Hydranautics
Hydranautics
27
Note: The Composite Polyamide type of RO membrane elements may not be exposed to
chlorinated water under any circumstances. Any such exposure will cause irreparable
damage to the membrane. Absolute care must be taken following any disinfection of piping
or equipment or the preparation of cleaning or storage solutions to ensure that no trace of
chlorine is present in the feedwater to the RO membrane elements. If there is any doubt
about the presence of chlorine, perform chemical testing to make sure. Neutralize any
chlorine residual with a sodium bisulfite solution, and ensure adequate mixing and contact
time to accomplish complete dechlorination. Dosing rate is 1.8 to 3.0 ppm sodium bisulfite
per 1.0 ppm of free chlorine.
Note: It is recommended that all RO membrane cleaning operations should be closely coordinated
with Hydranautics during the RO membrane element warranty period. Hydranautics field
service personnel are available to be on site for cleaning assistance, should the need arise.
Please contact Hydranautics for current charges for this service.
Note: The use of cationic surfactants should be avoided in cleaning solutions, since irreversible
fouling of the membrane elements may occur. In regards to any proprietary chemicals,
Hydranautics position is that the vendor of these proprietary chemicals is responsible for
guaranteeing their product is compatible with Hydranautics membranes. Thus, the chemical
vendor would be solely responsible for the financial and other impacts a negative interaction
may have.
If additional information is needed, please contact the Technical Services Department at:
HYDRANAUTICS
401 Jones Rd.
Oceanside, CA 92058
Tel# (760) 901-2500
Fax# (760) 901-2578
e-mail: [email protected]
Internet: www.membranes.com
TSB107.27 Page 2
RO Membrane Fouling and Cleaning
During normal operation over a period of time, RO membrane elements are subject to fouling by
suspended or sparingly soluble materials that may be present in the feedwater. Common examples of
foulants are:
• Calcium carbonate scale
• Sulfate scale of calcium, barium or strontium
• Metal oxides (iron, manganese, copper, nickel, aluminum, etc.)
• Polymerized silica scale
• Inorganic colloidal deposits
• Mixed inorganic/organic colloidal deposits
• NOM organic material (Natural Organic Matter)
• Man-made organic material (e.g. antiscalant/dispersants, cationic polyelectrolytes)
• Biological (bacterial bioslime, algae, mold, or fungi)
The nature and rapidity of fouling depends on a number of factors, such as the quality of the feedwater and
the system recovery rate. Typically, fouling is progressive, and if not controlled early, will impair the RO
membrane element performance in a relatively short time. Cleaning should occur when the RO shows
evidence of fouling, just prior to a long-term shutdown, or as a matter of scheduled routine maintenance.
The elements shall be maintained in a clean or “nearly clean” condition to prevent excessive fouling by the
foulants listed above. Under normal circumstances, some fouling is allowed as long as the normalized
parameters listed below are not allowed to deviate more than the “Typical” values . In specific cases, such
as industrial and municipal wastewaters where fouling is more extreme, it may be necessary to allow for
greater deviation in normalized parameters as listed under “High Fouling”. In such extreme cases, the
deviation in normalized parameters should be based on the stabilized performance which may occur after a
week of operation.
Cleaning should be carried out as soon as is practical to maintain the elements in a clean or “nearly clean”
condition. Effective cleaning is evidenced by the return of the normalized parameters to their initial, Start-
up, value. In the event you do not normalize your operating data, the above values still apply if you do not
have major changes in critical operating parameters.
Of special note are wastewaters which have high concentrations of soluble organic compounds. Historical
studies have shown that it is common to have an initial sharp drop in normalized flow and decrease of salt
passage, which are characterized by 10-20% decrease over a 2-4 week time period.1 After this initial rapid
decline, the normalized flow will decline marginally over the next 6-12 months. Reasearch has shown that
the initial drop is due to the adsorption of organics onto the membrane surface. Once the membrane
surface is saturated with the mono-layer of organic, this effect no longer has significant impact on
membrane performance. Aggressive cleaning can recover much of this loss, but studies show the gain is
only short-lived and the system will quickly return to its previous performance. Thus, it is recommended
that decisions to clean be based on the decline rate after this initial stabilization.
The operating parameters that have to stay constant are permeate flow, permeate back-pressure,
recovery, temperature, and feed TDS. If these operating parameters fluctuate, then it is highly
recommended that you normalize the data to determine if fouling is occurring or if the RO is actually
operating normally based on the change in a critical operating parameter. Hydranautics offers a free
normalization software program called ROData, which can be downloaded from our web site at
www.membranes.com.
Monitoring overall plant performance on a regular basis is an essential step in recognizing when membrane
elements are becoming fouled. Performance is affected progressively and in varying degrees, depending
on the nature of the foulants. Table 1 “RO Troubleshooting Matrix” provides a summary of the expected
effects that common foulants have on performance.
RO cleaning frequency due to fouling will vary by site. A rough rule of thumb as to an acceptable cleaning
frequency is once every 3 to 12 months. If you have to clean more than once a month, you should be able
to justify further capital expenditures for improved RO pretreatment or a re-design of the RO operation. If
the cleaning frequency is every one to three months, you may want to focus on improving the operation of
your existing equipment but further capital expenditure may be harder to justify.
It is important to clean the membranes when they are only lightly fouled, not heavily fouled. Heavy fouling
can impair the effectiveness of the cleaning chemical by impeding the penetration of the chemical deep into
the foulant and in the flushing of the foulant out of the elements. If normalized membrane performance
drops 30 to 50%, it may be impossible to fully restore the performance back to baseline conditions.
When inorganic or polyelectrolyte coagulants are used in the pretreatment process, there can often be
incomplete reaction of the coagulant and thus insufficient formation of a filterable floc. The user should
ensure that excessive amounts of coagulant are not fed to the RO system, as it can lead to fouling.
Polyelectrolyte fouling can often be very difficult to remove and result in higher than expected feed
pressure. Excessive amounts of inorganic coagulant can be measured by using SDI filter equipment. In
the case of iron, the iron on the SDI filter pad should typically be 3 µg/pad and never above 5 µg/pad. In
regards to polymer coagulants, the user should discuss the concern with their chemical supplier and have
them ensure that the chemical will not adversely affect the membrane.
In addition to the use of turbidity and SDI, particle counters are also very effective to accurately measure
the suitability of the feedwater for NF/RO elements. The measure of particles greater than 2 microns in
size should be < 100 particles per millilitre.
One RO design feature that is commonly overlooked in reducing RO cleaning frequency is the use of RO
permeate water for flushing foulants from the system. Soaking the RO elements during standby with
permeate can help dissolve scale and loosen precipitates, reducing the frequency of chemical cleaning.
What you clean for can vary site by site depending on the foulant. Complicating the situation frequently is
that more than one foulant can be present, which explains why cleanings frequently require a low pH and
high pH cleaning regimen.
Note: The membrane elements shall not be exposed to feed water containing oil, grease, or other foreign
matter which proves to chemically or physically damage the integrity of the membrane.
TSB107.27 Page 4
Table 1: RO Troubleshooting Matrix
(Pressure Drop is defined as the Feed pressure minus the Concentrate pressure)
Calcium Carbonate Scale: Calcium carbonate is a mineral scale and may be deposited from almost
any feedwater if there is a failure in the antiscalant/dispersant addition system or in the acid injection pH
control system that results in a high feedwater pH. An early detection of the resulting calcium carbonate
scaling is absolutely essential to prevent the damage that crystals can cause on the active membrane
layers. Calcium carbonate scale that has been detected early can be removed by lowering the feedwater
pH to between 3.0 and 5.0 for one or two hours. Longer resident accumulations of calcium carbonate scale
can be removed by a low pH cleaning with a citric acid solution.
Calcium, Barium & Strontium Sulfate Scale: Sulfate scale is a much “harder” mineral scale than
calcium carbonate and is harder to remove. Sulfate scale may be deposited if there is a failure in the
antiscalant/dispersant feed system or if there is an over feed of sulfuric acid in pH adjustment. Early
detection of the resulting sulfate scaling is absolutely essential to prevent the damage that crystals can
cause on the active membrane layers. Barium and strontium sulfate scales are particularly difficult to
remove as they are insoluble in almost all cleaning solutions, so special care should be taken to prevent
their formation.
Calcium Phosphate Scale: This scale is particularly common in municipal waste waters and polluted
water supplies which may contain high levels of phosphate. This scale can generally be removed with
acidic pH cleaners. Calcium phosphate scaling potential is currently modelled in our IMSD software. As a
rule of thumb, contact Hydranautics technical department if phosphate levels in the feed are 5 ppm or
higher.
Metal Oxide/Hydroxide Foulants: Typical metal oxide and metal hydroxide foulants are iron, zinc,
manganese, copper, aluminum, etc. They can be the result of corrosion products from unlined pipes and
tanks, or result from the oxidation of the soluble metal ion with air, chlorine, ozone, potassium
permanganate, or they can be the result of a pretreatment filter system upset that utilizes iron or aluminum-
based coagulant aids.
Polymerized Silica Coating: A silica gel coating resulting from the super-saturation and polymerization
of soluble silica can be very difficult to remove. It should be noted that this type of silica fouling is different
from silica-based colloidal foulants, which may be associated with either metal hydroxides or organic
matter. Silica scale can be very difficult to remove by traditional chemical cleaning methods. Contact
Hydranautics technical department if the traditional methods are unsuccessful. There does exist harsher
cleaning chemicals, like ammonium biflouride, that have been used successfully at some sites but are
considered rather hazardous to handle and can damage equipment.
Colloidal Foulants: Colloids are inorganic or mixed inorganic/organic based particles that are
suspended in water and will not settle out due to gravity. Colloidal matter typically contains one or more of
the following major components: iron, aluminum, silica, sulfur, or organic matter.
Dissolved NOM Organic Foulants: The sources of dissolved NOM (Natural Organic Matter) foulants
are typically derived from the decomposition of vegetative material into surface waters or shallow wells.
The chemistry of organic foulants is very complex, with the major organic components being either humic
acid or fulvic acid. Dissolved NOMs can quickly foul RO membranes by being absorbed onto the
membrane surface. Once absorption has occurred, then a slower fouling process of gel or cake formation
starts. It should be noted that the mechanism of fouling with dissolved NOM should not be confused with
the mechanism of fouling created by NOM organic material that is bound up with colloidal particles.
Microbiological Deposits: Organic-based deposits resulting from bacterial slimes, fungi, molds, etc.
can be difficult to remove, particularly if the feed path is plugged. Plugging of the feed path makes it
difficult to introduce and distribute the cleaning solutions. To inhibit additional growth, it is important to
clean and sanitize not only the RO system, but also the pretreatment, piping, dead-legs, etc. The
membranes, once chemically cleaned, will require the use of a Hydranautics approved biocide and an
extended exposure requirement to be effective. For further information on biocides, refer to Hydranautics
TSB107.27 Page 6
Technical Service Bulletin TSB-110 “Biocides for Disinfection and Storage of Hydranautics Membrane
Elements”.
There are a number of factors involved in the selection of a suitable cleaning chemical (or chemicals) and
proper cleaning protocol. The first time you have to perform a cleaning, it is recommended to contact the
manufacturer of the equipment, the RO element manufacturer, or a RO specialty chemical and service
supplier. Once the suspected foulant(s) are identified, one or more cleaning chemicals will be
recommended. These cleaning chemical(s) can be generic or can be private-labeled proprietary
chemicals. Typically, the generic chemicals can be of technical grades and are available from local
chemical supply companies. The proprietary RO cleaning chemicals can be more expensive, but may be
easier to use and you cannot rule out the advantage of the intellectual knowledge supplied by these
companies. Some independent RO service companies can determine the proper chemicals and cleaning
protocol for your situation by testing at their facility a fouled element pulled from your system.
It is not unusual to use a number of different cleaning chemicals in a specific sequence to achieve the
optimum cleaning. Typically, a high pH cleaning is used first to remove foulants like oil or biological matter,
followed by a low pH cleaning to remove foulants like mineral scale or metal oxides/hydroxides fouling.
There are times that order of high and low pH cleaning solutions is reversed or one solution only is required
to clean the membranes. Some cleaning solutions have detergents added to aid in the removal of heavy
biological and organic debris, while others have a chelating agent like EDTA added to aid in the removal of
colloidal material, organic and biological material, and sulfate scale. An important thing to remember is that
the improper selection of a cleaning chemical, or the sequence of chemical introduction, can make the
foulant worse.
Hydranautics recommends that the membrane system operator thoroughly investigate the signs of fouling
before they select a cleaning chemical and a cleaning protocol. Some forms of fouling (iron deposits and
scaling commonly associated with well waters) may require only a simple low pH cleaning. However, for
most complex fouling phenomena, Hydranautics recommends the following sequence:
1. Flushing with permeate with addition of non oxidizing biocide (DBNPA or similar type) at the end of
the flushing
2. High pH CIP – Temperature versus pH as per recommendations in this TSB
3. Flushing with permeate until pH on the brine side is below pH 8.5
4. Low pH CIP
5. Acid flushing with permeate and non oxidizing biocide (DBNPA or similar type)
• If you are using a proprietary chemical, make sure the chemical has been qualified for use with your
Hydranautics membrane by the chemical supplier. The chemical supplier’s instructions should not be
in conflict with Hydranautics recommended cleaning parameters and limits listed in this Technical
Service Bulletin.
• If you are using generic chemicals, make sure the chemical has been qualified for use with your
Hydranautics membrane in this Technical Service Bulletin.
