Abstract
In this work the adsorption of phenol solutions onto activated carbon Calgon F400 has been studied. The carbon was modified by acid treatment,
using soxhlet extraction with hydrochloric acid 2N for 120 cycles. The treatment did not affect significantly the surface area of the activated
carbon but affected significatively the different functional groups, and thus its adsorption properties. Tóth model reproduced satisfactorily the
experimental isotherm data and an adsorption enthalpy of −17.9 kJ mol−1 was found, which indicates that the process is exothermic. The pH
affected significatively to the adsorption process and an empirical polynomial equation was able to reproduce maximum capacity as a function
of pH. The isotherms obtained at pH 3 and 7 are very similar and showed a higher adsorption capacity compared with that obtained at pH
13. The use of phosphate buffer solutions decreased the maximum phenol adsorption capacity, due to the competitive adsorption between the
phenol and phosphates. Finally, it was demonstrated that the acid treatment introduced chloride ions into the carbon, giving it properties of ion
exchanger.
© 2005 Elsevier B.V. All rights reserved.
0304-3894/$ – see front matter © 2005 Elsevier B.V. All rights reserved.
doi:10.1016/j.jhazmat.2005.09.037
244 P. Cañizares et al. / Journal of Hazardous Materials B131 (2006) 243–248
Table 1
Activated carbon characterization
To take into account the effect of temperature in both models,
it can be assumed that the maximum adsorption capacity (in both
Carbon Ratios (%) BET surface Micropore volume models) and the dissociation constant (in the Tóth model) do not
area (m2 g−1 ) (cm3 g−1 )
O/C Al/C Si/C depend on the temperature and that the equilibrium constant can
F400 DW 3.60 0.98 1.00 1026.5 0.423
be related with temperature through the following equation, in
F400 AW 5.40 0.31 0.90 1000.9 0.417 which H is the heat of adsorption and S is the entropy change
[26].
K1 or K = exp((S/R) − (H/RT ))
band of 3400 cm−1 in the F400 DW spectrum, indicates that
this carbon has hydroxyl functional groups. As can be observed Taking into account this, the three isotherms obtained were
in the F400 AW spectrum, this vibration disappears, indicating simultaneously fitted to one equilibrium equation using Lang-
that the acid treatment could have transformed these groups into muir equation or Tóth model and the thermodynamic expression
carboxylic, carbonyl, or ether groups because of the big vibra- for the equilibrium constant as a temperature function. A non-
tions that appeared at broad bands of 1200 and 950 cm−1 [23]. linear least-square method was used to estimate the parameters
It is also possible that with the acid treatment some chlorine (parameters of the equilibrium model and the thermodynamic
remained chemisorbed on the carbon surface as it is indicated values). Parameters obtained after this fitting procedure and the
by the micropore volume reduction [24]. determination coefficient (R2 ) for each isotherm model used
are summarized in Table 2. Experimental data and modeling
3.2. Effect of temperature results achieved with Tóth model for both carbons are shown in
Fig. 2.
Three adsorption isotherms (corresponding to 288.13, 298.13 As can be seen in Table 2, the Langmuir equation offers
and 308.13 K) of phenol onto both activated carbons used in this a poor fit of the experimental data for both types of carbons
work were obtained to study the effect of temperature. To avoid with very low regression coefficients. On the contrary, Tóth
the effect of pH, the liquid solution was buffered to pH 7.0 by equation reproduces them satisfactorily. It supports that the
means of a phosphate buffer solution. surfaces of the carbons are heterogeneous and contain dif-
In order to fit the experimental data, two models have been ferent functional groups. The important improvement in the
used in this work: the Langmuir and the Tóth models. Both regression coefficient obtained when Langmuir model is used
are widely used in literature to describe acceptably different to fit the experimental data of the carbon F400 AW, confirms
adsorption isotherms. the reduction of the heterogeneity with the acid treatment.
