Summary of Choke Valve API 6A 21 Edition
Summary of Choke Valve API 6A 21 Edition
List of Content
API 6A 21st Edition
1. Choke Valve
This summary created for preparation of
2. Service Conditions
Choke Valve ceritification API 6A 21st Edition.
3. Design Methods
4. Material Contains all things that relevant with Choke
5. Heat Treating Valve as API 6A 21st Edition.
6. Qualification Test Coupon (QTC)
7. Quality Control and Testing Provided by:
Research and Development Department
8. Inspection
9. Marking
10. Storing and Shipping
ATTACHMENTS
1. Choke Valve
Choke valve is a type of control valves, mostly used in oil and gas production wells to control
the flow of well fluids being produced. Another purpose that the choke valves serve is to kill the
pressure from reservoir and to regulate the downstream pressure in the flowlines
For chokes having an upstream end connector of higher rated working pressure than
the downstream end connector, the choke shall have a two-part rated working pressure
consisting of the rated working pressure of the upstream end connector and the rated
working pressure of the downstream end connector, for example 20.7 MPa x 13.8 MPa
(3000 psi x 2000 psi).
Design for temperature ratings above 121oC (250oF), classifications X and Y (see table 2.1)
Table 2.1 Temperature Ratings
Note: Choosing material class and specific materials for specific conditions is ultimately the
responsibility of the purchaser.
3. Design Methods
b. Stems
Stems shall be designed to satisfy the manufacture’s documented performance
characteristics and service conditions in accordance with 2.Service Condition. The
manufacturer shall document engineering practices and acceptance criteria on which
the design is based.
1. API Standard 6X
If used, design calculations for pressure-containing equipment shall conform to
design methodology of API 6X. The use of von Mises equivalent stress shall be
permitted.
SE = S Y
Where;
- SE is the maximum allowable equivalent stress at the most highly stressed distance
into pressure vessel wall, computed by the distortion energy theory method;
- SY is the material-specified minimum yield strength.
d. Flanges
Three types of end and outlet flanges are covered by this specification, type 6B, 6BX,
and segmented. Types 6B and 6BX flanges may used as integral, blind or weld-neck
flanges. Type 6B may be used as threaded flanges and some type 6BX flanges may be
used as test flanges.
Types 6B and 6BX are designed for use in the combinations of nominal size ranges
and rated working pressure as shown below.
1. Type 6B weld-neck flanges with a rated working pressure of 13.9 MPa, 20.7
MPa, or 34.5 MPa (2000 psi, 3000 psi, or 5000 psi).
2. Type 6BX weld-neck flanges with a rated working pressure 69.0 MPa, 103.5
MPa, or 138.0 MPa (10.000 psi, 15.000 psi or 20.000 psi).
Dimensions of the weld-neck flange section shall conform to Table D.1, Table D.2,
Table D.3, Table D.4, Table D.5, Table D6, and Table D.7 (see ATTACHMENT A !).
For Corrosion-resistant ring grooves on the flange, the minimum thickness of the
finished corrosion-resistant weld overlay applied for ring grooves in partial overlay
equipment shall be 3 mm (0.12 in.) for the outer 23o surface.
For ring groove surface:
- For 6B, all 23o on R ring grooves shall have a surface finish no rougher than 1.6
µm Ra (63 µin. RMS).
- For 6BX, all 23o on RX ring grooves shall have a surface finish no rougher than
0.8 µm Ra (32 µin. RMS).
(for ring groove dimension see ATTACHMENT B !)
Proration beans shall have a net effective orifice length of 152.4 mm ± 1.5 mm (6 in ±
0.06 in.). The orifice diameters of these beans shall be specified in 1/64 in. diametrical
increments, i.e 5/64 in. , 6/64 in. , 7/64 in. , 8/64 in.
g. Other Parts
All other pressure containing parts and all pressure controlling shall be designed to
satisfy the manufacturer’s documented performance characteristics and service in
accordance 2. Service Conditions.
4. Material
Material requirements in this section shall apply to Carbon steels, low alloy steels, and
martensitic stainless steels (other than precipitation-hardening types).