• Use the least harshest cleaning regimen to get the job done. This includes the cleaning parameters of
pH, temperature, and contact time. This will optimize the useful life of the membrane.
• Clean at the recommended target temperatures to optimize cleaning efficiency and membrane life.
• Use the minimal amount of chemical contact time to optimize membrane life.
• Be prudent in the adjustment of pH at the low and high pH range to extend the useful life of the
membrane. A “gentle” pH range is 4 to 10, while the harshest is 2 to 12.
• Oil and biologically -fouled membranes should not use a low pH clean-up first as the oil and biological
matter will congeal.
• Cleaning and flushing flows should usually be in the same direction as the normal feed flow to avoid
potential telescoping and element damage. In certain cases, where heavy feed end fouling has
occurred, reverse flow cleaning may be more effective in removing the foulant. In these cases, please
see TSB-125 “Reverse Direction Cleaning of RO Membrane Elements” and follow all recommended
guidelines to prevent element damage.
TSB107.27 Page 7
• When cleaning a multi-stage RO, the most effective cleaning is one stage at a time so cleaning flow
velocities can be optimized and foulants from upstream stages don’t have to pass through down-
stream stages.
• Flushing out detergents with higher pH permeate can reduce foaming problems.
• Verify that proper disposal requirements for the cleaning solution are followed.
• If your system has been fouled biologically, you may want to consider the extra step of introducing a
sanitizing biocide chemical before and after a successful cleaning. Biocides can be introduced
before and immediately after cleaning, periodically (e.g. once a week), or continuously during
service. You must be sure that the biocide is compatible with the membrane, does not create any
health risks, is effective in controlling biological activity, and is not cost prohibitive.
• For safety reasons, make sure all hoses and piping can handle the temperatures, pressures and pH’s
encountered during a cleaning.
• For safety reasons, always add chemicals slowly to an agitated batch of make-up water.
• For safety reason, always wear safety glasses and protective gear when working with chemicals.
• For safety reasons, don’t mix acids with caustics. Thoroughly rinse the 1st cleaning solution from the
RO system before introducing the next solution.
Table 2 lists the recommended generic chemical solutions for cleaning an RO membrane element based
on the foulant to be removed. See section below on Description of Cleaning Solutions and Table 4 for
cleaning solution formulations.
Important: It is recommended that the SDS of the cleaning chemicals be procured from the
chemical supplier and that all safety precautions be utilized in the handling and storage of
all chemicals.
Table 3 “Hydranautics Recipes for Cleaning Solutions” offers instructions on the volumes of bulk chemical
to be added to 100 U.S. gallons (379 liters) of make-up water. Prepare the solutions by proportioning the
amount of chemicals to the amount of make-up water to be used. Make-up water quality should be of RO
permeate or deionized (DI) quality, and be free of chlorine and hardness (See Table 4 below). Before
forwarding the cleaning solution to the membranes, it is important to thoroughly mix it, adjust the pH
according to the target pH, and stabilize the temperature at the target temperature. Unless otherwise
instructed, the cleaning design parameters are based on a chemical recirculation flow period of one hour
and an optional chemical soak period of one hour.
Table 5 “Hydranautics Maximum pH and Temperature Limits for Cleaning” highlights the maximum pH and
temperature limits for specific membranes, after which irreparable membrane damage can occur. A
suggested minimum temperature limit is 70 °F (21 °C), but cleaning effectiveness and the solubility of the
cleaning chemical is significantly improved at higher temperatures.
TSB107.27 Page 8
Note: The notation (w) denotes that the diluted chemical solution strength is based on the actual weight of
the 100% pure chemical or active ingredient.
Solution 1: This is a low pH cleaning solution of 2.0% (w) citric acid (C 6H8O7). It is useful in removing
inorganic scale (e.g. calcium carbonate, calcium sulfate, barium sulfate, strontium sulfate) and metal
oxides/hydroxides (e.g. iron, manganese, nickel, copper, zinc), and inorganic-based colloidal material.
Note: Citric acid is available as a powder.
Solution 2: This is a high pH cleaning solution (target pH of 10.0) of 2.0% (w) of STPP (sodium
tripolyphosphate) (Na5P3O10) and 0.8% (w) of Na-EDTA (sodium salt of ethylaminediaminetetraacetic acid).
It is specifically recommended for removing calcium sulfate scale and light to moderate levels of organic
foulants of natural origin. STPP functions as an inorganic-based chelating agent and detergent. Na-EDTA
is an organic-based chelating cleaning agent that aids in the sequestering and removal of divalent and
trivalent cations and metal ions. STPP and Na-EDTA are available as powders.
