1
Scope
This standard defines requirements for corrosion protection of black paint coatings on metal
surfaces (code letter x in Volkswagen standard VW 137 50), e.g., for body parts. It does not apply
to paint coatings on zinc-coated metal surfaces (see TL 227), to decorative protective varnishes
(see TL 218) or to paint coatings on chassis parts that may form cavities (see TL 262).
2
Designation
Requirements
3.1
Protection types
Form FE 41 - 01.03
Protection type
Characteristic
Ofl-x010
Ofl-x130, Ofl-x330
Ofl-x630
Fachverantwortung/Responsibility
K-QS-32
Koeppen
Laudien
Wiesner
Tel: +49-5361-9-29064
Sobanski
Confidential. All rights reserved. No part of this document may be transmitted or reproduced without the prior written permission of a Standards Department of the Volkswagen Group.
Parties to a contract can only obtain this standard via the responsible procurement department.
VOLKSWAGEN AG
Norm vor Anwendung auf Aktualitt prfen / Check standard for current issue prior to usage.
Klass.-Nr. 50 23 4
Page 2
TL 260: 2004-05
Protection type
Characteristic
Ofl-x631
Ofl-x634
Zinc phosphated, heavy coat cathodic dip paint or cathodic dip paint
+ conventional dip paint (for very highly stressed parts, e.g., front
end, engine compartment)
3.2
General requirements
Base material
Protection types/appearance
See Table 1. The color is always black unless otherwise specified in the drawing.
3.5
Conditioning
If air-drying coating systems are used and/or no paint system baking process at elevated
temperature (> 60 C) will be carried out, the components shall be conditioned for 24 h at 60 C
before the tests. The specimens are then cooled to room temperature (18 to 28) C according to
DIN 50014.
3.6
See Table 2. For joining and contact surfaces, paint coat thickness limits may be necessary which
are to be specified in the drawing.
Table 2
Protection type
15 to 35, in cavities 12
Ofl-x631
40 to 60
Ofl-x634
35 to 60, in cavities 20
3.7
Test according to DIN 55996-1, method B with visual examination. Requirement: characteristic value 2.
Page 3
TL 260: 2004-05
3.9
Further characteristics
See Table 3.
Table 3
No.
1
1.1
1.1.1
Property
Ofl-x100
Ofl-x130
Ofl-x300
Ofl-x330
Corrosion behavior 1)
After aging in salt spray fog according to DIN 50021-SS
no blisters, no base
48 h without
metal corrosion
scribe mark 2)
no blisters, no base
1.1.2 96 h without
metal corrosion
scribe mark 2)
1.1.3 240 h with scribe
mark 2)
-
1.2
After corrosion cycle test according to Test Specification PV 1210
1.2.1 5 cycles
1.2.2 30 cycles with
scribe mark 2)
1.2.3 60 cycles with
scribe mark 2)
1.3
After aging in moisture condensate constant climate DIN 50017-KK
no blisters, no base
1.3.1 72 h 3)
metal corrosion, the
requirement according
to Section 3.7 must be
fulfilled
no blisters, no base
1.3.2 144 h 3)
metal corrosion, the
requirement according
to Section 3.7 must be
fulfilled
1.3.3 240 h 3)
-
Ofl-x600
Ofl-x630
Ofl-x631
Ofl-x634
no blisters,
no base
metal
corrosion,
adhesion loss
D 2.5 mm
Page 4
TL 260: 2004-05
Referenced standards*)
PV 1210
TL 766
TL 774
TL 521 07
TL 521 46
VW 011 55
VW 137 50
VW 911 01
VDA 621-412
DIN 50014
DIN 50017
DIN 50021
DIN 55996-1
Paints and Varnishes; Stone Chip Resistance Test for Coatings; Part 1: