A
AEROSPACE MATERIAL
SPECIFICATION Issued 1997-07
Reaffirmed 2010-05
Stabilized 2014-07
Superseding AMS-QQ-A-225/9
RATIONALE
AMS-QQ-A225/9A stabilizes this document because equivalent technical requirements are contained in AMS4122,
AMS4124, and AMS4186.
STABILIZED NOTICE
AMS QQ-A-225/9A has been declared "STABILIZED" by AMS Committee D. This document will no longer be updated and
may no longer represent standard industry practice. This document was stabilized because it contains requirements that
are no longer state of the art and are also contained in alternate documents that contain equivalent requirements.
Previously this document was reaffirmed. AMS Committee D has never performed a technical update of this document.
Users of this document should refer to the cognizant engineering organization for disposition of any issues with
reports/certifications to this specification; including exceptions listed on the certification. NOTE: In many cases, the
purchaser may represent a sub tier supplier and not the cognizant engineering organization.
AMS Committee D recommends that the following technically equivalent specifications be used for future procurement.
This listing does not constitute authority to substitute these specifications for the “STABILIZED” specification.
AMS4122 Aluminum Alloy Bars, Rods, and Wire Rolled or Cold Finished, and Rings, 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr
(7075-T6, 7075-T651), Solution and Precipitation Heat Treated
AMS4124 Aluminum Alloy, Rolled or Cold Finished Bars, Rods, and Wire 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T73,
T7351), Solution Heat Treated, Stress Relieved By Stretching, and Overaged
AMS4186 Aluminum Alloy, Bars, Rods, and Wire, Rolled or Cold Finished, 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-F),
as Fabricated or when specified, Annealed (7075-O)
__________________________________________________________________________________________________________________________________________
SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is
entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the sole responsibility of the user.”
SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and
suggestions.
Copyright © 2014 SAE International
All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying,
recording, or otherwise, without the prior written permission of SAE.
TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) SAE values your input. To provide feedback
Tel: +1 724-776-4970 (outside USA) on this Technical Report, please visit
Fax: 724-776-0790 http://www.sae.org/technical/standards/AMSQQA225/9A
Email: [email protected]
SAE WEB ADDRESS: http://www.sae.org
SAE INTERNATIONAL AMS-QQ-A-225/9A Page 1 of 6
NOTICE
This document has been taken directly from Federal Specification QQ-A-225/9E and contains only
minor editorial and format changes required to bring it into conformance with the publishing
requirements of SAE technical standards.
The original Federal Specification was adopted as an SAE standard under the provisions of the SAE
Technical Standards Board (TSB) Rules and Regulations (TSB 001) pertaining to accelerated
adoption of government specifications and standards. TSB rules provide for (a) the publication of
portions of unrevised government specifications and standards without consensus voting at the SAE
Committee level, (b) the use of the existing government specification and standard format, and (c)
the exclusion of any qualified product list (QPL) sections.
The complete requirements for procuring 7075 aluminum alloy bar, rod, wire, and special shapes
described herein shall consist of this document and the latest issue of AMS-QQ-A-225.
SAE INTERNATIONAL AMS-QQ-A-225/9A Page 2 of 6
1.1 Scope:
This specification covers the specific requirements for 7075 aluminum alloy bar, rod, wire, and
special shapes produced by rolling, drawing, or cold finishing.
1.2 Classification:
1.2.1 Tempers: Bar, rod, wire, and special shapes are of the following tempers, as specified (See 6.2):
O, T6, T62, T651, T73, or T7351 temper. Definitions of these tempers are specified in
AMS-QQ-A-225.
2. APPLICABLE DOCUMENTS:
See AMS-QQ-A-225.
3. REQUIREMENTS:
Chemical Composition 1/
Percent
Element
Minimum Maximum
Zinc 5.1 6.1
Magnesium 2.1 2.9
Copper 1.2 2.0
Chromium 0.18 0.28
Iron - 0.50
Silicon - 0.40
Manganese - 0.30
Titanium - 0.20
Other Elements, each - 0.05
Other Elements, total - 0.15
Aluminum Remainder
3.2.1 Mechanical Properties of Material as Supplied: The mechanical properties in the direction of
working shall conform to the requirements of Table II for the temper specified.
