CHAPTER 2
The use of fibers in brittle matrix materials has a long history going back at least 3500
years when sun-baked bricks reinforced with straw were used to build the 57 meter high hill of
Aqar Quf near Baghdad. In more recent times, asbestos fibers have been used to reinforce
cement products for about 100 years, cellulose fibers for at least 50 years, and steels,
polypropylene and glass fibers have been used for the same purpose for the past 30 years. The
main objectives of the modern engineer in attempting to modify the properties of concrete by the
inclusion of fibers are as follows:
• To improve the rheology or plastic cracking characteristics o the material in the
fresh state or up to about 6 hours after casting
• To improve the tensile and flexural strength
• To improve the impact strength and toughness
• To control cracking and the mode of failure by means of post-cracking ductility
• To improve durability
10
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
demonstrated that the fiber content increases the density of concrete when 0.25% fiber is added,
but the density decreases when 0.50% fiber is added to the concrete. The study on palm oil fiber
shows that adding palm oil fiber to concrete increases the compressive and flexural strength of
concrete after 28 days. Even though adding fiber contributes to strength increase, but the strength
does not increase with the increasing fiber content (percentage). In other words, the increase in
strength is only upto certain amount of fiber content.
Labadan (2001), in his study entitled “Ultimate compressive and tensile strength of fiber-
reinforced concrete containing Coconut Fibers” tested a fiber reinforced concrete cylinder with
fiber lengths 3cm, 6cm, and 12cm in different percentages of fiber (0.25%, 0.50%, 1.0%) by
weight of plain concrete prepared in 18 batches. He included that a 0.25% fiber by weight of
plain concrete with a length of 6cm gave a good result in splitting tensile strength but no
significant results on compressive strength. He also concluded that the higher tensile strength
could be obtained by immersing the fibers in a cement solution for four hours before mixing
them with concrete.
According to Santha (1999), coconut fibers are good materials for soil erosion and
sedimentation control especially in environmentally-sensitive agricultural areas. This is due to
the low decomposition rate of coconut fibers. In his study coir rolls were used as a stabilization
of riverbanks. This is an innovative fabric-encapsulated technique in stabilization.
Previous studies and investigation of the use of natural fibers as reinforcement to cement
composites showed positive results. Coconut fibers use as reinforcement to cement composite
board satisfies ASTM specifications.
11
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
2.1.4. “Contribution of fibers to crack reduction of cement composite during the initial and
final setting period” by Balaguru (1994)
12
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
steel fibers three fiber length of 1.2, 2.0 and 2.4 inches were investigated at volume contents of
75 and 100 lbs/yd3. The non-metallic fibers were made of cellulose in pulp form (microfiber)
with lengths in the order of a few millimeters and microns. The matrix consisted of cement
mortar with various cement-sand ratios, coarse and light weight aggregates in the test methods,
the primary variables were specimen thickness and plane dimensions of test panels. Results
indicated that both steel and synthetic fibers make a definite contribution to shrinkage crack
reduction during the initial and final setting periods. The microfibers (pulp form) are more
effective in rich cement mortar; whereas, the longer fibers are more effective in lean mortars and
concrete. None of the test methods available in the published literature are suitable for
standardization in the present form. The primary drawbacks of the test methods are the attempt to
induce cracks in plain matrices and normal temperature, humidity and wind velocity, and the
possible errors that can occur in the measurement of crack area.
The use of natural fibers to improve strength and ductility of brittle materials has been
investigated at the Asian Institute of Technology, Bangkok Thailand. The group of Sera, Robles-
Austriaco and Palma (1990) came out with a research entitled “Natural Fiber as reinforcement”.
Their objective is to use the fibers as reinforcement to offer a unique low cost material for
roofing and other structural elements. The mechanical property of wood, bamboo and bamboo
pulp, coir, bagasse and palm fiber cement composites and the durability of jute, ramie, sisal and
coir fiber cement composites with pozzolanas were investigated. The mechanical properties of
straw-clay composites were also studied for use in grain storage silos. Results the investigation
showed that the natural fiber could be use as reinforcement in cement-based composites to
produce low-cost housing elements. Cost comparisons with commercial boards showed that the
natural fibers are not only least in cost, but they offer higher strength, ductility and toughness. It
was also found out that the durability of natural fibers in cement paste could be improved by
partial replacement of cement with pozzolana. The best results in strength were obtained when
49% silica fume is used. It was also concluded that the natural fibers used in non-cement
composites were also applicable.
13
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
2.1.6. “Cement mortar reinforced with natural fibers” by Castro and Naaman (1981)
The relatively high cost of man made fibers and wire meshes used in fiber reinforced
concrete and ferrocement, combined with a reduction in the usage of asbestos fibers prompted
Castro and Naaman (1981) to evaluate natural fibers of the Agave family that are widely
available in Mexico. In their published paper entitled “Cement mortar reinforced with natural
fibers”, they used two types of fibers of the Agave family – the Lechuguilla and Maguey
Pulquero which were bought in the market place of Mexico city and were sold in bulk. Four
specimens of 12.5mm x 75mm x 300mm dimensions were prepared, mixing the components
manually and cured After 28 days, the flexural strength was tested and the result was very
encouraging. They concluded that natural fibers of the Agave family have significant mechanical
properties that made them eligible as potential reinforcement of cementitious matrices. Likewise,
it was concluded that length of fibers of up to 75mm and volume fractions of up 11 percent can
be mixed with a Portland cement matrix and that the elasto-plastic behavior in flexure and
multiple matrix cracking were achieved for volume fraction of fibers above 7 percent.
It was also suggested that further systematic research should be encouraged to discover
other behavior of natural fibers that affect the strength of the composite.
The oldest form of fiber-reinforced composites was made with naturally occurring fibers
such as straw and horse hair. Modern technology has made it possible to extract fibers
economically from various plants, such as jute and bamboo, to be used in cement composites. A
unique aspect of these fibers is the low amount of energy required to extract these fibers. The
primary problem with the use of these fibers is their tendency to disintegrate in an alkaline
environment. Efforts are being made to improve the durability of these fibers in concrete by
using admixtures to make the concrete less alkaline and by subjecting the fibers to special
treatment.
14
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
Chemical Properties
Physical Properties
Tensile strength (kg/g.m) Low Median7.70 High
Ash (%) (%)
Elongation 1.54 2.2410.62 5.40
Solubilities in:
1% NaOH (%) 25.10 25.30 25.50
Alcohol-Benzene (%) 1.70 2.50 10.56
Hot water (%) 2.40 5.15 10.63
Lignin (%) 23.20 40.30 45.84
Holocellulose (%) 49.81 55.55 62.00
Alpha cellulose (%) 32.86 43.44 57.99
Hemi cellulose (%) 0.10 0.25 0.50
15
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
Chemical Properties
Physical Properties
Tensile strength (kg/g.m) Low Median- High
Ash (%) (%)
Elongation 1.5 2.2 - 5
Solubilities in:
1% NaOH (%) - - -
Alcohol-Benzene (%) - - -
Hot water (%) - - -
Lignin (%) 19 21 24
Holocellulose (%) 32 40 48
silica 0.7 2.1 3.5
16
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
Pentosan 27 29 32
* These result was given by FIDA
17
CHAPTER 2: REVIEW OF RELATED LITERATURE 2009-2010
in its long leaf sheaths, which grow to be 12 to 20 feet high. All parts of the stalk—from the
outer dark layer to the inner most layers—can be extracted, stripped and processed.
Abaca is amazingly strong, long, light and elastic fiber that outperforms hemp, sisal,
cotton, and synthetic fibers.
18