The Langmuir model describes satisfactorily monolayer The higher heterogeneity of the F400 DW is also observed in
adsorption processes [5,25]. It has two parameters: n∞ which is Fig. 2.
the total monolayer capacity and K that is the Langmuir equi- On the other hand, Fig. 2 shows that the adsorption equi-
librium constant: librium decreases as the temperature increases, indicating that
the adsorption phenomena is exothermic. The enthalpy val-
q = n∞ KC/(1 + KC) ues obtained for both models were similar, and lower than
40 kJ mol−1 (this value is considered to be the upper limit of
The Tóth model describes adequately heterogeneous systems
the enthalpy for physical adsorption in a general adsorption pro-
[5,26] and has three parameters: qm that represents the total
cess). These small values indicate that the adsorption of phenol
adsorption capacity, m the dissociation parameter, and K1 the
by F400 DW and F400 AW is a physical adsorption process
adsorption equilibrium constant:
[5,26].
q = qm C/(1/K1 + Cm )1/m According to the results obtained, although the shapes of the
isotherms are significatively different, both carbons present a
similar adsorption capacity. This indicates that the acid treatment
does not affect the adsorption capacity of the carbon although
Table 2
Adsorption parameters of F400 DW and F400 AW carbons at different
temperatures
Parameters F400 DW F400 AW
3.4. Role of the ion exchange in the overall adsorption Fig. 5. Isotherm of ion exchange for activated carbon F400 AW at T = 308.13 K,
process using the Langmuir type empirical equation.
Fig. 4 shows the dynamic response of an adsorption exper- In order to clarify the role of the activated carbon as ion
iment at anoxic conditions in which 3.0 g of activated carbon exchanger, different amounts of activated carbon F400 AW were
F400 AW are placed into 2.0 dm3 of a solution containing added to sodium hydroxide solutions (without phenol). In every
3000 ppm of phenol at natural pH. case it was observed that the pH decreases and the concen-
It can be observed a decrease in the concentration of phenol tration of chloride ions increase, indicating an ion exchange
and an increase in the concentration of both H+ and Cl− ions. between hydroxyl and chloride ions. The following Langmuir-
This behaviour is obtained in all the experiments carried out at type empirical equation was used to model the experimental
natural pH. According to the equilibrium in solution for both data:
acid–base phenol and water, a decrease in the concentration of
phenol should deal to an increase in the pH, as the concentration YB∗ = XB
∗ ∗
/(R1 + (1 − R1 )XB )
of the acid (phenol) decreases in the bulk solution: where
− +
C6 H5 OH ⇔ C6 H5 O + H ∗
R1 = 1/KAB , XB = C∗ /CT , YB∗ = q∗ /n∞
II
H2 O ⇔ OH− + H+ where KAB is the separation factor. This equation has been suc-
cessfully applied in literature [28–31].
Thus, in order to justify the decrease in the pH and the appear-
The experimental data obtained for both ions in dissolu-
ance of chloride ions other processes must be considered. Taking
tion, were fitted to previous equation by nonlinear least-squares
into account that the charge balance must be accomplished, the
regression analysis. The values of n∞ II and KAB obtained were
increase in the concentration of H+ indicates that the phenolate
0.55 mol kg−1 and 5.91, respectively. The predicted isotherm is
and/or the OH− ions were exchanged by Cl− from the carbon:
plotted together with the experimental data in Fig. 5.
[C6 H5 O− ] + [Cl− ] + [OH− ] = [H+ ] As can be observed, the model fits well with the experimental
data. The dimensionless form of the isotherm allows to conclude
These observations can be justified taking into account that that ion exchange equilibrium is unfavorable for OH− and favor-
the acid treatment introduces chloride ions to the activated car- able for Cl− . As it was expected, the maximum capacity obtained
bon and this type of ions can be released from the solid phase by ion exchange (0.55 mol kg−1 ) is lower than the value obtained
by ion exchange. Then, it is possible that a high pH, the anionic by adsorption at lower pH values.
phenolate could be load to the carbon by ion exchange and that
this mechanism has an important role in the understanding of
the overall adsorption process at any pH. The higher adsorption 4. Conclusions
capacity at acidic pH values indicates that, the carbon prefers
neutral specie than ionic phenolate, but even at non alkaline From this work the following conclusions must be drawn:
pH the ion exchange process has to be considered to explain the
overall process as indicates the observed chloride release, which An acid treatment, using soxhlet extraction with hydrochloric
can not be justified only in terms of hydroxyl ion exchange. It acid 2N for 120 cycles, does not affect significantly to the
is also well known that at high initial concentration the control- surface area of the activated carbon but it affects significatively
ling step to mass transfer is the internal diffusion. Thus, the time to the different functional groups, and thus to the adsorption
required to achieve the equilibrium is high. properties.
