submerged service. Stainless steels, copper alloys, and nickel alloys are sometimes selected
for their resistance to specific corrosive environments. The properties and selection of
such corrosion resistant metals is covered in Chapter 8.
6.4.3 Structural Features That Lead to Corrosion. In piping systems, flow
velocity and turbulence can have a significant effect on corrosion. In some cases, such
as steel, where the corrosion resistance of the metal is not due to the presence of a passive film, corrosion rates can be roughly proportional to flow rate. In other cases, such
as copper piping, where a passive film is responsible for the corrosion resistance of the
metal, the corrosion rates are low at low velocity, but if a critical velocity limit is exceeded, the corrosion rate becomes high.
6-5
6.4.4 Examples of Corrosion and Means for Control. The following are examples of commonly encountered corrosion problems and suggested methods for
preventing or avoiding such problems. These examples also illustrate the various structural and environmental features that can lead to attack and offer suggestion for controlling corrosion in piping systems. Table 6-3 contains additional examples of the
corrosion of piping systems and means for corrosion control.
Galvanic Corrosion. Figure 6-7 is an example of galvanic corrosion
between the copper heating coils and the steel tank that can be prevented by electrically
isolating the coils from the tank. While coating the copper coils would improve the
anode/cathode area ratio and reduce the amount of attack, copper alloys are difficult to
coat and the geometry of the coils would also make coating difficult. The steel tank
should not be coated unless the coils are isolated from the tank as the ratio of exposed
cathodic copper to the steel exposed at coating defects would be particularly adverse.
Cathodic protection using either sacrificial anodes or an impressed current system could
also reduce the impact of the galvanic attack in this situation.
Mating steel and copper pipes as shown in Figure 6-8 should be avoided. If the pipe
material cannot be changed, then use an isolating flange or non-metallic coupling to
prevent the galvanic corrosion that will otherwise cause rapid failure of the steel pipe at
the joint.
Concentration Cell Attack. In addition to attack at crevices or flanges, the
accumulation of debris corrosion products over an active corrosion site can also create a
concentration cell as shown in Figure 6-9. Cleaning and cathodic protection can be used
to prevent this type of attack.
Velocity Related Attack. As shown in Figure 6-10, many features can lead
to either a high velocity flow in a system or turbulence. These situations should be
avoided as high velocities are always undesirable from the stand point of corrosion.
6.5 UNDERGROUND. Corrosion of buried structures is of particular importance at
Naval shore activities. The facilities that are buried (utility and fuel systems, etc.) are
needed to provide critical Fleet support and in the case of fuel systems, the environmental consequences of failure can be significant. Corrosion of buried structures is often accelerated by stray electrical currents and differential environmental cells. Due to the
difficulty in inspecting buried structures many are never inspected until they are
removed from service or fail.
Cathodic protection, usually combined with protective coatings, is the most widely
used means for controlling underground corrosion. Cathodic protection not only can effectively control corrosion on buried structures, periodic confirmation of the proper
operation of the cathodic protection system through electrical inspections can be used
6-6
6-7
TABLE 6.1
Structures Exposed to Atmospheric Corrosion
Construction Materials
Structure
Automotive Equipment
Buildings, exterior:
Roof gutters, corrugated roofing,
leader pipes,
window frames, and
vent flashing.
Exposure to atmosphere or to
steam or industrial vapors;
handling.
Piping
Condensation on exterior of
pipe (cold water).
Structure Members
Exposure to atmosphere or to
other vapors.
Steel
Buildings, interior:
Hardware
(Continued)
Electrical Equipment
TABLE 6.2
Submerged Structures
Structure
Construction Materials
Steel Piling
Steel Piles
(Cellular)
Steel Piers
(H-Piling)
Construction Materials
Steel Piers
(H-Piling) (contd)
Sheet-Piling
Bulkheads
Atmospheric corrosion,
chemical pollution, splash
and submerged zones, differential oxygen content,
and dissimilar metals.
S t e e l , c a s t i r o n , and bronze.
Construction Materials
Drydocks, Caission
Gates, and Lock
Gates
Atmospheric corrosion,
chemical pollution, splash
and submerged zones, differential oxygen content,
and dissimilar metals.
Seadrome Lighting
and Harbor
Installations
Atmospheric corrosion,
chemical pollution, splash
and submerged zones, differential oxygen content,
and dissimilar metals.
Steel
Ships (Inactive)
Atmospheric corrosion,
chemical pollution, splash
and submerged zones, differential oxygen content,
and dissimilar metals.
Ships (Active)
Atmospheric corrosion,
chemical pollution, splash
and submerged zones, differential oxygen content,
and dissimilar metals.
(continued)
Construction Materials
Steel
TABLE 6.3
Waterside Piping
Power Plant Equipment
(continued)
Construction Materials
Pumps
Sewage Disposal
Plants
Structure
(continued)
TABLE 6.3.
(Continued)
Structure
Construction Materials
Surface Condensers
Water Treatment
Plants (including
flocculators and
sedimentation
basins)
TABLE 6.4
Underground Structures
Structure
Construction Materials
TABLE 6.4.
Structure
(Continued)
Construction Materials
Gas Distribution
Systems
Compressed Air
Distribution System
S t e e l , b r a s s , or bronze valves
valves, and copper piping.
TABLE 6.4.
Structure
(Continued)
Construction Materials
Tank Bottoms in
Contact with the
Ground
Metallic Sewers
TABLE 6.4.
Structure
(Continued)
Construction Materials
Metallic Culverts
Steel
Deep Wells
Tower Footings
Galvanized steel.
Construction Materials
Steel and concrete.
Electrical Grounding
Systems
Sheet Piling,
H-Piling, and
Reinforcing Rods
Steel
(continued)
TABLE 6.4.
(Continued)
Figure 6-1
Structural Features That Lead to Corrosion
6-23
Figure 6-2
Aboveground Galvanic Cells from Dissimilar Metals
Figure 6-3
Edge Effects and Coatings
6-24
Figure 6-4
Tie-Rod Corrosion
Figure 6-5
Pile Corrosion Profile
6-25
Figure 6-6
Protective Jacket
6-26
Figure 6-7
Example of Thread Corrosion
Figure 6-8
Interior Corrosion Resulting From Mating Copper and Steel Pipe
6-27
Figure 6-9
Oxygen Concentration Cell: Rust Tubercle on Tank Wall
Figure 6-10
Velocity Related Attacks
6-28
Figure 6-11
Four-Pin Method for Measuring Soil Resistivity
Figure 6-12
Long-Line Currents: Differential Environment Underground
6-29
Figure 6-13
Differential Environment Underground
6-30
Figure 6-14
Additional Differential Environment Underground
Figure 6-15
Stray Current Electrolysis From Electric Railway
6-31
Figure 6-16
Stray Current Electrolysis From Local Sources
CORRECT
INCORRECT
Figure 6-17
Correct and Incorrect Grounding
6-32
7-2
property. They are considered to be in the resin or pigment part depending whether
they exist in the coating as a liquid or solid.
7.3.2 Mechanisms of Curing. All coatings cure from one of three basic
mechanisms: air-oxidation of drying oils, solvent or water evaporation, or a chemical
reaction of components. Coatings that cure by the same basic mechanism tend to be
compatible with each other but not with coatings that cure by other mechanisms.
Air Oxidation of Drying Oils. Coatings that cure by air oxidation of drying oils
have oxygen from the air react with the unsaturated fatty acids in their drying oils. By
this reaction, liquid resins are converted to a solid film.
Examples of coatings that are cured by this mechanism are unmodified drying oils
(e.g., linseed oil), alkyds (usually formed by reaction of oils with phthalic anhydride),
silicone alkyds, oleoresinous phenolics, and epoxy esters. They wet surfaces very well
and generally perform well in mild environments, but they have limited durability in
chemical environments, particularly alkaline environments. They cannot be used in
water immersion service, except for oleoresinous phenolics. Formulating oil-based
coatings with low solvent content presents difficulties and requires unique changes.
Solvent Evaporation. Coatings that cure by simple solvent evaporation are
sometimes called lacquers. They are made by dissolving solid resins in an appropriate
solvent. After application, the solvent evaporates to deposit the resin in a thin film. No
chemical change occurs to the resin. Resins that are softened by solvent or heat are
called thermoplastic.
Examples of coatings that cure by this mechanism are vinyls (polyvinyl chlorides)
and chlorinated rubbers. The polyvinyl-butyral resin used in wash primers also belong
to this category, as do asphaltic and coal tar coatings. Coatings of this class have limited
solvent resistance, since they were deposited from a solvent, but are easy to topcoat and
repair because the topcoat solvent bites into the undercoat to bond tightly. Because lacquers are high in solvent (VOC) content, their use will be greatly curtailed.
Water Evaporation. Latex and many other water-borne coatings cure by simple
water evaporation. Emulsified particles of solid resin coagulate to form a film as the
water is lost. The range of acceptable ambient temperature and humidity values is
much more critical for water-borne than for other coatings.
Examples of latex coatings are acrylics and vinyls (polyvinyl acetate). Latex films
are quite flexible but tend to be more permeable and less durable than many other films.
7-3
Chemical Reaction. Coatings that cure by chemical reaction are usually the most
durable. They are generally packaged in two separate containers and mixed to initiate
the reaction. Components must be combined in the specified proportions in the manner specified by the supplier to achieve a complete reaction. Sometimes, an induction
period is required after mixing and before application to permit the reaction to get
started. After mixing, there is always a pot life during which the coating must be applied, before the reaction has advanced so far as not to permit proper application and
curing.
Examples of this class are epoxies, coal tar epoxies, urethanes, and polyesters.
Because the chemical reaction is irreversible, they are called thermosetting coatings.
Although this makes the coating very chemical and solvent-resistant, it also makes the
cured coatings difficult to topcoat. Thus, the topcoat is best applied while the undercoat
still has some residual tack. After the coating has completely cured, it is necessary to
first spray a thin tie coat and then apply a full coat to it when it is still tacky.
Another example of chemically curing coatings is the inorganic zinc coating. They
may cure by different types of reaction. Thus, some cure by reaction with water from
the air, and thus cure slowly in dry environments. A one-package urethane water-based
inorganic zinc coating cures by chemical reaction after evaporation of the water.
Zinc-rich organic coatings may contain different organic resins. Their curing
mechanisms are those of the resin-solvent evaporation for zinc-rich vinyls and chemical
reaction for zinc-rich epoxies.
7.4 ENVIRONMENTAL, HEALTH, AND SAFETY RESTRICTIONS ON COATINGS.
Environmental restrictions have greatly limited the compositions of coatings, the surface preparation, and the coating application techniques that can be used in many locations. These restrictions can be expected to become even tighter in the near future.
Although much general information is provided in this section, personnel concerned
with products or procedures described should confer with local authorities to determine
what are the prevailing regulations.
7.4.1 VOC Limitations. Volatile organic compounds (VOCs) make up the solvent portion of coatings. Regulations have been enacted in many locations that have
not achieved the ozone level established by the Environmental Protection Agency.
These regulations cover architectural coatings, coatings for miscellaneous metal parts
(shop Painting), aerospace coatings, and architectural coatings. This chapter will concern itself only with VOC restrictions on architectural coatings and coatings for miscellaneous metal parts, since the others are outside the scope of this manual. An
architectural coating is for a structure fixed in place, while a miscellaneous metal part is
defined as a structural component that can be taken to a shop for coating. Presently,
7-4
most architectural coatings have a VOC limit of 250 g/liter, while metal part coatings
have a VOC limit of 340 g/liter.
The effects of the two regulations of concern are such as to cause reformulation or
elimination of virtually all coatings previously used on metals. Only the latex military
coatings seldom specified for steel are in conformance. Indeed, use of latex coatings on
steel has created many costly problems, because it not only is hard to formulate a highperformance water-based coating for metals, but the range of acceptable temperature
and humidity conditions for suitable application is limited.
VOC emissions into the air have been further reduced by regulations restricting the
methods of shop application of coatings to those with 65 percent transfer efficiency. For
most configurations coated in shops, this effectively means that spray applications must
be accomplished by electrostatic spray, or air-assisted airless spray.
7.4.2 Lead and Chromium Concerns. Lead and chromium pigments have been
used for many years as corrosion inhibitors for metal primers. Recently, concern has
been expressed for possible toxic effects of these pigments in coatings. Thus, lead can
no longer be used on housing or other structures where children might come into contact. Probably more important are new regulations concerning the removal of leadbased coatings. They require that removal of existing coatings be preceded by testing
the coatings for lead and that lead-containing paint be contained during removal, the air
be monitored for lead in the particulates formed during removal, and that the old paint
and blasting abrasive be disposed of in a manner required for toxic waste. This great expense, as well as health concerns for children exposed to lead-based paints, has effectively eliminated their use for Navy and Marine Corps facilities. Concern has also been
expressed for problems in removing chromium-containing coatings. Thus, using coatings containing lead or chromium is not recommended. When removing old coatings,
they should be tested for lead, chromium, and other heavy metals, and then removed
and disposed of in accordance with appropriate local regulations.
The corrosion inhibitive pigments commonly used for coatings are listed below in
two columns, those considered to be toxic and those considered relatively nontoxic:
Toxic
Nontoxic
Red Lead
White Lead
Zinc Chromate
Strontium Chromate
Basic Lead Silica-Chromate
Zinc Oxide
Zinc Phosphate
Zinc Molybdate
Calcium Borosilicate
Calcium Phosphosilicate
Zinc Phosphosilicate
7-5
7-6
7-7
Spot repair of coatings is best accomplished with a material similar to that already
in place, in order to avoid incompatible products. Because of new environmental
restrictions, this may not be possible. Then, special care may be required to insure compatibility. The one exception to spot repairing with a like material occurs with inorganic
zinc coatings with organic topcoats. Since inorganic zinc coatings do bond well to organic coatings, zinc-rich organic coatings are used.
7.5.2 General Properties of Differently Curing Coatings. Each of the generic
coating types formulated for metal surfaces that are commonly used in Naval shore
facilities will be discussed separately.
The advantages and limitations of using the different coatings are listed separately
after each discussion.
Oil-Based Coatings. Oil-based coatings were the first coatings used to protect
steel from corrosion. They are still used extensively today but have only limited service
lives in severe environments. Because the drying oil wets surfaces so well, they are
more tolerant of incomplete surface preparation than are other coatings (e.g., they perform reasonably well on steel cleaned by hand or power tools). These coatings
deteriorate rather rapidly in water immersion (except for oleoresinous phenolics) or on
alkaline surfaces, such as galvanized steel and or concrete. For this reason they are not
used in these environments. Oil-based coatings include unmodified drying oils, alkyds,
epoxy esters, and oleoresinous phenolics. Unmodified drying oils can be formulated
into VOC-conforming coatings more easily than the other resins. It is usually necessary
to use the exempt solvent 1, 1, 1-trichloromethane to be VOC conforming. This solvent
may be eliminated from exemption in a few years because of toxicity concerns.
Limitations
Advantages
Latex Coatings. Latex coatings have been a boom to homeowners because they
are easy to apply to a variety of surfaces and are easy to clean up. They are also environmentally acceptable, as they are VOC conforming, even if they may contain compatible
organic solvents. Limitations include limited durability, especially on steel and other
metals; poor chemical and solvent resistance; and limited acceptable application condi7-8
tions. Their excellent flexibility is offset by their poor wetting of surfaces. When applied over a smooth enamel, it is necessary to lightly sand the enamel to achieve good
topcoat bonding. They are available as acrylics, vinyls (polyvinyl acetates), or
copolymers of these resins. Acrylic latexes may be applied over epoxy systems to provide improved exterior weathering.
Limitations
Advantages
Low cost
Easy to apply, topcoat,
and repair
Good flexibility
Environmentally acceptable
Limited durability
Poor chemical/solvent resistance
Poor wetting of surfaces
Poor immersion service
Poor heat resistance
Must apply above 70F
Bituminous Coatings. Bituminous (coal tar and asphalt) coatings have been used
for many years.
Advantages
Low cost
Good water resistance
Good film build
Easy surface preparation
Easy to apply
Limitations
Poor exterior weathering
Poor chemical/solvent resistance
Available in black only
7-9
Advantages
Limitations
Epoxy Coatings. Epoxy coatings have some of the best combinations of chemical,
solvent, and water resistance. They form a tightly adhering, hard, slick film with good
abrasion resistance and durability. Their shortcomings include inflexibility, poor
weathering (chalking and poor gloss retention in sunlight), and difficulties associated
with a chemically-curing coating (two- package mixing, limited pot life, and difficulty in
topcoating, as described earlier). The surface must be cleaned to a near white finish,
but epoxy-polyamide coatings are a little more tolerant of incomplete cleaning. Of the
two types of epoxy most commonly used on shore facilities, epoxy-polyamides usually
have the better water-resistance and amine-cured epoxies have the better chemical resistance. Epoxies can be formulated to make them high solids (even 100% solids) or
water-based to make them VOC conforming.
Advantages
Limitations
Coal Tar Epoxy Coatings. Coal tar epoxy coatings have coal tar added to the
epoxy formulation. This increases the water resistance and film build up per coat while
reducing the price. The properties of coal tar epoxies are similar to other epoxies, but
they become more brittle (inflexible) in sunlight.
Advantages
Limitations
7-10
Limitations
7-11
formed during cathodic protection. As mentioned in Paragraph 7.5.1, topcoated inorganic zinc coatings are repaired using compatible zinc-rich organic coatings.
In new construction, steel is usually abrasively blasted and primed with inorganic
zinc primer in a shop under controlled conditions to give high quality application not
received so easily in the field. Also, there is less contamination of the environment by
the blasting particulates. The preconstruction primer may then be topcoated later after
the structure steel has been erected. Welding has been successfully reported through
some inorganic zinc coatings. If the primer can be properly maintained, abrasive blasting may not be required later for maintenance painting.
Advantages
Limitations
High costs
Requires a skilled applicator
Constant stirring required
during application
Requires careful selection
and application of topcoats
Stringent surface preparation
requirements
Unsuitable for acid or alkali
environments
May have special curing requirements
Limitations
High cost
Constant agitation required
during application
Unsuitable for acid or alkali
service unless topcoated
7-12
7-13
near sparks or flames, or be inhaled unnecessarily. Solvent cleaned metals may require
further cleaning before coating.
Hand and Power Tool Cleaning. Removes only loosely adhering paint, rust, and
mill scale. It is slow and produces a burnished rather than a textured surface that permits only limited coating adhesion. Thus, it is used mostly for spot cleaning. Hand tools
include scrapers, wire brushes, and sanders.
Power tools (electrical and pneumatic) clean much faster than comparable hand
tools and are essentially a duplication of them in power-driven equipment. They include sanders, grinders, wire brushes, chipping hammers, scalers, and needle guns.
They clean by impact, abrasion, or both. Cleaning of metal surfaces is less expensive
using power tools than using hand tools, and less particulate contamination occurs than
when abrasive blasting. Thus, they are used mostly for spot cleaning, where contamination of adjacent areas by abrasive blasting is unacceptable, and when a surface tolerant
coating, such as an oil-based paint is used.
Flame (Thermal) Cleaning. Flames and electric heating guns are use only to
remove loose scale or rust from metal surfaces. The surface is then cleaned to achieve
the desired level of cleanliness. Extreme caution must be used to keep open flames
away from flammable materials.
Steam Cleaning. Steam cleaners may be used to clean dirt and grime from coated
surfaces, so that repainting may be unnecessary. High temperature and velocity wet
steam can also remove heavy oil and grease. Commercial detergents can be added to
the wet steam to improve the cleaning power. Steam-cleaned steel is then further
cleaned by other methods before coating.
Chemical Cleaning. Chemicals can often be used to clean metals for coating.
Alkaline cleaners remove grease, oil, and oil-based coatings from steel but can damage
other metals. Solvent strippers are appropriate for removing other coatings. Baths can
be used for dip cleaning of some metals. Chemicals can also be used to treat metal surfaces (e.g., phosphating) to promote coating adhesion.
Abrasive Blasting. Abrasive blasting is usually the preferred method of preparing
steel and some other metal surfaces for cleaning. The impact of high velocity abrasive
particles can completely remove all rust, scale, dirt, and old coating, but not grease or
oil. It also roughens the surface to produce a texture that promotes tight coating adhesion. Aluminum and other softer metals require softer abrasives (e.g., plastic beads)
for removing old coatings and not damage the metal. Because of the importance of
abrasive blasting of steel, it is discussed in considerable detail in Paragraph 7.6.3.
7-14
Wet and Water Blasting. Water is sometimes added to the abrasive by using a
ring water sprayer at the nozzle to reduce the amount of particulate dust produced in
blast cleaning of steel. Chemical corrosion inhibitors such as sodium, potassium
dichromate, or phosphate must be dissolved in the water to prevent flash rusting of steel
before coating. The possible adverse effects of inhibitor residue on coating performance has not been established.
Water blasting, sometimes called hydroblasting is sometimes used to clean metal
surfaces for coating. The water may be heated and detergent may be added to help with
the cleaning. Power washing with pressures up to about 2,000 psi is effective in removing dirt and mildew on coated metals and is generally safe on adjacent wood and concrete/masonry. Bare steel can be cleaned with water pressures over 30,000 psi and
water volumes of only 2 to 15 gallons per minute. Ultrahigh waterblasting begins at
20,000 psi. Abrasives can be added to the stream of water or used separately later to
roughen the metal surface to achieve good coating adhesion. Extreme caution must be
maintained with these high pressures. Again, corrosion inhibitors must be used in the
water.
7.6.2 Recommended Cleaning Methods
Steel. The preferred method of cleaning uncoated steel is washing it with a
solvent followed by abrasive blasting. The preferred method of cleaning coated steel is
also by abrasive blasting followed by a solvent cleaning, if the coating is to be removed.
Other cleaning methods such as hand or power tools are more practical for spot repair
of coatings. The standards for different levels of abrasive blasting of steel and for alternative methods of cleaning are discussed in Paragraph 7.6.3.
Galvanized Steel. The recommended method of cleaning galvanized steel varies
with the condition of its surface. Simple solvent cleaning is usually adequate for new,
clean galvanized steel. If loose zinc corrosion products or coatings are present, they
should be removed by bristle or wire brushing only as heavy as necessary for complete
removal. If rust is present on older steel, it should be spot removed by abrasive blasting
or wire brushing so as not to disturb remaining in-tact galvanizing. A thin coat (0.3 to
0.5 mils) of wash primer (see MIL-P-15328) is often used on new galvanized steel to
promote adhesion of oil-based or latex coatings.
Aluminum and Other Soft Metals. New, clean aluminum and other soft metals
may be cleaned for coating by solvent washing. Detergent washing may be required for
removing dirt. Abrasive blasting with plastic beads or other soft abrasive may be necessary to remove old coatings. These metals, like galvanized steel, are sometimes wash
primed to promote adhesion of oil-based or latex coatings.
7-15
7.6.3 Standards for Cleaning Steel Surfaces. The most frequently used written
standards for cleaning steel surfaces are from the Steel Structures Painting Council
(SSPC). They include standards for all common methods of cleaning. Volume I of
SSPCs Steel Structures Painting Manual contains all the available standards, as well as
other useful information. The National Association of Corrosion Engineers (NACE)
has a set of standards for blasted steel surfaces similar to those of the SSPC. Pictorial
standards NACE standard steel specimens encased in plastic are also available for determining the level of abrasive blasting. However, the written standards constitute the
legal requirements for contract work.
The four grades of blast-cleaned steel are:
White Metal Blast -
Commercial Blast -
Brush-off Blast -
Before using the pictorial standards, you must first determine the grade of steel
blasted, since different grades of steel blast cleaned to the same level will not look the
same.
Rust Grade A - Adherent mill scale (tight scale with little rust)
Rust Grade B - Rusting mill scale (rusting started; scale flaking)
Rust Grade C - Rusted (mill scale easily removed; little pitting)
Rust Grade D - Pitted and rusted (no mill scale; visible pitting)
7-16
SSPC standards for steel surfaces cleaned by methods other than blasting are:
Method
SSPC No.
Intended Use
Solvent
Cleaning
SP-1
Hand Tool
Cleaning
SP-2
Power Tool
Cleaning
SF-3
Flame
Cleaning
SP-4
Pickling
SP-8
Different types of coatings require different levels of cleaning. The most commonly
agreed upon levels are:
Coating Type
Drying oil
Alkyd
Coal tar
Asphaltic
Latex
Vinyl lacquer
Chlorinated rubber
Epoxy
Coal tar epoxy
Urethane
Organic zinc
Inorganic zinc
cleaning
white
white
white
white
white
white
blast
blast
blast
blast
blast
For immersion or other severe environments, the higher level of two options should
be used.
7-17
7-18
Blast Hose. The blast hose carrying the air and abrasive from the blasting
machine to the nozzle must be sturdy, flexible, and treated to prevent electrical shock.
A 4-ply blast hose with a 1.25 ID is sold in short, joinable sections to minimize frictional
loses.
ID hose called a whip is sometimes joined at the nozzle. It is easier to handle, particularly in tight areas, but is not recommended, because its reduced diameter causes
frictional losses of pressure.
Nozzles. Nozzles are available with several lengths, designs, sizes of
openings (throats), and lining materials. Nozzle lengths of 5 to 8 inches are generally
used for removing tightly adhering rust and scale. Shorter nozzles, 3 inches or less, are
appropriate for behind beams and in other inaccessible places when a whip might be
used.
The tapered shape of the venturi nozzle is more efficient than the cylindrical shape
of the straight bore nozzle. The venturi creates a larger, more uniform blast pattern and
can increase cleaning rates by 30 to 50%.
The orifice size is chosen according to the available volume of air. The largest
practical size that does not permit loss of pressure is usually best. A 1/2-inch nozzle
with proper air supply can clean four times the area of a 1/4-inch nozzle.
The lining, particularly at the orifice, is gradually worn away by the abrasive. Since
enlarged openings reduce efficiency, the liner is usually replaced after the original
diameter has increased by 50%. Tungsten, carbide, and Norbide liners may have service
lives of 300, 750 to 1,000 hours, respectively, as compared to 6 to 8 hours for cast iron
liners. Dropping or banging the more brittle tungsten, carbide, and Norbide nozzles can
reduce their service lives. Nevertheless, they are much more economical to use in the
long term.
All nozzles are equipped with deadman valves that permit blasting when they are
depressed. If the operator drops the nozzle, the flow of air and abrasive is immediately
stopped.
A hypodermic needle gage is used to measure nozzle pressure. It is inserted into
the blast hose immediately in front of the nozzle in the direction of abrasive flow to minimize damage to it from the flowing abrasive.
Alternative Approaches to Blasting. Automatic cleaning by centrifugal blasting
can be achieved in shops in a controlled environment. It utilizes machines with motordriven, bladed wheels to hurl abrasive at high speed by centrifugal force. Its advantages
over conventional blasting include: (1) savings of time, labor, energy, and abrasives; (2)
7-19
a superior, more uniform cleaning; (3) reduces blasting waste by recycling the abrasive
several times; and (4) protects the environment.
A centrifugal blast cabinet with four 25-hp wheels can throw 2,400 pounds of abrasive
per minute. The amount of abrasive throw requires 33 conventional blasters. Portable
centrifugal blasting equipment is also available for regular steel surfaces like the decks
of ships or sides of storage tanks.
Vacuum blasting systems are now available which collect, clean, and recycle
abrasives. Production is slow but very effective in eliminating blasting dust, cleaning
welds, and reducing hazardous waste from toxic paints.
Another approach of avoiding contamination of the environment with blasting dust
is to conduct the blast cleaning in an enclosed building where particulates are trapped
and collected and the abrasive can be cleaned and recycled.
Blasting Procedures
Choosing Abrasives. Abrasives are available in a variety of sizes, shapes,
hardnesses, and breakdown characteristics. The proper abrasive for a particular coating
is one that provides the necessary cleaning and profile at a good rate, and permits the
coating to perform well.
A larger size abrasive will cut deeper than a smaller size abrasive, but the greatest
rate of cleaning is achieved with as small a size as possible to give the desired surface.
Particles in the 40- to 50-mesh range are commonly used today. Those larger than 16to 18-mesh have a slow clean rate and may gouge the surface; those 100-mesh or finer
may not be able to give the desired profile.
The size and shape of the abrasive is responsible for the type of blasted profile
produced. Round shot tends to peen the steel surface to a wavy profile. It is effective in
removing brittle deposits, such as mill scale. Grit is angular and so produces a more
jagged finish, generally preferred for tight coating adhesion. The variety of grit
materials available produces a variety of surface patterns. Sand and slag abrasives are
semiangular and produce surface patterns somewhere between those for shot and grit.
Hard abrasives cut faster and deeper than softer or more brittle ones. A hard, but
brittle abrasive tends to shatter on impact, which reduces its cleaning rate.
The manner in which abrasive particles fracture and change shape upon impact is
called their breakdown characteristic. It limits the number of times recycling is possible, the amount of particulate dust emitted into the air, and the amount of dust that
must be removed from the cleaned surfaces before coating.
7-20
7-21
occur in a few hours. If this occurs, the rust must be removed by brush blasting before
coating.
It only takes one spray painter to keep up with four blasters, so the work must be
properly scheduled.
7.7 APPLICATION OF COATINGS. The basic choices for applying coatings are brush,
roller, and spray. Selecting the most appropriate method for a particular job is not so
easy today, because the modern high-performance, VOC-conforming coatings are more
difficult to apply than coatings previously used. The following considerations must be
made before selecting the application method:
Application methods appropriate for the particular coating.
Desired appearance.
Ease and speed of application.
Simplicity of equipment and required operator skills.
Safety/environmental requirements.
Economics of application.
If the coating like inorganic zincs can only be applied by spray, the application
choices will be limited. Such coatings are also likely to require highly skilled operators
for specialized equipment. Ease and speed of application will affect the ability to provide not only an economical but also a quality, cosmetically acceptable finished product.
Safety and environmental restraints may limit the available methods to those with high
transfer efficiencies or require safety gear than will slow operations. Some of these factors may be much more important than others.
The relative rates of different application rates are given below:
Square Feet Applied
in 8-Hour Day
Application Method
1,000
2,000 to 4,000
4,000 to 8,000
8,000 to 12,000
Brush
Roller
Conventional Air Spray
Airless Spray
7-22
In contract painting, the contractor is usually given his choice of application method.
We, however, should be aware of the problems associated with the particular method he
chooses for his work plan and advise him of any concerns we may have about this
method.
7.7.1 Brush Application. Brushing is an effective, relatively simple coating application method. It is particularly good for priming, since it works the paint into the
surfaces irregularities. Because it is slow, brushing is used primarily for touch-ups,
small areas (e.g., trim), complex configurations, or where overspray may be a serious
problem. It does not produce a very uniform thickness.
Natural brush bristles of good quality are preferred for paint brushes, but synthetic
filaments resistant to strong solvents may be also be satisfactory. Bristles that are
naturally or artificially flagged (with split tips) are preferred, because they hold more
paint. Nylon and polyester filaments are more water resistant than natural fibers and so
are preferred for latex paints.
Brushes can leave brush marks in paints that do not level well. They may also leave
areas of low thickness. Thus, a second coat should be applied at right angles to the first
in order to minimize overlap of brush marks or thin areas. Additional coats should be
applied at right angles to the previous coat.
Tips for painting with brushes are:
Shake loose any unattached bristles by spinning the brush
between the palms of the hand.
Remove any stray bristles with a putty knife.
Dip the brush to cover one-half the bristle length. Too much paint
may wet the heel of the brush and run down the handle.
Remove excess paint by tapping the brush on the edge of the can.
Apply paint with a light touch. Use the bristle tips rather than
pressing down hard; this will minimize brush marks.
Work from the dry to the wet surface; this will minimize lap marks.
Hold the brush at a 75-degree angle to the surface; this produces
the best results.
7-23
7.7.2 Roller. A roller is best used on large, relatively flat areas that do not require the smooth surface or uniformity received from spraying and in interior areas
where overspray may present a masking or cleaning problem. The nap fiber length normally varies between 1/4 to 3/4 inch. A longer nap holds more paint but does not give as
smooth a finish. Thus, it is used on rougher surfaces. Rollers with extra long naps (11/4 inches) are used to coat chain link fences. Handle extensions 10 feet or longer allow
the painter to reach high areas but usually at a reduction in application quality.
The roller cannot penetrate pores, cracks, or other surface irregularities as well as
a brush. Also, rolling can mix air into the paint to permit moisture to penetrate the
cured film. Lacquers are difficult to apply by roller because of their rapid solvent
evaporation, particularly on warm days.
Tips for painting with a roller are:
For thick-bodied coatings, dip the roller directly in the paint
container; for thin-bodied coatings, use a roller tray.
Load the roller uniformly for even application at the desired
thickness. Too little or too much coating may cause tracking or
skidding.
Do not apply heavy pressure to the roller.
Apply the second coat at right angles to the first to avoid areas of
low thickness or holidays.
7.7.3 Spray.
Conventional Air Spray. Air spray features the finest atomization and finish and
the greatest versatility. The basic parts of conventional air spray equipment are: air
compressor, paint tank, hoses for air and fluid, and spray gun.
The air compressor powers the conventional air spray equipment. It must
continuously supply both adequate air pressure for paint atomization and uniform flow
of paint to the spray gun. Air pressure and flow are directly related to each other. If
one drops, so does the other. The air flow, measured in cfm, must be great enough that
the pressure does not drop during triggering to give short bursts rather than a continuous stream of atomized paint. Pulsation indicates an inadequate air supply. The air
supply must also provide power for agitators or other accessories. Data sheets of paint
suppliers provide information on recommended spraying pressures (and thus necessary
compressor capacities), air caps, and fluid tips. Oil and water in the air supply must be
removed by separator or extractor attachments to provide clean air.
7-24
The tank that holds the paint material (usually in a paint pail) has an air compressor
to control the operational pressure. Some tanks have agitators that continuously mix
the paint to prevent settling of heavy pigments. When large quantities of material are
required, a pressure pump can be used directly in the paint container.
The air hose carries the compressed air, and the fluid hose carries the paint to the
gun. An air hose with too small an ID can cause the air line pressure to drop and starve
the gun. As with blasting hoses, frictional losses of pressure can be minimized by using
relatively large diameter and short hoses. Avoid kinking or compressing these hoses. A
large diameter may be necessary on a long hose to maintain adequate air pressure. The
ID of the hose from the compressor to the pressure tank is usually at least 3/8 inch and
the ID of the hose from the pressure pot to the gun should be at least 5/16 inch.
The ID of the fluid hose is determined by the necessary volume and pressure of the
particular paint at the gun. Heavy paint may require as large an ID as 1/2 or 3/4 inch.
Small guns often use a 1/4 inch ID fluid hose. The hoses must be resistant to the paints
and solvents that flow through them.
The conventional spray gun is relatively complex and requires a great deal of skill
to operate. The basic parts of a spray gun are: air nozzle or cap, fluid nozzle or tip,
fluid needle, trigger, fluid adjustment valve, air valve, side port control, gun body and
handle, air inlet, and fluid inlet. Supplier instructions provide much information on
their operation.
Most spraying problems are related to improper or inadequate cleaning of guns.
Recommended maintenance items include:
Lubricate the air gun daily.
Wash the gun body with a rag dipped in solvent. (Only wet the front
end of the gun with solvent. The solvent will remove lubricants and
dry out the packing.)
Unclog nozzle by washing it separately in solvent. Use only a pipe
cleaner, broom bristle, or match in cleaning the hole to prevent damage.
Never use oils or lubricants containing silicone.
With conventional air spray, outer jets of air atomize the paint. The external mix air
nozzle is almost always used. The external mix nozzle is used for production work that
does not require a fine finish. They are not used with catalyzed or fast drying paints,
these paints tend to clog the nozzle.
7-25
A proper spray pattern when the trigger is fully depressed may be round or fan
shaped (a long oval). As long as the fluid and air pressure remain the same, the amount
of sprayed paint will remain the same. Increasing the pattern size decreases the paint
thickness and vice versa. The ideal spray pattern for production work is a long oval with
clearly defined edges and little overspray or rebound. The individual particles of
atomized paint should be uniform in shape, size, and distribution. Spray pressures
should be kept as low as possible for such a pattern.
Special spray equipment may be designed to apply thick paints. This includes
heating accessories to reduce paint viscosities and components for mixing of metered
components at the gun. Guns on extension arms permit spraying in difficult to reach
places. It is considered a better technique to use scaffolding to get to such areas, if at all
possible.
Airless Spray. Airless spray features the greatest production rate and
consequently the greatest economy. The basic parts of airless spray equipment are:
high-pressure paint pump, fluid hose, and airless spray gun.
A high pressure pump forces paint from the container to the spray gun and
atomizes it into a spray. It is rated according to the ratio of paint pressure produced to
the air pressure that produced it. Thus, a pump that delivers a paint pressure of 30 psi
for each psi of air pressure from the compressor has a 30:1 ratio. There must be sufficient pressure and material flow to produce a constant spray of paint.
The fluid hose must be able to withstand the high pressures necessary to deliver
the paint to the gun and atomize it. While pressures of 1,800 to 3,500 psi are commonly
used, most air hoses can handle pressures as high as 5,000 psi. A 1/8- to 1/4-inch ID
hose is used for medium viscosity paints, and 3/8- to 1/2-inch ID for high viscosity paints.
The airless spray gun is basically a fluid nozzle with a valve. A spray tip filter screens
out particles that might clog the tip. Each spray tip is designed for a particular spray pattern. Indeed, changing tips is the only way to change the spray pattern. The orifice size
(0.007 to 0.0072 inch) controls the atomization and the amount of fluid delivered. The
tip angle (10 to 80 degrees) controls the fan width. Tips with the same orifice size but
different angles will deliver the same amount of paint but at different fan widths and
thicknesses. A large spray pattern is required for a high application rate. Paint viscosity
is the chief factor in selecting a particular tip.
Airless spray guns may be powered by electricity, gasoline, or compressed air. As
with conventional air spray, a good pattern will have a smooth oval outline, clearly
defined edges, and a uniform distribution of paint particles. However, a round pattern
is not acceptable. To correct a faulty airless spray pattern tips, filters, or atomization
pressures may need to be replaced or adjusted.
7-26
Air-Assisted Airless Spray. Air-assisted airless spray uses compressed air to assist
in the atomization of paint from an airless system. It makes it easier to apply heavy
products.
Electrostatic Spray. Electrostatic spray can apply coatings to hard-to-coat
conductive surfaces with minimum loss of paint. This ability to paint around corners
permits a painter to coat very complex configurations. It can be used for airless or conventional air application. A charged probe is used for external ionization of the
atomized paint, which is attracted to a grounded surface. It presents no safety hazard to
ability to
properly trained personnel. Electrostatic spray has the following features:
wrap around edges and irregular surfaces; increased transfer efficiency (lower material
usage), more uniform paint application, and less overspray.
Thermal Spray of Metals. Equipment and techniques are available for the thermal
(flame or electric arc) spraying of metal coatings on steel. The metals are melted, and
the molten metal is sprayed to produce a porous coating that protects by cathodic
protection. For longer protection, they may be sealed with a thin conventional organic
coating or silicone. Aluminum and zinc are the most frequently used thermal sprayed
metals. Zinc presents a health hazard and so is seldom sprayed by the Navy. A very
clean steel surface is required for coating. Metal spray coatings are normally very
abrasion resistant.
Powder Coatings. Organic polymers (e.g., epoxies and acrylics) in powder form
can be applied to a conductive (usually metal) surface and fused to it by heating in an
oven at a predetermined temperature to form a tough, corrosion resistant coating. Application is done by electrostatic spray to a preheated metal component to permit the
powder to stick to it before fusing. Application can also be done in a fluidized bed. In
addition to being free of organic solvent, the system has a high transfer efficiency. Any
powder not sticking to the metal surface can be collected and blended with virgin powder and used again.
7.7.4 Recommended Spraying Procedures. The recommended aspects of paint
spraying, for both airless and conventional air spray are described below.
Stroking. Stroking during spraying should be done with the gun, wrist, arm, and
shoulder at right angles to the work and moving parallel to it. This prevents arcing,
varying the distance of the gun to the work, which results in variation of the paint thickness. For large, flat surfaces, each stroke should overlap the previous one by 50%. This
produces a relatively uniform surface and eliminates holidays at the ends of the fan.
The stroke length should be from 18 to 36 inches, depending on the sprayers arm
length and comfort. Long areas should be divided up into smaller sections of appropriate length. Each section should slightly overlap the adjacent ones.
7-27
Triggering. The stroke of the spray gun should begin before the gun is triggered
and continue briefly after releasing the trigger. This produces a smooth, continuous
film without a heavy build up of paint at the start and end of each stroke. It also helps
keep the fluid nozzle or airless tip clean.
Distance. The amount of material delivered and the atomization pressure determine
the proper gun-to-surface distance for a uniform, wet film. It is usually about 6 to 12 inches for conventional air spraying and 12 to 15 inches for airless spraying. If the gun is
held too close to the surface, the paint can sag or run. If the gun is held too far from the
surface, a dry spray with a sandy finish and holidays (pinhole or skip areas) may result.
Corners. Each side of inside corner should be sprayed separately. A vertical
stroke on one side, followed by a short horizontal stroke on the other will usually result
in a relatively uniform coating. Spraying directly into the corner will produce a film of
varying thickness, thinner in the corner and heavier on the sides.
An outside corner is sprayed directly when the sides are sprayed. This results in
uniform paint thickness, without lap marks.
7.7.5 Storing and Mixing of Coatings Before Application.
Storing Coatings. Proper storage of coatings will protect these costly products
from premature deterioration and minimize fire hazard. Long term storage should be
in a room or building isolated from other work areas. The room or building should be
dry, well-ventilated, and protected from sunlight, sparks, and flames. Shelves or pallets
should be used to keep the cans up away from the dampness of floors. Labels should be
kept in tact and free of paint to permit easy identification. Material safety data sheets
(MSDSs) should be available for each coating and solvent stored, as required by law.
Stocks of coating should be rotated and used so that old ones are used first, and no coating should be kept more than 1 year after manufacture. Once opened, the contents of a
can should be used before opening up another can of the same coating. Coatings stored
for more than 1 year should be checked for quality, as described in Paragraph 7.8,
before using.
No more coating should be taken to the job site than is actually required. It should
also be protected from the weather. Water-borne coatings can freeze in cold weather
and can be damaged permanently.
Mixing Coatings. During storage, the coatings heavy pigments tend to settle and
cake at the bottom of cans. These coatings must be reblended to their original uniform
consistency before applying to obtain complete curing and satisfactory film properties.
Mixing of coatings may be done either manually or mechanically, the latter usually
7-28
the coating may harden in the pot, lines, or gun. Mixed coatings not used at the end of
the day cannot be kept over night. The mixed coatings must be discarded.
Two-component are mixed as follows.
Stir the base component (usually Package A) with a clean paddle
to disperse pigment lumps that may have settled. (Five minutes
is usually adequate.)
While continuing to stir, slowly add all of Package B (usually
called the catalyst, co-reactant, or curing agent) which is
frequently unpigmented. (The mixing container must be large
enough to hold both components.)
Agitate the two mixed components with a manual or power stirrer
until smooth.
Note: Vary these instructions if specified by the supplier.
Environmental Conditions and Thinning (Reducing) Mixed Coatings. Properly
formulated coatings seldom require mixing when applied in the recommended temperature range. Most coatings should be applied between 50 and 90F. However, the best
temperature range for conventional spraying is 60 to 80F, and airless spraying can be
used at 90F. Lacquers such as vinyls and chlorinated rubbers can be applied at
temperatures as low as 35F. The coatings temperature being applied should always be
as high as that of the surface being coated but not significantly higher, unless formulated
for hot application.
The coating being applied should have a viscosity level for proper application.
Three factors may affect viscosity: (1) solvent/solids ratio; (2) coating temperature: and
(3) mixing of thixotropic coatings.
The solvent/solids ratio is established by the coating supplier, so that no thinning is
usually necessary. The colder the coating, the greater will be its viscosity. Thus, it is
generally best to warm cold paints rather than thin them to achieve proper application
viscosity. Should thinning be necessary, the type and amount of thinner specified by the
supplier should be used. The amount is not ordinarily more than 1 pint per gallon of
coating and should not cause the coating to exceed the VOC limits discussed in Paragraph 7.4.1. With two-component coatings, viscosity of the mixed products is important,
not the viscosities of the original components.
Some coatings called thixotropic or false-bodied reach the desired viscosity after
being stirred or agitated. They seem very thick in the can but when stirred become
7-30
more fluid, so that they can be applied. On further standing, the viscosity will increase
until the coating reaches its previous gel-like stage. Thus, thixotropic coatings may require continual agitation during application.
