  • Properties: Test Conditions Units Properties Test Conditions Units Typical Values

    Uploaded by

    zaher
    28 views1 page
    This document provides information on TML, a transparent BOPP film for label applications. It has good antistatic properties and is suitable for pressure sensitive and cut and stack applications. The document lists typical property values for the film's thickness, unit weight, yield, haze, gloss, tensile strength, elongation at break, heat seal temperature, and more. It also notes that the test results provided are for standard production samples but may vary under actual use conditions.

    Original Description:

    Original Title

    tml-tds

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on TML, a transparent BOPP film for label applications. It has good antistatic properties and is suitable for pressure sensitive and cut and stack applications. The document lists typical property values for the film's thickness, unit weight, yield, haze, gloss, tensile strength, elongation at break, heat seal temperature, and more. It also notes that the test results provided are for standard production samples but may vary under actual use conditions.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Flag for inappropriate content
    Download as pdf or txt
    28 views1 page

    Properties: Test Conditions Units Properties Test Conditions Units Typical Values

    Uploaded by

    zaher
    This document provides information on TML, a transparent BOPP film for label applications. It has good antistatic properties and is suitable for pressure sensitive and cut and stack applications. The document lists typical property values for the film's thickness, unit weight, yield, haze, gloss, tensile strength, elongation at break, heat seal temperature, and more. It also notes that the test results provided are for standard production samples but may vary under actual use conditions.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Flag for inappropriate content
    Download as pdf or txt
    of 1

    TML

    Both sides treated, transparent BOPP film for label applications.

    Properties
    • Suitable for cut&stack and roll-fed applications
    • Good antistatic properties
    • Suitable for pressure sensitive applications.

    Applications
    Designed especially for cut and stack and all general labeling applications.

    PROPERTIES TEST CONDITIONS UNITS


    UNITS TYPICAL VALUES

    µ 35 40 50 55 58
    THICKNESS ......
    Gauge 140 160 200 220 232

    THICKNESS TOLERANCE …… % 5

    UNIT WEIGHT ASTM D 2673 g / m² 32 36,4 45,5 50 52,8

    YIELD ASTM D 2673 m² / kg 31 27,5 22 20 19

    HAZE ASTM D 1003 % < 1.8

    GLOSS ASTM D 2457 % > 85.0

    OPTICAL DENSITY MACBETH ..... …..

    B/B* < 0.35


    COEFFICIENT OF FRICTION* ASTM D 1894 .....
    B/M* < 0.25
    MD 120 ± 20
    TENSILE STRENGTH ASTM D 882 N/mm²
    TD 280 ± 30
    MD 190 ± 40
    ELONGATION AT BREAK ASTM D 882 %
    TD 45 ± 10

    HEAT SEAL TEMPERATURE 3 Bar / 0.5 Sec °C …..

    SEAL STRENGTH 130°C / 3 Bar / 0.5 Sec N / 15 mm …..


    ASTM F 1249
    WVTR 38°C / 90% RH
    g / m² / day .....

    TREATMENT LEVEL ASTM D 2578 dyne / cm ≥ 38 (both)


    MD ≤ 5.0
    HEAT SHRINKAGE 130°C / 7 mİn %
    TD ≤ 3.0

    *B : Back side *All COF values are dynamic results


    *M : Metal

    The above information is the result of laboratory test which are applied on samples from standart production.Since the varying conditions
    under which our products used are beyond our control all of the above results are without guarantee and warranty.

    POLİBAK Plastik Film San. ve Tic.A.Ş. AOSB Izmir-TURKIYE


    Phone : +90 232 3767970 Fax : +90 232 3767730
    E-Mail : [email protected] www.polibak.com.tr Reference No : 2015/01/04