Wire rope forms an important part of many machines and structures. It is comprised of continuous wire strands wound
around a central core. There are many kinds of wire rope designed for different applications. Most of them are steel wires
made into strands wound with each other. The core can be made of steel, rope or even plastics.
Wire ropes (cables) are identified by several parameters including size, grade of steel used, whether or not it is preformed,
by its lay, the number of strands and the number of wires in each strand.
A typical strand and wire designation is 6x19. This denotes a rope made up of six strands with 19 wires in each strand.
Different strand sizes and arrangements allow for varying degrees of rope flexibility and resistance to crushing and
abrasion. Small wires are better suited to being bent sharply over small sheaves (pulleys). Large outer wires are preferred
when the cable will be rubbed or dragged through abrasives.
There are three types of cores. An independent wire rope core (IWRC) is normally a 6x7 wire rope with a 1x7 wire strand
core resulting in a 7x7 wire rope. IWRCs have a higher tensile and bending breaking strength than a fiber core rope and a
high resistance to crushing and deformation.
http://www.machinerylubrication.com/Articles/Print/372 1/5
10/7/2017 Lubrication Basics for Wire Ropes
A wire strand core (WSC) rope has a single wire strand as its core instead of a multistrand wire rope core. WSC ropes are
high strength and are mostly used as static or standing ropes.
Wire ropes also have fiber cores. Fiber core ropes were traditionally made with sisal rope, but may also use plastic
materials. The fiber core ropes have less strength than steel core ropes. Fiber core ropes are quite flexible and are used
in many overhead crane applications.
The lay of a wire rope is the direction that the wire strands and the strands in the cable twist. There are four common lays:
right lay, left lay, regular lay and lang lay. In a right lay rope the strands twist to the right as it winds away from the
observer. A left lay twists to the left. A regular lay rope has the wires in the strands twisted in the opposite direction from
the strands of the cable. In a lang lay rope, the twist of the strands and the wires in the strands are both twisted the same
way. Lang lay ropes are said to have better fatigue resistance due to the flatter exposure of the wires.
Wire ropes are made mostly from high carbon steel for strength, versatility, resilience and availability and for cost
consideration. Wire ropes can be uncoated or galvanized. Several grades of steel are used and are described in Table 1.
Steel cable wire is stiff and springy. In nonpreformed rope construction, broken or cut wires will straighten and stick out of
the rope as a burr, posing a safety hazard. A preformed cable is made of wires that are shaped so that they lie naturally in
their position in the strand, preventing the wires from protruding and potentially causing injury. Preformed wire ropes also
have better fatigue resistance than nonpreformed ropes and are ideal for working over small sheaves and around sharp
angles.
2. To provide corrosion protection and lubrication in the core and inside wires and on the exterior surfaces.
There are two types of wire rope lubricants, penetrating and coating. Penetrating lubricants contain a petroleum solvent
that carries the lubricant into the core of the wire rope then evaporates, leaving behind a heavy lubricating film to protect
and lubricate each strand (Figure 2). Coating lubricants penetrate slightly, sealing the outside of the cable from moisture
and reducing wear and fretting corrosion from contact with external bodies.
http://www.machinerylubrication.com/Articles/Print/372 2/5
10/7/2017 Lubrication Basics for Wire Ropes
Both types of wire rope lubricants are used. But because most wire ropes fail from the inside, it is important to make sure
that the center core receives sufficient lubricant. A combination approach in which a penetrating lubricant is used to
saturate the core, followed with a coating to seal and protect the outer surface, is recommended. Wire rope lubricants can
be petrolatum, asphaltic, grease, petroleum oils or vegetable oil-based (Figure 3).
Petrolatum compounds, with the proper additives, provide excellent corrosion and water resistance. In addition,
petrolatum compounds are translucent, allowing the technician to perform visible inspection. Petrolatum lubricants can
drip off at higher temperatures but maintain their consistency well under cold temperature conditions.
Asphaltic compounds generally dry to a very dark hardened surface, which makes inspection difficult. They adhere well for
extended long-term storage but will crack and become brittle in cold climates. Asphaltics are the coating type.
Various types of greases are used for wire rope lubrication. These are the coating types that penetrate partially but usually
do not saturate the rope core. Common grease thickeners include sodium, lithium, lithium complex and aluminum complex
soaps. Greases used for this application generally have a soft semifluid consistency. They coat and achieve partial
penetration if applied with pressure lubricators.
