Korethan Topcoat UT6585 (Two-Component) : Physical Properties

Korethan Topcoat
UT6585 (Two-Component)
Product
Description
A two-component, acryl polyurethane resin based finish coat with excellent weather resistance and
color retention. It also has good resistance to chemicals, solvents, seawater, so it provides long lifetime
of exposed parts.
Recommended Use
As a finish coat for use on steel or concrete structure under severe chemical or weathering corrosion
condition at chemical processing, petrochemical and similar industries such as marine tank, waste
treatment equipment.
Physical Properties
Finish and Color
High gloss. White (1000), Grey (1128), Black (1999)

* For more available color, consult with KCCs business department.
Drying Time
5 /41
20 /68
30 /86
Set to touch
7h
2h
1h
Dry through
48 h
24 h
18 h
Substrate temperature
* The actual drying time is subject to the film thickness, ventilation, humidity etc., and drying time under other temperature
conditions should be checked and informed by KCC.
Solids by Volume
Approx. 55 % (Determined by ISO 3233)
Theoretical
Spreading Rate
11.0 /L in 50 dry film thickness on a smooth surface.
Specific Gravity
Approx. 1.2 ~ 1.4 for Mixture of Base and Curing agent.
Flash Point
Base (UT6585 PTA)

: 29 /84 (Closed cup)
Curing Agent (UT6585 PTB) : 38 /100 (Closed cup)
Application Details
Surface
Preparation
Remove any oil, grease, dirt and any other contaminants from the surface before painting by proper
method such as solvent cleaning and fresh water washing, etc.
Application
Conditions
The surface should be cleaned and dried completely. Do not apply when relative humidity is above
85 %. The surface temperature should be at least 2.7 (5 ) above dew point to prevent
condensation. In confined spaces, provide adequate ventilation during application and drying.
Mixing
Base (UT6585 PTA) : Curing Agent (UT6585 PTB) = 9 : 1 (by volume)

Mix thoroughly together prior to application in the proportions with power agitator as delivered
Preceding Coat
Korepox EH2350, Korepox EH2351, Korethan H.B. UH279, or according to specification
Pot Life
4 h at 20 /68
Thinning
Thinner No. TH0373

Do not dilute each components separately.
Disclaimer : The information in this data sheet is believed to the best of our knowledge based on laboratory test and practical experience.
However, there are many factors affecting the performance of product and the product quality itself, so we are not able to guarantee
without the confirmation of the purpose of using the product from us in writing. We reserve the right to change the data without notice and
you should check that this data sheet is current prior to using the product.
KCC Corporation
Korethan Topcoat UT6585 (Two-Component)

Application
Method
Spray (Airless or Air), Roller or Brush application.

For airless spray application ;
Nozzle orifice
: 381 ~ 533 (0.015 ~ 0.021)
Output pressure
: 15.2 MPa
Fan
: 40 ~ 60
(Airless spray data are indicative and subject to adjustment)
Typical
Film Thickness
40 ~ 50 dry.
Depending on the purpose and the area of use, different film thickness may be applied.
Recoating Interval
At 20 / 68 , Minimum
Maximum
: 18 h
: Free
Before overcoating, remove the oil, salts, chalking materials and any other contaminants on aged
coating film completely by proper cleaning method such as solvent cleaning and/or fresh water
washing.
Shelf Life
12 months
Heat Resistance
Continuous
Non-continuous
Chemical
Resistance
Splash & Spillage
Fumes
Standard
Unit
Packing
: 93 /200 (Non-immersion service)

: 121 /250 (Non-immersion service)
Acids
Alkalis
Solvents
Salts
Water
Good
Good
Fair
Excellent
Excellent
Excellent
Excellent
Good
Excellent
Excellent
16 L (UT6585 PTA : 14.4 L, UT6585 PTB : 1.6 L)
Remarks
Do not store at temperature below 5 /41 or above 40 /104 .

Protect skin and eyes from direct contact with liquid paint, and avoid prolonged breathing of solvent
vapors.
Use with adequate ventilation.
Respiratory protection is recommended when applying this product in confined spaces or stagnant air.
Issued
April 2008
Disclaimer : The information in this data sheet is believed to the best of our knowledge based on laboratory test and practical experience.
However, there are many factors affecting the performance of product and the product quality itself, so we are not able to guarantee
without the confirmation of the purpose of using the product from us in writing. We reserve the right to change the data without notice and
you should check that this data sheet is current prior to using the product.
KCC Corporation

Korethan Topcoat UT6585 (Two-Component) : Physical Properties

Uploaded by

Document Information

Original Description:

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Korethan Topcoat UT6585 (Two-Component) : Physical Properties

Uploaded by

Copyright:

Available Formats

Korethan Topcoat

High gloss. White (1000), Grey (1128), Black (1999)

Approx. 55 % (Determined by ISO 3233)

11.0 /L in 50 dry film thickness on a smooth surface.

Approx. 1.2 ~ 1.4 for Mixture of Base and Curing agent.

Base (UT6585 PTA)

Base (UT6585 PTA) : Curing Agent (UT6585 PTB) = 9 : 1 (by volume)

Korepox EH2350, Korepox EH2351, Korethan H.B. UH279, or according to specification

Thinner No. TH0373

Korethan Topcoat UT6585 (Two-Component)

Spray (Airless or Air), Roller or Brush application.

: 93 /200 (Non-immersion service)

16 L (UT6585 PTA : 14.4 L, UT6585 PTB : 1.6 L)

Do not store at temperature below 5 /41 or above 40 /104 .

You might also like