Metallic Requirements
The Manufacturer’s written specified requirements for metallic materials for bodies,
bonnets, end and outlet connectors, stems shall define the following, along with
accept/reject criteria:
- Material qualification;
- Heat-treatment procedure, including cycle time, quenching practice and
- NDE requirements;
- Forming practices, including hot working, hot isostatic pressing, and cold working
practices;
Nonmetallic Requirements
Nonmetallic pressure-containing or pressure-controlling seals in contact with retained
fluids shall have written material specifications. The Manufacturer’s written specified
requirement for nonmetallic materials shall define the following:
Nonstandard materials for parts shown in Table 7 shall have a specified minimum yield
at least equal to that of the lowest-strength standard material permitted for that
application.
Nonstandard materials shall be materials with properties that do not meet all the
requirements of Table 8 for a standard material. Nonstandard material shall conform to the
manufacturer’s written specification that shall include minimum requirements for:
- Tensile strength;
- Yield strength;
- Hardness;
FOOTNOTES
b If end connectors are of the material designation indicated, design is in accordance with 3.1
A. Composition Limits-Requirements
Bodies, bonnets and end and outlet connectors manufactured from carbon, low-
alloy, and martensitic stainless steels (other than precipitation-hardening types) shall
conform to the compositional limits given in table 9 and 10.
Table 9-Steel Composition Limits for Bodies, Bonnets, and End and Outlet Connector Materials
FOOTNOTES
a Alloy of carbon and iron containing a maximum of 2% mass fraction carbon, 1.65% mass fraction manganese,
and residual quantities of other elements, except those intentionally added in specific quantities for deoxidation
(usually silicon and/or aluminum).
b Steel containing less than 5% mass fraction total alloying elements, or steels with less than 11% mass fraction
chromium, but more than that specified for carbon steel.
c For each reduction of 0.01% below the specified carbon maximum (0.35%), an increase of 0.06% manganese
above the specified maximum (1.05%) is permitted up to a maximum of 1.35%
d see table 10
e 1.00 max.nickel is for sour-service applications meeting NACE MR0175/ISO 15156. For nonsour service, a nickel
content of 3.00 max. is acceptable.
Table-10 Phosphorus and Sulfur Concentration Limits
B. Tolerance Ranges
If the manufacturer specifies a material for PSL 3 or PSL 4 with chemical
composition requirements by reference to a recognized industry standard, the material
shall meet the tolerance ranges of the referenced industry standard. If the
manufacturer specifies a material chemistry not covered by a recognized industry
standard, the tolerance ranges shall meet the requirements in the table 11.
Table 11. Maximum Tolerance Range Limits for Alloying Elements (PSL 3 and PSL
4)
FOOTNOTES
a Values are the total allowable variation in any one element and shall not exceed the
maximum specified in Table 9.
A. Casting
Production castings shall meet the requirements of API 20A and this specification.
The API 20A CSL (Casting Specification Level) shall be accordance with table 12.
5. Heat Treating
- The temperature requirements of PSL 1, PSL 2, and PSL 3 shall apply with the
addition that the temperature levels for PSL 4 parts shall be determined by using a
heat sink.
Note: For alloy materials that are processed in accordance with API 6ACRA,
temperature levels may be monitored using a contact thermocouple.
- The heat sink shall be made of the same class of material if the parts are made of an
alloy of the following classes: carbon steel, alloy steel, stainless steel, titanium-based
alloy, nickel-cooper alloys, and nickel-based alloys.
- For parts that do not meet one of the preceding classes, the heat sink shall be made
from the same alloy as the part. The equivalent round of all heat sinks shall be
determine in accordance with method equivalent round (6.4.1). The ER of the heat
sink shall be greater than or equal to the largest ER of any single part in a heat-
treatment load.
The temperature-sensing tip of the thermocouple shall be within the part or heat sink and
be no closer than 25 mm (1 in.) to any external or internal surface.
For furnaces having a working zone less than or equal to 0.3 m 3 (10 ft3), a minimum
of 3 thermocouples located either at the front, center and rear or at the top, center
and bottom of the furnace working zone shall be used.