In order to prevent condensation of moisture from the air on wet paint, it should
be applied only when the temperature is at least 5F above the dew point and rising.
Also, coating should never be applied when the prevailing wind is blowing 15 mph or
greater or when the temperature is expected to fall below freezing, before the coating is
fully cured.
7.8 INSPECTION OF PAINTING. Inspecting contract painting work is done to verify
that the requirements of the specification are met in full and that a quality product has
been obtained. Obviously, the latter requires that the specification has been properly
prepared. Any apparent errors, omissions, or potential problems should be brought to
the attention of the contract officer. Before work has begun, there should be a pre-construction conference to be sure that there is a complete understanding of what is expected. At this time, the inspector should become aware of the times when critical
items of inspection must be made and that the areas to be inspected will be accessible
and checked before the work proceeds further. The inspectors daily reports must be
complete and clearly written, since they may become legal evidence. Any field changes
must be written and approved by the contracting officer.
7.8.1 Inspection of Materials. The coating materials must be inspected before
work is started to insure that there are sufficient quantities of each product to fulfill all
requirements and that they are of the specifications or brands required. The amount of
each material required can be determined from the coverage rate given on the
2
suppliers data sheet or by calculation. Use the 16,000 ft /gal as the wet film covering
rate of paints, if the volume of solids in the wet paint is known. Along with the data
sheet and label identification, each material must have a material data safety sheet. The
material should be stored off the ground or floor, protected from the weather, and away
from a source of sparks or flame. If laboratory testing of products is required, it should
be verified that each product meets its specification requirement. If testing was not required, two l-quart authentic samples of each product should be taken and stored
during the warranty period, normally 1 year, to be tested should a problem arise.
7.8.2 Inspection of Surface Preparation. Industrial standards should be used for
surface preparation, whenever they are available. For steel surfaces, the standards are
normally those of the Steel Structures Painting Council (SSPC). These include:
SSPC-SP 1 - Solvent Cleaning
SSPC-SP 2 - Hand Tool Cleaning
SSPC-SP 3 - Power Tool Cleaning
7-31
SSPC-SP
SSPC-SP
SSPC-SP
SSPC-SP
SSPC-SP
The standard chosen should be the one appropriate for the coating and the environment, as recommended by the coating supplier or by the guide specification used. SSPCSP 5 or 10 are normally specified for high-performance coatings. All four blast cleaning
standards require solvent cleaning (SSPC-SP 1) to remove grease and oil before blasting. Visual standards are available from SSPC and others to assist in verifying the level
of blast cleaning. Different visual standards are available for different conditions (extent of rusting) of the steel. Hand and power tool cleaning are most frequently used for
touch-up or when abrasive blasting cannot be used.
The supplier of the primer or the guide specification may also recommend a
particular abrasive for blasting or a particular profile for the blast cleaned surface. The
latter is obtained by selecting an appropriate abrasive. To verify that the specified
profile height has been received, it will be necessary to use a comparitor, profilometer,
or test paper.
7.8.3 Inspection of Coating Application. It is customary to test for appropriate
weather conditions before starting to apply any coating. Temperature can easily be
checked with a thermometer and humidity with a sling psychrometer to determine if
they meet specification requirements. The temperature should always be at least 5F
above the dew point and rising, to prevent condensation of moisture on the wet paint.
Also, exterior spray painting should not be started, if the wind affects the sprays pattern.
By determining the wet film thickness of a coating, you can determine if the specified
dry film thickness will be received. Several types of wet film gages are available. Since
such measurements disturb the wet film, it will have to be repaired before continuing.
Several types of magnetic gages are available for determining if the dry film thickness
meets specification requirements. They should all be checked for calibration before
using. The Tooke gage is a destructive gage (cuts into the coating film) for determining
dry film thickness on any substrate surface.
Electrical holiday detectors are used to locate holidays or other imperfections in
coatings on metal or other conductive surfaces. The low holiday detector (e.g., 67 volts)
is normally used on coatings less than 10 mils thick, and the high voltage detector on
thicker coatings such as those used on underground piping.
7-32
coating, it is wise to apply a test patch about 1 ft in size over the existing paint and
check for incompatibility problem that should occur within a few days.
7.10.2 Spot Repairing. Spot repairs require cleaning of exposed metal and surrounding tightly adhering topcoat(s). The coating edges at damaged areas should be
feathered (beveled) to achieve good adhesion of the patch and provide an attractive
finish. Primer and topcoats used in these repairs should completely cover the metal and
overlap onto the existing coating system to prevent weak joints of new to old coating.
7.11 PAINTING SPECIAL STEEL STRUCTURES.
7.11.1 Fuel and Water Storage Tanks.
Interiors. Interiors of steel fuel and water tanks should be cleaned for coating by
abrasive blasting to a white or near white metal finish (i.e., SSPC-SP 5 or 10). The
cleaned steel should then be coated with three coats of the epoxy-polyamide (see MILP-24441) each applied at 3 mils dry film thickness. Formula 150 green primer should be
followed by Formula 156 red intermediate coat (Formula 151 gray is also suitable for
fuel tanks but not potable water tanks) and Formula 152 white finish coat.
Exteriors. Exteriors of steel fuel and water tanks should be coated as described
for their interiors except that the finish coat of Formula 152 should be replaced by 1-1/2
mils dry film thickness of white (see MIL-C-85282) aliphatic polyurethane. The latter
provides good exterior weathering.
7.11.2 Piping.
Underground. Underground piping can be coated with a variety of thick coatings
or wraps. These include extruded and fusion-bonded coatings and plastic and heatshrinkable tapes. Coal tar and asphalt materials are not applied very much any more because of health and safety concerns. They are best applied in a shop under controlled
conditions. They should be checked for holidays both immediately after application and
above the ditch before burial. Required properties include: good electrical insulation,
good moisture (barrier) resistance, easy application and field repair, good adhesion,
resistance to damage during handling, and resistance to cathodic disbonding.
Above Ground. Coating piping located above ground should be done as previously
described above for steel fuel and water tank exteriors.
Underwater. Coating piping located underwater, should be done as previously
described for steel fuel and water storage tank interiors.
7-34
7.11.3 Waterfront Structures. Steel waterfront structures (e.g., piling and other
pier structures) are normally coated with the epoxy-polyamide system previously
described for steel fuel and water tanks interiors. An alternative system is two coats of
SSPC Paint 16 (coal tar epoxy-polyamide) applied to a total of 16 mils dry film thickness
over a near-white (SSPC-SP 10) abrasively blasted surface.
7.11.4 Antenna and Other Tall Towers and Supporting Equipment.
Towers. Because of the extreme expense of repainting steel antenna towers, it is
best to apply and maintain a high-performance coating system. If possible, the primer
or the total system should be applied in a shop under controlled conditions and touch up
the damaged coating areas after erection in the field. A recommended coating system
consists of one coat of zinc-rich epoxy (SSPC Paint 20, Type II), one coat of epoxypolyamide (MIL-P-24441) Formula 150 green primer, and one coat of white aliphatic
polyurethane (MIL-C-85285).
Anchors and Guys. Anchors and guys can be protected by applying a petrolatum
paste that encapsulates the metal. A special applicator has been developed for remote
application of steel guy lines with petrolatum paste. Alternatively, anchors may be
coated as described for the exteriors of steel fuel and water storage tanks.
7.12 PAINTING GALVANIZED SURFACES. Because new galvanized steel is smooth
and may contain oil to protect it during storage, it is difficult to get coatings to bond well
to it. Weathered galvanizing that has developed a surface texture is much easier to coat.
Historically, galvanizing has been wash primed and coated with two coats of alkyd or
latex coating. Because wash primer and the recommended alkyd coating are no longer
considered environmentally acceptable, this method is no longer applicable. Latex coatings may, however, be applied to weathered galvanizing. A much better performance
will be received from one coat of epoxy-polyamide Formula 150 green primer and one
coat of aliphatic polyurethane (MIL-P-85285). New galvanizing should always be solvent washed (SSPC-SP 1) before coating. Weathered galvanizing should be washed to
remove all loose surface contamination before coating.
7.13 PAINTING ALUMINUM AND OTHER NONFERROUS METALS. In the past,
aluminum and other nonferrous metals were frequently wash primed and coated with
alkyd. Because this system is no longer environmentally acceptable, a two or more coat
epoxy (MIL-P-24441) is recommended.
7.14 PAINTING SAFETY. Because coating operations are frequently hazardous, special
safety precautions must be taken. Local safety offices can provide detailed information
and safety equipment.
7-35
7.14.1 High Places (Scaffolding, Lifts, Nets, and Lines). Workers in high places
should be protected by life lines or nets. Scaffolding should be the required design, and
instructions on their use should be followed.
7.14.2 High Pressures.
Abrasive Blasting Respirators/Training/Physicals. Abrasive blasters should have
the necessary safety training, equipment, and physical examinations to meet all prevailing safety requirements.
Waterblasting. Waterblasting equipment must have a safety certificate and must
be used as described in the instructions.
Airless Spraying. Airless spray guns should always be used with safety guards.
Back flushing with solvents should be done only when special adapters for this purpose
are used.
7.14.3 Flammable Materials. Flammable paint materials should be stored in accordance with local safety requirements and used in enclosed areas only with grounded
equipment and structures and with nonsparking electrical fixtures. Proper ventilation of
vapors is required.
7.14.4 Toxic Materials. Toxic paint materials must be stored in accordance with
local safety requirements. Clothing and respirators should be used to avoid contact and
inhalation. Exposure time should be limited as much as practical.
7.14.5 Caustic Materials (Acids, Alkalis, Steam). Acids, alkalis, and steam can
cause serious burns. Gloves, face shields, and protective clothing should be used when
working with them.
7.14.6 Safety Plan. All shops conducting cleaning or application operations
should have a safety program. This program should include first-aid and safety training
related to these operations to keep all workers aware of hazardous conditions and
methods to provide protection from the hazards.
7-36
8-1
8-2
8-3
steels with pitting being only three to five times the rate calculated from weight loss.
Alloy steels are selected for their higher strength but can be susceptible to hydrogen
embrittlement or stress corrosion cracking at yield strengths in excess 100 ksi. The alloy
steels are somewhat more cathodic than carbon steels.
Cast Irons. Cast iron refers to a wide variety of materials. Commonly, they are
ferrous alloys that contain more than 2% carbon that is found in the alloy such as
graphite or large carbide aggregates. These alloys are used primarily for their formability by casting rather than their mechanical properties or corrosion resistance.
Many of the low alloy cast irons are subject to graphitization. This occurs fairly uniformly with a penetration rate of 0.010 to 0.020 inches per year in seawater immersion or in
many soil environments. Alloy cast irons containing 20% nickel have improved corrosion resistance and corrode uniformly at a low rate. The potential of graphitized cast
iron can be very cathodic with respect to most other materials and can approach that of
graphite. Thus, when graphitized, cast irons can cause corrosion when electrically
coupled to most other metals. Alloy cast irons are somewhat more cathodic than carbon
steels.
8.3.3 Stainless Steels. Stainless steels can be defined as a ferrous alloys that contain more than 11% chromium and are resistant to general rusting in mild atmospheric
conditions. They are generally subject to non-uniform attack in chloride containing environments with crevice corrosion and pitting attack being common on many alloys.
Due to the high rate of localized attack that occurs at the start of the attack, the incubation time for attack is often a more significant measure of corrosion resistance than
penetration rates. The stainless steels exhibit two potential states: (1) active and (2)
passive. The passive state is substantially cathodic to the active state. It is this potential
difference that drives non-uniform attack, such as pitting and crevice corrosion on these
alloys. For purposes of evaluating possible galvanic corrosion between the stainless
steels and other alloys, the potential of the passive state should be used. As these alloys
polarize readily, their potentials can have a wide range in some conditions and may be
of little value in assessing galvanic corrosion problems based on field measurements.
200 Series Stainless Steels. This group of alloys is similar to the more common
300 Series alloys described below as they are non-magnetic and have an austenitic structure. The basic alloy contains 17% chromium, 4% nickel and 7% manganese. Although
these alloys are somewhat more resistant to attack than the more common 300 series
stainless steels, their overall performance is similar. Some proprietary grades related to
the 200 series, have performance equal or superior to the best 300 series stainless steels.
These alloys are, however, not immune to attack and are very susceptible to concentration cell and pitting attack. When corrosion starts they usually corrode rapidly and nonuniformly. In seawater immersion, the incubation time for these alloys is in the range of
1 to 3 months with some of the Nitronic grades having incubation times of up to 1 year.
8-4
300 Series Stainless Steels. This group of alloys are non-magnetic and have an
austenitic structure. The basic alloy contains 18% chromium and 8% nickel. These alloys are subject to crevice corrosion and pitting. They have a range of incubation times
in seawater ranging from essentially zero in the case of the free machining grades, such
as Type 303, to 6 months to 1 year for the best alloys, such as Type 316. They have been
widely used in facilities with mixed results. If used in an application where chloride
levels are low or where concentration cell corrosion has been prevented through design,
they are likely to perform well. When chloride levels are high and where concentration
cells can occur, the performance of these alloys is often poor. They must always be
selected with care for a specific application and the effect of potential non-uniform attack on system performance must be addressed.
400 Series Stainless Steels. This group of alloys are magnetic and have a martensitic
structure. The basic alloy contains 11% chromium and 1% manganese. These alloys
can be hardened by heat treatment but have poor resistance to corrosion. They are subject to both uniform and non-uniform attack in seawater. The incubation time for nonuniform attack in chloride containing environments is very short, often only hours or a
few days. Unless protected, using these alloys in seawater or other environments where
they are susceptible to corrosion is not recommended.
600 Series Stainless Steels. This series of stainless steels is commonly referred to
as Precipitation Hardening stainless steels. These steels can be heat treated to high
strength levels. They are subject to crevice corrosion and pitting in chloride containing
environments and are also subject to stress corrosion cracking and hydrogen embrittlement. The incubation time for crevice corrosion and pitting in seawater is relatively
short, often only a few days. The incubation time for stress corrosion cracking can be
very short, sometimes measured in hours. The use of these alloys in chloride containing
environments is not normally recommended unless they are carefully selected, their
heat treatment is carefully specified and controlled, and the effect of pitting and crevice
corrosion is properly addressed.
Miscellaneous Cast and Wrought Stainless Steels. Alloy 20, a proprietary cast
and wrought stainless steel has superior corrosion resistance to Type 316 stainless steel.
Many newly developed proprietary stainless steels have given good service in many applications and have corrosion resistance superior to Type 316 stainless steel. The use of
these alloys must be evaluated based upon their specific corrosion properties. While
the resistance of these alloys is superior to many other grades of stainless steels, the
benefits of using these alloys in critical applications instead of more corrosion resistant
or corrosion immune alloys must be balanced against the consequences of failure.
8.3.4 Aluminum Alloys. Aluminum alloys are used primarily because of their
low weight, the ease with which they can be formed and fabricated, and their corrosion
8-5
resistance in many atmospheric and immersion environments. They are not, however,
resistant to corrosion in many marine environments and are subject to crevice corrosion,
pitting, and in some alloys, stress corrosion cracking. The alloys are also very subject to
galvanic corrosion as they have an anodic potential with respect to most other metals.
1000 Series Aluminum Alloys. This series of alloys are essentially unalloyed
aluminum. While they have fairly good corrosion resistance as compared to other
aluminum alloys, they have relatively low strength. They are subject to crevice corrosion and pitting.
2000 Series Aluminum Alloys. This series of alloys are alloys of aluminum and
copper. These alloys are relatively high in strength and are widely used in the aerospace
industry. The corrosion resistance of these alloys is inferior to most other aluminum alloys.
3000 Series Aluminum Alloys. This series of alloys are alloys of aluminum and
manganese. Their corrosion performance is roughly comparable to the 1000 series alloys.
5000 Series Aluminum Alloys. This series of alloys are alloys of aluminum and
magnesium. The are relatively low in strength and cannot be heat treated to obtain
higher strengths. Their corrosion performance in most environments is superior to
other aluminum alloys with the exception of the 1000 series. They are, however,, subject to both pitting and crevice corrosion, particularly in marine applications.
6000 Series Aluminum Alloys. This series of alloys are alloys of aluminum, magnesium, and silicon. They are relatively high in strength and can be heat treated to obtain higher strengths. Their corrosion performance in most environments is somewhat
inferior to the 5000 series alloys but is acceptable in many applications. They are subject to both pitting and crevice corrosion.
7000 Series Aluminum Alloys. This series of alloys are alloys of aluminum and
zinc. They are heat treatable to obtain high strengths. Their corrosion performance in
chloride containing environments application is inferior to other aluminum alloys. If
they are used, care must be used to control crevice and pitting attack unless the effects
of these forms of attack are not functionally significant. Some of the 7000 series alloys
are subject to stress corrosion cracking when heat treated to high strength levels.
Cast Aluminum Alloys. Of the cast aluminum alloys, alloy A-356 has the best
overall balance between mechanical properties, castability, and corrosion resistance and
is the most commonly used aluminum casting alloy for corrosion service. Its corrosion
performance is comparable to the 6000 series wrought alloys.
8-6
8.3.5 Copper. Although copper has a relatively low strength, its electrical and
thermal conductivity make it an appropriate material for some marine applications.
Copper corrodes uniformly at a low rate in many environments. Copper is subject to
metal ion concentration attack and the corrosion of this alloy is usually reduced within
crevices. Copper and copper alloys are cathodic to steel and many other commonly
used alloys.
Bronzes. Bronzes are copper-tin, copper-aluminum, or copper-silicon alloys.
Many of these alloys corrode uniformly at a relatively low rate. Some of the alloys, particularly the aluminum bronzes with aluminum contents in excess of 10%, are subject to
dealloying and should not be used if this form of attack is functionally significant. Nickel-aluminum bronzes are widely used as casting alloys and, if properly heat treated, can
give excellent service. Most bronzes are subject to metal ion concentration attack and
the corrosion of this alloy is usually reduced within crevices.
Brasses. Brass is a copper-zinc alloy. Unless the zinc content is below 10% or inhibitors are added to the alloy, brasses are subject to dealloying in immersion service,
particularly in seawater. The use of other copper alloys such as the aluminum bronzes
or copper-nickel alloys in lieu of brass is recommended for most applications where
resistance to corrosion in immersion conditions is important.
Copper-Nickel Alloys. The nickel content of the most common copper-nickel
alloys ranges from 10% to 30%. They are most commonly used for heat exchanger
tubes. The resistance of the alloys to velocity attack is good with the limiting velocity for
the 10% nickel alloy being about 8 feet per second and for the 30% nickel alloy being
about 20 feet per second. They also have good resistance to low flow conditions. The alloys corrode uniformly below their limiting velocities. Both alloys are subject to metal
ion concentration attack and the corrosion of this alloy is usually reduced within
crevices.
Beryllium Copper. Beryllium copper alloys can have very high strengths of up to
200 ksi. They corrode uniformly at a low rate. Beryllium copper is subject to metal ion
concentration attack and the corrosion of this alloy is usually reduced within crevices.
Beryllium copper is widely used as a spring and electrical contact material.
8.3.6 Nickel Alloys. Many nickel alloys have been developed specifically for
their high resistance to corrosion. The alloys in this group are among the most corrosion resistant materials in many environments and some of the alloys are essentially
immune to attack.
Nickel. Nickel, as usually applied as a plating material, is resistant to corrosion
in mildly corrosive environments but is not resistant to corrosion in chloride containing
8-7
Cobalt Alloys. Stellite 6 is a cobalt based alloy that is widely used for a
combination of abrasion and corrosion resistance. It is difficult to form and fabricate
but can be used when its relatively high yield strength (90 ksi), abrasion resistance, and
immunity to corrosion are required. MP-35N is another cobalt based alloy that is widely
used as an aerospace fastener material. Its combination of extremely high yield strength
(285 ksi) and immunity to corrosion are unique. The potential of cobalt alloys are
cathodic to most other metals.
Noble Metals. Gold and platinum are essentially inert in most environments.
Gold is sometimes used as a plating on copper alloys to improve electrical contact resistance. Platinum is primarily used as an anode material for impressed current cathodic
protection. It is either used as wire anodes or is bonded to titanium or niobium supports. Platinum and gold are cathodic to most other metals.
Lead Alloys. Lead and lead alloys corrode uniformly at a low rate in many
environments where the protective film of corrosion products formed on their surface is
insoluble. However, in the presence of nitrates, acetates, or chlorides, lead alloys can
corrode non-uniformly as the corrosion products formed are not protective. Lead-tin
solder corrodes in a similar manner.
8-9
9-1
Resistance to weather
Resistance to sunlight
Hardness
9.1.4 Chemical Resistance Versus Molecular Structure. Natural macromolecules frequently have some inconvenient or undesirable properties. This problem
has been approached on the basis of: (a) modification of the natural macromolecules;
and (b) the synthesis of other new types, often from natural macromolecules. In selecting a plastic material, the following characteristics should be considered: Polar and nonpolar classification, resistance to specific environments, resistance to specific chemicals,
service tests under specific conditions, and toxicity.
9.1.5 Laboratory Tests. Methods of testing plastics are outlined in the following
specifications:
Plastics, Organic: General Methods of Testing. Federal
Specification L-P-406
Rubber: Sampling and Testing, Federal Test Method. Standard No.
601
Paint, Varnish, Lacquer, and Related Materials: Methods of
Inspection, Sampling, and Testing. Federal Specification TT-P-141
1988 Book of ASTM Standards. ASTM Volumes 08.01, 08.02, 08.03,
08.04, 09.01, 09.02, and 10.01
Tentative specifications. Society of the Plastics Industry
9.1.6 Organic Matrix Composites (Reinforced Plastics). Composites have high
tensile strength and impact resistance. The reinforcement can be embedded in the
matrix or external. The composites design structure can be fiberglass, honeycomb,
single to multiple plys, or any number of other construction designs.
The majority of organic matrix composites uses the first two types of plastics as the
matrix material but there are still many uses for the elastomers where flexibility may be
a requirement, as in flexible fuel hoses.
9.1.7 Fiber Reinforced Plastics (FRP). A broad group of composite materials
composed of fibers embedded in a plastic resin matrix. In general, they have high
strength-to-weight ratios and excellent corrosion resistance compared to metals. They
can be formed economically into virtually any shape and size.
9-2
In size, FRP products range from tiny electronic components to large boat hulls.
In between these extremes, there is a wide variety of FRP gears, bearings, bushings,
housings, and parts used in all product industries.