1/ Tempers T651 and T7351 are available only in rod, bar and shapes
2/ Maximum
3/ For rounds (rods), maximum diameter is 3 or 4 inches, whichever is applicable; for square,
hexagonal, or octagonal bar, maximum thickness is 3 or 3-1/2 inches, whichever is
applicable; for rectangular bar, maximum thickness is 3 inches with corresponding maximum
width of 6 inches; for rectangular bar less than 3 inches in thickness, maximum width of 10
inches.
4/ Material in the T62 temper is not available from the materials producers
5/ Definition of T73 and T7351 tempers: The T73 temper applies to material which has been
solution heat-treated and stabilized to develop the required mechanical properties and
resistance to stress-corrosion cracking. The T7351 temper applies to material which has
been solution heat-treated, stress-relieved by stretching to produce a permanent set of 1-1/2
percent nominal, but not less than 1 nor more than 3 percent, and stabilized to develop the
required mechanical properties and resistance to stress-corrosion cracking.
6/ See AMS-QQ-A-225 for yield strength and elongation requirement exceptions
SAE INTERNATIONAL AMS-QQ-A-225/9A Page 4 of 6
3.2.2 Mechanical Properties After Heat Treatment: In addition to conforming to the requirements of
3.2.1, the mechanical properties in the direction of working of material ordered in the annealed (O)
temper, and without subsequent cold-working or forming operations, and subsequently solution
heat-treated and artificially aged shall conform to the requirements specified in Table II for the T6,
T62, and T73 tempers. Material as received in the T6, T651, T73, and T7351 tempers shall, after
proper re-solution heat treatment and aging, be capable of conforming to the requirements
specified in Table II for the T6, T62, and T73 tempers. Material in the T6, T62, and T651 tempers
shall after proper aging be capable of conforming to the requirements specified in Table II for the
T73 or T7351 tempers, as applicable. See AMS-QQ-A-225 for the solution and aging treatments.
3.3 Finish:
Unless otherwise specified in the contract or purchase order (See 6.2), rod up to and including 3
inches in diameter, and bar up to and including 2 inches thick (with maximum width for rectangles of
4 inches) shall be processed to size by cold finishing.
3.4.1 Resistance to SCC: Material in the T73 or T7351 tempers shall be capable of exhibiting no
evidence of stress-corrosion cracking when subjected to the test specified in 4.2. The supplier
shall maintain records of the performance of all lots so tested.
3.4.2 Acceptance Criteria: Susceptibility to stress-corrosion cracking for each lot of 7075-T73 and T7351
material shall be established by testing the previously selected tensile specimens to the following
criteria:
3.5 Marking:
In addition to marking required in AMS-QQ-A-225, material in the T6, T651, T73 and T7351 tempers
shall be identified by a lot number marked in at least one location on each piece (See 6.2).
From material in the annealed (O) temper, an additional number of specimens equal to those
required by AMS-QQ-A-225 shall be taken and tested after solution heat treatment and artificial
aging to determine compliance with 3.2.2.
Specimens of 7075-T73 and T7351 alloy shall be selected in a manner that will permit application of
the specified tensile stress in the short-transverse grain direction (See 4.2.4). The specimens shall
be subjected to the following stress-corrosion test:
4.2.2 Stressed in the short-transverse direction with respect to grain flow and held at a constant strain.
The stress level shall be 75 percent of the specified longitudinal yield strength.
4.2.3 The stressed specimens shall be exposed to a solution of 3.5 percent NaCl conforming to the
purity and pH requirements of ASTM B 117, at room temperature, by alternate immersion. The
exposure cycle shall consist of 10 minutes immersion in the solution and 50 minutes out of the
solution.
4.2.4 For material thicknesses under 0.700 inch, the specimen tested shall be a tension specimen
selected so that the applied stress is, if possible, parallel in direction to the smallest dimension of
the product which is over 0.700 inch.
See AMS-QQ-A-225.
6. NOTES:
This alloy is intended for use where high strength and good corrosion resistance are required.
SAE INTERNATIONAL AMS-QQ-A-225/9A Page 6 of 6
Purchasers should select the preferred options permitted herein and include the following
information in procurement documents:
6.3 Product produced and marked to the requirements of AMS-QQ-A-225/9 also meets the requirements
of QQ-A-225/9E. Product produced and marked to the requirements of QQ-A-225/9E also meets the
requirements of AMS-QQ-A-225/9.
6.4 Properties listed in 3.2.1 are exactly the same as QQ-A-225/9, Revision E. These properties have
not been substantiated in accordance with the AMS Manual for Preparation of Aerospace
Specifications.