For furnace having a working zone greater than 0.3 m 3 (10 ft3) and not greater than
31.5 m3 (1125 ft3), a minimum of 9 thermocouples shall be used. For each additional 3.5
m3 (125 ft3) beyond 31.5 m3 (1125 ft3) of furnace working zone surveyed, at least one
additional thermocouple shall be used, up to a total of 40 thermocouples. The first 9
thermocouple shall be located as per figure M.1 and figure M.2 and thermocouples
shall be placed in the furnace working zone(s) and protected from furnace
atmospheres by means of suitable protective devices. Each additional thermocouple
location shall be equally spaced in the central additional working zone volume.
Once the furnace temperature has reached the set-point temperature, the
temperature of all test locations shall be recorded at two-minute intervals, maximum
for at least 10 min. Then, readings shall be taken at five-minute intervals, maximum, for
sufficient time (at least 30 min) to determine the recurrent temperature pattern of the
furnace working zone.
B. Temperature Tolerance for Batch-type Furnaces
- The temperature at any point in the working zone of furnace used for
austenitizing, normalizing, annealing, or solution annealing shall not vary by
more than ± 14oC (± 25oF) from the furnace set-point temperature after the
furnace working zone has been brought up to temperature. Before the furnace
set-point temperature is reached, none of the temperature readings shall exceed
the set-point temperature by more than the temperature tolerance.
- Furnaes that are used for tempering, aging, and/or stress-relieving shall not vary
by more than ± 8oC (± 15oF) from the furnace set-point temperature after the
furnace working zone has been brought up to temperature. Before the furnace
set-point temperature is reached, none of the temperature readings shall exceed
the set-point temperature by more than the temperature tolerance.
The SAE AMS2750 sections on furnace modification and furnace repairs shall be
used to determine whether a new furnace survey is required. All furnace repairs and
modifications shall be documented, and the responsible quality assurance organization
shall make determination whether and additional furnace survey and calibration is
required based on the repairs or modifications in accordance with SAE AMS2750 or SAE
AMS-H-687.
5.5 Quenching
The temperature of the water shall not exceed 38 oC (100oF) at the start of the quench.
For bath-type quenching, the temperature of the water shall not exceed 49 oC (120oC) at any
time during the quench cycle.
The temperature range of other quenching media, such as oil or polymer, shall meet the
manufacturer’s written specification.
6 Qualification Test Coupons (QTC)
The properties exhibited by the QTCs shall represent properties of thermal response of
the material comprising the production parts it qualifies.
- For material heat treated in a batch furnace, the QTC shall qualify only material and
parts produced from the same heat. For material heat treated in a continuous furnace,
the QTC shall qualify only material and parts produced from the same heat and heat-
treat lot.
- It shall remain integrally attached during all heat-treatment operations, except post-
weld heat-treatment, stress relief, and any re-tempering or re-aging that can be
required.
- For tubular parts, bar stock, mill shapes, and other raw material with a uniform cross-
section, the prolongation shall have the same cross-section as that of the raw material.
- For a production part with a complex shape or varying cross section, it is not necessary
that the prolongation be an extension of the largest of the largest cross-section of the
part, but the extension shall meet or exceed the minimum ER (Equivalent Round)
required for separate QTC.
6.4 Equivalent Round (ER)
The size of a QTC for a part shall be determined using the ER methods, ER methods is
typical basic models for determining the ER of simple solid and hollow parts and more
complicated parts shall apply as illustrated in figure 3A, 3B and 3C.
The ER of a studded type part shall be determined by using a thickness, T, equal to that
of thickest flange of that part. An ER determination for these parts shall be in accordance
with the methods for complex-shaped parts.
Figure 3A
Figure 3B
Figure 3C
6.5 ER Size Requirements
The manufacturer shall use the same foundry practice(s) for the QTC as those used
for parts it qualifies to ensure accurate representation.
- For PSL 1 and PSL 2, for parts with an ER ≥ 63 mm (2.5 in.), the QTC size shall be 63
mm (2.5 in.) ER as a minimum, regardless of part size.
