Foamed Concrete
Foamed Concrete
Note
Thats why I choose foamed concrete in my research theme,
because I used this material in my practice work in zarya
company(Faruk Holding) in Shry jwan project in(Shary jwan
apartments)
1
FOAMED CONCRETE
1)Foam concrete is a type of porous concrete. According
to its features and uses it is similar to aerated concrete. The
synonyms are:
1) Aerated concrete
2) Lightweight concrete
3) Porous concrete
Light weight concrete - or foamed concrete - is a
versatile material which consists primarily of a cement
based mortar mixed with at least 20% of volume air.
It possesses high flow ability, low self-weight, minimal
consumption of aggregate, controlled low strength and
excellent thermal insulation properties.
It can have a range of dry densities, typically from 400
kg/m3 to 1600 kg/m3 and a range of compressive
strengths, 1 MPa to 15 MPa .
2
FOAMED CONCRETE BLOCK
3
Foamed Concrete can be placed easily, by pumping if
necessary, and does not require compaction, vibrating or
levelling.
It has excellent resistance to water and frost, and
provides a high level of both sound and thermal
insulation.
History
Foamed concrete has a surprisingly long history and was
first patented in 1923, mainly for use as an insulation
material
The first comprehensive review on foamed concrete was
presented by Valore in 1954 and a detailed treatment by
Rudnai and Short and Kinniburgh in 1963, summarising
the composition, propertSignificant improvements over
the past 20 years in production equipment and better
quality surfactants (foaming agents) has enabled the use
of foamed concrete on a larger scale.
Significant improvements over the past 20 years in
production equipment and better quality surfactants
(foaming agents) has enabled the use of foamed
concrete on a larger scale.
4
Constituent materials
1) Constituents of base mix
2) Foam
1)Constituents of base mix
Ordinary Portland cement, Rapid hardening Portland
cement and , high alumina and Calcium
Sulfoaluminate have been used for reducing the setting
time and to improve the early strength of foame concrete.
Fly ash and ground granulated blast furnace slag have
been used in the range of 3070% and 1050%,
respectively and as cement replacement to reduce the
cost, enhance consistence of mix and to reduce heat of
hydration while contributing towards long term strength.
Silica fume up to 10% by mass of cement has been added
to intensify the strength of cement . Alternate fine
aggregates, viz., fly ash and lime, chalk and crushed
concrete , recycled glass, foundry sand and were used
either to reduce the density of foam concrete .
5
The water requirement for a mix depends upon the
composition and use of admixtures and is governed by the
consistency and stability of the mix .
2)Foam
Foam concrete is produced either by :-
1) pre-foaming method
2) mixed foaming method
Pre-foaming method comprises of producing base mix and
stable preformed aqueous foam separately and then
thoroughly blending foam into the base mix.
In mixed foaming, the surface active agent is mixed along
with base mix ingredients and during the process of mixing,
foam is produced resulting in cellular structure in concrete .
6
6) admixtures.
7
plant, according to the mix design, by either the DRY or
WET method.
8
Making Foamed Concrete
9
It is important to make the slurry first, before making the
foam. Ideally the foam should be generated and delivered
directly into the mixer of the ready mix truck that contains
the slurry. The mixer should be rotated at approximately
10 revolutions per minute. All of the foam should be
allowed to blend into the slurry.
10
11
Properties of foam concrete
Fresh state properties
1) Consistency
2) Stability
Physical properties
1) Drying shrinkage
2) Air-void systems
12
3) Density
Mechanical properties
1) Compressive strength
2) Flexural and tensile strengths
3) Modulus of elasticity
13
Fresh state properties
As foam concrete cannot be subjected to compaction or
vibration the foam concrete should have flow ability and
self-compact ability. These two properties are evaluated
in terms of consistency and stability of foam concrete.
Consistency
Flow time using marsh cone and flow cone spread tests
are adopted to assess the consistency of foam concrete.
14
The consistency reduces with an increase in volume of
foam in the mix, which may be attributed to the
(i) reduced self-weight and greater cohesion resulting
from higher air content .
Stability
The stability of foam concrete is the consistency at which
the density ratio is nearly one (the measured fresh
density/design density), without any segregation and
bleeding .
15
Physical properties
Drying shrinkage
Foam concrete possesses high drying shrinkage due to the
absence of aggregates, i.e., up to 10 times greater than
those observed on normal weight concrete.
Autoclaving is reported to reduce the drying shrinkage
significantly by 1250% of that of moist-cured concrete
due to a change in mineralogical compositions.
The shrinkage of foam concrete reduces with density which
is attributed to the lower paste content affecting the
shrinkage in low-density mixes.
16
Well-Bonded Body
Foam concrete forms a rigid, well-bonded body after
hydrating. It is effectively a free-standing (monolithic)
structure and once hardened, does not impose lateral loads
on adjacent structures.
Self Levelling
Foam concrete is naturally self-levelling and self-
compacting, filling the smallest voids, cavities and seams
within the pouring area.
In excavations with poor soils that cannot be easily
compacted, foam concrete forms a 100% compacted
foundation over the soft sub-soil. Compaction of
conventional, granular backfill against retaining structures
or deep foundations can cause damage or movement to
17
the adjacent structure. In these situations, foam concrete
with its reduced lateral loading is a safe solution.
Compressive strength
The compressive strength decreases exponentially with a
reduction in density of foam concrete .
The parameters affecting the strength of foam concrete
are cementsand and watercement ratios, curing regime,
type and particle size distribution of sand and type of
foaming agent used.
18
For dry density of foam concrete between 500 and
1000 kg/m3, the compressive strength decreases with an
increase in void diameter.
For densities higher than 1000 kg/m3, as the air-voids are
far apart to have an influence on the compressive strength,
the composition of the paste determines the compressive
strength .
Flexural and tensile strengths
Splitting tensile strengths of foam concrete are lower than
those of equivalent normal weight and lightweight
aggregate concrete with higher values observed for mixes
with sand than those with fly ash.
Use of Polypropylene fibers has been reported to
enhance the performance with respect to tensile and
flexural strength of foam concrete.
19
The oxygen and water vapour permeability of foam
concrete have been observed to increase with increasing
porosity and fly ash content.
Sorptivity : The moisture transport phenomenon in
porous materials has been defined by an easily
measurable property called sorptivity (absorbing and
transmitting water by capillarity), which is based on
unsaturated flow theory .
Sorptivity of foam concrete is reported to be lower than
the corresponding base mix and the values reduce with an
increase in foam volume.
20
A study on accelerated carbonation of foam concrete by
Jones and McCarthy indicate that lower density concrete
appears to carbonate at a relatively higher rate.
Functional characteristics
Fire resistance
Thermal insulation
Thermal insulation
Foam concrete has excellent thermal insulating properties
due to its cellular microstructure.
The thermal conductivity of foam concrete of density
1000 kg/m3 is reported to be one-sixth the value of typical
cementsand morter.
Fire resistance
Foam concrete is extremely fire resistant and well suited
to applications where fire is a risk.
Test have shown that in addition to prolonged fire
protection, the application of intense heat, such as a high
energy flame held close to the surface, does not cause the
concrete to spall or explode as is the case with normal
dense weight concrete.
21
Advantages of Foamed Concrete
1) Does not settle, hence requires no compaction.
2) Lightweight - does not impose large loadings.
3) Free flowing - spreads to fill all voids.
4) Excellent load spreading characteristics.
5) Once placed requires no maintenance.
Does not impose significant lateral loads.
Reliable quality control - batches are easy to reproduce .
Resistant to freeze-thaw cycle (1000 cycles of -180c
to+200C).
Low water absorption over time.
23