Solution 3: This is a high pH cleaning solution (target pH of 10.0) of 2.0% % (w) of STPP (sodium
tripolyphosphate) (Na5P3O10) and 0.025% (w) Na-DDBS (C6H5(CH2)12-SO3Na) (sodium salt of
dodecylbenzene sulfonate). It is specifically recommended for removing heavier levels of organic foulants
of natural origin. STPP functions as an inorganic-based chelating agent and detergent. Na-DDBS
functions as an anionic detergent.
Solution 4: This is a low pH cleaning solution (target pH of 2.5) of 0.5% (w) of HCL (hydrochloric) acid. It
is useful in removing inorganic scale (e.g. calcium carbonate, calcium sulfate, barium sulfate, strontium
sulfate and metal oxides/hydroxides (e.g. iron, manganese, nickel, copper, zinc) and inorganic-based
colloidal material. This cleaning solution is considered to be harsher than Solution 1. HCL acid, a strong
mineral acid, is also known as muriatic acid. HCL acid is available in a number of concentrations: (18 0
Baume = 27.9%), (20 0 Baume = 31.4%), (22 0 Baume = 36.0%).
Solution 6: This is a high pH cleaning solution (target pH of 11.5) of 0.1% (w) of NaOH (sodium
hydroxide) and 0.03% (w) of SDS (sodium dodecylsulfate). It is useful in the removal of organic foulants of
natural origin, colloidal foulants of mixed organic/inorganic origin, and biological material (fungi, mold,
slimes and biofilm). SDS is a detergent that is an anionic surfactant that will cause some foaming. This is
considered to be a harsh cleaning regimen. Note: Do not exceed maximum pH and temp limits for
specific elements. See Table 5.
Solution 7: This is a high pH cleaning solution (target pH of 11.5) of 0.1% (w) of NaOH (sodium
hydroxide). It is useful in the removal of polymerized silica. This is considered to be a harsh cleaning
regimen. Note: Do not exceed maximum pH and temp limits for specific elements. See Table 5.
Important: It is recommended that the SDS of the cleaning chemicals be procured from the
chemical supplier and that all safety precautions be utilized in the handling and storage of
all chemicals.
TSB107.27 Page 9
Table 3: Hydranautics Recipes for Cleaning Solutions
The quantities listed below are to be added to 100 U.S.gallons (379 liters) of dilution water. Dilution water
should meet the water quality standards in Table 4.
Cleaning Bulk Ingredients Quantity Target 1 Target 1
Solution pH Adjustment Temp.
1 Citric acid 17.0 pounds No pH adjustment is 104 °F (40 °C)
(as 100% powder) (7.7 kg) Required.
2 STPP 17.0 pounds Adjust to pH 10.0 with 104 °F (40 °C)
(sodium tripolyphosphate) (7.7 kg) sulfuric or hydrochloric
(as 100% powder) acid.
Na-EDTA 7.0 pounds
(Versene 220 or equal) (3.18 kg)
(as 100% powder)
3 STPP 17 pounds Adjust down to pH 10.0 104 °F (40 °C)
(sodium tripolyphosphate) (7.7 kg) with sulfuric or
(as 100% powder) hydrochloric acid.
Na-DDBS 0.21 pounds
Na-dodecylbenzene sulfonate (0.1 kg)
4 HCl acid 0.47 gallons Slowly adjust pH down 95 °F (35 °C)
(hydrochloric acid (1.78 liters) to 2.5 with HCL acid.
(as 220 Baume or 36% HCL) Adjust pH up with
sodium hydroxide.
5 Sodium hydrosulfite 8.5 pounds No pH adjustment is 95 °F (35 °C)
(as 100% powder) (3.86 kg) required.
6 NaOH (sodium hydroxide) Slowly adjust pH up to 86 °F (30 °C)
(as 100% powder) 0.83 pounds 11.5 with sodium
(0.38 kg) hydroxide. Adjust pH
(or as 50% liquid) 0.13 gallons down to 11.5 by adding
(0.49 liters) HCL acid.
SDS
(sodium dodecylsulfate) 0.25 pounds
(0.11 kg)
7 NaOH (sodium hydroxide) Slowly adjust pH up to 86 °F (30 °C)
(as 100% powder) 0.83 pounds 11.5 with sodium
(0.38 kg) hydroxide. Adjust pH
(or as 50% liquid) 0.13 gallons down to 11.5 by adding
(0.49 liters) HCL acid.