Glass is by far the most used fiber in FRPs. Glass-fiber-reinforced plastics are often
referred to as GFRP or GRP. Asbestos fiber has some use, but is limited in applications where maximum thermal insulation or fire resistance is required. Other fibrous
materials used as reinforcements are paper, sisal, cotton, nylon, and Kevlar. For high
performance parts and components, fibers, such as boron and graphite, can be used.
Although a number of different plastic resins are used as the matrix for reinforced
plastics, thermosetting polyester resins are the most common. The combination of
polyester and glass provides a good balance of mechanical properties as well as corrosion resistance, low cost, and good dimensional stability. In addition, curing can be
done at room temperature without pressure, thus making for low processing equipment
costs. For high volume production, special sheet-molding compounds are available in
continuous sheet form. Resin mixtures of thermoplastics with polyesters have been
developed to produce high quality surfaces in the finished molding. The common
thermoplastics used are acrylics, polyethylenes, and styrenes.
Other glass-reinforced thermosets include phenolics and epoxies. GRP phenolics
are noted for their low cost and good overall performance in low strength applications.
Because of their good electrical resistivity and low water absorption, they are widely
used for electrical housings, circuit boards, and gears. Since epoxies are more expensive
than polyesters and phenolics, GRP epoxies are limited to high performance parts
where their excellent strength, thermal stability, chemical resistance, and dielectric
strength are required.
Initially, GRP materials were limited to thermosetting plastics. Today, however,
more than 1,000 different types and grades of reinforced thermoplastics are commercially available. Leaders in volume use are nylon and styrenes; others include sulfones and
ABS. Unlike thermosetting resins, GRP thermoplastic parts can be made in standard injection-molding machines. The resin can be supplied as pellets containing chopped
glass fibers. As a rule, a GRP thermoplastic with chopped fibers at least doubles the
plastics tensile strength and stiffness. Glass-reinforced thermoplastics are also
produced as sheet materials for forming on metal stamping equipment.
9.1.8 Polymerization. Most synthetic organic materials (plastics) are produced
by adding small unsaturated molecules together to form long chains that can be straight
or branched and with or without cross-linking. This process is usually carried out under
pressure, under heat, chemical action, radiation, or any combination of these catalysts
known as curing agents.
9-3
9-4
The resins vary from soft, sticky semi-solids to hard, brittle solids, depending on
the constitution of the monomers and on the polymerization. They are used for adhesives, protective coatings, finishes, laminated glass, transparent structural sheet, and
molded products. Acrylic resins, or acrylate resins, are stable and resistant to chemicals.
They do not cloud or fade in light when used as laminating material in glass and are
used as air-curing adhesives to seal glass to metals or wood. Water-based acrylics are
also used for caulks and sealants. They have better adhesion and weather resistance
than butyl rubbers and dry more quickly. The sealants usually contain about 80% solids.
Most acrylic plastics are based on polymers of methyl methacrylate, which can be
modified by copolymerizing or blending with other monomers. Noted for excellent optical properties, they have a light transmission of about 92%. Besides the transparent
grades, they come in translucent or opaque colors as well as the natural water white
color. Moldings have a deep luster and high surface gloss, and for this reason are widely
used for decorative parts. Acrylic plastics have excellent weathering characteristics. Because they are hardly affected by sunlight, rain, and, corrosive atmospheres, they are well
suited for outdoor use. In general, the majority of grades can be used up to about 200F
(100C). Thermal expansion is relatively high.
Acrylic plastics are hard and stiff. They are a relatively strong plastic; their tensile
2
strength ranges from 5,000 to about 11,000 lb/in. (34 to about 75 MPa). However,
regular grades are somewhat brittle. High impact grades are produced by blending with
rubber stock. The high strength is useful only for short term loading, For long term use,
to avoid crazing or surface cracking, tensile stresses must be limited to about 1,500
2
lb/in. (10 MPa).
Acrylic plastics are available as cast sheets, rods, tubes, and blocks. They are also
processed by injection or compression molding. Sheets are produced in thicknesses
from 1/8 to 3/8 inch (0.32 to 0.95 cm) and in sizes up to 10 by 12 feet (3 by 4 meters). A
special process that produces molecular orientation in the cast product is used to make
crack-resistant aircraft cabin windows and fighter plane canopies. Acrylic moldings as
2
2
large as 1 yd (1 m ) have been produced. A lead-filled acrylic sheet, produced by
Kyowa Gas Chemical Industry Co., Japan, is used as a radiation shielding material. It is
transparent and has better impact strength and fabricability than leaded glass. Moldings
include knobs, handles, escutcheons, parts for vending machines, and a wide variety of
lenses for light control, signal lamps, etc. the like.
Tough molding resins are made by copolymerizing methyl methacrylate with
styrene.
9-5
Product
Manufacturer
Zerlon 150
Thiacril
Remarks
Manufacturer
Gafite
Remarks
A polymethyl alphachloroacrylate
( C H2 C C I C O O C H 3 ) x. A transparent
and crack-resistant resin used for aircraf
windows. The heat distortion point is
260F (127C), and has higher tensile
and flexural strength than other acrylics.
Cyclohexyl methacrylate has optical
properties similar to crown glass, and
is used for cast lenses, where its
softness and low softening point, 160F
(71C), are not objectionable.
Lucite
E.I. du Pont
de Nemours &
Co., Inc.
Lucite
HM-140
E.I. du Pont
de Nemours &
Co., Inc.
9-6
Product
Manufacturer
Remarks
Acrylic
syrup
E.I. du Pont
de Nemours &
Co., Inc.
Crystalite
Plexiglas
Perspex
Plexiglas V
An injection molding.
Plexiglas VM
Vernonite
Acryloid
Resins
Plexene M
Rhoplex
Resin
Crilicon
Resin
Jersey State
Chemical Co.
9-7
Product
Manufacturer
Polyco 296
American Polymer
Corp.
Remarks
A water-soluble acrylic copolymer used for
thickening natural or synthetic rubber latex
for paper and textile coatings.
Coatings made with acrylics have good adhesion and gloss, are resistant to oils and
chemicals, and have good dielectric strength.
Product
Manufacturer
Carboset 511
B.F. Goodrich
Chemical Co.
Cavalon
Du Pont
Remarks
9-8
Remarks
Product
Manufacturer
Lumarith EC
Celanese Corp.
Hercocel E
Hercules, Inc.
Ethocel
The same material is marketed by a number of other companies for the same purpose
under a variety of trade names.
Cellulose Acetate. An amber colored, transparent material made by the reaction
of cellulose with acetic acid or acetic anhydride in the presence of sulfuric acid. In Germany it was made by treating beechwood pulp with acetic acid in the presence of an excess of zinc chloride. It is used for lacquers and coatings, molding plastics, rayon, and
photographic film. Cellulose acetate may be the triacetate C6H7O2(OOOCCH 3)3, but
may be the tetracetate or the pentacetate, or mixtures. It is made in different degrees of
acetylation with varying properties, Unlike nitrocellulose, it is not flammable, and it has
better light and heat stability. It has a refractive index of 1.47 to 1.50, and a sheet 1/8inch (0.32 cm) thick will transmit 90% of the light. The specific gravity is 1.27 to 1.37,
hardness 8 to 15 Brinell, tensile strength 3,500 to 8,000 lb/in. 2 (24 to 55 MPa), compressive strength up to 20,000 lb/in.2 (137 MPa), elongation 15 to 80%, dielectric strength
300 to 600 volts per mil (12 to 24 x 106 volts per meter), and softening point 122 to
205F (50 to 96C). It is thermoplastic and is easily molded. The molded parts or
sheets are tough, easily machined, and resistant to oils and many chemicals. In coatings
and lacquers the material is adhesive, tough, and resilient, and does not discolor easily.
Cellulose acetate fiber for rayons can be made in fine filaments that are strong and
flexible, nonflammable, mildewproof, and easily dyed. Standard cellulose acetate for
molding is marketed in flake form.
9-9
Cellulose triacetate, with 60 to 61.5% combined acetic acid, is more insoluble, has
higher dielectric strength, and is more resistant to heat and light than other types. It is
cast into sheets and is also used for resistant coatings and textile fibers.
Cellulose acetate lacquers are sold under many trade names. They are the acetate
in solvents with plasticizers and pigments.
Remarks
Product
Manufacturer
Vimlite
Celanese Corp.
Miramesh
National Research
Corp.
Masuron
Nixonite
Nixon Nitration
Works
Plastacele
Du Pont
Acele
Du Pont
Celanese
Celanese Corp.
Celairese
Celanese Corp.
Lanese
Celanese Corp.
Fortisan
Celanese Corp.
9-10
Product
Manufacturer
Forticel
Celanese Corp.
Remarks
Cellulose propionate plastic used in
injection molding. Has a flow point at
(161C), has high impact resistance, and
requires less plasticizier than cellulose
acetate.
Arnel
Celanese Corp.
Arnel 60
Celanese Corp.
Avcovel
American Viscose
Corp.
Cellulose acetate butyrate is made by the esterification of cellulose with acetic acid
and butyric acid in the presence of a catalyst. It is used for coatings, insulation, varnishes, and lacquers. Called butyrate or CAB, is somewhat tougher, has lower moisture
absorption, and a higher softening point than acetate. Special formulations with good
weathering characteristics plus transparency are used for outdoor applications, such as
signs, light globes, and lawn sprinklers. Clear sheets of butyrate are available for
vacuum-forming applications. Other uses include: transparent dial covers, television
screen shields, tool handles, and typewriter keys. Extruded pipe is used for electric conduits, pneumatic tubing, and low pressure waste lines.
Cellulose acetate propionate is similar to butyrate in both cost and properties.
Some grades have slightly higher strength and modulus of elasticity. Propionate has better molding characteristics but lower weatherability than butyrate. Cellulose acetate
9-11
propionate is used to make steering wheels, fuel filter bowls, and appliance housings.
Transparent sheeting is used for blister packaging and food containers.
Product
Manufacturer
Tenite III
Remarks
A cellulose acetate propionate used for
extrusion rod and moldings of high impact
strength.
Hercose C
Hercules, Inc.
Ester
EAB-171
Eastman
9.2.4 Chlorinated Polyether. A high priced, high molecular weight thermoplastic used chiefly in the manufacture of process equipment. Crystalline in structure, it
is extremely resistant to the thermal degradation at molding and extrusion temperatures. The plastic is resistant to more than 300 chemicals at temperatures up to 250F
(120C) and higher, depending on environmental conditions.
Along with the mechanical capabilities and chemical resistance, chlorinated polyether
has good dielectric properties. Loss factors are somewhat higher than those of polystyrenes, fluorocarbons, and polyethylenes, but are lower than many other thermoplastics. Dielectric strength is high and electrical values- show a high degree of consistency
over a range of frequencies and temperatures.
The material is available as a molding powder for injection molding and extrusion
applications. It also comes in sheets, rods, tubes, pipes, and blocks for lining tanks and
other equipment, and for machining gears, plugs, etc. Rods, sheets, tubes, pipes, blocks,
and wire coatings can be extruded on conventional equipment and by normal production techniques. Parts can be machined from blocks, rods, and tubes on conventional
metal working equipment.
9-12
Sheets can be used to convert carbon steel tanks into vessels capable of handling
highly corrosive liquids at elevated temperatures. Using a conventional adhesive system
and hot gas welding, sheets can adhere to sandblasted metal surfaces.
Coatings of chlorinated polyether powder can be applied by several processes.
Using the fluidized bed process, pretreated and preheated metal parts are dipped in an
air-suspended bed of finely divided powder to produce coatings, which after baking are
tough, pinhole free, and highly resistant to abrasion and chemical attack. Parts clad by
this process are protected internally and externally against corrosion.
9.2.5 Fluoroplastics (also known as fluorocarbon resins and fluorine plastics).
A group of high performance, high price engineering plastics. They are composed basically of linear polymers in which some or all of the hydrogen atoms are replaced with
fluorine, and are characterized by high crystallinity and molecular weight. All
fluoroplastics are natural white and feel waxy. They range from semi-rigid to flexible.
As a class, they rank among the best of the plastics in chemical resistance and elevated
temperature performance. Their maximum service temperature ranges up to about 500F (260C). They also have excellent frictional properties and cannot be wet by many liquids. Their dielectric strength is high and is insensitive to temperature and power
frequency. Mechanical properties, including tensile creep and fatigue strength, are only
fair, although impact strength is high.
Manufacturer
Teflon
Du Pont
Remarks
A tetrafluoroethylene of specific gravity
up to 2.3. Tensile strength: up to 3,500
2
lb/in. (23.5 MPa). Elongation: 250 to
350%. Dielectric strength: 1,000 volts
6
per mil (39.4 x 10 volts per meter).
Melting point: 594F (312C). Is water
and chemical resistant.
9-13
Product
Manufacturer
Teflon S
Du Pont
Remarks
A liquid resin of 22% solids. Can be
sprayed by conventional methods and is
curable at low temperatures. Gives a hard,
abrasion-resistant coating. Temperature
service range is up to 400F (204C). Is
used as conveyors and chutes.
T-film
Eco Engineering
Co.
Teflon
Fiber
Du Pont
Teflon
Tubing
Du Pont
Remarks
Product
Manufacturer
Whitcon
Plaskon
Halon
(Grade G80)
Allied Chemical
Co.
A tetrafluoroethylene powder 25 to 30 m
fine particles. Molded parts have tensile
2
strengths to 6,500 lb/in. (44.5 MPa).
KEL-F
3M
Fluorocarbon
Rubber
3M
9-15
Product
Aclar
Manufacturer
Allied Chemical
Co.
Remarks
A chlorotrifluoroethylene transparent
packaging film that is exceptionally
resistant to oils and chemicals, has a
moisture-barrier efficiency 400 times that
of polyethylene film, has good strength to
390F (199C), and retains its flexibility
to -300F (-184C). It is also used for
wire covering.
9.2.6 Polyamide Resins (Nylon). A group of polyamide resins that are longchain polymeric amides in which the amide groups form an integral part of the main
polymer chain and have the characteristic that when formed into a filament, the structural elements are oriented in the direction of the axis.
Nylon was originally developed as a textile fiber, and high strengths (above 50,000
lb/in.2 (344 MPa)) are obtainable in the fibers and films. But this high strength is not
obtained in the molded or extruded resins because of the lack of oriented stretching.
When nylon powder, which has been precipitated from the solution is pressed and
sintered, the parts have high crystallinity and very high compressive strength, but they
are not as tough as molded nylon.
Nylons are produced from the polymerization of a dibasic acid and a diamine. The
most common one of the group is that by the reaction of adipic acid with
hexamethylenediamine. The nylon molding and extruding resin of Du Ponts Elvamide
2
8042, formerly Zytel 42, has a tensile strength of 12,500 lb/in. (106 MPa) with elonga2
tion above 100%, a flexural strength of 13,800 lb/in. (95 MPa), Rockwell hardness of
R118, a flow temperature of 480F (249C), and a dielectric strength of 350 volts per
6
mil (14 x 10 volts per meter).
All of the nylons are highly resistant to common solvents and to alkalies, but are
attacked by strong mineral acids. Molded parts are light weight, with a specific gravity
of about 1.14, good shock-absorbing ability, good abrasion resistance, very low coefficient of friction, and high melting point, up to about 482F (250C). One disadvantage
of nylon is its high water absorption and the resulting dimensional changes in moldings
in service. Nylon is used to make gears, bearings, cams, and linkages. The electrical
characteristics are about the same as those of the cellulosic plastics. As a wire insulation, nylon is valued for its toughness and solvent resistance.
Nylon fibers are strong, tough, elastic, and have a high gloss. The finer fibers are
easily spun into yarns for weaving or knitting either alone or in blends with other fibers,
and they can be crimped and heat set.
9-16
Remarks
Product
Manufacturer
Nyloft
Fiber
Firestone Tire
& Rubber Co.
Caprolan
Tire Cord
Firestone Tire
& Rubber Co.
Nylon
Film
Du Pont
Nylon
Sheet
Du Pont
Nylon
Monofilament
Du Pont
Nylon 6
Du Pont
9-17
Remarks
Product
Manufacturer
Nylon Foam or
Cellular Nylon
Du Pont
Nylon 6/10
Du Pont
Nylon 9
Du Pont
Nylon 11
Du Pont
Nylon 12
Du Pont
Nylon 4
Du Pont
9-18
Remarks
Product
Manufacturer
Alrac Nylon
Radiation Research
Corp.
Is Nylon 4.
Nylon 6/6
Du Pont
Nylatron G
Polymer Corp.
Nylasint
Polymer Corp.
Flalon
Burgess-Berliner
Assoc.
Raynile
Hewitt-Robbins,
Inc.
Fiberthin
Facilon
Sun Chemical
Corp.
9-19
Product
Manufacturer
Lexan Resin
General Electric
Remarks
Has a molecular weight of 18,000, a tensile
2
strength of 10,500 lb/in. (71 MPa), with an
elongation of 60%, dielectric strength to
6
2,500 volts per mil (98 x 10 volts per
meter), and a Rockwell hardness of M70.
The deformation temperature under load is
290F (143C), and the specific gravity is
1.20. Is transparent and the 1/8-inch
(0.318-cm) transmits 85% of the light. This
material is called Makrolon in Germany.
Merlon
Mobray Chemical
Co.
Polycarbonate resin.
Plestar
Film
Ansco
Polycarbonate.
9-20
Remarks
Product
Manufacturer
Lexan 145
General Electric
Lexan FL 1800
General Electric
Cycolac KM
9.2.8 Polyester Resins. A large group of synthetic resins produced by condensation of acids such as maleic, phthalic, or itaconic with an alcohol or glycol, such as allyl
alcohol or ethylene glycol to form an unsaturated polyester. When polymerized the
resins will give a cross-linked, three-dimensional molecular structure, which in turn will
copolymerize with an unsaturated hydrocarbon such as styrene or cyclopentadiene to
form a copolymer of complex structure of several monomers linked and cross-linked.
At least one of the acids or alcohols of the first reaction must be unsaturated. The
polyesters made with saturated acids and saturated hydroxy compounds are called alkyd
resins, and these are largely limited to the production of protective coatings and are not
copolymerized.
The resins undergo polymerization during cure without releasing water, and do not
require high pressure for curing. Through the second modification stage with hydrocarbons, a wide range of characteristics can be obtained. The most important use of the
polyesters is as laminating and molding materials, especially glass-fiber-reinforced plastic products. The resins have high strength, good chemical resistance, high adhesion,
and capacity to take bright colors. They are also used, without fillers, as casting resins,
for filling and strengthening porous materials, such as ceramics and plaster of Paris, and
for sealing the pores in metal castings. Some of the resins are tough and are used to
produce textile fibers and thin plastic sheets and film. Other resins are used with fillers
2
to produce molding powders that cure at low pressures of 500 to 900 lb/in. (3 to 6 MPa)
with fast operating cycles.
9-21
Product
Manufacturer
Mylar Film
Du Pont
Remarks
Polyester made by condensing terephthalic
acid and ethylene glycol. The extremely
thin film, 0.00025 to 0.0005 in. (0.00063
to 0.0013 cm) is used for capacitors and
for insulating motors and transformers.
The film has: a high dielectric strength,
6
up to 6,000 volts per mil (236 x 10 volts
per meter); a tensile strength of 20,000
2
lb/in (137 MPa) with elongation of 70%;
is highly resistant to chemicals and has
low water absorption; is thermoplastic,
with a melting point at about 490F
(254C).
Polyester fibers are widely used in clothing fabrics. The textile fiber produced
from dimethyl terephthalate is known as Dacron. The English textile fibers called
Teron and Terylen are similar materials. Melinex is the English name for the film.
Product
Manufacturer
Mylar 50T
Du Pont
Remarks
Used for magnetic sound-recording tape.
The 0.005-in. (0.013-cm) tape has breaking
strength of 120 oz (3.4 kg) per 1/4 in.
(0.64 cm) of width.
Japanese fiber that has a low specific
gravity, 1.07, and a high melting point,
482F (250C). The fiber is produced
from azelaic acid.
Urylon
Product
Manufacturer
Terefilm
Acme Backing
Corp.
Remarks
Polyester film that is a cyclohexylene
dimethylene terephthalate. Film has a
dielectric strength of the 0.0005-in.
(0.0013-cm), is 8,000 volts per mil (315 x
6
10 volts per meter), with tensile strength
2
of 20,000 lb/in (137 MPa), and heat
distortion temperature of 340F (171C).
Is used for insulation and magnetic tape.
9-22
Electronic tape can also have a magnetic-powder coating on the polyester. But
where high temperature may be encountered, as in a spacecraft, the magnetic coating is
applied to metal tapes.
Remarks
Product
Manufacturer
Densimag
Whittaker Corp.
Koplac Resins
Vibrin 135
Vibrin 136A
Product
Manufacturer
Vulcollan
Goodyear Tire
& Rubber Co.
Chemigum SL
Goodyear Tire
& Rubber Co.
Polyester rubber.
Product
Manufacturer
Kodel
Eastman Chemical
Products, Inc.
Trevira 271
Hoechst Fibers
Industries
teristic is their low water absorption and permeability. This is the reason for their wide
use in sheet form as moisture barriers. The resins are white in thick sections, but otherwise the range varies from translucent to opaque. They feel waxy. There are many available types, ranging from flexible to rigid materials, are classified by density (specific
gravity) into three major groups: Low density = 0.910 to 0.925, medium density =
0.926 to 0.940, and high density = 0.941 to 0.959.
The variations in properties among these three groups are directly related to density.
As density increases, polymer cross-bonding or branching and crystallinity increase.
Thus stiffness, tensile strength, hardness, and heat and chemical resistance increase with
density in polyethylenes. Low density polyethylenes are flexible, tough, and less translucent than high density grades. High density grades, often called linear polyethylene
grades, are stronger, more rigid, and have high creep resistance under load, but they
have lower impact resistance. Low density polyethylenes are used in blow-molded bottles and containers, gaskets, paintbrush handles, and flexible film packaging. High density grades are used in wire insulation, beverage cases, dishpans, toys and the film is
used in boil-in-bag packaging. In general, polyethylenes are not used in load bearing applications because of their tendency to creep. However, a special type, high molecular
weight polyethylene is used for machine parts, bearings, bushings, and gears.
Polyethylenes can be blended or combined with other monomers -- propylene, ethyl
acrylate, and vinyl acetate -- to produce copolymers to improve such properties as stresscrack resistance and clarity and to increase flexibility. They can also be modified by exposure to high energy radiation, which produces cross-linking and, thereby, increases
heat resistance and stiffness.
