CHARACTERIZATION OF PROPERTIES AND REDUCTION BEHAVIOUR OF
IRON ORES FOR APPLICATION IN SPONGE IRONMAKING
Studies on chemical and physical properties, and reduction behaviour (in coal) of
hematite iron ores, procured from ten different mines of Orissa, were undertaken to
provide information to the iron and steel industries (sponge iron plants in particular).
Majority of the iron ores were found to have high iron and low alumina and silica
contents. All these iron ores were free from the deleterious elements (S, P, As, Pb,
alkalies, etc.). The results indicated lower values of shatter and abrasion indices, and
higher values of tumbler index in all the iron ore lumps except Serazuddin (previous)
and Khanda Bandha OMC Ltd.. For all the fired iron ore pellets, the degree of reduction
in coal was more intense in the first 30 minutes after which it became small. Slow
heating led to higher degree of reduction in fired pellets than rapid heating. All the iron
ores exhibited more than 90% reduction in their fired pellets in 2 hrs. time interval at a
temperature of 9000C. Iron ore lumps showed lower degree of reduction than the
E-mail: [email protected]
2
3
1. INTRODUCTION
direct reduction processes. The world production of sponge iron has increased from
in the literature (World Direct Reduction Statistics 2000), the world DRI production
may reach up to 75 MT by the year 2010. Presently, India has emerged as the largest
producer of sponge iron (11.82 MT in 2005-06) in the world (Patnaik 2006). In this
total production of 11.82 MT, the contribution of coal-based sponge iron plants was
Bountiful iron ore and coal deposits in the state of Orissa (India), constituting
26 and 24% of the country's total reserves (Das etal. 2004), have attracted many
companies in the recent past for setting up of various sponge iron and steel making
plants in this state. At present, there are 18 sponge iron plants (coal-based) in Orissa
producing about 0.90 MT of sponge iron per annum (Das etal. 2004) and few more
are likely to be commissioned very soon. This has brought riot of colors in the mining
districts of the state. A detailed characterization of these iron ores is essential for their
effective utilization.
In selecting iron ore for iron and steel industries, the properties which need to
present investigation, 10 different types of hematite iron ore (obtained from different
4
mines of Orissa) having the possibility to be exploited by sponge iron plants have
been examined for their above mentioned chemical and physical properties. The aims
have been: (1) to ascertain the behaviour of these iron ores in advance, and (2) to
provide sufficient technical information to the iron and steel industries, particularly to
those which do not have R & D facilities. This work will certainly help in assessing
the cost and selection of iron ore for a particular sponge iron industry.
2. EXPERIMENTAL
2.1 Materials Selection
In this investigation, ten types of hematite iron ore samples were collected from
different mines of Orissa. Non-coking coal, used in the reduction studies, was
collected from Brajrajnagar mine of Orissa and examined for its proximate analysis
(Indian Standard 1350: 1969), sulphur content, caking index and reactivity towards
carbon dioxide (Indian Standard 12381 : 1994). The results obtained indicated (i)
volatile matter : 39.25 wt. %, (ii) ash : 40.25 wt %, (iii) fixed carbon : 20.50 wt. %,
(iv) sulphur : 0.55 wt. %, (v) caking index : nil, and (vi) reactivity : 5.17 cc of
were determined by X-ray fluorescence technique at Rourkela steel plant. The results
Assessments of physical properties of all these selected iron ores were carried
out by determining their tumbler, abrasion and shatter indices, and apparent porosity.
