Replica Metallography and Penetrant Testing
Replica Metallography and Penetrant Testing
TECHNICAL REPORT
ON
REPLICA METALLOGRAPHY AND PENETRANT TESTING
i
Intentionally Left Blank
iii
Contents
1. INTRODUCTION ........................................................................................................................................ 1
4. CONCLUSION ............................................................................................................................................ 8
iv
List of Figures
v
1. INTRODUCTION
Nondestructive testing (NDT) consists of test methods used to examine an object, material or system
without impairing its future usefulness. A limited scale NDT laboratory has been established in PNRA for
training purpose of nuclear inspectors and to enhance the quality of regulatory oversight of nuclear power
plants in Pakistan. The following equipments are available in the laboratory:
A PNRA task force comprising officers of CNS and SNRS was established to make the equipment
functional. This report is submitted after completion of self training on the Replica Metallographic
Equipment and Penetrant Technique. The following team was engaged in this activity:
2. REPLICA METALLOGRAPHY
Surface Replication is a well developed electron microscopy sample preparation technique that
can be used to conduct in situ measurements of the microstructure of components. The in situ
determination of microstructural deterioration and damage of materials subjected to various
environments is an objective of any nondestructive evaluation (NDE) of structural components.
The need to assess the condition of power plant and petrochemical metallic components on a
large scale recently led to the application of surface replication to the problem of determining
remaining life. The usual method of metallographic investigation which may involve cutting
large pieces from the component so, that laboratory preparation and examination can be
performed, usually renders the component unfit for service or necessitates a costly repair. As a
result, metallographic investigations are avoided, and important microstructural information is
not available for evaluating the component for satisfactory performance. Therefore, an in situ or
field microscopy examination is needed to aid in the proper determination of component life.
1
This technique gives the flexibility of observing microstructures in the comfort of a lab instead of harsh
plant conditions (heat, radiation etc.).
In Replica Metallography steps followed are similar to that of common methods used in
laboratory metallography with the exception that the part to be viewed is not required to be
brought to the laboratory
Surface preparation holds key in revealing the microstructure to be studied. It involves steps like
grinding, polishing and etching. Components in service usually have a well-developed corrosion
or oxidation product or a decarburized layer on the surface that must be removed before
replication. In Situ, Replication Metallography utilizes portable grinding and polishing unit to
serve this purpose. Grinder/Polisher unit is shown in figure 1.
Note: During work at NDT Lab SNRS these steps were omitted because the equipment was not in
working condition. Instead already prepared specimens were used for preparation of replicas.
Replication of a surface can involve either direct or indirect methods. In the direct, or single-
stage, method, a replica is made of the specimen surface and subsequently examined in the
microscope, while in the indirect method; the final replica is taken from an earlier primary
replica of the specimen surface. Only the direct method will be considered in this effort because
it lends itself more favorably to on-site preparation.
Replication of surface was performed by using Transcopy Replica-Kit. Replica of the sample
was prepared as:
i. Two drops of replication fluid were applied to the replica foil.
2
ii. Replica strip was pressed firmly against the prepared sample surface for at least 30
seconds so that clear impression of the specimen can be obtained for observation
under microscope.
iii. Prepared replica was fixed on a glass slide by removing its back cover tape.
Microstructural observation is the key step for which all the specimen preparation and replication
is done. It is the step which reveals type of microstructure and the extent of damage sustained by
the component since it went into service. Crack determination is important to help establish the
root cause of a potential failure in a component. Creep defects cause the majority of failures in
power plant components operating under stress and thermal load, and the replica method is
especially suitable for the detection of these defects. The detection of various deleterious
precipitates in components subjected to high temperature and stress can lead to improved life
assessment analysis of these components.
Prepared replicas were viewed by using portable microscope and were compared with actual
microstructure of the specimens as shown in figure 3. Basic technique of utilizing the equipment
for preparation and observation of replicas has been practiced whereas interpretation of results
will require the team to be trained at advanced level to interpret the results.