Remarks
Product
Manufacturer
Zetafax Resin
Dow Chemical
Corp.
Ultrathene
UE630-81A
U.S. Industrial
Chemicals Co.
Aircoflex
Resins
9-25
Remarks
Product
Manufacturer
Polythene
and Alathon
Du Pont
Agilene
American Agile
Corp.
Irrathane
General Electric
Co.
Irrathene
Tape SPT
General Electric
Co.
Fortiflex A
Celanese Corp.
Fortiflex
F-087
Celanese Corp.
9-26
Product
Manufacturer
Remarks
Microthene
U.S. Industrial
Chemical Co.
Dylan
Koppers Co.
The fibers and fabrics are marketed under trade names. One such trade name is
Reevon, by Reeves Brothers, Inc. The fibers and fabrics are used as upholstery fabric
woven of polyethylene monofilament.
Polyethylene foam is light weight, has negligible water absorption, and is used in
sheet and film for thermal insulation, and for wire insulation.
Remarks
Product
Manufacturer
Orthofoam
and Metafoam
Ludlow Papers
Polyethylene
DGDA-2580
Union Carbide
Corp.
Foam is used for extruded insulation coatings on electric cables. Gives uniformly
dispersed closed cells so that the material
has about 30% gas by volume. Extruded coatings have a smooth surface, a tensile
2
strength of 2,800 lb/in. (18 MPa), and a
dielectric constant of 15 to 1.7.
Polyethylene film is resistant to oils, greases, and fatty acids; also has good tear
strength and fold endurance, and the light weight gives a large area per pound. It is
widely used for packaging.
9-27
Remarks
Product
Manufacturer
Tenite 161M
Eastman Chemical
Products, Inc.
Cryovac L
Panelyte
Sheet
Product
Manufacturer
Hypalon S-2
Du Pont
Is a chlorinated polyethylene.
Plaskon
CPF200
Allied Chemical
Corp.
9-28
Product
Manufacturer
Remarks
Ethylenepropylene
rubber
Various
companies
Ethylene
butadiene
resin
Phillips
Petroleum Co.
Polyethylene of low molecular weight is used for extending and modifying waxes.
Is also used in coating compounds to increase toughness, gloss, and heat-sealing properties.
Product
Manufacturer
Epolene N-11
Eastman Chemical
Products, Inc.
Epolene N
Eastman Chemical
Products, Inc.
Epolene LVE
Eastman Chemical
Products, Inc.
Epolene HDE
Eastman Chemical
Products, Inc.
Remarks
Such materials are called polyethylene wax, but they are not chemical waxes. They can
be emulsified by oxidation, and they can be given additional properties by copolymerization with other plastics.
9-29
Remarks
Product
Manufacturer
Elvax
Du Pont
Ladcote
Chemetron
100
Chemetron Corp.
Polymethylene waxes are microcrystalline and have sharper melting points than the
ethylene waxes. They are more expensive, but have high luster and durability.
Polybutylene plastics are rubber-like polyolefins with superior resistance to
creep and stress cracking. Films of this resin have high tear resistance, toughness, and
flexibility, and are used widely for industrial refuse bags. Chemical and electrical
properties are similar to those of the polyethylene and polypropylene plastics.
Polymethyl pentene is a moderately crystalline polyolefin plastic resin that is
transparent even in thick sections. Almost optically clear, it has a light transmission
value of 90%. Parts molded of this plastic are hard and shiny with good impact strength
down to -20F (-29C). Specific gravity (0.83) is the lowest of any commercial solid plastic. A major use is for molded food containers for quick frozen foods that are later
heated by the consumer.
9.2.10 Polypropylene Resins. An important group of synthetic plastics used for
molding resins, film, and texture fibers. Developed in 1957 in Italy and Germany, they
are produced as polypropylene by catalytic polymerization of propylene, or may be
copolymers with ethylene or other material. Propylene is a methyl ethylene
(CH3CH:CH 2) produced in the cracking of petroleum, and also used for making
isopropyl alcohol and other chemicals. The boiling point is 48.2C. It belongs to the
class of unsaturated hydrocarbons known as olefins, which are designated by the word
ending ene. These unsaturated hydrocarbons tend to polymerize and form gums, and
thus are not used in fuels although they have anti-knock properties.
In polyproplyene plastics the carbon atoms linked in the molecular chain between
the CH2 units each have a CH3 and an H attached as side links, with the bulky side
9-30
groups spiraled regularly around the closely packed chain. The resulting plastic has a
crystalline structure with increased hardness and toughness and a higher melting point.
This type of stereosymmetric plastic has been called isotactic plastic. It can also be
produced with butylene or styrene, and the general term for the plastics is polyolefins.
Copolymers of propylene are termed polyallomers.
Polyproplyene is low in weight. The molded plastic has a density of 0.910, a tensile
2
strength of 5,000 lb/in. (34 MPa), with elongation of 150%, and Rockwell hardness of
6
R95. The dielectric strength is 1,500 volts per mil (59 x 10 volts per meter), dielectric
constant 2.3, and a softening point at 150C. Blown bottles of polypropylene have good
clarity and are nontoxic. The melt flow is superior to that of ethylene. A unique property is that thin sections of polyproplyene can withstand prolonged flexing. This characteristic has made polypropylenes popular for living hinge applications. In tests, they
have been flexed over 70 million times without a failure.
The many different grades of polypropylenes fall into three basic groups:
(1) homopolymers, (2) copolymers, and (3) reinforced and polymer blends. Properties
of the homopolymers vary with molecular weight distribution and the degree of crystallinity. Commonly, copolymers are produced by adding other types of olefin monomers
to the propylene monomers to improve properties, such as low temperature toughness.
Copolymers are also made by radiation grafting. Polypropylenes are reinforced with
glass or asbestos fibers to improve mechanical properties and increase resistance to
deformation at elevated temperatures.
Remarks
Product
Manufacturer
Tenite
Eastman Chemical
Products, Inc.
Olefane
Avisun Corp.
Dynafilm 200
U.S. Industrial
Chemicals Co.
9-31
Product
Manufacturer
Dynafilm 300
U.S. Industrial
Chemicals Co.
Remarks
Has the appearance, feel, and machine
handling properties of a Cellophane film.
Consists of oriented polypropylene coated
on both sides with vinyl acetate. The film
ranges in thicknesses of 0.0008 to 0.0012 in.
(0.0020 to 0.0030 cm) and heat seals at
100F (38C).
Polypropylene fiber was originally produced in Italy under the name of Merkalon.
Unless modified, it is more brittle at low temperatures and has less light stability than
polyethylene, but it has about twice the strength of high density linear polyethylene.
Monofilament fibers are used for filter fabrics. They have a high abrasion resistance
and a melting point at 310F (154C).
Multifilament yarns are used for textiles and rope. Polypropylene rope is used for
marine hawsers, will float on water, and does not absorb water like Manila rope. It has
a permanent elongation, or set, of 20%, compared to 19% for nylon rope and 11% for
Manila rope. The working elasticity is 16% compared to 25% for nylon and 8% for
2
Manila. The tensile strength of the rope is 59,000 lb/in. (406 MPa). Fine denier multifilament polypropylene yarn used for weaving and knitting dyes easily and comes in
many colors.
Chlorinated polypropylene is used in coatings, paper sizing, and adhesives.
It has good heat and light stability, and high abrasion and chemical resistance.
9.2.11 Polystyrene. Often referred to as styrene resin, it is used for molding, in
lacquers, and for coatings formed by the polymerization of monomeric styrene, which is
a colorless liquid of the composition C6H 5CH:CH 2, specific gravity 0.906, and boiling
point at 145C. It is made from ethylene, and is ethylene with one of the hydrogen
atoms replaced by a phenyl group. It is also called phenyl ethylene and vinyl benzene.
As it can be made by heating cinnamic acid, C6H 5CH:CHCO2H, an acid found in
natural balsams and resins, it is also called cinnamene. In the form of vinyl toluene,
which consists of mixed isomers of methyl styrene, the material reacts with drying oils to
form alkyd resins for paints and coatings.
The polymerized resin is a transparent solid, very light in weight with a specific gravity
2
of 1.054 to 1.070. The tensile strength is 4,000 to 10,000 lb/in (27 to 68 MPa), a com2
pressive strength of 12,000 to 17,000 lb/in. (82 to 117 MPa), and a dielectric strength of
6
450 to 600 volts per mil (18 to 24 x 10 volts per meter). It is also tougher and stronger
at low temperatures than most other plastics. It is valued as an electrical insulating
material, and the films are used for wrapping cable.
9-32
When produced from methyl stryene, parts have a hardness to Rockwell M83, with
2
tensile strengths to 8,900 lb/in (61 MPa), and a stiffness that makes them suitable for
such products as cabinets and housings. Dielectric strength is also high, above 800 volts
6
per mil (32 x 10 volts per meter). The resin is also used for electronic parts. The heat
distortion temperature is 215F (101C).
Styrenes are subject to creep. Therefore, the long term bearing strength (over 2
weeks) is only about one-third the short time tensile strength. Since their maximum useful service temperature is about 160F (71C), their use is restricted to room-temperature applications. Because of their low cost and ease of processing, polystyrenes are
widely used for consumer products. The impact gradesand glass-filled types are used
for engineering parts and semi-structural applications. Also, polystyrene foams are used
more than all of the foam plastics. Because of good processing characteristics, polystyrenes are produced in a wide range of forms. They can be extruded, injection-, compression-, and blow-molded, and thermo formed. They are also available as film sheets
and foam.
Polystyrenes can be divided into the following major types: general purpose grades,
the lowest in cost, are characterized by clarity; colorability; and rigidity. They are applicable where appearance and rigidity, but not toughness, are required. Common uses
are: wall tiles, compact cases, knobs, brush backs, and container lids. Impact grades of
polystyrenes are produced by physically blending styrene and rubber. Grades are
generally specified as medium, high, and extra high. As impact strength increases,
rigidity decreases.
Medium impact grades are used where a combination of moderate toughness and
translucency is desired. For example, products such as containers, closures, and small
radio cabinets.
High impact grades have improved heat resistance and surface gloss. They are
used for refrigerator door liners and crisper trays, containers, toys, and heater ducts in
automobiles.
Extra high impact grades are quite low in stiffness. Their use is limited to parts
subject to high speed loading.
Styrene can be polymerized with butadiene, acrylonitrile, and other resins. The terpolymer, acrylonitrile-butadiene-styrene (ABS) is one of the common combinations.
Styrene-acrylonitrile (SAN) has excellent resistance to acids, bases, salts, and some solvents. It also is among the stiffest of the thermoplastics, with a tensile modulus of
2
400,000 to 550,000 lb/in (2,757 to 3,791 MPa). Styrene resins for molding are now
marketed under a wide variety of trade names, with or without fillers and reinforcing
9-33
agents. Many of these are copolymer resins, or are modified with plasticizers or crosslinking agents.
Remarks
Product
Manufacturer
Victron
Lustron
Stymer
---
Piccotex
Pennsylvania
Industrial
Chemical Corp.
Styron and
Styraloy
Tyril
Loalin
Catalin Corp.
Exon 860
Firestone Plastics
Co.
9-34
Product
Manufacturer
Fibertuff
Koppers Co.
Remarks
Styrene-butylene resins are copolymers that mold easily and produce thermoplastic
products of low water absorption and good electrical properties. They have strength
equal to the vinyls with greater elongation. Foamed polystyrene is available in blocks
3
3
and heavy sheets for thermal insulation. It weighs about 1 lb/ft (16 kg/m ) and is rigid.
Flexible styrene foam is also made into very thin sheets for wrapping frozen foods. It is
grease resistant and a good insulator, and is low in cost. Styrene is now best known for
its use in synthetic rubbers, but the difference between resins and rubbers is flexibility.
9.2.12 Urethanes (also known as polyurethanes). A group of plastic materials
based on polyether or polyester resin. The chemistry involved is the reaction of a
diisocyanate with a hydroxyl-terminated polyester or polyether to form a higher
molecular weight prepolymer, which in turn is chain-extended by adding difunctional
compounds containing active hydrogens, such as water, glycols, diamines, or amino alcohols. The urethanes are block-polymers capable of being formed by a literally indeterminate number of combinations of these components. The urethanes have excellent
tensile strength and elongation, good ozone resistance, and good abrasion resistance.
Combinations of hardness and elasticity not available with other systems are possible in
urethanes, ranging from Shore hardness of 15 to 30 on the A scale for most industrial
or mechanical goods applications, to the 70 to 85 Shore D scale. Urethanes are fairly
resistant to many chemicals, such as aliphatic solvents, alcohols, ether, certain fuels, and
oils. They are attacked by hot water, polar solvents, and concentrated acids and bases.
Urethane elastomers are made with various isocyanates, the principal ones being
tolylene diisocyanate (TDI) and 4,4-diphenylmethane diisocyanate (MDI) reacting with
linear polyols of the polyester and polyether families. Various chain extenders, such as
glycols, water, diamines, or aminoalcohols, are used in either a prepolymer or a oneshot of system to form the long-chain polymer.
Urethane textile fibers were first made in Germany under the name of Igamide. The
Fiber K, or Lycra, of Du Pont, and the Vyrene, of the U.S. Rubber Co., are flexible
urethane fibers used for flexible garments. They are more durable than ordinary rubber
fibers or filaments, and are 30% lighter in weight. They are resistant to oils and to washing chemicals, and also have the advantage that they are white in color. Spandex fibers
9-35
are stretchable fibers produced from a fiber forming substance in which a long chain of
synthetic molecules are composed of a segmented polyurethane. Stretch before break
of these fibers is from 520 to 610%, compared to 760% for rubber. Recovery is not as
good as rubber. Spandex is white and dyeable. Resistance to chemicals is good but is
degraded by hypochlorides.
9.2.13 Polyvinyl Resins. A group of products varying from liquids to hard solids,
made by the polymerization of ethylene derivatives, used in finishes, coatings, and molding resins, or it can be made directly by reacting acetic acid with ethylene and oxygen.
In general, the term vinyl designates plastics made by polymerizing vinyl chloride; vinyl
acetate, or vinylidene chloride, but may include plastics made from styrene and other
chemicals.
The term is generic for compounds of the basic formula RCH:CRCR". The simplest
are the polyesters of vinyl alcohol, such as vinyl acetate. This resin is lightweight, with a
specific gravity of 1.18, and is transparent, but it has poor molding qualities and its
2
strength is no more than 5,000 lb/in. (34 MPa). The vinyl resins are brittle at low
temperatures. Elvacet, of Du Pont, and Lemac, of the American Monomer Corp., are
vinyl acetate molding resins. But the vinyl halides, CH 2:CHX also polymerize readily to
2
form vinylite resins, which mold well, have tensile strengths to 9,000 lb/in (62 MPa),
high dielectric strength, and high chemical resistance, and a wide range of useful resins
is produced by copolymers of vinyl acetate and vinyl chloride. Various grades of
Bakelite, Geon, Tygon, and other resins are these chloride acetate copolymers.
Vinyl alcohol, CH2:CHOH, is a liquid boiling at 96F (35.5C). Polyvinyl alcohol
is a white, odorless, tasteless powder, which when dry forms a colorless and tough film.
The material is used as a thickener for latex, in chewing gum, and for sixes and adhesives. It can be compounded with plasticizers and molded or extruded into tough and
elastic products. Hydrolized polyvinyl alcohol has greater water resistance, higher adhesion, and its lower residual acetate gives lower foaming. Soluble film, for packaging
detergents and other water-dispersible materials to eliminate the need of opening the
package, is a clear polyvinyl alcohol film. Textile fibers are also made from polyvinyl alcohol, either water-soluble or insolubilized with formaldehyde or another agent. Vinal,
manufactured by the Air Reduction Chemical Co., is a polyvinyl alcohol textile fiber
that is hot-drawn by a semi-melt process and insolubilized after drawing. The fiber has
a high degree of orientation and crystallinity, which gives good strength and is resistant
to water. Polyvinyl alcohol fibers are called Vinylon in Europe and Kuravilon in Japan.
Vinyl alcohol reacted with an aldehyde and an acid catalyst produces a group of
polymers known as vinyl acetal resins, and separately designated by type names, as
polyvinyl butyral and polyvinyl formal. The polyvinyl alcohols are called Solvars, and
the polyvinyl acetates are called Gelvas. The vinyl ethers range from vinyl methyl ether,
CH 2:CHOCH 3, to vinyl ethylhexyl ether, from soft compounds to hard resins. Vinyl
9-36
ether is a liquid which polymerizes, or can react with hydroxyl groups to form acetal
resins. Gantrez M, of General Aniline & Film Corp., is a water-soluble polyvinyl
methyl ether for use in paints, inks, and adhesives. Alkyd vinyl ethers are made by reacting acetylene with an alcohol under pressure, producing methyl vinyl ether, ethyl vinyl
ether, or butyl vinyl ether. They have reactive double bonds that can be used to
copolymerize with other vinyls to give a variety of physical properties.
Polyvinyl formals, Formvars, are used in molding compounds, wire coatings, and
impregnating compounds. It is one of the toughest of the thermoplastics. Formvar, of
the Shawinigan Products Corp., has a specific gravity of about 1.3, a tensile strength up
2
to 12,000 lb/in (82 MPa), elongation from 5 to 20%, Rockwell hardness of M85, and
6
dielectric strength of 450 volts per mil (17 x 10 volts per meter). This type of plastic is
resistant to alkalies but is attacked by acids.
A plastisol is a vinyl resin dissolved in a plasticizer to make a pourable liquid
without a volatile solvent for casting. The poured liquid is solidified to increase viscosity. The polyvinyl acetals, Alvars, are used in lacquers, adhesives, and phonograph
records. The transparent polyvinyl butyrals, Butvars, are used as interlayers in
laminated glass. They are made by reacting polyvinyl alcohol with butyraldehyde,
C 3H 7CHO. Vinal is a general name for vinyl butayl resin used for laminated glass.
Vinyl acetate is a water-white mobile liquid with a boiling point of 70C, usually
shipped with a copper salt to prevent polymerization in transit. The composition is
C H3:COO:CH:CH 2. It may be polymerized in benzene and marketed in solution, or in
water solution for use as an extender for rubber, and for adhesives and coatings. The
higher the polymerization of the resin, the higher the softening point of the resin. The
formula for polyvinyl acetate resin is given as (CH 2:CHOOCCH 3)x. It is a colorless,
odorless thermoplastic with a density of 1.189, unaffected by water, gasoline, or oils, but
soluble in the lower alcohols, benzene, and chlorinated hydrocarbons.
Polyvinyl acetate resins are stable to light, transparent to ultraviolet light, and are
valued for lacquers and coatings because of ther high adhesion, durability, and ease of
compounding with gums and resins. Resins of low molecular weight are used for coatings, and those of high molecular weight for molding.
Product
Remarks
Manufacturer
Darex and
Everflex
Vinylite and
Vinyloid
Union Carbide
9-37
Remarks
Product
Manufacturer
Wood Glu
Paisley Products,
Inc.
Aircoflex
500
Air Reduction
Co.
Product
Manufacturer
Polvin
and Opalon
Monsanto
Ultron
Monsanto
Kraloy Plastic
Pipe Co.
Carlon V
Carlon Products
Vyflex Sheet
Kaykor Industries,
Inc.
9-38
Polyvinyl chloride sheet, unmodified, may have a tensile strength of 8,200 lb/in.
2
(57 MPa), flexural strength of 12,600 lb/in (86 MPa), and a light transmission of 78%.
But in bends or comers of moldings, or in folds of a sheet, the resin shows opaque
whitening. This can be eliminated by modifying the resin with an acrylic. The resins
have improved processing qualities and flexibility, especially for blown bottles and extruded parts, but the light transmission is reduced.
Product
Manufacturer
Acryloid
KM-607
Remarks
A white acrylic powder. When used in
polyvinyl sheet to a content of 20%, it
2
gives a tensile strength of 6,700 lb/in
(46 MPa) and a light transmission of 72%.
Vinylidene chloride plastics are derived from ethylene and chlorine polymerized
to produce a thermoplastic with softening point of 240 to 280F (116 to 138C). The
resins are noted for their toughness and resistance to water and chemicals. The molded
2
resins have a specific gravity of 1.68 to 1.75, tensile strength of 4,000 to 7,000 lb/in. (27
2
to 48 MPa), and flexural strength of 15,000 to 17,000 lb/in. (103 to 117 MPa).
Remarks
Product
Manufacturer
Saran
Saran Latex
Saranex
9-39
Product
Remarks
Manufacturer
Saran
Bristles
Bristles on brushes that are made in diameters from 0.10 to 0.20 in. (0.025 to
0.051 cm).
Velon
Firestone Tire
& Rubber Co.
Zetex
A polyvinylidene cyanide.
9-40
Remarks
Manufacturer
Product
Marvinol
VR-10
Glenn L. Martin
Co.
Marvinol
Resins
Kalitex
U.S. Plywood
Corp.
Vinyon
Union Carbide
Vinyon N
Union Carbide
Carilan
---
9-41
Remarks
Manufacturer
Product
Advagum
Advance Solvents
& Chemical Corp.
Pliovac
Goodyear Tire
& Rubber Co.
Victron
Saflex
Monsanto Co.
Butacite
Du Pont
Formex
General Electric
Co.
Boltaron
6200
Bolta Products,
Inc.
Ingerin
---
Cosal
---
Mipolam
---
Kynar
Pennwalt
9-42
9-43
other resins, such as urea or melamine, to make them compatible with drying oils and to
impart special characteristics.
Since alkyd resins are basically esterification products of innumerable polybasic
acids and polyhydric alcohols, and can be modified with many types of oils and resins,
the actual number of different alkyd resins is unlimited, and the users specification is
normally by service requirements rather than composition. Short-oil alkyds, with 30 to
45% nonoxidizing oils, are used in baking enamels, while the long-oil alkyds, with 56 to
75% oxidizing oils, are soluble in mineral spirits and are used for brushing enamels.
Alkyd coatings are used for such diverse applications as air-drying water emulsion
wall paints and baked enamels for automobiles and applicances.
The properties of oil-modified alkyd coatings depend on the specific oil used as well as
the percentage of oil in the composition. In general, they are comparatively low in cost
and have excellent color retention, durability, and flexibility, but only fair drying speed,
chemical resistance, heat resistance, and salt spray resistance. The oil-modified alkyds
can be further modified with other resins to produce resin-modified alkyds. The resin is
sometimes added during manufacture of the alkyd and becomes an integral part of the
alkyd, or the modifying resin is blended with the alkyd when the paint is formulated.