5
2.3.1 Tumbler and abrasion indices
lump iron ore of size —40 + 10 mm in a standard drum, as per Indian Standard
through 0.5 mm screen represented its abrasion index, while the % weight of iron
In shatter test, a dried lump iron ore sample (10 kg) of size —40 + 10 mm was
dropped four times from a height of 2 m on a cast iron floor. The iron ore was then
screened and the shatter index was expressed as the wt.% passing through 5 mm
The apparent porosity values of iron ore lumps and pellets were determined by
The pellets ( size: 15 mm dia. approx. ) were made by prolonged hand rolling
of moistened (12% water) iron ore fines of -100 mesh size. The pellets were dried at
110°C for 2 hours and then indurated in a muffle furnace at 12000C for one hour to
attain workable strength. These indurated pellets were then kept in a desicator for
Majority of the reduction experiments were carried out under rapid heating
condition at a temperature of 900°C for varying time periods in the range 30 — 120
6
minutes. Few experiments under slow heating condition were carried out for
comparison. The weighed amount of oven dried pellet (size: 15 mm diameter approx)
was placed centrally on a packed bed of non-coking coal in a stainless steel reactor
(size: 77 mm height × 40 mm inside diameter) tightly closed with an air tight cover
In case of reduction studies under rapid heating condition, usually four stainless
steel reactors were inserted inside the muffle furnace maintained at the predetermined
reduction temperature of 900°C. In doing so, the furnace first cooled down to 8500C
and then took nearly 10 minutes in reaching to the required reduction temperature of
9000C. Each reactor was taken out one by one at an interval of 30 minutes and cooled
to room temperature in air. The weight loss in each of the pellet was recorded.
Reduction under slow heating condition was carried out by heating the stainless steel
reactor containing the iron ore pellet/lump in coal from room temperature to the
required temperature of 900°C at a rate of about 7°C min-1 and kept there for one
hour. The reactor was then taken out and cooled in air. The pellets thus reduced were
weighed and the degree of reduction was expressed as the wt.% of oxygen removed
the furnace operation. The chemical and physical characteristics of iron ores
under investigation have been listed in Tables 1 and 2. Data for the mineralogical
composition (Table 1) indicated that the gangue materials in these iron ores
7
mainly consisted of alumina and silica with a negligible amount of TiO2 and
MnO. The ores were found to be free from deleterious elements S, P, As, Pb,
alkalies, etc. The results (Table 1) established that the iron ores obtained from
Zenith, Sakaruddin, Serazuddin (current), M.G. Mohanty, G.M. OMC Ltd. and
D.R. Pattnaik mines were rich in iron (> 64%) and poor in alumina (1.6 - 3.0 %)
and silica (0.9 - 2.6 %) contents, whereas other ores contained higher amounts of
these gangue materials. Hence, more slag formation is expected during melting of
sponge irons produced from Khanda Bandha OMC Ltd., BPJ OMC Ltd. Nos. 6
and 7, and Serazuddin (previous) iron ores. Alumina raises the melting point of
Data for the porosity values and strength properties (tumbler, abrasion and
shatter indices) of these iron ores have been presented in Table 2. These are the
shown in Table 2, all the iron ores except Serazuddin (previous) and Khanda
Bandha OMC Ltd. offered high resistance to abrasion and tumbling, most
probably due to their hard fine grained structure and lower porosity. Furthermore,
results obtained (Table 2) indicated lower value of shatter index (for —5 mm size
fraction) in all of them except Serazuddin (previous) and Khanda Bandha OMC
Ltd. iron ores. Based on the tumbler, abrasion and shatter indices results, the iron
ores procured from Sakaruddin, Serazuddin (current), BPJ OMC Ltd. Nos.6 and
7, M.G. Mohanty and D.R. Pattnaik mines appear to be hard and strong. On the
other hand, all these tests ascertained Serazuddin (previous), Khanda Bandha
OMC Ltd., and Zenith iron ores to be more porous, soft and friable, and hence are
8
liable to produce more deleterious fines (—5 mm fraction) during handling or in
iron blast furnaces, rotary kilns, etc. As evident from Table 2, no definite
shatter indices) exists due to wide scattering of points (data). The loss on ignition
values (2–4 wt.% in general), associated with these hematite iron ores, are
The degree of reduction values of these iron ore lumps and fired pellets, reduced
at 900°C for different time periods in the range 30 —120 minutes under rapid and slow
pellets were carried out with a point of view of utilization of fines generated from
these iron ores. The observations made during this study are discussed below.
