TECHNICAL DATA SHEET

Silcoset 151
1 part Adhesive Sealant
Description Test
Property Value
This is a 1-part, RTV (Room Temperature Vulcanizing) Method
silicone adhesive sealant. It is one in a range of Acetoxy Uncured Product
cure products which are solvent free. During cure, it Appearance Viscous liquid
liberates a very small amount of acetic acid, giving rise
Cure Through to 3 mm
to the familiar ‘vinegar’ odor, which quickly dissipates 12 hr
Depth
after cure. It exhibits good primer-less adhesion to many
substrates including but not limited to; aluminum, non Cure Type Acetoxy
ferrous metals, steel, glass, enameled surfaces, fabrics 23+/-2°C and 60+/-
Drying / Fixing Conditions
ceramics, thermosetting, thermoplastics and wood 5% humidity
and cures rapidly at room temperature when in contact Extrusion Rate g/min 92 g/min
with atmospheric moisture. This product is not to be
Rheology Self Level
recommended for use with galvanized metals, ferrous
metals, copper and its associated alloys or in electronic Self Bonding Yes
assemblies. Tack Free Time / Skin
10 min
Key Features Formation at 23°C/73°F
Aerospace approved MSRR 9085 Viscosity Mixed mPas Brookfield 210000 mPas
Flexible from -60/-76°F to +300°C/572°F
FDA CFR 177,2600 for aqueous and fatty foods Cured Product
EC 1935/2004 framework EN 1186-1 / EN1186-3 7 days at 23+/-2°C and 60+/-5% humidity
compliance 100% Modulus (N/mm2) 1.71 MPa / 248 psi
Key Applications CTE Linear ppm/°C 297 ppm / °C
Germany food contact approval LFGB §31 (1), §35 CTE Volumetric ppm/°C 892 ppm/°C
LMBG L 00.90-7 and DIN 10955
Flexibility from - 60 to +300°C Colour White
NATO Stock ref: 5970-99-224-1408 BS ISO
Density 1.14 g/cm3
Rolls Royce MSRR 9085 2781
Application Elongation at Break (%) ISO 37 180 %
Conveyor belts in food industry ASTM D
Hardness Shore A 43
These products are highly resistant to weathering and 2240-95
aging, largely stable to many solvents, oils, water, sea Linear Coefficient of
water, industrial waste gasses, diluted acids, saline Thermal Expansion 297 ppm/°C
solutions detergents, cleaners, propellants and fruit (ppm/°C)
acids. Linear Shrinkage (%) 0.5 %
Use and Cure Information Max Working Temp (°C) 300 °C / 572 °F
This product is a ready for use 1 Part system and can be Min Working Temp (°C) -60 °C / -76 °F
directly dispensed from the original container without BS ISO 34-
mixing. If supplied in cartridges it can be applied using Tear Resistance (N/mm) 6.2 N/mm / 36 ppi
1
either manual or pneumatic dispensing guns. It can also
be applied from bulk containers using conventional drum Tensile Strength (N/mm2) ISO 40 2.93 N/mm2 / 425 psi
dispensing equipment. Thermal Conductivity
0.2 W/mK
All surfaces to which the sealant is to be applied should (W/mK)
be clean, dry and free from grease, dust, dirt, and loose Youngs Modulus (N/mm2) 1.59 N/mm2 / 231 psi
material. Priming of surfaces is not normally required but
in some cases it may be necessary to pretreat the Electrical Properties
surface. Please check this in each individual case. For ASTM D-
degreasing of non-porous surfaces such as metal, and Dielectric Constant 3.5
150
glass, KORASOLV GL is recommended (use undyed crepe
paper or similar). If using as an adhesive, it should be Dielectric Strength (V/mil) 535 V/mil
applied to one clean surface and the other clean surface Dielectric Strength ASTM D-
22 kV/mm / 559 V/mil
brought into contact with it within the stated tack free kV/mm 149
time. For optimum bond strength, the thickness of the ASTM D-
sealant joint should be a minimum of 1 mm. Dissipation Factor 0.0025
150
The sealant will cure upon exposure to atmospheric Volume Resistivity (Ohms ASTM D-
moisture, ideally between 20 to 70 ºC and >40% 3.49E+16 ohms cm
cm) 257
humidity. Time taken for cure will depend on the
thickness of the joint, humidity and temperature. Storage
Increasing the temperature and humidity will accelerate Max Storage
the curing process, do not cure the sealant at or above 40 °C / 104 °F
Temperature
70°C as bubbles may form in the sealant and affect the