Note: A QTC larger than 63 mm (2.5 in.) ER may be used when required by the
manufacturer or purchaser.
- For PSL 3 for parts with an ER < 125 mm (5 in.), the ER of the QTC shall be equal to
or greater than the dimensions of the part it qualifies.
- For PSL 3, for parts with an ER ≥ 125 mm (5 in.), the QTC size shall be 125 mm (5 in.)
ER as minimum.
Note: A QTC larger than 125 mm (5 in.) ER may be used when specified by the
manufacturer or purchaser.
- For PSL 3, for bodies that require a yield strength of 75K or greater and where the
part’s weight during heat-treat is greater than 454 kg (1000 lb), the QTC ER shall be
the same or greater than the part it qualifies but is not required to exceed 250 mm
(10 in.), with the following exception.
design documentation provides the stress distribution and demonstrates that the
part meets the design acceptance criteria of Section 3 where the mechanical
properties are lower than the requirements specified in 4.2 for the QTC;
a qualification forging or sacrificial part is used to document that the part meets the
Charpy impact requirements of this specification at depth of 63 mm (2.5 in.) or T/4
of the thickest section of the parts, whichever is less; and
a qualification forging or sacrificial part that shall qualify all the production parts
covered by the analysis using the same heat-treat geometry, material grade, and
heat-treat paramaters, as defined by the manufacturer.
Note: A QTC larger than 250 mm (10 in.) ER may be used when specified by the
manufacturer or purchaser.
The tampering temperature for the part(s) shall not be lower than 14 oC (25oF)
below that of the QTC.
The upper limit not be higher than that permitted by the heat-treat procedure for
that material. The cycle time at each temperature shall not exceed that for the
part(s).
- For PSL 3, THE QTC shall be heat-treated in the same heat-treated furnace and same
quench tank as the production parts it qualifies.
- For PSL 4 only, the mechanical testing shall be performed per heat per heat-treat lot.
The testing shall use a prolongation or production part for each heat-treat lot.
Individual prolongations or production parts corresponding to each quench shall be
used for multiple quench bathes from the same furnace load.
For material heat-treated in a continuous furnace, the QTC shall be from the same
heat-treat lot as the material it qualifies.
For all heat-treating of parts, QTCs shall be performed with “production type”
equipment meeting the requirements of this specification. “Production type” heat-
treating equipment shall be considered equipment that is routinely used to process
production parts having an ER equal to or greater than the ER of the subject QTC.
Automatic controlling and recording instruments shall be used. The controlling and
recording instruments used for heat-treatment processes shall be accurate ± 1 % of
their full-scale range.
The Instruments shall be calibrated at least once every 3 months. Equipment used
to calibrate the production equipment shall be accurate to ±0.25% of full-scale range.
Then for measuring pressure records for PSL 3 and PSL 4, the following records shall be
maintained.
- A pressure recording device shall be used on all hydrostatic tests. The record shall
identify the recording device, shall be dated, and shall be signed.
Personnel performing visual inspection for acceptance shall take and pass an annual
vision examination in accordance with the manufacturer’s documented procedures that
meet applicable requirements of the following:
- ISO 9712, or
- ASNT SNT SNT-TC-1A, or
- A national or international standard that is equivalent to ISO 9712 or ASNT SNT-TC-
1A.
C. Welding Inspectors
Personnel performing visual inspections of welding operations and completed welds
shall be qualified and certified as follows:
- AWS QC1 or Equivalent certified welding inspector, or
- AWS QC1 or equivalent senior certified welding inspector, or
- AWS QC1 or equivalent certified associate welding inspector, or
- Welding Inspector certified by the manufacturer’s documented training program.
D. Other Personnel
All other personnel performing measurements, inspections, or tests for acceptance
shall be qualified in accordance with the manufacture’s documented procedures and
requirements.
Each pressure-containing or pressure-controlling part for use in material classes DD, EE,
FF, and HH shall be hardness tested individually to confirm that the NACE MR0175/ISO
15156 hardness values have been satisfied (except for ring gaskets).
