SA-995
1575
Copyright ASME International
Provided by IHS under license with ASME Licensee=Occidental Chemical Corp New sub account/5910419101
No reproduction or networking permitted without license from IHS Not for Resale, 02/25/2008 08:15:53 MST
,,,,``,`,`,,,`,,``,,-`-`,,`,,`,`,,`---
SA-995 2007 SECTION II, PART A
5.1.4 Grade of steel, 11.2 The composition of the deposited weld metal may
5.1.5 Supplementary requirements including accept- be similar to that of the casting or may be suitably alloyed
ance criteria, to achieve the desired corrosion resistance and mechanical
properties.
5.1.6 Additional requirements.
11.3 Weld repairs shall be subject to the same quality
standards as used to inspect the castings.
6. Process
6.1 The steel shall be made by the electric furnace 11.4 When postweld heat treatment is believed neces-
process with or without separate refining. sary for adequate corrosion resistance or impact toughness,
Supplementary Requirement S11, Post Weld Heat Treat-
ment, shall be included in the purchase order.
7. Heat Treatment
7.1 All castings shall be heat treated in accordance
with Table 1. 12. Post Weld Heat Treatment After Major Weld
Repair
12.1 Weld repairs shall be considered major in the the
8. Chemical Composition case of a casting that has leaked on hydrostatic testing, or
8.1 The steel shall conform to the requirements as to when the depth of the cavity after preparation for repair
chemical composition prescribed in Table 2. exceeds 20% of the actual wall thickness or 1 in. [25 mm],
whichever is smaller, or when the extent of the cavity
exceeds approximately 10 in.2 [65 cm2]. All other weld
9. Tensile Properties repairs shall be considered minor.
9.1 One tension test shall be made from each heat and
shall conform to the requirements as to tensile properties 12.2 Castings shall be heat-treated after major weld
prescribed in Table 3. repairs. Heat treatment after minor weld repairs is not
required except upon agreement between the manufacturer
and the purchaser.
10. Quality
12.3 Post weld heat treatment shall be in accordance
10.1 When additional inspection is desired, Supplemen-
with Table 1.
tary Requirements S5, S6, and S10 may be ordered.
1576
Copyright ASME International
Provided by IHS under license with ASME Licensee=Occidental Chemical Corp New sub account/5910419101
No reproduction or networking permitted without license from IHS Not for Resale, 02/25/2008 08:15:53 MST
2007 SECTION II, PART A SA-995
TABLE 1
HEAT TREATMENT REQUIREMENTS
Grade Heat Treatment
TABLE 2
CHEMICAL REQUIREMENTS
TABLE 3
TENSILE REQUIREMENTS
Grade 1B 2A 3A 4A 5A 6A
Type 25Cr-5Ni-Mo-Cu-N 24Cr-10Ni-Mo-N 25Cr-5Ni-Mo-N 22Cr-5Ni-Mo-N 25Cr-7Ni-Mo-N 25Cr-7Ni-Mo-N
Tensile strength, ksi [MPa], min 100 [690] 95 [655] 95 [655] 90 [620] 100 [690] 100 [690]
Yield strength (0.2% offset), ksi 70 [485] 65 [450] 65 [450] 60 [415] 75 [515] 65 [450]
[MPa], min
Elongation in 2 in. [50 mm], 16 25 25 25 18 25
%, minA
A
When ICI test bars are used in tensile testing as provided for in this specification, the gage length to reduced section diameter ratio shall
be 4:1.
1577
Copyright ASME International
Provided by IHS under license with ASME Licensee=Occidental Chemical Corp New sub account/5910419101
No reproduction or networking permitted without license from IHS Not for Resale, 02/25/2008 08:15:53 MST
SA-995 2007 SECTION II, PART A
SUPPLEMENTARY REQUIREMENTS
The following supplementary requirements shall not apply unless specified in the purchase
order. A list of standardized supplementary requirements for use at the option of the
purchaser is included in Specification A 703 /A 703M. Those which are ordinarily consid-
ered suitable for use with this specification are given below. Others enumerated in Specifica-
tion A 703 /A 703M may be used with this specification upon agreement between the
manufacturer and purchaser.
S11. Post Weld Heat Treatment S51. Prior Approval of Weld Material
S11.1 Castings shall be given a post weld solution heat S51.1 The purchaser must give approval of all weld
treatment in accordance with Table 1. filler materials to be used prior to any weld repairs.
1578
Copyright ASME International
Provided by IHS under license with ASME Licensee=Occidental Chemical Corp New sub account/5910419101
No reproduction or networking permitted without license from IHS Not for Resale, 02/25/2008 08:15:53 MST