Petroleum and vegetable oils penetrate best and are the easiest to apply because proper additive design of these
penetrating types gives them excellent wear and corrosion resistance. The fluid property of oil type lubricants helps to
wash the rope to remove abrasive external contaminants.
Wire ropes are lubricated during the manufacturing process. If the rope has a fiber core center, the fiber will be lubricated
with a mineral oil or petrolatum type lubricant. The core will absorb the lubricant and function as a reservoir for prolonged
lubrication while in service.
If the rope has a steel core, the lubricant (both oil and grease type) is pumped in a stream just ahead of the die that twists
the wires into a strand. This allows complete coverage of all wires.
After the cable is put into service, relubrication is required due to loss of the original lubricant from loading, bending and
stretching of the cable. The fiber core cables dry out over time due to heat from evaporation, and often absorb moisture.
Field relubrication is necessary to minimize corrosion, protect and preserve the rope core and wires, and thus extend the
service life of the wire rope.
If a cable is dirty or has accumulated layers of hardened lubricant or other contaminants, it must be cleaned with a wire
brush and petroleum solvent, compressed air or steam cleaner before relubrication. The wire rope must then be dried and
lubricated immediately to prevent rusting. Field lubricants can be applied by spray, brush, dip, drip or pressure boot.
Lubricants are best applied at a drum or sheave where the rope strands have a tendency to separate slightly due to
bending to facilitate maximum penetration to the core. If a pressure boot application is used, the lubricant is applied to the
http://www.machinerylubrication.com/Articles/Print/372 3/5
10/7/2017 Lubrication Basics for Wire Ropes
rope under slight tension in a straight condition. Excessive lubricant application should be avoided to prevent safety
hazards.
Corrosion can cause shortened rope life due to metal loss, pitting and stress risers from pitting. If a machine is to be shut
down for an extended period, the cables should be removed, cleaned, lubricated and properly stored. In service, corrosion
and oxidation are caused by fumes, acids, salt brines, sulfur, gases, salt air, humidity and are accelerated by elevated
temperatures. Proper and adequate lubricant application in the field can reduce corrosive attack of the cable.
Abrasive wear occurs on the inside and outside of wire ropes. Individual strands inside the rope move and rub against one
another during normal operation, creating internal two-body abrasive wear. The outside of the cable accumulates dirt and
contaminants from sheaves and drums. This causes three-body abrasive wear, which erodes the outer wires and strands.
Abrasive wear usually reduces rope diameter and can result in core failure and internal wire breakage. Penetrating wire
rope lubricants reduce abrasive wear inside the rope and also wash off the external surfaces to remove contaminants and
dirt.
Lubrication Engineers, Inc. has found through years of field experience, that longer wire rope life can be obtained through
the use of penetrating lubricants, either alone or when used in conjunction with a coating lubricant. Practical experience at
a South African mine suggests that life cycles may be doubled with this approach. At one mine site, the replacement rate
for four 44-mm ropes was extended from an average 18.5 months to 43 months. At another mine, life cycles of four 43-
mm x 2073 meter ropes were extended from an average 8 months to 12 months.
In another study involving 5-ton and 10-ton overhead cranes in the United States that used 3/8-inch and 5/8-inch diameter
ropes, the average life of the ropes was doubled. The authors attribute this increased performance to the ability of the
penetrating lubricant to displace water and contaminants while replacing them with oil, which reduces the wear and
corrosion occurring throughout the rope. A good spray with penetrating wire rope lubricant effectively acts as an oil
change for wire ropes.
In these examples, the savings in wire rope replacement costs (downtime, labor and capital costs) were substantial and
dwarfed the cost of the lubricants. Companies who have realized the importance of proper wire rope lubrication have
gained a huge advantage over those who purchase the lowest priced lubricant, or no lubricant at all, while replacing ropes
on a much more frequent basis.
References
1. American Iron and Steel Institute. (1985). Wire Rope Users Manual, Second Edition. p. 5-17, 67-68.
http://www.machinerylubrication.com/Articles/Print/372 4/5
10/7/2017 Lubrication Basics for Wire Ropes
http://www.machinerylubrication.com/Articles/Print/372 5/5