Data listed in Table 3 (rapid heating) indicate that the reduction time has
an approximately identical effect on the reduction behaviour of almost all the iron
ore pellets studied. As shown in Table 3, all the fired iron ore pellets showed
reduction) and thereafter the rate of reduction decreased with increasing reduction
time up to the range studied (i.e. 120 minutes) . It was also observed that all the
fired iron ore pellets were almost completely reduced (more than 90% reduction)
in about 120 minutes. This indicates that the utilization of these iron ores in
sponge ironmaking is likely to allow the rotary kiln operations to be carried out at
9
low temperatures (i.e. less than 10000 C) resulting in greater savings of energy
1987), the excessively high degree of reduction in the first 30 minutes is mainly
associated with the release of volatiles from coal, their reformation into H2 , CO,
etc. and major participation of these reducing gases in the reduction of iron oxide
in the reduction rate). The decrease in reduction rate with increasing time above
metallic layer thickness and diminished evolution of volatile matter from coal. An
increase in the thickness of product iron layer offers greater resistance in the
diffusion of carbon and reducing gas to the surface of unreduced iron oxide.
In order to study the effect of mode of heating, the fired iron ore pellets were
reduced in coal at 900°C (soak time at this temperature: 1 hr.) under rapid and slow
heating conditions. The results obtained have been listed in Tables 3 and 4. It is
fairly clear from these tables that in comparison to rapid heating, the slow heating to
It is more likely that rapid heating to 900°C causes a higher rate of volatile
matter escape from coal, thereby providing less time for H2 and CO (reducing
gases) to be in contact with iron ore pellet. The result is thus lower degree of
reduction in rapid heating. During slow heating operation, volatile matters are
released from coal at a slower rate and hydrocarbons get sufficient time to undergo
10
the process of cracking (CnHm = nC + mH). The more deposition of highly reactive
pyrolytic carbon, and increased time of contact of carbon and reducing gases (H2
and CO) with the pellet appear to be the obvious reasons for the higher degree of
In this study, reduction behaviours of dried hematite iron ore lumps (size: 15
mm approx.) have been compared with those of corresponding fired pellets reduced
(in coal) under identical slow heating conditions (heating rate: 70C min-1,
temperature: 9000C, soak time: 1 hr.). Data for their degree of reduction values have
been recorded in Table 4 and plotted as a function of their total iron contents in Fig.
1. The results (Table 4 and Fig. 1) established lower degree of reduction in lumps
Table 2 clearly indicates that the dried iron ore lumps have much lower
porosity values than those of corresponding fired pellets. The appreciably lower
porosity in iron ore lumps appears to be the most likely reason for their lower
reducibility. As outlined in the literature (Moinpour and Rao 1988), hematite pellets
tend to form disordered and hence more reactive/easily reducible wustite (FeO) .
This may be the another reason for relatively higher reducibility of pellets, as
observed in the present investigation. It was noted that Khanda Bandha OMC Ltd.,
BPJ OMC Ltd. No.6, Zenith, and D.R. Pattnaik iron ore lumps cracked into fine
11
fragments during reduction at 9000C, and hence their degree of reduction values
could not be measured. The breakdown in these lumps may be attributed to the
higher rate of Fe2O3 - Fe3O4 transformation and generation of higher therma1 strain.
3.2.4 Comparison of the degree of reduction values of different fired hematite iron
ore pellets
hematite iron ore pellets (fired) reduced in coal under identical conditions. As can
be seen in these Tables, Zenith, Sakaruddin, Serazuddin (current), BPJ OMC Ltd.