3
Figure 3: Micrographs; Specimen (Left) and Prepared Replica (Right)
Liquid penetrant inspection is a method that is used to reveal surface breaking flaws by bleed out of a
colored or fluorescent dye from the flaw. The technique is based on the ability of a liquid to be drawn
into a "clean" surface breaking flaw by capillary action. After a period of time called the "dwell," excess
surface penetrant is removed and a developer applied. This acts as a blotter. It draws the penetrant from
the flaw to reveal its presence. Colored (contrast) penetrant require good white light while fluorescent
penetrant need to be used in darkened conditions with an ultraviolet "black light"
Surface Preparation: One of the most critical steps of a liquid penetrant inspection is the surface
preparation. The surface must be free of oil, grease, water, or other contaminants that may prevent
penetrant from entering flaws. The sample may also require etching if mechanical operations such as
machining, sanding, or grit blasting have been performed. These and other mechanical operations can
smear metal over the flaw opening and prevent the penetrant from entering.
Penetrant Application: Once the surface has been thoroughly cleaned and dried, the penetrant material
is applied by spraying, brushing, or immersing the part in a penetrant bath.
Penetrant Dwell: The penetrant is left on the surface for a sufficient time to allow as much penetrant as
possible to be drawn from or to seep into a defect. Penetrant dwell time is the total time that the penetrant
is in contact with the part surface. Dwell times are usually recommended by the penetrant producers or
required by the specification being followed. The times vary depending on the application, penetrant
materials used, the material, the form of the material being inspected, and the type of defect being
inspected for. Minimum dwell times typically range from five(5) to sixty (60) minutes. Generally, there
is no harm in using a longer penetrant dwell time as long as the penetrant is not allowed to dry.
4
Excess Penetrant Removal: This is the most delicate part of the inspection procedure because the excess
penetrant must be removed from the surface of the sample while removing as little penetrant as possible
from defects. Depending on the penetrant system used, this step may involve cleaning with a solvent,
direct rinsing with water, or first treating the part with an emulsifier and then rinsing with water. These
steps are shown in figure 4.
Developer Application: A thin layer of developer is then applied to the sample to draw penetrant trapped
in flaws back to the surface where it will be visible. Developers come in a variety of forms that may be
applied by dusting (dry powdered), dipping, or spraying (wet developers).
Indication Development: The developer is allowed to stand on the part surface for a period of time
sufficient to permit the extraction of the trapped penetrant out of any surface flaws. This development
time is usually a minimum of 10 minutes. Significantly longer times may be necessary for tight cracks.
5
Figure 5: Indication development after application of developer
Inspection: Inspection is then performed under appropriate lighting to detect indications from any flaws
which may be present.
Liquid penetrant inspection can only be used to inspect for flaws that break the surface of the
sample. Some of these flaws are listed below:
• Fatigue cracks
• Quench cracks
• Grinding cracks
• Overload and impact fractures
• Porosity
• Seams
• Pin holes in welds
• Lack of fusion or braising along the edge of the bond line
6
Figure 6: Inspection of indication and position measurement
Clean Surface: The final step in the process is to thoroughly clean the part surface to remove the
developer from the parts that were found to be acceptable.
Like all nondestructive inspection methods, liquid penetrant inspection has both advantages and
disadvantages. The primary advantages and disadvantages when compared to other NDE methods are
summarized below:
Advantages:
7
Disadvantages:
4. CONCLUSION
Two experiments were performed each by Replica Metallography and Penetrant Testing technique.
Penetrant testing experiment was performed successfully as a whole. It is to be noted that
grinding/polishing of specimens was not possible due to inoperable condition of portable polishing unit.
Steps should be taken to ensure that this equipment is in operational condition. On the plus side the basic
process of replication and microscopy was performed on already polished samples available in the lab.
Advance steps of Metallography i.e. interpretation of results require advanced level of training and skill in
the field of physical metallurgy and require more sophisticated tools.
FUTURE TASKS