7.4 Testing
A. Tensile Testing
If tensile test specimens are required, they shall be removed from a QTC after the
final QTC heat-treatment cycle.
- For solid QTC, their longitudinal centerline axis is wholly within the center
core 1/4 T envelope (see figure 3A, 3B, 3C).
- Or within 3 mm (1/8 in.) of the mid-thickness of the thickest section of a
hollow QTC (see figure 3A, 3B, 3C).
For diameter tensile test specimens, ASTM A370 standard sized 12.5 mm (0.500
in.) shall be used, Unless the physical configuration of the QTC prevents their use.
Standard-sized specimens cannot be used because of the physical configuration of the
QTC, the subsize specimens referenced in ASTM 1370 may be used.
A minimum of one tensile test shall be performed. The result of the tensile test(s)
shall satisfy the applicable requirement table 8.
If the result test of the tensile test(s) do not satisfy the applicable requirements,
two additional tests on tensile specimens removed from required location within the
same QTC with no additional heat-treatment may be performed to qualify the material,
and the results of each of these tests shall satisfy the applicable requirements.
C. Impact Testing
If impact test specimens are required, they shall be removed from QTC after the final
QTC heat-treatment cycle. Impact specimens shall be removed such that the notch is
within the ¼ T envelope.
Impact test of a QTC shall be used to qualify a heat and the bodies, bonnets, and end
and outlet connectors produced from that heat and shall conform to the requirements
of table 13.
Table 13 – Charpy V-notch Impact Requirements – 10 mm x 10 mm
If subsize specimens are used, the Charpy V-notch impact requirements shall be
equal to that of 10 mm x 10 mm specimens multiplied by the adjustment factor listed in
Table 14.
Note: For PSL 4, subsize specimens shall not be used
If a test fails, then retest of three additional specimens removed from the required
location within the same QTC, with no additional heat-treatment, may be made, each of
which shall exhibit an impact value equal to or exceeding the required minimum
average value of table 13 or table 14.
D. Hardness Testing
- For PSL 1m bodies, bonnets, end and outlet connectors, stems, loose connectors, and
clamp hub end connectors with 13.8 MPa, 20.7 MPa, and 34.5 MPa (2000 psi, 3000
psi, and 5000 psi) working pressure, sampling shall be in accordance with ISO 2859-
1:1999, level II, 4.0 AQL (acceptance quality limit), with the following exception. For
DD, EE, FF and HH material class equipment, each pressure containing or pressure-
controlling part shall be individually hardness tested.
- For PSL 2, PSL 3 and PSL 4, all parts shall be hardness tested.
- For PSL 3 and PSL 4, additionally one hardness test shall be performed on each
finished part (body, bonnet and end connectors).
Parts manufactured from nonstandard materials shall meet the minimum hardness
shall meet the minimum hardness requirements of the manufacturer’s material
specification.
Parts manufactured from standard materials shall meet the requirements of table
15.
For parts manufactured from a standard material that does not conform to the
specified minimum hardness value of table 15, the material shall be acceptable if
the measured hardness exceeds the minimum acceptable Brinell hardness value
calculated using equation below.
HBWc, min: is the minimum acceptable Brinell according to the HBW method for
the part after the final heat-treatment cycle;
Rm, min : is the minimum acceptable ultimate tensile strength for the applicable
material designation;
R, QTC : is the average ultimate tensile strength determined from the QTC
tensile tests;
HBW, QTC : is the average of the Brinell hardness values according to the HBW
method observed among all tests performed on the QTC.
FOOTNOTES
- The equipment used in any pressure test shall be free of paint or other coatings that
can impede leak detection and/or leak observation.
- All pressure testing shall be conducted prior to the addition of body-filler grease.
Lubrication applied during assembly is acceptable.
- The equipment shall show no visible leakage while subjected to test pressure (Fluid
released during pressure build-up or pressure bleed-down shall not considered leakage).
- Monitored pressure shall not vary from the test at the start of the test by more than
5% or 3.45 MPa (500 psi), whichever is less, during the entire hold period. The initial
test pressure shall not be greater than 5% above the specified test pressure. During the
entire hold period, the monitored pressure shall not drop below the specified pressure.