248 P. Cañizares et al. / Journal of Hazardous Materials B131 (2006) 243–248
The adsorption of phenol by F400 DW and F400 AW is [11] M. Tomaszewska, S. Mozia, W. Morawski, Removal of organic matter by
an exothermic physical adsorption process. The enthalpy coagulation enhanced with adsorption on PAC, Desalination 162 (2004)
values obtained for both activate carbons were similar 79–87.
[12] T. Özbelge, Ö. Özbelge, S. Baskaya, Removal of phenolic compounds
(−17.9 kJ mol−1 ). Tóth model reproduces satisfactorily the from rubber-textile wastewaters by physicochemical methods, Chem.
experimental isotherm data. Eng. Process. 41 (2002) 719–730.
The isotherms corresponding to pH 3 and 7 are very similar and [13] Z. Lazarova, S. Boyadzhieva, Treatment of phenol-containing aqueous
show a higher adsorption capacity compared with that obtained solutions by membrane-based solvent extraction in coupled ultrafiltration
at pH 13. The effect of the pH on the adsorption capacity can be modules, Chem. Eng. J. 100 (2004) 129–138.
[14] W. Kujawski, A. Warszawski, W. Ratajczak, T. Porebski, W. Capala, I.
satisfactorily modeled using an empirical polynomial equation. Ostrowska, Removal of phenol from wastewater by different separation
A higher adsorption capacity is observed in non-buffered techniques, Desalination 163 (2004) 287–296.
isotherms. This can be interpreted in terms of the competi- [15] P. Cañizares, J.A. Domı́nguez, M.A. Rodrigo, J. Villaseñor, J. Rodrı́guez,
tive adsorption of phenol and the phosphates contained in the Effect of the current intensity in the electrochemical oxidation of aque-
buffer system. ous phenol wastes at an activated carbon and steel electrode, Ind. Eng.
Chem. Res. 38 (1999) 3779–3785.
The acid treatment introduced chloride ions into the carbon, [16] P. Cañizares, F. Martı́nez, J. Garcı́a-Gómez, M.A. Rodrigo, Combined
giving it properties of ion exchanger. electrooxidation and assisted electrochemical coagulation of aqueous
Ion exchange must be considered in the understanding of the phenol wastes, J. Appl. Electrochem. 32 (2002) 1241–1246.
overall adsorption process of phenol onto activated carbon. It [17] G. Bercic, A. Pintar, J. Levec, Desorption of phenol from activated
helps to justify the changes in the pH observed during this carbon by hot water regeneration. Desorption isotherms, Ind. Eng. Chem.
Res. 35 (1996) 4619–4625.
process. [18] J. Kilduff, C. King, Effect of carbon adsorbent surface properties on
Ion exchange isotherm allows to conclude that this carbon the uptake and solvent regeneration of phenol, Ind. Eng. Chem. Res. 36
prefers the Cl− than OH− ions. (1997) 1603–1613.
[19] M. Franz, H. Arafat, N. Pinto, Effect of chemical surface heterogeneity
on the adsorption mechanism of dissolved aromatics on activated carbon,
Acknowledgments
Carbon 38 (2000) 1807–1819.
[20] A. Uribe, P. Bishop, N. Pinto, The influence of pH and temperature
This work was supported by the Ministerio de Ciencia y Tec- changes on the adsorption behavior of organophilic clays used in the
nologı́a (MCT), Spain and by the European Union through the stabilization/solidification of hazardous waste, J. Environ. Eng. Res. 1
Project REN2001-0560. (2002) 123–133.
[21] A. Arafat, M. Franz, N. Pinto, Effect of salt on the mechanism of adsorp-
tion of aromatics on activated carbon, Langmuir 15 (1999) 5997–6003.