When mixed with urea formaldehyde or melamine resin, harder and more resistant
baked enamels are produced. Alkyds blended with ehtyl cellulose are used as tough
flexible coatings for electric cable. Other resins blended with alkyds to produce special
or improved properties include phenolic, rosin, vinyl, and silicone.
Alkyd plastics molding compounds are composed of a polyester resin and usually
a diallyl phthalate monomer plus various inorganic fillers, depending on the desired
properties. The raw material is produced in three forms: granular, putty, and glass-reinforced. As a class, the alkyds have excellent heat resistance up to about 300F (150C),
high stiffness, and moderate tensile and impact strength. Their low moisture absorption
combined with good dielectric strength makes them particularly suitable for electronic
and electrical hardware such as switchgear, insulators and parts for motor controllers,
and automotive ignition systems. They are easily molded at low pressures and cure
rapidly. Amberlac and Duraplex, manufactured by Rohm & Haas Co., are alkyd resins
that come in a wide range of formulations.
Paraplex resins are oil-modified soft resins used for coatings for textiles and paper,
and for blending with cellulose plastics for better adhesion on lacquers. Paraplex, P43HV, however, is a polyester-styene copolymer supplied as a clear liquid for laminating, molding, or casting at low pressure.
9-44
Product
Remarks
Manufacturer
Aquaplex
Teglac
American Cyanamid
Co.
Cycopol
American Cyanamid
Co.
Beckosol
1341
Reichhold
Chemicals, Inc.
Petrex
Resin
Hercules, Inc.
Arpolaz
1248-M
U.S. Industrial
Chemicals, Inc.
Iso Burnok
32-0
Dyal
Sherwin-Williams
Co.
American Alkyd
Amalite
and Amavar
Palaskon
Alkyd
Allied Chemical
Corp.
Neolyn
Resins
Hercules, Inc.
9-45
Product
Manufacturer
Cellolyn 501
Hercules, Inc.
Remarks
A lauric acid-penta-erythritol alkyd used
in durable, color stable nitrocellulose
lacquers.
A series of alkyd resins is produced when maleic anhydride or fumaric acid is reacted
with rosin and then esterified with glycerol or other polyhydric alcohol. Isocyanate
resins are linear alkyds lengthened by isocyanates and then treated with a glycol or a
diamine to cross-link the molecular chain. Plastics made from these resins are noted for
good abrasion resistance.
9.3.3 Epoxy Resins. A class of synthetic resins characterized by having in the
molecule a highly reactive oxirane ring of triangular configuration consisting of an
oxygen atom bonded to two adjoining and bonded carbon atoms. They are usually made
by the reaction of epichlorohydrin with phenol compounds, but epoxidation is also done
by the oxidation of a carbon-to-carbon double bond with an organic peracid such as
peracetic. Epichlorohydrin is produced from ally1 chloride, and is a colorless liquid with
a chlorine atom and an epoxide ring. The dipoxy resins made by the oxidation of olefins
with peracetic acid have higher heat resistance than those made with bisphenol.
Epoxidation is not limited to making plastic resins, and epoxidized oils, usually
epoxidized with peracetic acid, are used as paint oils and as plasticizers for vinyl resins.
Epoxy resins are more costly than many other resins, but, because of their unusual
combinations of high mechanical and electrical properties, they are important, especially for such uses as adhesives, resistant coatings, and for encapsulation of electron units.
For encapsulation, they cast easily with little shrinkage. They have very high adhesion
to metals and nonmetals, heat resistance from 350 to 700F (177 to 260C), dielectric
strength to 550 volts per mil (22 volts per meter), and Rockwell hardness of M110. The
2
tensile strength may be up to 12,000 lb/in (82 MPa), with elongation to 2 to 5%, but
some resilient encapsulating resins are made with elongation to 150% with lower tensile
strengths. The resins have high resistance to common solvents, oils, and chemicals.
An unlimited variety of epoxy resins is possible by varying the basic reactions with
different chemicals or different catalysts, or both, by combining with other resins, or by
cross-linking with organic acids, amines, and other agents. To reduce cost when used as
laminating adhesives they may be blended with furfural resins, giving adhesives with
high strength and high chemical resistance. Blends with polyamides have high dielectric
strength, mold well, and are used for encapsulating electrical components.
9-46
Remarks
Product
Manufacturer
Epon Resins
Shell Chemical
Corp.
Kern-Krete
Sherwin-Williams
Co.
Erkopon
Remarks
Manufacturer
Dow Chemical Co.
Oxiron resins, of FMC Corp., are epoxidized polyolefins. They have five or more reactive epoxy groups along each molecule of the chain instead of the usual two terminal
epoxy groups on each molecule. With dibasic acids or anhydrides they form strong, hard
resins of high heat resistance; or resins of lower viscosity are made for laminating and
casting.
Product
Novolac
DEN 438
Remarks
Manufacturer
Dow Chemical Co.
9-47
Product
Narmco
Adhesive
Remarks
Manufacturer
Whittaker Corp.
Epoxies can be copolymerized with other resins. Epoxy-acrylate resin, used for
glass-fiber laminates, combines the resistance and adhesiveness of the epoxy with the
fast cure and strength of the acrylate.
Remarks
Product
Manufacturer
ERRA-0300
Union Carbide
Aracast
Ciba-Geigy
Corp.
Novoloids are fibers that contain at least 85%, by weight, cross-linked novalac
epoxies. Kynol is a novoloid noted for its resistance to exceptionally high temperatures.
At 1,920F (1,049C) the fiber is virtually unaffected. The fiber also has high dielectric
strength and excellent resistance to all organic solvents and nonoxidizing acids.
A family of one-component epoxy resins, named Arnox, are produced by General
Electric Co. Suitable for compression, transfer, injection molding, filament winding,
and pultrusion, they cure rapidly at temperatures of 250 to 350F (121 to 177C). The
compression and transfer molding grade is a black, mineral-filled compound. The injection molding grade is a pelletized glass-fiber reinforced compound with a shelf life of 9
to 12 months below 80F (27C).
9.3.4 Melamine Resins. A synthetic resin of alkyd type made by reacting
melamine with formaldehyde. The resin is thermosetting, colorless, odorless, and resistant to organic solvents. It is more resistant to alkalies and acids than urea resins, has
9-48
better heat and color stability, and is harder. The melamine resins are used as molding
plastics, and are also valued for dishes for hot food or acid juices. They do not soften or
warp when washed in hot water. Melamine, a trimer of cyanamide, has the composition
(N:C"NH 2) 3.
Melamine may be made by reacting urea with ammonia at elevated temperatures
and pressure. It has a specific gravity of 1.56 and melting point of 354C. Melamine
alone imparts to other resins a high gloss and color retention. The melamine resins
have good adhesives but are too hard for use alone in coatings and varnishes. They are
combined with alcohol-modified urea-formaldehyde resins to give coating materials of
good color, gloss, flexibility, and chemical resistance.
Product
Uformite
MU-56
Remarks
Manufacturer
Resinous Products
& Chemical Co.
A urea-modified melamine-formaldehyde
resin used for coatings and varnishes.
A phenol-modified melamine-formaldehyde
resin solution used for laminating fibrous
materials.
9-49
Product
Lanoset
Resimene 812
Remarks
Manufacturer
---
Monsanto
The tensile strength is 7,000 lb/in (48 MPa) and it will withstand continuous temperatures to 500F (260C).
Product
Flexiphen
160
Remarks
Manufacturer
Koppers Co.
Synvar
Durez
Synvar Corp.
Hooker Chemical
Corp.
Phenol resins may also be cast and then hardened by heating. The cast resins
usually have a higher percentage of formaldehyde and do not have fillers. In a syrupy
state they are poured into lead molds and hardened in a slow oven.
Product
Remarks
Manufacturer
Crystallin Crystallin
Products Corp.
Phenol plastic.
Phenalin
Du Pont
Phenol plastic.
Catalin
American Catalin
Corp.
Phenol plastic.
Ivoricast
West Cost
Enterprises
Prystal
American Catalin
Corp.
Bois Glace
American Catalin
9-52
Product
Remarks
Manufacturer
Fiberlon
Fiberloid Corp.
Marblette
Marblette Corp.
A cast plastic.
9.3.6 Polyester Resins. Polyester laminates are usually made with high proportions of glass-fiber mat or glass fabric, and high strength reinforced moldings may
also contain a high proportion of filler. A resin slurry may contain as high as 70% calcium carbonate or calcium sulfate, with only about 11% of glass fiber added, giving an
2
impact strength of 24,000 lb/in (165 MPa) in the cured-material.. Bars and structural
shapes of glass-fiber reinforced polyester resins of high tensile and flexural strengths are
made by having the glass fibers parallel in the direction of the extrusion. Glastrusions,
of Hugh C. Marshall Co., in rods and tubes, are made by having the glass-fiber rovings
carded under tension, then passing through an impregnating tank, an extruding die, and
a heat-curing die. The rods contain 65% glass fiber and 35% resin. They have a flexural
2
strength of 64,000 lb/in. (441 MPa), and a Rockwell M hardness of 65.
Physical properties of polyester moldings vary with the type of raw materials used
and the type of reinforcing agents. A standard glass-fiber-filled molding may have a
2
specific gravity from 1.7 to 2.0, a tensile strength of 4,000 to 10,000 lb/in (27 to 68
2
MPa), with elongation of 16 to 20%, a flexural strength to 30,000 lb/in (206 MPa), a
6
dielectric strength to about 400 volts per mil (16 x 10 volts per meter), and a heat distortion temperature of 350 to 400F (177 to 204C). The moldings have good acid and
alkali resistance. But, since an almost unlimited number of fatty acids are available
from natural fatty oils or by synthesis from petroleum, and the possibilities of by combining with alcohols, glycols, and other materials are also unlimited, the polyesters form an
ever-expanding group of plastics.
9.3.7 Polyurethane Resins (Urethanes). Urethane foams are made by adding a
compound that produces carbon dioxide or by reaction of a diisocyanate with a compound containing active hydrogen. Foams can be classified somewhat according to
modulus as flexible, semi-flexible or semi-rigid, and rigid. No sharp lines of demarcation have been set on these different classes as the gradation from the flexibles to the
2
3
rigids is continuous. Densities of flexible foams range from about 1.0 lb/ft (16 kg/m )
2
3
at the lightest to 4 to 5 lb/ft (64 to 80 kg/m ) depending on the end use. Applications of
flexible foams range from comfort cushioning of all types, e.g., mattresses, pillows, sofa
sets, backs and arms, automobile topper pads, and run underlay, to lightweight clothing
interliners for increasing warmth. Densities of rigid urethane foams range from about
2
3
1.5 to 50 lb/ft (24 to 800 kg/m ).
There are six basic types of polyurethane coatings, or urethane coatings, as defined
by ASTM Specification D16. Types 1, 2, 3, and 6 have long storage life and are formu9-53
the alkylchlorosilanes are made that have high adhesion to metals and are used in
enamels. Methyl chlorosilane, (CH3)2SiCl 2, is a liquid used for waterproofing ceramic
electrical insulators. The material reacts with the moisture in the ceramic, forming a
water-repellent coating of methyl silicone resin and leaving a residue of hydrochloric
acid that is washed off.
Product
Remarks
Manufacturer
Dry-Film
9977
General Electric
Co.
Silicone
SC-50
General Electric
Co.
Velvasil
General Electric
Co.
The dimethyl polysiloxanes are very stable fluids used widely in cosmetics, but
valued also for use in shock absorbers, transformers, and in automatic control systems.
Product
Remarks
Manufacturer
Sun Filter
Polish
Westley Industries
Silcone
cement
Charles Englehard
Inc.
The strong cements developed by the Naval Ordnance Laboratory for making
chemical bonds between glass fibers and resin in plastic laminates are made by reacting
allyl trichlorosilane with phenon resorcinol, or xylenol.
Silcone insulating varnishes will withstand continuous operating temperatures at
350F (177C) or higher. Silicone enamels and paints are more resistant to chemicals
than most organic plastics, and when pigmented with mineral pigments will withstand
temperatures up to 1,000F (538C). For lubricants the liquid silicones are com-
9-55
pounded with graphite or metallic soaps and will operate between -50 and 500F (-46
and 260C).
Product
Remarks
Manufacturer
Silicone liquids are stable at their boiling points, between 750 and 800F (399 and
427C), and have low vapor pressures, so that they are also used for hydraulic fluids and
heat transfer media.
Silicone oils, used for lubrication and as insulating and hydraulic fluids, are methyl
silicone polymers. They retain a stable viscosity at both high and low temperatures. As
hydraulic fluids they permit smaller systems to operate at higher temperatures. In
general, silicone oils are poor lubricants compared with petroleum oils, but they are
used for high temperatures, 150 to 200C, at low speeds and low loads.
Silicone resins are blended with alkyd resins for use in outside paints, usually
modified with a drying oil. Resin XR-807, Dow Corning, is such a silicone-alkyd containing 25% silicone resin that is used to produce paints with high weather and sunlight
resistance. A catalyst is added so that the paint can be air dried. Silicone-alkyd resins
are also used for baked finishes, combining the adhesiveness and flexibility of the alkyd
with the heat resistance of the silicone. A phenyl ethyl silicone is used for impregnating
glass-fiber cloth for electrical insulation and it has about double the insulating value of
ordinary varnished cloth.
Silicone rubber is usually a long chain dimethyl silicone that will flow under heat and
pressure, but can be vulcanized by cross-linking the linear chains. Basically, it consists
of alternate silicon and oxygen atoms with two methyl groups attached to each silicon
2
atom. The tensile strength is 300 lb/in (2 MPa), but with fillers it is raised to 600
2
lb/in. (4 MPa). It is usually compounded with silica and pigments. It is odorless and
tasteless, is resistant to most chemicals but not to strong acids and alkalies, will resist
heat to 500-F (260C), and will remain flexible to -70F (-57C). The dielectric strength
6
is 500 volts per mil (20 x 10 volts per meter).
9-56
Remarks
Product
Manufacturer
Silastic
Dow Corning
Silastic
RTV 601
Dow Corning
and Mayan Indians, but was cultivated only in Mexico and in Panama where it was
called Panama rubber. The latex and rubber are identical with hevea rubber after
purification. Euphorbia rubber is from vines of the genus Euphoria, of which there are
120 species in tropical Africa. Mangabeira rubber was formerly produced in the
Amazon Valley. It is the latex of the mangabeira tree, which comprises various species
of the genus Hancoria and yields the edible fruit mangaba The latex is coagulated with
alum or sodium chloride, but the native Indians coagulated it with the latex of the
caxiguba tree, Ficus anthelmintica, giving a better rubber. The rubber is softer than
hevea rubber, but ages better. The low grade Assam rubber is from a species of ficus
tree, F. elastica, of India and Malaya. Ceara rubber comes from the small, rapid growing tree, Manihot glaziovii, native to the semi-desert regions of Brazil, but now grown in
India and Sri Lanka. The rubber is a good grade.
Rubber latex is a colloidal emulsion of the gathered sap, containing about 35% of
rubber solids, blended from various sources to give average uniformity. The latex is
coagulated with acid and milled into ribbed sheets called crepe rubber, or into sheets exposed to wood smoke to kill bacteria. These rubber sheets are known as smoked sheet
rubber. These sheets constitute the commercial crude rubber, although rubber latex is
used directly, especially for dipped goods such as gloves; toys; and balloons; for coatings,
and for making foam rubber. Rubber can be vulcanized with sulfur and heat, removing
the tackiness and making it harder and more elastic in the low sulfur compounds. All
natural rubber, except adhesive rubbers, is vulcanized rubber.
Ordinary soft rubber contains only 3 to 6% sulfur, but also contains softners, fillers,
antioxidants, or other compounding agents, giving varying degrees of elasticity, strength,
and other qualities. When as much as 30% sulfur is added, the product is called hard
rubber.
Vapor-cured rubber is rubber vulcanized by sulfur chloride fumes and neutralized
with magnesium carbonate. This rubber is used for thin goods only. Acid-cured rubber
is rubber cured in a bath of sulfur chloride in a solvent.
2
The tensile strength of rubber of low vulcanization is 800 to 1,200 lb/in (6 to 8 MPa)
of the original cross section. A good soft rubber can be stretched as much as 1,000%
without rupturing, and will return close to the original length with little permanent set.
The specific gravity is about 1.05, but with fillers may be as high as 1.30. When the term
vulcanized rubber is now used, it refers to hard rubber vulcanized to a rigid but resilient
solid. Vulcanized rubber is used in electrical parts and tool handles. Ace hard rubber,
of the American Hard Rubber Co., has a specific gravity of 1.27, a tensile strength of
2
6
8,700 lb/in (60 MPa), dielectric strength of 485 volts per mil (19 x 10 per meter), distortion temperature 172F (78C), and water absorption 0.04%. Vulcanite and Ebonite
are old names for hard rubber.
9-58
Reclaimed rubber is produced largely from old tires and factory scrap. It is usually
lower in cost than new rubber, but is easier to process and is used in large quantities
even when the price is higher. Reclaimed rubber is sold in sheets, slabs, pellets, and
powder, but much of the rubber powder, or granulated rubber, used for adhesives and
molding is not reclaimed rubber but is made by spray-drying latex. Vultex is a natural
rubber powder in paste form for coatings and adhesives. Mealorub is a rubber powder
developed by the Indonesian Rubber Research Institute for mixing with asphalt for road
surfacing.
Several types of modified natural rubber are used in the production of coatings,
protective films, and adhesives. These are chlorinated rubber, rubber hydrochloride,
and cyclized or isomerized rubber. Chlorinated rubber, for example, modified with any
one of a number of plastic resins, provides maximum protection against a wide range of
chemical. These coatings are widely used in chemical plants, in gas works, and as tankcar linings.
Red rubber is rubber colored red, but was originally rubber vulcanized with
antimony pentasulfide that broke down with the heat of vulcanization, yielding sulfur to
the rubber and coloring it red with the residual antimony trisulfide. Many trade names
accelerators, fillers, and stiffeners are marketed for rubber compounding.
Crumb rubber is any form of porous particles than can be dissolved easily without
milling, cutting, or pelletizing. It is used in adhesives and plastics.
Magnetic rubbers, produced in sheets and strips of various magnetic strengths, are
made of synthetic rubbers compounded with magnetic metal powders.
Chlorinated Rubber. An ivory-colored or white powder produced by the reaction
of chlorine and rubber. It contains about 67% by weight of rubber, and is represented
by the empirical formula (C10H 13C l7)x, although it is a mixture of two products, one
having a CH2 linkage instead of a CHCl. Chlorinated rubber is used in acid- and corrosion-resistant paints, in adhesives, and in plastics.
The uncompounded film is brittle, and for paints chlorinated rubber is plasticized to
produce a hard, tough, adhesive coating, resistant to oils, acids, and alkalies. The
specific gravity of chlorinated rubber is 1.64, and bulking value of 0.0735 gal/lb. The ten2
sile strength of the film is 4,500 lb/in. (31.5 MPa). It is soluble in hydrocarbons, carbon
tetrachloride, and esters, but insoluble in water. The unplasticized material has a high
6
dielectric strength, up to 2,300 bolts per mil (90.6 x 10 volts per meter).
9-59
Remarks
Manufacturer
Product
Tornesit
and Parlon
Hercules Inc.
Chlorinated rubbers.
Paratex
Truscon
Laboratories
Roxaprene
Roxalin Flexible
Lacquer Co., Inc.
Pliofilm
Pliolite
Dartex and Alloprene are German chlorinated rubbers, and Rulahyde is Dutch.
Resistant fibers have also been made from chlorinated rubbers.
Product
Tensolite
Remarks
Manufacturer
Tensolite Corp.
plastic. For example, hard rubbers, which have the highest cross-linking of the elastomers, in many respects are similar to phenolics. In the unstretched state, elastomers
are essentially amorphous because the polymers are randomly entangled and there is no
special preferred geometrical pattern present. However, when stretched, the polymer
chains tend to straighten and become aligned, thus increasing in crystallinity. This tendency to crystallize when stretched is related to an elastomers strength. Thus, as crystallinity increases, strength also tends to increase.
There are roughly 15 major classes of elastomers that have been identified. The
major characteristics of each group are highlighted. Two basic specifications that provide a standard nomenclature and classification system for these classes are: ASTM
Standard D1418, which categorizes elastomers into compositional classes, and joint
ASTM D2000/SAE J200 provides a classification system based on material properties.
The first letter indicates specific resistance to heat aging, and the second letter denotes
resistance to swelling in oil.
Chlorinated polyethylene elastomers are produced by substituting chlorine for
hydrogen on a high density polyethylene chain resulting in a fully saturated structure
with no double or triple bonds. The elastomer requires the catalytic reaction of a
peroxide for curing. Thus, most molded parts are black Five grades of CPE polymers
are produced, differing principally in chlorine content. The higher chlorine content
grades have best oil and fuel resistance, tear resistance, gas impermeability, and hardness. The lower chlorine content grades have lower viscosities, better low temperature
properties, and improved resistance to heat and compression set.
Chlorosulfonated polyethylene elastomer, commonly known as Hypalon, contains
about one-third chlorine and 1 to 2% sulfur. It can be used by itself or blended with
other elastomers. Hypalon is noted for its excellent resistance to oxidation, sunlight,
weathering, ozone, and many chemicals. Some grades are satisfactory for continuous
service at temperatures up to 350F (177C). It has moderate oil resistance. It also has
unlimited colorability. Its mechanical properties are good but not outstanding, although
abrasion resistance is excellent. Hypalon is often used in blends to improve oxidation
and ozone resistance. Hypalon is used as tank linings, high temperature conveyor belts,
shoe soles and heels, seals, gaskets, and spark plug boots.
Epichlorohydrin elastomers are noted for their resistance to oils, and excellent
resistance to ozone, weathering, and intermediate heat. The homopolymer has extremely low permeability to gases. The copolymer has excellent resilience at low temperatures. Both have low heat buildup, making them attractive for parts subjected to
repeated shocks and vibrations.
9-62
Ethylene-propylene elastomers, or EPR rubber, are available as copolymers and terpolymers. They offer good resilience, flexing characteristics, compression set resistance,
and hysteresis resistance, along with excellent resistance to weathering, oxidation, and
sunlight. Although fair to poor in oil resistance, their resistance to chemicals is good.
Their maximum continuous service temperature is around 350F (177C). They are
used in electrical insulation, footwear, and auto hoses and belts.