- If a shell test is specified in Table 17, each piece of equipment shall be hydrostatically
shell tested prior to shipment from the manufacturer’s facility.
Hydrostatic Test Method
Chokes shall be in the partially open during testing. The hydrostatic shell test from
assembled equipment shall consist of three parts:
a. primary pressure-holding period;
b. reduction of the pressure to 0 psig;
c. secondary pressure-holding period.
After testing, the pressure in the test article shall be reduce to 0 psig.
For choke having an inlet connector with higher rated working pressure than the
outlet connector, two hydrostatic shell tests shall be performed. The body portion from
the inlet connector to the body-to-bean seal point of the replaceable seat or flow bean
shall be tested at the shell test pressure for the inlet connector. The remainder of the
body, downstream from the seal point, shall be tested at the shell test pressure for the
outlet connector. Temporary seat seals and/or a blank seat may be used to facilitate
testing.
- The test medium shall be air, nitrogen, or other gas mixture that will remain in the gas
phase at test pressure.
- The equipment used in any pressure test shall be free of paint or other coatings that
can impede leak detection and/or leak observation.
- Gas testing shall be performed at ambient temperature (4 oC and 50oC or 40oF and
120oF) and wit the tested equipment completely submerged in a water bath.
- All pressure testing shall be conducted prior of body-filler grease. Lubrication applied
during assembly shall be acceptable.
- No visible leakage (bubbles) shall appear in the water bath during the pressure-holding
period. If the leakage is observed, the rate shall be less than the rates shown in Table
20, measured at atmospheric pressure, during specified pressure hold-periods.
- Choke with rated working pressures of 69.0 MPa (10.000 psi) and higher shall be gas
tested.
C. Post-test Examination
The tested prototype shall be disassembled and inspected. All relevant items should be
photographed. The examination shall include a written statement (test report) that neither
the final product nor part design contains defects to the extent that any performance
requirement is not met.
8. Inspection
- For PSL 1 and PSL 2, other features shall be checked on sample parts in accordance with ISO
2859-1:1999, level II, 1.5 AQL.
- For PSL 3 and PSL 4, sampling shall not be allowed; all parts shall be dimensionally
inspected.
Visual examination requirements do not apply to PSL 3 and PSL 4 except for welds. For PSL 1
and PSL 2, each part shall be visually examined.
A. Ferromagnetic Materials
Casting Materials
- For PSL 1, all accessible wetted surfaces and all accessible sealing surfaces for one casting
from each heat lot shall be examined by liquid penetrant or magnetic particle methods
after final heat-treatment and final machining operations.
- For PSL 2 and PSL 3, all accessible wetted surfaces and all accessible sealing surfaces of
each finished part shall be examined by liquid penetrant or magnetic particle methods
after final heat-treatment and final machining operations.
- For PSL 3, additionally all accessible surfaces of each finished part shall be inspected.
Surface NDE shall be performed on all surfaces prepared for “weld metal overlay”.
Forging Materials
- For PSL 2, PSL 3, and PSL 4, all accessible wetted surfaces and all accessible sealing surface
of each finished part shall be examined by liquid penetrant or magnetic particle methods
after final heat-treatment and final machining operations.
- For PSL 3 and PSL 4, additionally all accessible surfaces of each finished part shall be
inspected. Surface NDE shall be performed on all surfaces prepared for “weld metal
overlay”.
For ASTM E709, The following is acceptance criteria shall apply for examination:
-no relevant indication with a major dimension equal to or greater than 5mm (3/16 in);
-no more than ten relevant indications in any continuous 40 cm2 (6 in2) area;
-no four (or more) relevant rounded indications in a line separated by less than 1.6mm
(1/16 in.) (edge-to-edge);
-no relevant indication in pressure-contact sealing surfaces.
B. Nonferromagnetic Materials
Casting Materials
- For PSL 1, all accessible wetted surfaces and all accessible sealing surfaces for one casting
from each heat lot shall be examined by liquid penetrant after final heat-treatment and
final machining operations.