overall physical properties and adhesion. Low Shelf Life (mths) 24
temperatures and humidity will retard the curing process.
Since curing times progressively increase with the thickness, the sealant depth should be limited to 10 mm. Joints should
The content set out in the technical data sheet does not contain information upon which you should rely. It is provided for general information purposes only and does
not constitute a product specification. You must obtain professional or specialist advice before taking any action based on the information provided in the technical data
sheet.
CHT make reasonable efforts to ensure that information set out in the technical data sheet is complete, accurate, and up-to-date. CHT do not, however, make any
representations, warranties or guarantees (whether express or implied) that information set out in the technical data sheet is complete, accurate, or up-to-date or that
the product will be suitable for your requirements. You should carry out your own testing to determine the applicability of such information and whether the product will
be suitable. CHT reserve the right to modify the technical data sheet at any time.
The CHT technical service department is available to offer further information and advice and should it be needed to look at modifying current products or custom
formulate a new one to meet your specific requirements. Please contact the technical service department.
CHT Germany GmbH: Postfach 12 80, 72002 Tübingen, Bismarckstraße 102, 72072 Tübingen, Germany
Telephone: 07071/154-0, Fax: 07071/154-290, Email: [email protected], Homepage: www.cht.com / www.cht-silicones.com
be left undisturbed for at least 24 hours, but preferably longer to effect sufficient depth of cure. Full cure requires 7 days at
thicknesses of 1 - 5 mm and 14 days at thicknesses of 5 - 10 mm.
“For pneumatic dispensing of 310 ml cartridges, the recommended pressure is 2.25 to 3.45 bar (40 to 50 psi). Dispensing
pressure above the recommended limits may lead to gas bypassing the piston, causing spluttering at the nozzle and poor
bead quality”
Solvents and cleaning agents.
For cleaning of the substrates to be bonded : KORASOLV GL.
For cleaning working tools and for removing fresh uncured material: KORASOLV GL
Care must be taken when cleaning synthetic materials which tend to form stress cracks, for example, polycarbonate and
acrylic. Please contact our technical service team for advice.
For removal of vulcanized product this can be done by mechanical means or by use of a chemical digester, please contact
our technical service team for advice.
Health & Safety
Health and Safety
Safety Data Sheets available on request.
Packaging
CHT Adhesives are available in a variety packaging including cartridges and bulk containers. Please contact our sales
department for more information.

Revision Date 29 Apr 2021

The content set out in the technical data sheet does not contain information upon which you should rely. It is provided for general information purposes only and does
not constitute a product specification. You must obtain professional or specialist advice before taking any action based on the information provided in the technical data
sheet.
CHT make reasonable efforts to ensure that information set out in the technical data sheet is complete, accurate, and up-to-date. CHT do not, however, make any
representations, warranties or guarantees (whether express or implied) that information set out in the technical data sheet is complete, accurate, or up-to-date or that
the product will be suitable for your requirements. You should carry out your own testing to determine the applicability of such information and whether the product will
be suitable. CHT reserve the right to modify the technical data sheet at any time.
The CHT technical service department is available to offer further information and advice and should it be needed to look at modifying current products or custom
formulate a new one to meet your specific requirements. Please contact the technical service department.