1 - Note: These pH and temperature targets are recommendations only. For maximum pH and temperature
Parameter Units
Chlorine Free 0 ppm
pH 6.5.-7.5
Hardness
RO permeate, DI, or Soft water < 30 ppm as CaCO3
Calcium (Ca) < 5 ppm
Iron (Fe) < 0.05 ppm
Manganese (Mn) < 0.02 ppm
Aluminium (Al) < 0.05 ppm
Copper (Cu) < 0.01 ppm
Cobalt (Co) < 0.01 ppm
Silica (SiO2)
Reactive silica < 10 ppm
Colloidal silica < 0.1 ppm
Particle Size < 5 microns
Turbidity < 0.5 NTU
Silt Density (SDI15) <1
Total Organic Carbon (TOC) < 1 ppm
Fats, Oils and Grease 0 ppm
TSB107.27 Page 11
Table 5a: Hydranautics pH and Temperature Limits for Cleaning Standard Membranes
Note: The above cleaning parameters denote the maximum temperature limits for a corresponding range of pH. Cleaning operations performed at the extremes
may result in a more effective cleaning, but can shorten the useful life of the membrane due to hydrolysis. To optimize the useful life of a membrane, it is
recommended to use the least harshest cleaning solutions and minimize the contact time whenever possible. The pH of the feed stream or cleaning solution
should be closely monitored and controlled. The pH meters used to measure and control pH should be regularly calibrated to ensure accuracy. It is typical to
re-circulate cleaning chemicals through the RO for 1 hour. At the pH limits shown above, cleaning exposure at temperatures less than 40 °C is limited to 60
minutes, at temperatures greater than 40 °C exposure is limited to 30 minutes. Extended soaking is possible, but at less aggressive pH levels.
TSB107.27 Page 12
Table 5b Hydranautics pH and Temperature Limits for Cleaning PRO Series Membranes
Note: The above cleaning parameters denote the maximum temperature limits for a corresponding range of pH. Cleaning operations performed at the extremes
may result in a more effective cleaning, but can shorten the useful life of the membrane due to hydrolysis. To optimize the useful life of a membrane, it is
recommended to use the least harshest cleaning solutions and minimize the contact time whenever possible. The pH of the feed stream or cleaning solution
should be closely monitored and controlled. The pH meters used to measure and control pH should be regularly calibrated to ensure accuracy. It is typical to
re-circulate cleaning chemicals through the RO for 1 hour. At the pH limits shown above, cleaning exposure at temperatures less than 40 °C is limited to 60
minutes, at temperatures greater than 40 °C exposure is limited to 30 minutes. Extended soaking is possible, but at less aggressive pH levels.
TSB107.27 Page 13
Note: In cases where the pressure drop in the membrane elements is excessively high, the cleaning
flow rates should be limited to 1/3 of the normal cleaning flow rate initially. This will help prevent
the element from telescoping and the feed spacer from migrating. As the foulant is removed, the
cleaning flow can slowly be brought up to normal cleaning flow rates. When flushing system before
and after cleaning flow rates should be half of values listed in Table 6.
The successful cleaning of an RO on-site requires a well designed RO cleaning skid. Normally this skid is
not hard piped to the RO skid and uses temporary hosing for connections. It is recommended to clean a
multi-stage RO one stage at a time to optimize cross-flow cleaning velocity. The source water for chemical
solution make-up and rinsing should be clean RO permeate or DI water and be free of hardness, transition
metals (e.g. iron), and chlorine (See Table 4 above). Components must be corrosion proof. Major cleaning
system components are:
• RO Cleaning Tank: This tank needs to be sized properly to accommodate the displacement of water
in the hose, piping, and RO elements. The Table 7 above denotes the amount of chemical solution
that needs to be made for a single RO element. The tank should be designed to allow 100 %
drainage, easy access for chemical introduction and mixing, a recirculation line from the RO Cleaning
Pump, proper venting, overflow, and a return line located near the bottom to minimize foam formation
when using a surfactant.
• RO Cleaning Pump: This pump needs to be sized to develop the proper cross-flow velocity to scrub
the membrane clean. The maximum recommended pressure is 60 psi (4 bar) at the inlet to the
pressure vessels to minimize the production of permeate during cleaning and reduce the convective
redeposition of foulant back on to the membrane surface. Table 6 above denotes the flow rate ranges
for each pressure tube. The high pressure pump shold not be used for cleaning.
• RO Cleaning Cartridge Filter: Normally 5 to 10-micron and is designed to remove foulants that have
been displaced from the cleaning process.
• RO Tank Heater or Cooler: The maximum design temperature for cleaning is 113 0 F (450 C). It should
be noted that heat is generated and imparted by the RO Cleaning Pump during recirculation. A less
expensive option to consider for heating the cleaning solution is adding a return line from the
discharge of the Clean-Up Pump back to the Cleaning Tank, which is plumbed to the bottom of the
tank to reduce foaming and air introduction, but this can take a long time.
