1 s2.0 S0013468605008200 Main PDF
1 s2.0 S0013468605008200 Main PDF
Received 23 June 2004; received in revised form 22 October 2004; accepted 25 February 2005
Available online 24 August 2005
Abstract
The electrochemical behavior of Ti6Al4V and Ti6Al7Nb alloys, commonly used implant materials, particularly for orthopaedic and
osteosynthesis applications, was investigated together with that of Ti13Nb13Zr alloy in Hanks solution at 37 C. The aim of present study
was to evaluate their corrosion resistance in an artificial physiological solution. This evaluation was carried out through the analysis of the
corrosion potential variation with time, potentiodynamic polarization curves, and electrochemical impedance spectroscopy (EIS) tests. Very
low current densities were obtained (order of nA/cm2 ) from the polarization curves, indicating a typical passive behavior for all investigated
alloys. The EIS results exhibited capacitive behavior (high corrosion resistance) with phase angles close to 90 and high impedance values
(order of 106 cm2 ) at low and medium frequencies, which are indicative of the formation of a highly stable film on these alloys in the test
solution. The obtained EIS spectra indicated two relaxation time constants and their interpretation in terms of an equivalent circuit with
the circuit elements representing the electrochemical properties of a two-layer oxide, composed of a porous outer layer and a dense inner
layer, was in good agreement. The electrochemical impedance spectroscopy (EIS) technique, therefore, was able to provide reliable data for
determination of the passive film structure.
2005 Elsevier Ltd. All rights reserved.
0013-4686/$ see front matter 2005 Elsevier Ltd. All rights reserved.
doi:10.1016/j.electacta.2005.02.121
1816 S.L.d. Assis et al. / Electrochimica Acta 51 (2006) 18151819
Table 1
Chemical composition (wt.%) of Ti13Nb13Zr, Ti6Al4V and Ti6Al7Nb alloys
Alloy C H N O Fe Al S Hf V Ta Nb Zr Ti
Ti13Nb13Zr 0.035 0.011 0.004 0.078 0.085 0.001 0.055 13.18 13.49 Bal.
Ti6Al4V 0.024 0.005 0.006 0.18 0.17 6.0 4.1 Bal.
Ti6Al7Nb 0.08 0.009 0.05 0.20 0,25 6.50 0.50 7.50 Bal.
S.L.d. Assis et al. / Electrochimica Acta 51 (2006) 18151819 1817
Table 3
Average values of Ecorr and icorr determined for the three titanium alloys
from the polarization curves obtained in naturally aerated Hanks solution
at 37 C
Alloy Ecorr (mV (SCE)) Icorr (nA/cm2 )
Ti13Nb13Zr 374 18 28 16
Ti6Al4V 407 28 19 0.9
Ti6Al7Nb 368 8 53 18
expected that in terms of corrosion resistance and osseointe- densities were obtained for the three titanium alloys tested
gration ability the Ti13Nb13Zr implants should have the in Hanks solution showing that they are passive in this elec-
same performance as those made with the other two alloys. trolyte. The EIS results indicated that the film formed on the
The corrosion potential curves shown in Fig. 1 indicate Ti alloys is composed of a bi-layered oxide consisting of an
that the potential of the Ti alloys in the Hanks solution at inner barrier layer associated to high impedance and respon-
37 C increases rapidly with time and this initial increase sible for corrosion protection, and an outer porous layer, of
seems to be related to the thickening of the oxide film improv- lower impedance, which apparently facilitates the osseointe-
ing its corrosion protection ability [19]. gration.
The very low current densities (order of 108 A/cm2 )
obtained previous to the establishment of a typical passive
behavior above 500 mV (SCE), could suggest a direct tran- References
sition from the immunity region to the passive region [19].
The increase in current density with potential could occur [1] C. Sittig, M. Textor, N.D. Spencer, M. Wieland, P.-H. Vallotton, J.
if the increase in potential is not accompanied by a corre- Mater. Sci : Mater. Med. 10 (1999) 35.
