SHEARING
SHEARING
SHEARING
Shearing is a cutting operation used to remove a blank of required dimensions from a large sheet. To
understand the shearing mechanism, consider a metal being sheared between a punch and a die, Fig 5.1 Typical
features of the sheet and the slug are also shown in this figure. As can be seen that cut edges are neither smooth nor
perpendicular to the plane of the sheet.
Fig 5.1 (a) Shearing with a punch and die (b) features of a punched hole and (c) features of the slug.
Shearing starts as the punch presses against the sheet metal. At first, cracks form in the sheet on both the top
and bottom edges (marked T and T', in the figure). As the punch descends further, these cracks grow and eventually
meet each other and the slug separates from the sheet. A close look at the fractured surfaces will revel that these are
quite rough and shiny; rough because of the cracks formed earlier, and shiny because of the contact and rubbing of
the sheared edge against the walls of the die.
The clearance between the punch and the die plays an important role in the determination of the shape and
quality of the sheared ege. There is an optimum range for the clearance, which is 2 to 10% of the sheet thickness, for
the best results. If the clearance increases beyond this, the material tends to be pulled into the die and the edges of
the sheared zone become rougher. The ratio of the shining (burnished) area to the rough area on the sheared edge
decreases with increasing clearance and sheet thickness. The quality of sheared edge is also affected by punch
speed; greater the punch speed better the edge quality.
Shearing Operations
For general purpose shearing work, straight line shears are used. as shown in Fig 5.2, small pieces (A, B, C,
D.) may be cut from a large sheet.
Fig 5.2
Shearing may also be done between a punch and die, as shown in Fig 5.1. The shearing operations make
which use of a die, include punching, blanking, piercing, notching, trimming, and nibbling.
Punching/Blanking
Punching or blanking is a process in which the punch removes a portion of material from the larger piece or a
strip of sheet metal. If the small removed piece is discarded, the operation is called punching, whereas if the small
removed piece is the useful part and the rest is scrap, the operation is called blanking, see Fig 5.3.
Example: A circular blank of 30 mm diameter is to be cut from 2 mm thick 0.1 C steel sheet. Determine the die and
punch sizes. Also estimate the punch force and the stripping force needed. You may assume the following for the
steel : Tensile strength: 410 MPa ; shear strength : 310 MPa
Solution:- For cutting a blank, die size = blank size
Die size = 30mm
Clearance = 0.003 x t x = 0.003 x 2 x 310
= 1.86 mm
Punch size = blank size 2 clearance
= 30 2 x 1.86 = 26.28 mm
Punch force needed = L. t. = x 30 x 2 x 310
= 58.5 kN
Stripping force needed = 0.02 L.t
= 0.02 x x 30 x 2
= 3.77 kN
Piercing:
It is a process by which a hole is cut (or torn) in metal. It is different from punching in that piercing does not
generate a slug. Instead, the metal is pushed back to form a jagged flange on the back side of the hole.
A pierced hole looks somewhat like a bullet hole in a sheet of metal.
Trimming:
When parts are produced by die casting or drop forging, a small amount of extra metal gets spread out at the
parting plane. This extra metal, called flash, is cut off before the part is used, by an operation called trimming. The
operation is very similar to blanking and the dies used are also similar to blanking dies. The presses used for
trimming have, however, relatively larger table.
Notching:
It is an operation in which a specified small amount of metal is cut from a blank. It is different from punching in
the sense that in notching cutting line of the slug formed must touch one edge of the blank or strip. A notch can be
made in any shape. The purpose of notching is generally to release metal for fitting up.
Nibbling:
Nibbling is variation of notching, with overlapping notches being cut into the metal. The operation may be
resorted to produce any desired shape, for example flanges, collars, etc.
Perforating:
Perforating is an operation is which a number of uniformly spaced holes are punched in a sheet of metal. The
holes may be of any size or shape. They usually cover the entire sheet of metal.