• RO Tank Mixer: This is recommended to get optimal mixing of chemical, though some designers rely
solely on the slow introduction of chemical while maintaining a recirculation through the RO Cleaning
Pump back to the tank.
TSB107.27 Page 15
• Instrumentation: Cleaning system instrumentation should be included to monitor flow, temperature,
pressure, and tank level.
• Sample Points: Sample valves should be located to allow pH and TDS measurements off the RO
Cleaning Pump discharge and the concentrate side recirculation return line. Permeate can be
measured at the RO skid sample valves.
• Permeate Return Line: A small amount of the cleaning solution can permeate through the membranes
and so a permeate-side return line back to the RO Cleaning Tank is required. The permeate return line
should not be combined with the concentrate return line. If the permeate return line is combined with
the concentrate line, there is the possibility that the permeate side of the membrane and the permeate
lines may be exposed to contaminated cleaning solution. The permeate return line should terminate at
a point above the cleaning solution tank level to avoid exposing the permeate side of the membranes
or the permeate lines to the contaminated cleaning solution.
• Concentrate Return Line: The concentrate return line should terminate near the bottom of the cleaning
tank to avoid foam formation in the cleaning tank caused by the introduction of air.
Important: The permeate line and any permeate valves must always be open to atmospheric
pressure during the cleaning and flushing steps or damage to RO elements can occur. If the
permeate line is closed, the permeate pressure can build up and become higher than the feed-side
pressure of the tail elements. This can result in excessive permeate back-pressure which can
damage the membrane glue lines in the tail elements. At no time should the elements be exposed to
permeate back pressure
(where permeate static pressure exceeds feed static pressure) greater than 0.35 bar (5 psig.)
The RO membrane elements can be cleaned in place in the pressure tubes by recirculating the cleaning
solution across the high-pressure side of the membrane at low pressure and relatively high flow. A
cleaning unit is needed to do this. RO cleaning procedures may vary dependent on the situation. The time
required to clean a stage can take from 4 to 8 hours. It is recommended to take data for RO performance
normalization just before and immediately after the cleaning to evaluate the efficiency of cleaning. It may
also be beneficial to start the RO rack after first cleaning step (alkaline or acid) and collect data for
normalization to evaluate efficiency of each cleaning step separately.
1. Perform a low pressure flush at 60 psi (4 bar) or less of the pressure tubes by pumping clean
water from the cleaning tank (or equivalent source) through the pressure tubes to drain for
several minutes to displace any feed/brine solution from RO membranes. Flush water should
be clean water of RO permeate or DI quality and be free of hardness, transition metals, and
chlorine. Flushing flow rates should normally be half of the cleaning flow rates listed in Table
6.
2. Mix a fresh batch of the selected cleaning solution in the cleaning tank. The dilution water
should be clean water of RO permeate or DI quality and be free of hardness, transition
metals, and chlorine. The temperature and pH should be adjusted to their target levels.
TSB107.27 Page 16
Check and record also the conductivity, turbidity and Iron concentration of freshly prepared
cleaning solution.
3. Circulate the cleaning solution through the pressure tubes for the desired period of time. At
the start of circulation, send the displaced water to drain so you don’t dilute the cleaning
chemical and then divert up to 20% of the most highly fouled cleaning solution to drain before
returning the cleaning solution back to the RO Cleaning Tank. For the first 5 minutes, slowly
throttle the flow rate to 1/3 of the maximum design flow rate. This is to minimize the potential
plugging of the feed path with a large amount of dislodged foulant.. For the second 5 minutes,
increase the flow rate to 2/3 of the maximum design flow rate, and then increase the flow rate
to the maximum design flow rate. If required, readjust the pH back to the target when it
changes more than 0.5 pH units. Temperature of cleaning solution should be controlled and
kept at maximum allowed value during the whole cleaning cycle for best cleaning efficiency.
After each circulation step, check the conductivity, turbidity and Iron content of cleaning
solution. If these will increase significantly compared to the initial startup values, the cleaning
solution shall be drained and new solution prepared to continue with cleaning to improve
cleaning efficiency.
Note: Do not exceed maximum pH and temperature limits for specific elements. See Table 5.
4. A soak and recirculation sequence is sometimes used during cleaning. The soak time can be
from 0.5 to 8 hours depending on the manufacturer’s and/or chemical supplier’s
recommendations. Typically, the cleaning consists of 30 minutes circulation followed by a 30
minutes soaking cycle, followed by another 30 minutes of circulation. Caution should be used
to maintain the proper temperature and pH during the whole cleaning cycle.Soaking time
does increase the chemical exposure time of the membrane.