[2] K. Wang, Mater. Sci. Eng. A213 (1996) 134.
sponding thickening of the oxide film, or could be due to [3] M. Niinomi, D. Kuroda, K. Fukunaga, M. Morinaga, Y. Kato, T.
the oxidation of TiO or Ti2 O3 to TiO2 [20]. Nevertheless, it Yashiro, A. Suzuki, Mater. Sci. Eng. A263 (1999) 193.
appears that the film formed above 500 mV (SCE) is differ- [4] K.J. Bundy, in: R. Baboian (Ed.), Corrosion Tests and Standards:
ent from that formed below this potential. Its higher ipp value Application and Interpretation, ASTM, Philadelphia, PA, 1995, p.
411.
indicates that it is a more defective oxide. It has been previ-
[5] T. Akahori, M. Niinomi, Mater. Sci. Eng. A243 (1998) 237.
ously proposed that the increase in current density observed [6] D. Kuroda, M. Niinomi, M. Morinaga, Y. Kato, T. Yashiro, Mater.
at potentials above 1200 mV (SCE) could be related to the Sci. Eng. A243 (1998) 244.
formation of Ti compounds such as NaTiPO4 [21]. [7] M.A. Khan, R.L. Williams, D.F. Williams, Biomaterials 20 (1999)
High impedance values (order of 106 cm2 ) were 631.
[8] M.A. Khan, R.L. Williams, D.F. Williams, Biomaterials 17 (1996)
obtained from medium to low and frequencies for all Ti alloys
2117.
suggesting, high corrosion resistance in the electrolyte used. [9] T.-I. Kim, J.-H. Han, I.-S. Lee, K.-H. Lee, M.-C. Shin, B.-B. Choi,
This result supports the passive behavior of the alloys, indi- Bio-Med. Mater. Eng. 7 (1997) 253.
cated by the polarization curves and the corrosion potential [10] Y. Okazaki, Y. Ito, K. Kyo, T. Tateishi, Mater. Sci. Eng. A213 (1996)
variation with time curves. 138.
[11] S. Rao, Y. Okazaki, T. Tateishi, T. Ushida, Y. Ito, Mater. Sci. Eng.
The Bode diagrams showing phase angles approaching
C 4 (1997) 311.
90 indicate a highly capacitive behavior typical of a com- [12] S.G. Schneider, Ph. D. thesis, University of Sao Paulo, Instituto de
pact passive film [22]. According to the proposed model, the Pesquisas Energeticas e Nucleares, Brazil (2001).
passive film consists of two layers, the inner barrier layer, [13] I. Ramires, A.C. Guastaldi, Quim. Nova 25 (2002) 25.
whose resistance values, Rb , are significantly larger than the [14] M.R. Souto, M.M. Laz, R.L. Reis, Biomaterials 24 (2003)
4213.
values associated to the outer porous layer, Rp . as Table 4
[15] R. Venugopalan, J.J. Wiemer, M.A. George, L.C. Lucas, Biomaterials
shows. These results indicate that the protection provided by 21 (2000) 1669.
the passive layer is predominantly due to the barrier layer. It [16] I.C. Lavos-Valereto, S. Wolynec, I. Ramires, A.C. Guastaldi, I. Costa,
has been previously proposed that while the corrosion resis- J. Mater. Sci. : Mater. Med. (2004) 55.
tance of the Ti6Al7Nb alloy is ascribed to the barrier layer, [17] F. Mansfeld, M.W. Kendig, J. Electrochem. Soc. 135 (1988) 828.
[18] J. Pan, D. Thierry, C. Leygraf, Electrochem. Acta 41 (1996)
the ability to osseointegrate should be attributed to the pres-
1143.
ence of the porous layer [16]. [19] I.C. Lavos-Valereto, I. Costa, S. Wolynec, J. Biomed. Mater. Res.
63 (2002) 664.
[20] S.Y. Yu, J.R. Scully, Corrosion 53 (1997) 965.
[21] D.M. Considine, in: DM. Considine (Ed.), Van Nostrands Scien-
5. Conclusions
tific Encyclopedia, fifth ed., Van Nostrand, New York, 1976, pp.
22102212.
The electrochemical techniques used in this investigation [22] J.E.G. Gonzalez, J.C. Mirza-Rosca, J. Electroanal. Chem 471 (1999)
led to the following conclusions. Very low corrosion current 109.