- For PSL 2 and PSL 3, all accessible wetted surfaces and all accessible sealing surfaces of
each finished part shall be examined by liquid penetrant after final heat-treatment and
final machining operations.
- For PSL 3, additionally all accessible surfaces of each finished part shall be inspected.
Surface NDE shall be performed on all surfaces prepared for “weld metal overlay”.
Forging Materials
- For PSL 2, PSL 3, and PSL 4, all accessible wetted surfaces and all accessible sealing surface
of each finished part shall be examined by liquid penetrant methods after final heat-
treatment and final machining operations.
- For PSL 3 and PSL 4, additionally all accessible surfaces of each finished part shall be
inspected. Surface NDE shall be performed on all surfaces prepared for “weld metal
overlay”.
- For PSL 3 and PSL 4 (casting and forgings) as far as practical, the entire volume of each part
shall be volumetrically inspected (radiography or ultrasonic) after heat-treatment for
mechanical properties and prior to machining operations that limit effective interpretation
of the result of the examination. For quench-and-tempered products, the volumetric
inspection shall be performed after heat-treatment for mechanical properties exclusive of
stress-relief treatments or re-tempering to reduce hardness.
- For PSL 2 and PSL 3 castings, ultrasonic examinations of castings shall be performed in
accordance with the flat-bottom hole procedure specified in ASTM A609 (except that the
immersion may be used) and ASTM E428.
- For PSL 3 and PSL 4 forgings, ultrasonic examination of hot worked parts shall be performed
in accordance with the flat-bottom hole procedures specified in ASTM A388/388M (except
that the immersion method may be used) and ASTM E428.
For PSL 2, PSL 3, and PSL 4, radiographic examination of hot worked parts or castings shall be
performed in accordance with methods specified in ASME BPVC, Section V, Article 2 (or
equivalent) with a minimum sensitivity of 2% (2-2T). Both X-ray and gamma-ray sources shall
be acceptable within the inherent thickness range limitation of each.
Radiographic examination acceptance criteria for PSL 2 and PSL 3, the following acceptance
criteria shall apply:
Forged Parts
- No cracks, laps or burst;
- No elongated indication with a length greater than that given in Table 23;
Table 23-Maximum Length of Elongated Indication
- No group of indications in a line that have an aggregate length greater than T in a length
12T.
Cast Parts
- ASTM E186;
- ASTM E280;
- ASTM E466;
- Maximum defect classification as follows:
9. Marking
Choke shall be marked with their nominal size and maximum orifice as specified in Section
3.3. For Ring Grooves, type 6B flanged and studded connectors shall be marked “R XX” where
“XX” is the ring groove number. Type 6BX flanged and studded connectors shall be marked “BX
YYY”, where “YYY” is the ring groove number.
Choke beans shall be marked as specified in Table 25, with the orifice size and the
manufacturer’s name or mark on its outside diameter or end.
- All equipment shall be drained and lubricated after testing and prior to storage or
shipment.
- Corrosion protection shall be applied to exposed (bare) metallic surfaces of steels with less
than 15% chromium on flange faces, exposed stems and internal surfaces of the
equipment using the manufacturer’s documented requirements. Corrosion protection
provided by a corrosion inhibitor shall resist runoff at temperature less than 50 oC (125 oF).
- Exposed sealing surfaces and seals shall be protected from damage or deterioration for
shipping.
- Loose ring gaskets shall be boxed or wrapped during shipping and storage.
- The manufacturer shall provide to the purchaser suitable drawings and instructions
concerning field assembly and maintenance, if requested.
- The manufacturer’s written specified requirements for nonmetallic seals that are not
assembled into equipment shall include the following minimum provisions:
d. Age control;
e. Indoor storage;
f. Maximum temperature no to exceed 49oC (120 oF);
g. Protected from direct natural light;
h. Stress conditions (packaging and storage of nonmetallic seals shall not impose tensile
or compressive stresses sufficient to cause permanent deformation).
i. Stored away from contact with liquids;
j. Protected from ozone and radiographic damage.
ATTACHMENT A
ATTACHMENT B