Note: Do not exceed maximum pH and temperature limits for specific elements. See Table 5.
5. Upon completion of the chemical cleaning steps, a low pressure Cleaning Rinse with clean
water (RO permeate or DI quality and free of hardness, transition metals, and chlorine) is
required to remove all traces of chemical from the Cleaning Skid and the RO Skid. Drain and
flush the cleaning tank; then completely refill the Cleaning Tank with clean water for the
Cleaning Rinse. Rinse the pressure tubes by pumping all of the rinse water from the
Cleaning Tank through the pressure tubes to drain. A second cleaning can be started at this
point, if required. Cleaning rinse flows should be half of those used for cleaning as listed in
Table 6.
6. Once the RO system is fully rinsed of cleaning chemical with clean water from the Cleaning
Tank, a Final Low Pressure Clean-up Flush can be performed using pretreated feed water.
The permeate line should remain open to drain. Feed pressure should be less than 60 psi (4
bar). This final flush continues until the flush water flows clean and is free of any foam or
residues of cleaning agents. This usually takes 15 to 60 minutes. The operator can sample
the flush water going to the drain for detergent removal and lack of foaming by using a clear
flask and shaking it. A conductivity meter can be used to test for removal of cleaning
chemicals, such that the flush water to drain is within 10-20% of the feed water conductivity.
A pH meter can also be used to compare the flush water to drain to the feed pH.
TSB107.27 Page 17
7. Once all the stages of a train are cleaned, and the chemicals flushed out, the RO can be
restarted and placed into a Service Rinse. The RO permeate should be diverted to drain until
it meets the quality requirements of the process (e.g. conductivity, pH, etc.). It is not unusual
for it to take from a few hours to a few days for the RO permeate quality to stabilize,
especially after high pH cleanings.
Other methods of recovering membrane performance are available and may be considered. Hydranautics
does not guarantee the effectiveness of these alternative procedures nor does Hydranautics accept
responsibility for any adverse effect such procedures may have on membrane performance. However,
Hydranautics is aware of instances where these procedures have proven to be very effective.
1. Electro Magnetic Fields (EMF). Claims have been made that the introduction of a continuous
electromagnetic field (EMF) around the RO membranes during operation will reduce the tendency
for the membranes to foul and will particularly reduce their tendency toward scaling. (Reference :
Ng, H. Y. and Winters, H., A Novel 16-Inch RO System for Water Reuse and Desalination. Israel
Desalination Society Annual Conference, 19-20 December, 2006.)
2. Direct Osmosis at High Salinities (DO-HS) is a process of daily backwashing of BWRO during
normal operation of desalination plant in which about 7% NaCl pulse is intentionally introduced for
6-12 seconds into the suction stream of high pressure pump without stopping the pump. As the
high salinity plug proceeds through the RO system, the reverse osmosis flow is momentarily
changed to a direct osmosis flow and permeate is sucked back through to the feed side of the
membrane. This process, if conducted regularly, may lift foulants, dehydrate bacteria, and sweep
out debris by increased flow velocity from the membrane surface to the brine outlet. (Reference:
USA Patent 7658852, Pat. Singapore, Australia, Israel WEB: www.membrane-recovery.com. )
3. Proprietary Cleaning Chemicals. There exist several RO cleaning chemical suppliers with a
number of proprietary formulations designed to address specific types of fouling. These
formulations are typically based on generic chemical formulations that have been enhanced or
modified through the suppliers’ own research and development. (see web sites for specific
chemical companies).
4. Air Scouring. It is known that two-phase (air bubbles and water) can increase shear forces and
improve the removal of foulants from a membrane surface. This has been used more in the
cleaning of individual elements.
5. Reverse Direction Cleaning. When the fouling is located primarily at the feed end of the RO
system, it is sometimes more effective to do reverse direction cleaning. There are certain
precautions that must be taken to ensure that damage to the membrane elements does not occur.
Please see TSB-125 “Reverse Direction Cleaning of RO Membrane Elements” for the guidelines
on this.
6. NaCl light salinity cleaning. As compared to the DO-HS above, NaCl light salinity is usually dosed
at 1% weight of total cleaning volume. Dissolve the NaCl into the CIP tank and it can be used in 2
different ways. First, as an NaCl solution by itself to use as a pre-cleaner prior to standard High /
Low pH solutions or, Second, as a supplement to High / Low pH solutions. NaCl increases osmotic
pressures of solution to suppress the production of permeate while cleaning.