Fluorocarbon elastomers, fluorine-containing elastomers, like their plastic
counterparts, are highest of all the elastomers in resisting oxidation, chemicals, oils, solvents, and heat. They are also the most expensive. They can be used continuously at
temperatures over 500F (127C) and do not support combustion. Their brittle
temperature is only -10F (-23C). Their mechanical and electrical properties are only
2
moderate. Unreinforced types have tensile strengths of less than 2,000 lb/in. (13 MPa),
and only fair resilience. They are used to make brake seals, O-rings, diaphragms, and
hoses.
The phosphonitrile plastics and elastomers have high elasticity and high temperature
resistance. They are derived from chlorophosphonitrile, or phosphonitrilic chloride,
P 3N 3Cl 3, which has a hexagonal ring of alternating atoms of phosphorus and nitrogen
with the chlorine atoms attached. In the plastic monomers the chlorine atoms are
replaced by other groups. The PN polymers, of Horizons, Inc., contain OCH and C3F 7
groups and are synthetic rubbers of high oxidation and chemical resistance. The tensile
2
strength is up to 700 lb/in. (4.9 MPa) with elongation up to 600%. The material is used
for as gaskets and cratings for severe service.
A phosphonitrilic fluorocarbon elastomer, of the Firestone Tire and Rubber Co.,
is a semi-organic phosphazene polymer. It remains flexible and serviceable at temperatures from -70 to 350F (-57 to 177C), and is highly resistant to oils and solvents over
that temperature range.
Viton is a vinylidene fluoride hexafluoropropylene tetrafluorethylene copolymer,
made by Du Pont, with extra high resistance to solvents, hydrocargons, steam, and
water. Elastomers of the same type produced by 3M have the trade name Fluorel.
Perfluoroelastomer is a specialty, costly, fully chlorinated elastomer, by Du Pont,
that resists commercial solvents, bases, and jet fuels. Kalrez can be used at continuous
service temperatures of up 550F (228C) and at temperatures up to 650F (343C) for
short time periods. Firestones phosphonitrilic fluoroelastomer (PNF200) has improved
low temperature flexibility and resistance to heat aging and fuels. Its maximum continuous service temperature is 350F (176C).
9-63
commercial grades range from 20 to 50% acrylonitrile. Those at the high end of the
range are used where maximum resistance to fuels and oils is required, such as in oilwell parts and fuel hoses. Low acrylonitrile grades are used when good flexibility at low
temperatures is important. Medium-range types, which are the most widely used, are
used in flexible couplings, printing blankets, rubber rollers, and washing machine parts.
Nitriles as a group are low in most mechanical properties. Because they do not crystallize appreciably when stretched, their tensile strength is low, and resilience is roughly
one-third to one-half that of natural rubber. Depending on acrylonitrile content, low
temperature brittleness occurs at from -15 to -75F (-26 to -60C). Their electrical insulation quality varies from fair to poor.
Polyacrylate elastomers are based on polymers of butyl or ethyl acrylate. They
are low volume use, specifically elastomers, used in parts involving oils (especially sulfur-bearing) at elevated temperatures up to 300F (149C) and even as high as 400F
(204C). A major use is for automobile transmission seals. Other oil resistance uses are
gaskets and O-rings. Mechanical properties such as tensile strength and resilience are
low. And, except for new formulations, they lose much of their flexibility below -10F (23C). The new grades extend low temperature service to -40F (-40C). Polyacrylates
have only fair dielectric strength, which improves, however, at elevated temperatures.
Polybutadiene elastomers are notable for their low temperature performance.
With the exception of silicone, they have the lowest brittle or glass transition temperature, -100F (-73C), of all of the elastomers. They are also one of the most resilient,
and have excellent abrasion resistance. However, resistance to chemicals, sunlight,
weathering, and permeability by gases is poor. Some uses are: shoe heels, soles, gaskets, and belting. They are also often used in blends with other rubbers to provide improved resilience, abrasion resistance, and low temperature flexibility.
Polysulfide elastomer, also known as Thiokol, is rated highest in resistance to oil
and gasoline. It also has excellent solvent resistance, extremely low gas permeability,
and good aging characteristics. Thus, it is used for such products as oil and gasoline
hoses, gaskets, washers, and diaphragms. Its major use is for equipment and parts in the
coating production and application field. It is also widely applied in liquid form in
sealants for the aircraft and marine industries. Thiokols mechanical properties, including strength, compression set, and resilience, are poor. Although Thiokol is poor in
flame resistance, it can be used in temperatures up to 250F (121C).
Silicone elastomers are polymers composed basically of silicon and oxygen atoms.
There are four major elastomer composition groups. In terms of application, silicone
elastomers can be divided into the following types: general purpose, low temperature,
high temperature, low compression set, high tensile high tear, fluid resistant, and room
temperature vulcanizing. All silicone elastomers are high performance, high price
materials.
The general purpose grades, however, are competitive with some of the other
specialty rubbers, and are less costly than the fluorocarbon elastomers. They have outstanding resistance to high and low temperatures, oils, and chemicals. High temperature grades have maximum continuous service temperatures up to 600F (316C); low
temperature grades have glass transition temperatures of -180F (-118C).
Electrical properties, which are comparable to the best of the other elastomers, are
maintained over a temperature range from -100F (-73C) to over 500F (260C). However, most grades have relatively poor mechanical properties. Tensile strength runs
2
only around 1,200 lb/in (8 MPa). However, grades have been developed with improved strength, tear resistance, and compression set.
Fluorosilicone elastomers have been developed that combine the outstanding
characteristics of the fluorocarbons and silicones. However, they are expensive and require special precautions during processing. A unique characteristic of one of these
elastomers is its relatively uniform modulus of elasticity over a wide temperature range
and under a variety of conditions. Silicone elastomers are used extensively in products
and components where high performance is required, such as, seals, gaskets, O-rings, insulation for wire and cable, and encapsulation of electronic components.
Styrene-butadiene elastomers, also called Buna S, SBR, and GR-S, are
copolymers of butadiene and styrene. They are similar in many ways to the natural rubbers, and were the first widely used synthetics. They top all elastomers in volume of use,
because of their low cost and use in automobile tires. A wide range of property grades
are produced by varying the amounts of sytrene and butadiene. For example, styrene
content varies from as low as 9% in low temperature resistant rubbers to 44% in rubbers with excellent flow characteristics. Those grades with 50% styrene are, by definition, considered plastics. Carbon black is sometimes added also as it substantially
improves processing and abrasion resistance. SBR elastomers are similar in properties
to natural rubber. They are non-oil resistant and are generally poor in chemical resistance. Although they have excellent impact and abrasion resistance, they are somewhat
below natural rubber tensile strength, resilience, hysteresis, and some other mechanical
properties. The largest single use is in tires. Other applications are similar to those of
natural rubber.
Urethane elastomers are copolymers of diisocyanate with their polyester or
polyether. Both are produced in solid gum form and viscous liquid. With tensile
2
2
strengths above 5,000 lb/in (34 MPa) and some grades approaching 7,000 lb/in (49
MPa), urethanes are the strongest elastomers available. They are also the hardest, and
have extremely good abrasion resistance.
Other notable properties are low compression set, good aging characteristics, and good
resistance to oil and fuel. The maximum temperature for continuous use is under 200F
9-66
(93C), and their brittle point ranges from -60 to -90F (-51 to -68C). Their largest
field of application is for parts requiring high wear resistance and/or strength, for example, forklift truck wheels, airplane tail wheels, shoe heels, bumpers on earthmoving
machinery, and typewriter damping pads.
9.4.3 Thermoplastic Elastomeric Applications.
Thermoplastic Elastomers. A group of polymeric materials having characteristics
of both plastics and elastomers (also called elastoplastics). They can be processed on
standard plastics processing equipment without vulcanizing or curing. They are
lightweight, resilient materials that perform well over-a wide temperature range; There
are a half-dozen different types of elastomplastics. The olefinics, as thermoplastic
olefinics (TPOs), are produced in durometer hardnesses from 54A to 96A Specialty
flame-retardant and semi-conductive grades are also available. The TPOs are used in
automobiles for paintable body filler panels and air deflectors, and as sound-deadening
materials in diesel-powered vehicles. Producers of olefinics include:
Company
Product
Uniroyal
Du Pont
Exxon Chemical
TPF
Somel
TPV
Vistaflex
Pro-fax
Telcar
Hercules
B. F. Goodrich
9-67
Company
Celanese Plastics
Eastman Chemical
General Electric
Celanex
Tenitre polyterephthalate
Valox
found brown coal, peat, and the mineral mellite, or honeystone, which is hydrous
aluminum mellate. Tetrahydrophthalic anhydride is easier to combine with styrene than
phthalic or maleic anhydride, and gives coating resins that are flexible and have quicker
cure with high gloss.
Urethanes. There are three types of thermoplastic urethanes, a high priced
specialty material: polyester-urethane, polyether-urethane, and caproester-urethane.
All three are linear polymeric materials, and, therefore, do not have the heat resistance
and compression set of the cross-linked urethanes. They are produced in three
durometer hardness grades -- 55A, 80A, and 90A. The soft 80A grade is used where
high flexibility is required, and the hard grade, 70D, is used for low deflection load bearing applications. Producers of these elastoplatics are:
Company
Product
B. F. Goodrich
American Cyanamid
Mobay Chemical
Uniroyal
K. J. Quinn
Upjohn
Hooker Chemical
Estane
Cyanaprene
Texin
Pellethane
Q-thene
9-69
9-70
9.4.6 Plastics Summary. The Modem Plastics Encyclopedia provides specifications/materials data that covers the physical and chemical properties of plastics with
ASTM test designation. Other references and sources covering specific physical and
chemical properties and the recommended uses, applications, and designs of various
plastics are given.
These tables are updated yearly and are available from the Modern Plastics
Reprint Department in New York. Other tables that address other aspects such as fire
retardants and machinery are also available. Subscription cost to Modern Plastics (in
1990) for a Government organization is $38.00 for 1 year and $76.00 for 3 years. The
subscription includes monthly issues of Modern Plastics and the yearly Modern Plastics
Encyclopedia wherein the tables are printed. The Encyclopedia is an excellent reference source for materials, machinery, and manufacturers.
9-71
tion combined with other means of corrosion control, such as protective coatings and
electrical insulation. These regulations provide excellent guidelines for the application
of cathodic protection to buried and submerged pipelines.
In addition to these regulations, primarily due to the safety and environmental
consequences of system failure, there are an increasing number of federal, state and
local governmental regulations regarding the storage and transportation of certain
materials that require corrosion control. Many of these regulations either specify
cathodic protection as a primary means of corrosion control or allow its use as an alternative method of controlling corrosion.
10.3 WHERE CATHODIC PROTECTION IS FEASIBLE. In order to be technically
feasible, cathodic protection requires that the structure to be protected be electrically
continuous and be immersed in an electrolyte of sufficient volume to allow the distribution of current onto the structure.
10.3.1 Electrical Continuity of Structure. Electrical continuity of the structure
to be protected may either be through metallic continuity provided by bolting or welding of the structure. Continuity is often achieved or insured by means of electrical connections installed specifically to insure the effectiveness of cathodic protection. These
connections are called bonds.
10.3.2 Electrolyte. The electrolyte is water or the water contained in moist
earth. The conductivity of the electrolyte is an important factor in the design of
cathodic protection systems.
10.3.3 Source of Current. Cathodic protection also requires the presence of a
source of electrical current at the proper voltage or potential to prevent attack on the
structure. These sources of current are called anodes. As described below, the anodes
can either be fabricated from an active metal, such as magnesium or zinc, which
provides a high potential source of electrons through corrosion on its surface or from a
relatively inert material. This inert material has the ability to pass current from its surface without being consumed at a high rate, but requires using an external energy source
to increase the potential of the electrons supplied to the structure being protected. The
systems that use active anodes are called sacrificial systems as the anode material is
sacrificed to protect the structure under protection. The inert anode systems are called
impressed current systems as the external energy source is used to impress a current
onto the structure under protection.
10.4 GUIDANCE FOR DESIGN, INSTALLATION, OPERATION, AND
MAINTENANCE. Guidance for the design and installation of cathodic protection systems is available in Military Handbook 1004/10 (Ref 5). Guidance for the operation
10-2
Figure 10-1
Cathodic Protection Cell
10-3
10.5.2 Current and Potential Requirements. In order to achieve these protective potentials, current must flow from the anode to the structure being protected. The
amount of current required to protect a given structure is proportional to the area of the
structure that is exposed to the electrolyte. Therefore, current requirements are usually
given as current densities in units of amperes or milliamperes (0.001 amperes) per
square foot of exposed surface. For coated structures the amount of current required is
much lower than for bare structures as only those areas on the coated structure where
the coating has been damaged or has deteriorated require or will receive current. Many
coatings can reduce current requirements by over 90%. The current densities required
for cathodic protection depend on the metal being protected and the environment.
Values for the current densities required for cathodic protection of bare steel structures
is shown in Table 10-1. Values of the current densities required for cathodic protection
of coated steel structures is shown in Table 10-2.
Table 10-1
Current Requirements for Cathodic Protection of Bare Steel
Milliamperes
per Square Foot
Environment
2.0 - 3.0
4.0 - 6.0
7.0 - 25.0
15.0 - 40.0
Still Freshwater
2.0 - 4.0
Moving Freshwater
4.0 - 6.0
Turbulent Freshwater
5.0 - 15.0
Hot Freshwater
5.0 - 15.0
Still Seawater
1.0 - 3.0
Moving Seawater
3.0 - 25.0
Concrete
0.5 - 1.5
10-4
Table 10-2
Current Requirements for Cathodic Protection of Coated Steel
Structure
0.001 - 0.005
0.005 - 0.025
0.05 - 0.150
0.001 - 0.005
0.05 - 0.35
0.10 - 0.30
Tank bottoms
0.05 - 2.0
0.05 - 2.0
0.05 - 4.0
0.30 - 3.0
0.10 - 1.5
0.10 - 2.0
0.05 - 1.0
10.5.3 Sacrificial Versus Impressed Current Systems. The method that is used
to supply the required current to the structure being protected depends on the type of
cathodic protection system being used: sacrificial anode or impressed current.
10.6 SACRIFICIAL ANODE CATHODIC PROTECTION SYSTEMS. In sacrificial
anode systems the high energy electrons required for cathodic protection are supplied
by the corrosion of an active metal. This is illustrated in Figure 10-2.
10-5
Figure 10-2
Sacrificial Anode Cathodic Protection System
Sacrificial anode systems depend on the differences in corrosion potential that are
established by the corrosion reactions that occur on different metals or alloys. For example, the natural corrosion potential of iron is about -0.550 volts in seawater. The
natural corrosion potential of zinc in seawater is about -1.2 volts. Thus if the two metals
are electrically connected, the corrosion of the zinc becomes a source of negative charge
which prevents corrosion of the iron. Sacrificial anode cathodic protection systems are
illustrated in Figure 10-3.
The materials used for sacrificial anodes are either relatively pure active metals,
such as zinc or magnesium, or are magnesium or aluminum alloys that have been specifically developed for use as sacrificial anodes. In applications where the anodes are
buried, a special backfill material surrounds the anode in order to insure that the anode
will produce the desired output.
Sacrificial anodes are normally supplied with either lead wires or cast-m straps to
facilitate their connection to the structure being protected. The lead wires may be attached to the structure by welding or mechanical connections. These should have a low
resistance and should be insulated to prevent increased resistance or damage due to corrosion. When anodes with cast-in straps are used, the straps can either be welded directly to the structure or the straps can be used as locations for attachment using mechanical
10-6
Figure 10-3
Cathodic Protection by the Galvanic Anode Method
10-7
Figure 10-4
Impressed Current System
10-8
The energy for the electron energy pump action of the rectifier is provided by
ordinary alternating current. The effect of these electrons at the structure being
protected is the same as that derived from the sacrificial anode type of cathodic protection system. However, the anode material serves only as a source of electrons and need
not be consumed in providing protective current. The materials used for impressed current cathodic protection can the pass a current into the environment without being consumed at a high rate. Graphite and high silicon cast iron are the most commonly used
impressed current cathodic protection anode materials, however, other materials (such
as magnetite, platinum, and newly developed ceramic materials) have been successfully
used. For buried anodes, a backfill of carbonaceous material is used to surround the
anode to decrease the electrical resistance of the anode, to provide a uniform, low resistivity environment surrounding the anode and to allow gasses produced at the anode surface to vent.
In practice, materials such as graphite are used for impressed current cathodic
protection system anodes that are slowly consumed. Anodes in impressed current systems must be inspected and replaced if consumed or otherwise damaged. As is the case
for any electrical equipment, rectifiers used for impressed current cathodic protection
systems require preventative maintenance to insure proper operation. An impressed
current cathodic protection system is shown in Figure 10-5.
Figure 10-5
Cathodic Protection by the Impressed Current Method
10-9
10.8 DESIGN AND INSTALLATION. Methods for designing a cathodic protection system are well developed and are described in MIL-HDBK-1004/10 (Ref 5).
10.9 OPERATION AND MAINTENANCE. In order to effectively provide the increased
structural lifetime and reliability intended, cathodic protection systems must be
monitored and maintained. Economic considerations made at the time that the
cathodic protection was selected as a means of corrosion control should have included
the cost of periodic monitoring and maintenance in the analysis.
10.9.1 Why Periodic Monitoring and Maintenance Are Required. The effectiveness of cathodic protection systems usually change with time. The consumption of both
sacrificial and impressed current anodes can result in decreased anode output that
results in inadequate protection. Deterioration of cable insulation or connections can
result in increased circuit resistance with similar effect. Rectifier output can be reduced
by aging of the stacks, or can be completely interrupted by electrical failure. The corrosion environment can change if there is a change in drainage patterns or the area
around an anode is paved reducing local soil moisture content. Construction of additional structures or modification to existing structure in the area can interfere with the
cathodic protection system.
In order for a cathodic protection system to be effectively monitored and maintained,
the parameters used in the design of the system and the as built configuration of the
system must be known. As built drawings of the cathodic protection system and the
structure being protected should be available as well as drawings of other structures in
the area that might cause interference problems. The cathodic protection system drawings should include, as a minimum, the location and configuration of all test stations, the
location and type of all anodes and rectifiers, and the location of all connections and insulating joints. These drawings should be periodically updated to show any changes
made to the cathodic protection system, the structure being protected or nearby structures.
The desired potentials used in the design of the cathodic protection system should
be indicated. In some cases, different criteria can be used to establish minimum protective potentials at different locations of the same structure.
The design current outputs of the rectifiers or sacrificial anodes in the system
should be recorded. These data are most important in the initial system checkout but
can also be used to evaluate discrepancies in structure to electrolyte potential readings.
The initial system settings and potential readings should be recorded. Changes to
the system such as rectifier adjustment should be periodically recorded. Potential readings taken both at the time of initial system adjustment and during periodic monitoring
should be recorded in order to detect trends in the readings. Changes in potential read10-10
ings are often more important than the actual values themselves in determining the
cause of improper system operation.
In order that any rectifiers in the system can be properly maintained, adjusted, and
repaired, instructions for the rectifiers should be retained. An original copy should be
kept in the maintenance files and a copy should be kept within the rectifier enclosure
for field reference.
10.9.2 Basic Maintenance Requirements. Basic maintenance requirements are:
Monthly: Take rectifier panel meter and tap setting readings. Record
readings on NAVFAC Form 11014-74B.
Quarterly: Take structure to electrolyte potential readings at
selected locations (not less than four points per system). Record
readings on NAVFAC Form 11014-74A.
Annually: Inspect submerged sacrificial and impressed current anodes
for consumption. Inspect test stations for broken wires, loose
connections, or other damage.
In addition to the basic requirements listed above, opportunities to inspect buried
or otherwise inaccessible structure surfaces should be used to inspect the surfaces for
evidence of corrosion or coating deterioration. Such opportunities may be presented by
construction or maintenance in the vicinity of the protected structure.
10-11
11-l
down exposing the metal to a new environment in an unprotected condition. In the new
condition, initial rapid corrosion of the clean surface can result on the formation of a
new protective layer. If the sequence is repeated, the attack experienced can be more
severe in the alternating exposure than an equivalent exposure in either of the environments.
In other cases, extreme conditions can be responsible for the breakdown of passive
films or other initiation of corrosion attack which can then proceed under the more
average conditions experienced. This often occurs when elevated temperatures are occasionally experienced or when salts concentrate by evaporation.
Immersion Service. Service under immersion conditions assumes that an
uncorroded material is fully exposed to a liquid environment during its entire service
life and that, when removed from immersion is quickly treated to arrest any corrosion
that can occur.
a. Temperature. In general, corrosion rates increase with increasing
temperature. In seawater, this increase is much less than the doubling of reaction rates
with each 18F rise in temperature that would be expected if the reactions were under
diffusion control as are many other chemical reactions. For many materials, such as
steels, where the oxygen content of the water directly affects the corrosion rate, the effect of temperature is minimal as in situations where the corrosion rate would be increased by increased temperature, the solubility of oxygen is decreased with increasing
temperatures and the two effects counteract each other. Steels and copper alloys are
particularly insensitive to temperature effects in normal marine immersion.
For other alloys that depend on a passive film for their corrosion resistance, the
effects of temperature can be more pronounced. At elevated temperatures the
solubility oxygen required for repairing protective oxide films found on many passive
materials is reduced and the reactions that cause the films to break down are enhanced
by the increased temperatures. Many stainless steels have what is essentially a critical
pitting temperature in seawater that is in the range of temperatures experienced in
natural seawater. In cold waters they do not pit but in warmer waters they are susceptible.
b. Chemical Composition. In some cases, the chemical composition of a
given environment for immersion service is fairly stable and a complete laboratory
analysis of a single sample can establish the environment responsible for corrosion. In
other cases, the environment varies considerably with time or location in the system and
multiple samples must be taken and analyzed.
c. Dissolved Gasses. The content of dissolved gasses, particularly oxygen
is often an important factor in corrosion in immersion service. Samples for determining
11-3
dissolved gasses must be taken on site using special techniques. Analysis of a liquid
sample for dissolved gasses will often give very misleading results unless the sample is
properly taken and handled.
d. pH. pH is a measurement of the acidic or alkaline nature of a solution.
Strictly speaking it is the negative logarithm of the hydrogen ion concentration. In
acidic solutions the pH is low and can be less than one in highly acidic solutions.