No.6, M.G. Mohanty and D.R. Pattnaik iron ore pellets, in general, have shown
higher degree of reduction than others for the same reduction conditions. The
higher rates of reduction in these iron ore pellets could be attributed, at least in part,
Fig. 1 shows the correlation between degree of reduction (%) and total iron
content (%) for these hematite iron ores (fired pellets and lumps both) reduced in
coal at 9000C (soak time: 60 min.) under slow heating condition. It can be seen in
this figure that despite considerable scatter in the data, there is, in general, a trend of
improvement in reducibility of an iron ore with increase of its iron content. This
could be ascribed to the decrease in total gangue (Al2O3, SiO2, etc.) content with
increasing iron content, as shown in Table 1. These gangue minerals are notoriously
distributed in the matrixes of Indian iron ores and offer a lot of hindrance in the
12
diffusion of reducing gases to the reaction sites. The result is thus less reduction of
4. CONCLUSIONS
The following results are concluded from the studied iron ores:
1. Zenith, Sakaruddin, Serazuddin (current), M.G. Mohanty, G.M. OMC Ltd and
D.R. Pattnaik iron ores were found to be rich in iron (> 64%) and poor in
2. Chemical analyses established that all the iron ores under investigation were
3. The results obtained indicated higher values of tumbler, abrasion and shatter
resistance in all the iron ore lumps except Serazuddin (previous) and Khanda
4. The rates of reduction in all the fired iron ore pellets were higher up to 30
5. For the same reduction temperature and time, slow heating revealed higher
degree of reduction in all the fired iron ore pellets than rapid heating.
6. The results established more than 90% reduction in all the fired iron ore
7. The results demonstrated that iron ore lumps were less reducible than their
13
REFERENCES
Bodsworth, C. and Taheri, S. K., 1987, “Progressive changes in iron ore and coal char
during direct reduction with coal gasification,” Ironmaking and Steelmaking, 14, pp.
278-290.
Chesters, J. H.., 1973, Refractories: production and properties, The Iron and Steel
Institute, London, p. 472.
Das, B., Reddy, P. S. R. and Misra, V. N., 2004, “R & D activities for effective
utilization of mineral resources of Orissa,” SGAT, 5, pp. 10-19.
Dutta, S. K. and Ghose, A., 1994, “Study of non-isothermal reduction of iron ore-
coal/char composite pellet,” Metallurgical and Materials Transaction B, 250,
pp. 15-20.
Indian Standard IS : 1350, Part-I, 1969, “Methods of test for coal and coke,” Bureau
of Indian Standards, Delhi, p. 3.
Indian Standard IS : 12381, 1994, “Coal (char) reactivity for direct reduction process
– Method of determination”, Bureau of Indian Standards, Delhi, pp. 1-7.
Moinpour, M. and Rao, Y. K., 1988, “Kinetics of reduction of hematite with He-H2
gas mixtures at moderate temperatures,” Transactions ISIJ, 28, pp. 714-720.
Patnaik, N. K., 2006, “Future of DRI industry and availability of coal”, DRI Update,
August, pp. 8-11.
SIMA – Community News, 2006, “DRI production still growing in 2005”, New
Delhi, www.simaindia.org/comm_news28.cfm.
World Direct Reduction Statistics, 2000, Midrex Direct Reduction Corporation, p.4.
14
Table 1 : Chemical composition and loss on ignition values of hematite
iron ores (wt.%, air-dried basis)
BPJ OMC Ltd. No.7 61.54 88.00 4.55 4.48 0.12 0.00 2.85
M.G. Mohanty mine 64.52 92.27 2.11 1.81 0.08 0.02 3.71
15
Table 2 : Physical properties of hematite lump iron ores (dried basis)
16
Table 3 : Degree of reduction values of different hematite
iron ore pellets (fired) reduced under rapid
heating condition in coal: Effect of reduction time
17
Table 4 : Degree of reduction values of different hematite iron ore pellets
(fired) and lumps reduced in coal under slow heating condition
18
100
0
Temperature - 900 C Slow Heating
Soak Time - 60 min.
80
70
60
60 62 64 66 68 70
Total Iron Content (%)
Fig. 1 : Relation between degree of reduction and total iron content for
hematite iron ore pellets (fired) and lumps reduced under slow
heating condition
19