References [22] N. Abuzald, G. Nakhla, Dissolved oxygen effects on equilibrium and
kinetics of phenolics adsorption by activated carbon, Environ. Sci. Tech-
[1] L. Barros, G. Macedo, W. Netto, M. Becerra, Phenol removal by bio- nol. 28 (1994) 216–221.
logical and photochemical–biological processes, Afinidad 60 (2003) [23] M. Jung, K. Ahn, Y. Lee, K. Kim, J. Rhee, J. Park, K. Paeng, Adsorption
568–572. characteristics of phenol and chlorophenols on granular activated carbons
[2] C. Fan, Y. Sun, Y. Min, X. Hao, X. Li, F. Li, Photocatalytic degradation (GAC), Microchem. J. 70 (2001) 123–131.
of phenol in aqueous solution using TiO2 /Ti thin film photocatalyst, [24] C. Moreno-Castilla, F. Carrasco-Marı́n, F. Maldonado-Hódar, J. Rivera-
Trans. Nonferrous Met. Soc. Chin. 13 (2003) 1008–1012. Utrilla, Effects of non-oxidant and oxidant acid treatments on the surface
[3] J. Wu, K. Rudy, J. Sapark, Oxidation of aqueous phenol by ozone and properties of an activated carbon with very low ash content, Carbon 36
peroxidase, Adv. Environ. Res. 4 (2000) 339–346. (1998) 145–151.
[4] S. Al-Asheh, F. Banat, L. Abu-Aitah, Adsorption of phenol using differ- [25] I. Langmuir, Chemical reactions at low pressure, J. Am. Chem. Soc. 37
ent types of activated bentonites, Sep. Purif. Technol. 33 (2003) 1–10. (1915) 1139.
[5] J. Chern, Y. Chien, Adsorption of nitrophenol onto activated carbon: [26] J. Chern, C. Wu, Desorption of dye from activated carbon beds:
isotherms and breakthrough curves, Water Res. 36 (2002) 647–655. effects of temperature, pH, and alcohol, Water Res. 35 (2001) 4159–
[6] V. Vinod, T. Anirudhan, Effect of experimental variables on phenol 4165.
adsorption on activated carbon prepared from coconut husk by single- [27] A. Heinen, J. Peters, H. Bekkum, Competitive adsorption of water and
steam pyrolysis: mass transfer process and equilibrium studies, J. Sci. toluene on modified activated carbon supports, Appl. Catal. A: Gen.
Ind. Res. 61 (2002) 128–138. 194–195 (2000) 193–202.
[7] R. Juang, F. Wu, R. Tseng, Adsorption isotherms of phenolic compounds [28] J. Valverde, A. de Lucas, M. Carmona, M. González, J. Rodrı́guez,
from aqueous solutions onto activated carbon fibers, J. Chem. Eng. Data Equilibrium data of the exchange of Cu2+ , Cd2+ and Zn2+ ions for H+
41 (1996) 487–492. on the cationic exchanger Lewatit TP-207, J. Chem. Technol. Biotechnol.
[8] P. Cañizares, J. Lobato, J. Garcı́a-Gómez, M.A. Rodrigo, Combined 79 (2004) 1371–1375.
adsorption and electrochemical processes for the treatment of acidic [29] D. Bilba, N. Bilba, M. Albu, Kinetics of cadmium ion sorption on ion
aqueous phenol wastes, J. Appl. Electrochem. 34 (2004) 111–117. exchange and chelating resins, Solvent Extract. Ion Exchange 17 (1999)
[9] C. Leng, N. Pinto, An investigation of the mechanisms of chemi- 155–1569.
cal regeneration of activated carbon, Ind. Eng. Chem. Res. 35 (1996) [30] A. Fernández, M. Dı́az, A. Rodrı́gues, Kinetic mechanisms in ion
2024–2031. exchange processes, Chem. Eng. J. 57 (1995) 17–25.
[10] P. Cañizares, F. Martı́nez, M. Dı́az, J. Garcı́a-Gómez, M.A. Rodrigo, [31] E. Costa, A. De Lucas, M.E. González, Ion-exchange. Determination
Electrochemical oxidation of aqueous phenol wastes using active and of interdiffusion coefficients, Ind. Eng. Chem. Fundam. 23 (1984) 400–
non-active electrodes, J. Electrochem. Soc. 149 (2002) 118–124. 405.