Interzinc 52
Interzinc 52
Epoxy Zinc-Rich
PRODUCT
DESCRIPTION
A two component, metallic zinc rich epoxy primer which complies with the composition and
performance requirements of SSPC Paint 20.
INTENDED USES
As a high performance primer to give maximum protection as part of any anti-corrosive coating
system for aggressive environments including those found on offshore structures, petrochemical
facilities, pulp and paper plants, bridges and power plants.
Interzinc 52 has been designed to provide excellent corrosion resistance in both maintenance and
new construction situations.
PRACTICAL
INFORMATION FOR
INTERZINC 52
Colour
Gloss Level
Matt
Volume Solids
59%
Typical Thickness
Theoretical Coverage
Practical Coverage
Method of Application
Drying Time
Touch Dry
Hard Dry
Minimum
Maximum
5C (41F)
2 hours
10 hours
8 hours
Extended
15C (59F)
90 minutes
6 hours
4 hours
Extended
25C (77F)
75 minutes
4 hours
3 hours
Extended
40C (104F)
45 minutes
2 hours
2 hours
Extended
Flash Point
Product Weight
EPA Method 24
EU Solvent Emissions Directive
(Council Directive 1999/13/EC)
See Product Characteristics section for further details
VOC
Protective Coatings
Page 1 of 4
Issue Date:07/07/2009
Ref:2561
Worldwide Product
Interzinc 52
Epoxy Zinc-Rich
SURFACE
PREPARATION
All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces
should be assessed and treated in accordance with ISO 8504:2000.
Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.
Abrasive Blast Cleaning
Abrasive blast clean to Sa2 (ISO 8501-1:2007) or SSPC-SP6. If oxidation has occurred between blasting and
application of Interzinc 52, the surface should be reblasted to the specified visual standard.
Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate
manner.
A surface profile of 40-75 microns (1.6-3.0 mils) is recommended.
Shop Primed Steelwork
Interzinc 52 is suitable for application to unweathered steelwork freshly coated with zinc silicate shop primers.
If the zinc shop primer shows extensive or widely scattered breakdown, or excessive zinc corrosion products,
overall sweep blasting will be necessary. Other types of shop primer are not suitable for overcoating and will
require complete removal by abrasive blast cleaning.
Weld seams and damaged areas should be cleaned to a minimum St3 (ISO 8501-1:2007) or SSPC-SP3.
Optimum performance will be achieved with blasting to Sa2 (ISO 8501-1:2007) or SSPC-SP6; where this is
not practical, hand preparation to SSPC-SP11 is recommended.
APPLICATION
Mixing
Material is supplied in two containers as a unit. Always mix a complete unit in the
proportions supplied. Once the unit has been mixed it must be used within the
working pot life specified.
(1)
Agitate Base (Part A) with a power agitator.
(2)
Combine entire contents of Curing Agent (Part B) with Base
(Part A) and mix thoroughly with power agitator.
Mix Ratio
5C (41F)
24 hours
Airless Spray
Recommended
Air Spray
(Pressure Pot)
Recommended
Gun
DeVilbiss MBC or JGA
Air Cap 704 or 765
Fluid Tip E
Brush
Roller
Not recommended
Thinner
International GTA220
(or International GTA415)
Cleaner
Work Stoppages
Do not allow material to remain in hoses, gun or spray equipment. Thoroughly flush
all equipment with International GTA822. Once units of paint have been mixed they
should not be resealed and it is advised that after prolonged stoppages work
recommences with freshly mixed units.
Clean Up
Clean all equipment immediately after use with International GTA822. It is good
working practice to periodically flush out spray equipment during the course of the
working day. Frequency of cleaning will depend upon amount sprayed, temperature
and elapsed time, including any delays.
15C (59F)
12 hours
25C (77F)
5 hours
40C (104F)
2 hours
All surplus materials and empty containers should be disposed of in accordance with
approrpriate regional regulations/legislation.
Page 2 of 4
Interzinc 52
Epoxy Zinc-Rich
PRODUCT
CHARACTERISTICS
In order to ensure good anti-corrosive performance, it is important to achieve a minimum dry film
thickness of Interzinc 52 of 40 microns (1.5 mils). To achieve a uniform, coalesced, closed film at this dry
film thickness, it will be necessary to thin Interzinc 52 10% with International thinners. The film thickness
of Interzinc 52 applied must be compatible with the blast profile achieved during surface preparation. Low
film thickness should not be applied over coarse blast profiles.
Care should be excercised to avoid the application of dry film thicknesses in excess of 150 microns (6
mils).
Care should be exercised to avoid over-application, which may result in cohesive film failure with
subsequent high builds, and to avoid dry spray which can lead to pinholing of subsequent coats. Overapplication will also result in slower curing and extended handling and overcoating times.
Over-application of Interzinc 52 will extend both the minimum overcoating periods and handling times,
and may be detrimental to long term overcoating properties.
When Interzinc 52 is allowed to weather before topcoating ensure all zinc salts are removed prior to paint
application and only topcoat with recommended materials.
