12l14 Bright Mild Steel
12l14 Bright Mild Steel
12L14 is a Re-Sulphurised, Re-Phosphorised Free Maching Steel. This is premium grade of free cutting steel is used by
repitition engineers and general machining for a wide variety of applicaitons. It has excellent machinability and is suitable
for case hardening and electroplating.
Typical applications are: Brake hose ends, pulleys, disc brake pistons, wheel nuts and inserts, control linkages, gear box
components (case hardened), domestic garbage bin axles, concrete anchors, padlock shackles, hydraulic fittings, vice jaws
(case hardened)
Material: Magnetic in all conditions
Colour Code
Purple (Bar
End)Rose Pink
(Band)
Stocked Sizes
Rounds
6.35mm - 60mm
Hexagons
10mm - 63.5mm
Bar Finish
Related Specifications
Australia
Germany
Great Britain
Japan
JIS: SUM22L
USA
Chemical Composition
Min. %
Max. %
Carbon
0.15
Silicon
0.10
Manganese
0.80
1.20
Phosphorous
0.04
0.09
Sulphur
0.25
0.35
Lead
0.15
0.35
Typical Mechanical Properties - Cold Drawn and Turned and Polished Condition
Cold Drawn Size mm
up to 16mm
17 - 38mm
39 - 63mm
Min
480
430
400
370
Max
760
690
630
520
Min
350
330
290
230
Max
590
550
500
310
Elongation in 50mm %
Min
17
Hardness HB
Min
142
120
115
105
Max
225
205
185
155
Forging
Heat to 1300 oC maximum, hold until temperature is uniform throughout the section and commence forging.Do not forge
below 950 oC
Finished forgings may be air cooled.
Heat Treatment
Annealing
Heat to 890 oC - 920 oC hold until temperature is uniform throughout the section, and cool in furnace.
Carburizing
Pack, salt or gas carburise at 900 oC holding for sufficient time to develop the required case depth and carbon content,
followed by a suitable refining/hardening and tempering cycle to optimise case and core properties.
Core Refine
Slow cool from carburising temperature and re-heat to 880 oC - 900 oC, hold until temperature is uniform throughout the
section and quench as required in oil, water.
Case Hardening
Following core refining, re-heat to 760 oC - 790 oC, hold until temperature is uniform throughout the section and quench in
water.Temper immediately while still hand warm.
Tempering - After Carburising, Core Refining and Case Hardening
Re-heat to 120 oC - 230 oC, hold until temperature is uniform throughout the section, soak for 1 hour per 25 mm of section
and cool in still air.NB. Tempering will improve the toughness of the case with only slight reduction in case hardness. It will
also reduce it's susceptibility to grinding cracks.
Normalizing
Heat to 900 oC - 940 oC hold until temperature is uniform throughout the section, soak for 10 - 15 minutes.Cool in still air.
Stress Relieving
Heat to 500 oC - 700 oC hold until temperature is uniform throughout the section, soak for 1 hour per 25mm of section, and
cool in still air.
Notes on Heat Treatment
Heating temperatures, rate of heating, cooling and soaking times will vary due to factors such as work piece size/shape,
also furnace type employed, quenching medium and work piece transfer facilities etc.Please consult your heat treater for
best results.
Machining
12L14 is a premium free cutting steel grade suitable for all types of high production and repitition machining.
Welding
12L14 is not recommended for welding due to its lead content. It is a health hazard
Interlloy believes the information provided is accurate and reliable. However no warranty of accuracy, completeness or
reliability is given, nor will any responsibility be taken for errors or omissions.