Neutral solutions have a pH of 7.0. Alkaline solutions have a pH greater than 7 and the
pH of a strongly alkaline solution can approach 14. pH solutions can be effectively
measured using either a special pH meter or special papers that change color.
e. Pollutants. Pollutants can have both direct and indirect affects on the
corrosion of metals. Acid or alkaline pollutants from industrial plants can have an adverse effect on the performance of many materials. Heavy metal ions can dramatically
affect the performance of many metals. Aluminum alloys are particularly susceptible to
increased corrosion from small amounts of dissolved metal ions such as copper. Pollution can also have an indirect affect on corrosion by affecting the biological activity that
controls the oxygen content in many seawater environments. In some cases, the oxygen
content can fall to zero and aggressive hydrogen sulfide can form. Polluted environments are often unique both to the environment at a specific site but over time at a particular site. Pollution effects are sometimes seasonal.
Atmospheric Service. Atmospheric exposure is considered to be a
continuous exposure to air without liquid immersion. Sea spray contamination and rain
are considered part of atmospheric exposure.
a. Relative Humidity. Corrosion can normally occur at perceptible rates
on surfaces where there is actually free moisture. Moist air where no moisture is
present on the surface is usually insufficient for corrosion to occur. Materials on the surface of metals such as corrosion products and salt deposits can be hydroscopic and can
absorb sufficient amounts of water from moist air to allow corrosion to proceed. The
relative humidity of the environment affects the ability of such layers to provide sufficient moisture on the surface for corrosion to proceed and also affects the time required
for the surfaces to dry after being wet by rain, dew, or spray. In general, corrosion is
more severe in humid environments than in dry environments. In order to arrest corrosion on equipment by storing in a dry atmosphere, the relative humidity must be
reduced to below 50% with 35% being necessary to completely arrest corrosion on
some materials. When hydroscopic materials are on the metal surface, these must be
removed before dehumidified storage will be effective unless very low humidities can be
achieved. Sea salts are particularly hydroscopic and must be removed in order to
prevent rapid atmospheric attack. Unless removed, the sea salts will effectively concentrate when dried and, unless very low humidities are achieved, will cause accelerated
attack on many metals.
11-4
cathodic to the continuously submerged area with oxygen concentration cell attack occurring in the submerged area.
In other cases, alternate immersion can be less severe than continuous immersion.
This is true for metals that depend on the availability of oxygen for the maintenance of
protective films on their surface. When exposed to alternate immersion, particularly
when well rinsed after immersion, many of the stainless steels that show poor performance in long-term immersion can give good service. In some cases, the time to initiation of corrosion can be very long, up to 2 or 3 years for some alloys, and cleaning and
atmospheric exposure can effectively restart the time to initiation. Thus, under conditions of alternate immersion with rinsing, a given material could withstand 20 years of alternate 6-month immersion when it would show severe attack after 1 year of continuous
immersion.
First Exposure. In many cases the environment to which a metal is
exposed is important in its subsequent performance. This is particularly true where
materials that are dependent on a protective film for their corrosion resistance are concerned. If a stainless steel is exposed to a very aggressive environment, its protective
film can be damaged and reduce corrosion resistance. In some configurations where
water will penetrate into crevices, it is best to first expose the equipment to freshwater.
Subsequent marine immersion may eventually allow salt to penetrate the crevice area
but freshwater can increase the stability of passive films in the crevice and will certainly
reduce the time the surfaces in the crevice are exposed to full strength seawater.
Mechanical Factors. In addition to the chemical nature of the
environment, there are many other factors that can affect both the severity of corrosion
and the impact of the corrosion damage on the function of the equipment.
a. Structural Versus Dynamic Applications. Structures are often designed
based on resistance to deformation rather than resistance to collapse. Localized corrosion often has a minimal effect on the stiffness of many structures and surprisingly
large amounts of corrosion can be tolerated before structural failure. In other cases, the
stiffness of a structure more depends on its shape to resist buckling forces. Considerable localized and general attack can be tolerated without reducing structural strength.
Such structures are also often overdesigned and, if failure does occur in one member,
stresses are transferred to other members and collapse is avoided. Under dynamic loadings and in many mechanical applications, small amounts of corrosion can have a large
affect on function. Small amounts of corrosion in bearings or seals can have a disastrous
effect. Small pits on cyclically loaded parts can serve as fatigue enhancing stress raisers.
In assessing the potential effect of corrosion on function, the consequences of corrosion
in specific locations must be carefully evaluated. Mechanical functions often have little
redundancy and a single point of failure can result in the failure of an entire system or
mission.
11-6
b. Stress. Areas of high stress are not only more likely to fail if corroded,
but corrosion in more likely to occur in such an area. Situations where the effect of
stress has established a type of concentration cell where the high energy of the highly
stressed areas has established a corrosion cell have been suspected but not well documented. High stress, however, often cracks the protective coatings and can also rupture
naturally occurring passive films. High strength materials also are commonly used in
areas of high stress and are subject to both gross corrosion and environmental cracking.
c. Wear. As described in the section on fretting corrosion, the combined
effect of corrosion and wear can be catastrophic. In such cases, materials that are effectively immune to attack are often used.
d. Fluid Flow. As described in the sections on erosion corrosion and
cavitation, high velocity fluid flow can adversely affect many materials. Aluminum alloys are particularly susceptible to velocity attack. Steels are somewhat susceptible even
at low velocities. At high velocities, copper alloys are used but most of these have a
limiting flow velocity that must not be exceeded. If flow is continuous, stainless steels
have a good resistance to velocity effects but if the flow is interrupted, they have poor
resistance to stagnant conditions. The corrosion that began under stagnant conditions
can propagate rapidly even under subsequent flow conditions. Corrosion resistant nickel base alloys and titanium alloys have excellent resistance at high velocities, but can
also be affected when the velocities are extreme (in excess of 25 fps).
Velocity. High velocities should be avoided whenever possible. In
hydraulic systems where high velocities cannot be avoided, the effect of velocity on corrosion must be carefully assessed. At velocities up to 10 fps 90-10 copper nickel has
been widely used with success. At velocities above 10 fps, stainless steels can be used if
the flow is never less than 5 fps. If both high velocity (10 fps) and low velocity (fps)
flow is anticipated, recommend titanium or Inconel 625 be used. Several recently
developed duplex and super austenitic stainless steels have been widely used in heat
exchanger applications, primarily in power plants and in offshore oil production. Their
performance has been good but some failures have occurred. Their performance under
extended low flow conditions remains questionable.
Turbulence. Turbulence causing features in hydraulic systems should
be avoided for not only corrosion considerations but from the standpoint of power or
pumping requirements. Such features as those described in the sections on erosion and
cavitation corrosion should be avoided in the design of seawater containing hydraulic
systems.
11.4.1.3 Material Composition. Like all man made materials, the composition of metals and alloys are subject to variability. In most cases, variability within
the limits established by the manufacturer will not have an effect on the proper11-7
ties of the materials that are critical in the application for which they are commonly
used. Variations of composition within normal manufacturers limits can affect a critical
performance characteristic of the material. It is vital that the material specifications
used are indeed specific. Using industrial standards, such as American Society for Testing and Materials (ASTM) standards or Copper Development Association (CDA) alloy
composition standards, is highly recommended. Proprietary materials procured by
trade name from the original manufacturer or from authorized distributors are usually
satisfactory. The specification and procurement of materials by common name such as
red brass, mild steel, or CRES, should be avoided. Proper quality control, certification, marking, and testing are necessary in order to insure that proper materials are
used. All personnel involved must be sensitized to the fact that using improper
materials can cause failures even though their intentions are to use a material that is
just as good as or better than the material specified. When a material has a characteristic property, such as the non-magnetic character of stainless steel or the color of
some of the copper alloys, this can often be used to identify material substitutions. In
critical applications, non-destructive tests, such as chemical spot tests or X-ray
spectrometry, can be used in a 100% inspection of final components to insure that the
proper materials have been used.
Composition Limits. Although it is common to report alloy composition
as nominal or typical or to report the actual analysis of a specific sample or heat of
material, manufacturers or standardization organizations have established composition
limits for most alloys. In most cases, all materials with compositions within these limits
will give similar performances. In some cases, however, special composition limits have
been identified for marine service and, when necessary, materials meeting these special
limits must be obtained. For example, nickel aluminum bronze is used for marine castings, but in order to give a satisfactory performance, it is important that the nickel content exceeds the iron content in the material, otherwise, pitting corrosion is likely to
occur. The composition limits for nickel in this alloy are 4 to 5% and the composition
limits for iron are 3.5 to 4.5%, thus a casting within the normal composition limits can
have the undesirable situation where the iron content exceeds the nickel content by up
to 0.5%, which can be significant.
Variability. There can also be considerable variability in alloy composition
from different domestic or foreign manufacturers. In very critical applications, mill certifications are required. Receipt analysis is sometimes used to verify that proper raw
materials have been supplied before expensive fabrication or catastrophic failure occurs.
Material Quality. In some cases, several grades of material are available
based on the level of defects that they contain. Often, rather than manufacturing the
materials to more stringent specifications, a single batch of material is simply inspected
and sorted according to its quality. In critical applications, special grades of material
11-8
may be required and, when specified, it must be insured that materials conforming to
the requirements are actually used.
Material Condition. Material properties, especially corrosion resistance,
strength, and toughness are sensitive not only to material composition but other metallurgical factors. When designing equipment it is vital that these factors be considered
when selecting materials and in their fabrication and use.
a. Heat Treatment. Heat treatment can dramatically affect many material
properties. It is vital that the proper heat treatment be specified and used. This is true
for all alloy systems. Aluminum alloys and stainless steels are particularly susceptible to
variations in corrosion properties with heat treatment. Carbon and alloy steels are
primarily susceptible to variations in mechanical properties in different heat treated conditions. In some cases, the material must be in a specific initial condition before subsequent heat treatment can be successfully performed. When this is required, the initial
condition must be verified either by certification or by metallurgical examination. Hardness testing can confirm the heat treatment. However, in some cases, particularly in
aluminum alloys and stainless steels, more than one heat treatment sequence can result
in a given material hardness but with significant differences in other properties, such as
toughness or corrosion resistance. It is often necessary to obtain specific heat treatment
validations from the manufacturer or heat treater and to verify the heat treatment by
mechanical tests, metallurgical examination, or both.
b. Cold Work. Cold work is often used to increase the strength of materials.
Aluminum alloys are particularly susceptible to variations in corrosion properties with
cold work. Almost any alloy will be more susceptible to damage by corrosion when it is
hard worked, not because corrosion is necessarily greater, but in high stress applications, the impact of attack on the function of the highly stressed component is increased.
c. Welding. Joining by welding is highly desirable as it can produce
mechanically sound and leak tight joints that exclude seawater from the interior of the
joints. However, welding is a complex metallurgical process. In the weld pool, alloys
are produced in few seconds from a mixture of the filler metal and base metal and are
contaminated by the weld slag or shielding gas. Unlike the manufacture of the base
alloy, there is not enough time for adjusting the composition of this molten metal before
it solidifies and there is usually no post solidification chemical analysis. In addition, the
base material adjacent to the weld is heat treated to varying degrees. Developing welding procedures that produce welded structures with appropriate strength, toughness,
and corrosion properties is often one of the most difficult steps in the development of
an alloy. As in the case of heat treatment, aluminum alloys and stainless steels are susceptible to variations in corrosion properties when welded and the mechanical properties of steels are sensitive to welding effects. If a welded component has been used with
success or tests of welded materials are the basis for design, it is important that identical
11-9
welding materials and processes be used. In addition, when manual welding is used, the
welders is critical. The welder must be qualified to perform the specific welding procedure being used and on the specific material being welded. In addition, the welder
should be periodically re-certified. In many applications, non-destructive testing, such
as magnetic particle inspection; radiography; and ultrasonic testing, are used in the
quality control of welded components. In some critical applications, random samples of
welded components are destructively tested to assure weld quality.
d. Form. Some materials are difficult to manufacture in some forms. This
affects their availability. While carbon and alloy steels are manufactured in bars, plates,
sheets, forgings, and rolled products; many materials are not as widely available in some
forms and some may be incompatible with manufacture in certain forms. For example,
many aluminum alloys are normally only produced as sheets or plates. While some of
these alloys can easily be made into extrusions, limited demand for specific shapes may
require that large amounts of material be ordered at one time in order to make a special
manufacturing run economical.
In some cases, again particularly in the case of aluminum alloys, variations in
product form can affect corrosion resistance as well as other material properties. As an
example, a plate of aluminum alloy 5086 suffered pitting of up to 0.020 inch in 1 year of
immersion in seawater. An extruded angle of the same material, within composition
limits, was pitted only to a depth of 0.001 inch.
11.4.2 Causes of Service Failures. It is important to realize that there is a difference between the mechanism by which a failure occurs and the cause of failure.
11.4.2.1 Causes Versus Mechanisms. The cause of a failure is a description of the conditions that lead to the failure. The mechanism of failure describes the
mode of failure rather than the conditions that lead to the failure. For example, a stainless steel part may fail due to crevice corrosion when the cause of failure was substituting an improper grade of stainless steel, improper assembly, or failure of a protective
coating.
11.4.2.2 Design Related Failures. Causes of failures often relate more
closely to features of design rather than the properties of the materials used. As
described in the sections on specific forms of corrosion, design features that create such
features as crevices, high stresses, and high velocity turbulent flow can be important factors leading to corrosion failures. The sensitivity of equipment to failure by corrosion attack is also primarily a function of design.
11.4.2.3 Material Related Failures. Some failures are caused by the actual material deficiencies. A material sometimes does not perform as it was expected to
based on its anticipated properties.
11-10
11-12
12-1
12-2
Appendix A
ECONOMIC LIFE GUIDELINES*
To provide a basis for comparison between competing projects, economic lives are
established for the general investment classifications listed below. These guidelines can
be used in the absence of better information. However, due to the constraints of mission life and technological life, the economic life chosen should not exceed the applicable figure below.
1.
ADP Equipment
8 years
2.
Buildings
a. Permanent
b. Semi-permanent, non-wood
c. Semi-permanent, wood
d. Temporary or rehabilitated
25 years
25 years
20 years
15 years
3.
Operating Equipment
25 years
4.
25 years
25 years
15 years
15 years
15 years
Appendix B
PROJECT YEAR DISCOUNT FACTORS*
Table B
Table A
PRESENT VALUE OF $1 (Single Amount -to be used when cash flows accrue
in varying amounts each year)
Project Year
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
18
19
20
21
22
23
24
25
10%
10%
0.909
0.826
0.751
0.683
0.621
0.564
0.513
0.467
0.424
0.386
0.350
0.319
0.290
0.263
0.239
0.218
0.198
0.180
0.164
0.149
0.135
0.123
0.112
0.102
0.092
0.909
1.736
2.487
3.170
3.791
4.355
4.868
5.335
5.759
6.145
6.495
6.814
7.103
7.367
7.606
7.824
8.022
8.201
8.365
8.514
8.649
8.772
8.883
8.985
9.077
NOTE: Table A factors are based on continuous compounding at a 10% effective annual discount rate, assuming uniform cash flows throughout state 1-year periods. Table
A factors are approximated by an arithmetic average of beginning and end of year single
amount factors found in standard present value tables. Table B factors represent the
cumulative sum of Table A factors through any given project year. Formulae for these
factors are provided in Appendix C.
*Source: Economic Analysis Handbook, NAVFAC P-442 of June 1986.
B-1
Appendix C
PRESENT VALUE FORMULAE*
1
an=
(1 + R)
(1 + R) - 1
b
=
n
R(1 + R)
where:
n = number of years
R = 0.10, effective annual discount rate.
INDEX
A
Abrasive blasters, 7-36
Abrasive cleaning, 7-14
Acetal resins, 9-4
Acrylic resins, 9-4
Acrylonitride-butadine styrene
(ABS), 9-43
Air-assisted airless spray, 7-27
Airless spray, 7-26
Air oxidation of drying oils, 7-3
Alternate immersion service, 11-5
Alkyd resins, 9-43
Aluminum alloys, 8-5
Anode, 4-2
Anodic reactions, 4-2
Antifouling paints, 7-6
Applying coatings, 7-22
Asbestos fibers, 7-6
Assembly errors, 11-12
Atmospheric service, 11-4
Austenitic stainless steel, 4-20
B
Beryllium copper, 8-7
Bituminous coatings, 7-9
Blast cleaning techniques, 7-21
Blasting equipment, 7-18
Blasting procedures, 7-20
Brasses, 8-7
Bronzes, 8-7
Brush-off blast, 7-16
Butyl rubbers, 9-64
C
Carbon steel, 8-3
Cast aluminum alloys, 8-6
Cast and wrought stainless steels, 8-5
Cast irons, 8-4
Catalog of corrosion data, 8-3
Index-1
Cathode, 4-2
Cathodic protection cell, 10-3
Cathodic reactions, 4-3
Cellulose acetate, 9-9
Cellulosic resins, 9-8
Centrifugal blasting, 7-19
Chain Link Security Fences (different
environments)
Alternative 1 (tropical marine environment), 3-67
Alternative 2 (tropical marine environment), 3-69
Alternative 1 (temperate marine
environment), 3-70
Alternative 2 (temperate marine environment), 3-71
Alternative 1 (non-marine environment), 3-72
Alternative 2 (non-marine
environment), 3-73
Chemical cleaning, 7-14
Chemical reaction, 7-4
Chlorinated polyethylene elastomers,
9-62
Chlorinated polyether, 9-12
Chlorinated rubber, 9-59
Chlorosulfonated polyethylene elastomer, 9-62
Cleaning methods, 7-15
Cleaning steel surfaces, 7-16
Coal tar and asphalt coatings, 7-6
Coal tar epoxy coatings, 7-10
Coatings, 7-1
Coating failures, 7-33
Coating Protection Methods
Barrier, 7-l
Cathodic, 7-1
Inhibitive pigments, 7-1
Cobalt alloys, 8-9
Cold work, 11-9
Cold worked brass, 4-19
Commercial blast, 7-16
Existing Seawall,
Alternative 1, 3-50
Alternative 2, 3-51
Alternative 3, 3-52
Alternative 4, 3-53
Alternative 5, 3-54
Alternative 6, 3-55
Existing steel fuel lines, 3-7
Exterior Doors of a Marine Barracks
Alternative 1, 3-58
Alternative 2, 3-59
D
Deadman valves, 7-19
Dead paint, 7-13
Depreciation, 3-5
E
Economic analysis, 3-1
Elastomers, 9-1
Electrochemical cell, 4-1
Electrolyte, 4-2
Electron energy pump, 10-9
Electrostatic spray, 7-27
Environmental contamination, 1-3
Epichlorohydrin elastomers, 9-62
Epoxy coatings, 7-10
Epoxy resins, 9-46
Ethyl cellulose, 9-8
Ethylene-propylene elastomers, 9-63
Index-2
G
Galvanic series, 4-9
Glass-fiber reinforced plastics, 9-3
Grades of rust, 7-16
Grain boundary attack, 4-17
Grain boundary material attack, 4-17
H
Hand cleaning, 7-14
Heat treatment, 11-11
High steel antenna tower,
Alternative 1, 3-29
Alternative 2, 3-32
Alternative 3, 3-34
Alternative 4, 3-36
High strength-low alloy steels, 8-3
Hydroblasting, 7-15
Hydrogen atom, 4-19
I
ID hose, 7-18
Immersion service, 11-3
Inflation, 3-3
Inspection of coating application, 7-32
Inspection of coating materials, 7-31
Inspection of painting, 7-31
Inspection of surface preparation, 7-31
Isoprene rubber, 9-64
L
Lacquers, 7-9
Latex coatings, 7-8
Lead alloys, 8-9
Lead and chromium pigments, 7-5
M
Maintenance and operation, 3-6
Maintenance control inspections, 11-1
Manufacturing related failures, 11-11
Index-3
S
Sacrificial anode, 10-5
Safety, 1-2
Sand pot, 7-18
Selecting corrosion resistant metals,
8-1
Selective attack, 4-16
Sensitivity analysis, 3-5
Service environment, 11-2
Service performance, 8-2
Service related failures, 11-12
Silica, 7-7
Silicones, 9-54
Silicone elastomers, 9-65
Silicone insulating varnishes, 9-55
Silicone resins, 9-54
Silicone rubber, 9-56
Slag abrasives, 7-21
Solvent, 7-2
Solvent cleaning, 7-13
Solvent evaporation, 7-3
Specifications for testing plastics, 9-2
Spot repairs, 7-34
Spray painting procedures, 7-27
SSPC standards, 7-17
Stainless steels, 8-4
Stainless steels sensitization, 4-17
Steam cleaning, 7-14
Steel piping under a pier,
Alternative 1, 3-40
Alternative 2, 3-42
Storing coatings, 7-28
Styrene-butadiene elastomers, 9-66
Styrene-butylene, 9-35
Superpolymers, 9-69
Synthetic abrasives, 7-21
Synthetic organic mildewcides, 7-6
Synthetics rubber, 9-61
R
Ram Gutters for Navy Housing
Alternative 1, 3-63
Alternative 2, 3-64
Alternative 3, 3-65
Reactions in,
Acidic solutions, 4-4
Neutral alkaline solutions, 4-4
Overall reactions, 4-4
Reaction rates, 4-4
Reclaimed rubber, 9-59
Index-4
T
Technological life, 3-4
Teflon, 9-13
Thermal spray of metals, 7-27
Thermoplastic, 9-1
Thermoplastic elastomers, 9-67
Thermoplastic urethanes, 9-69
Thinning mixed coatings, 7-30
Thixotropic coatings 7-30
Titanium alloys, 8-8
Toxic coatings, 7-7
Toxic pigments, 7-5
Turbulence, 11-7
Welding, 11-11
Wet and water blasting, 7-15
When to use cathodic protection, 10-1
White metal blast, 7-16
Z
Zinc-rich inorganic coatings, 7-11
Zinc-rich organic coatings, 7-12
U
Underwater inspections, 11-1
Urethane elastomers, 9-35
Urethane (polyurethane) coatings,
7-11
Urethane Resins, 7-6
Urethanes, 9-35
V
Vapor-cured rubber, 9-58
Velocity, 11-7
Vinyls,
Acetate, 9-37
Alcohol, 9-36
Benzoate, 9-40
Chloride, 9-38
Visual examination, 11-2
Volatile organic compounds, 7-4
W
Water-borne coatings, 7-28
Water evaporation, 7-3
Water storage tank,
Abrasive blasting, 3-24
Exterior, 3-21
Interior, 3-17
Index-5