Surface temperature must always be a minimum of 3C (5F) above dew point.
Interzinc 52 is not normally recommended for underwater use. Please consult International Protective
Coatings for details in this situation.
Interzinc 52 is suitable for the localised repair of damaged inorganic zinc primer - consult International
Protective Coatings for specific advice.
Low Temperature Curing
An alternative curing agent is available for applications at temperatures less than 5C (41F). When using
this alternative curing agent it should be noted that the VOC will increase to 360 g/l (3 lb/gal).
Interzinc 52 is capable of curing at temperatures below 0C (32F). However, this product should not be
applied at temperatures below 0C (32F) where there is a possibility of ice formation on the substrate.
Temperature
Touch Dry
Hard Dry
-5C (23F)
0C (32F)
5C (41F)
6 hours
3 hours
2 hours
32 hours
16 hours
6 hours
36 hours
18 hours
6 hours
Extended*
Extended*
Extended*
Touch dry times shown above are actual drying times due to chemical cure, rather than physical set due
to solidification of the coating film at temperatures below 0C (32F)
* See International Protective Coatings Definitions & Abbreviations
For further details regarding cure times and overcoatability, please contact International Protective
Coatings.
This product has the following specification approvals:
Steel Structures Painting Council - SSPC Paint 20
On consultation with International Protective Coatings this product is compatible with alternative
application methods such as flow coating.
Note: VOC values are typical and are provided for guidance purpose only. These may be subject to
variation depending on factors such as differences in colour and normal manufacturing tolerances.
Low molecular weight reactive additives, which will form part of the film during normal ambient cure
conditions, will also affect VOC values determined using EPA Method 24.
SYSTEMS
COMPATIBILITY
Interzinc 52 is designed for application to correctly prepared steel. However, it is also possible to apply
over approved prefabrication primers. Further details of these can be obtained from International
Protective Coatings.
Recommended topcoats are:
Intercure 200
Intercure 420
Interfine 629HS
Intergard 251
Intergard 269
Intergard 475HS
Intergard 740
InterH2O 401
Interseal 670HS
Interthane 990
Interzone 1000
Interzone 505
Interzone 954
Page 3 of 4
Interzinc 52
Epoxy Zinc-Rich
D ADDITIONAL
et INFORMATION
ail
T
o
p
Further information regarding industry standards, terms and abbreviations used in this data sheet
can be found in the following documents available at www.international-pc.com:
Definitions & Abbreviations
Surface Preparation
Paint Application
Theoretical & Practical Coverage
Individual copies of these information sections are available upon request.
SAFETY
PRECAUTIONS
This product is intended for use only by professional applicators in industrial situations in
accordance with the advice given on this sheet, the Material Safety Data Sheet and the
container(s), and should not be used without reference to the Material Safety Data Sheet (MSDS)
which International Protective Coatings has provided to its customers.
All work involving the application and use of this product should be performed in compliance with all
relevant national, Health, Safety & Environmental standards and regulations.
In the event welding or flame cutting is performed on metal coated with this product, dust and
fumes will be emitted which will require the use of appropriate personal protective equipment and
adequate local exhaust ventilation.
If in doubt regarding the suitability of use of this product, consult International Protective Coatings
for further advice.
Rect Top
Unit Size
PACK SIZE
Part A
Vol
Part B
Pack
Vol
Pack
10 litre
8 litre
10 litre
2 litre
2.5 litre
3 US gal
2.4 US gal
3.5 US gal
0.6 US gal
1 US gal
SHIPPING WEIGHT
Unit Size
Part A
Part B
10 litre
24.5 kg
2.1 kg
3 US gal
63.3 lb
5.3 lb
Shelf Life
STORAGE
Rect
Bottom
Important Note
The information in this data sheet is not intended to be exhaustive; any person using the product for any purpose other than that specifically recommended in this data sheet without first
obtaining written confirmation from us as to the suitability of the product for the intended purpose does so at their own risk. All advice given or statements made about the product
(whether in this data sheet or otherwise) is correct to the best of our knowledge but we have no control over the quality or the condition of the substrate or the many factors affecting the
use and application of the product. Therefore, unless we specifically agree in writing to do so, we do not accept any liability at all for the performance of the product or for (subject to the
maximum extent permitted by law) any loss or damage arising out of the use of the product. We hereby disclaim any warranties or representations, express or implied, by operation of
law or otherwise, including, without limitation, any implied warranty of merchantability or fitness for a particular purpose. All products supplied and technical advice given are subject to
our Conditions of Sale. You should request a copy of this document and review it carefully. The information contained in this data sheet is liable to modification from time to time in the
light of experience and our policy of continuous development. It is the user's responsibility to check with their local International Paint representative that this data sheet is current prior to
using the product.
Issue date: 07/07/2009
Copyright AkzoNobel, 07/07/2009.
, International and all product names mentioned in this publication are trademarks of, or licensed to, AkzoNobel.