  • 2.0550 - CW713R (CuZn40Al2, CZ135, CuZn37MnAl2PbSi)

    Uploaded by

    Eminent Rish
    249 views1 page
    CW713R is a high tensile brass alloyed with aluminum, manganese, and silicon, making it almost as hard as aluminum bronze but easier to process. It has good corrosion and wear resistance properties. This alloy is commonly used in the automotive and hydraulic industries for applications requiring high load bearing like bearings, slide plates, and piston parts. The alloy has specific composition ranges and physical properties such as a melting point between 1589-1625°F and density of 0.296 lb/cu in.

    Original Description:

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Report this Document
    CW713R is a high tensile brass alloyed with aluminum, manganese, and silicon, making it almost as hard as aluminum bronze but easier to process. It has good corrosion and wear resistance properties. This alloy is commonly used in the automotive and hydraulic industries for applications requiring high load bearing like bearings, slide plates, and piston parts. The alloy has specific composition ranges and physical properties such as a melting point between 1589-1625°F and density of 0.296 lb/cu in.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Flag for inappropriate content
    Download as pdf or txt
    249 views1 page

    2.0550 - CW713R (CuZn40Al2, CZ135, CuZn37MnAl2PbSi)

    Uploaded by

    Eminent Rish
    CW713R is a high tensile brass alloyed with aluminum, manganese, and silicon, making it almost as hard as aluminum bronze but easier to process. It has good corrosion and wear resistance properties. This alloy is commonly used in the automotive and hydraulic industries for applications requiring high load bearing like bearings, slide plates, and piston parts. The alloy has specific composition ranges and physical properties such as a melting point between 1589-1625°F and density of 0.296 lb/cu in.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Flag for inappropriate content
    Download as pdf or txt
    of 1

    CW713R HIGH TENSILE BRASS

    EQUIVALENT SPECIFICATIONS
    SPECIFICATIONS DESIGNATION
    BS 2872/4 CZ135
    DIN 2.0550 (CuZn40Al2)
    EN CuZn37MnAl2PbSi

    CW713R is a high tensile brass which is alloyed with aluminum, manganese and silicon etc. which makes this
    alloy almost as hard as aluminum bronze, but considerably easier to process. CW713R also has good corrosion,
    wear resistance and machinability.

    Typically this alloy is used in the automotive and hydraulic industries in forms of products such as Bearings for
    high load, slide- & wear-plates, valve guides, piston parts etc.

    CHEMICAL COMPOSITION
    Cu Pb Sn Zn Si Ni Fe Al Mn Other
    Min 57 0.2 - - 0.3 - - 1.3 1.5 -
    Max 59 0.8 Max 0.4 Rem. 1.3 Max 1.0 Max 1.0 2.3 3.0 Max 0.3

    PHYSICAL PROPERTIES

    Melting Point – Liquidus °F 1625


    Melting Point – Solidus °F 1589
    Density lb./cu in. at 68°F 0.296
    Specific Gravity 8.12
    Electrical Conductivity% IACS at 68°F 19
    Thermal Conductivity Btu/ sq. ft./ ft. hr./ °F at 68°F 36.42
    Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) 9
    Specific Heat Capacity Btu/ lb. /°F at 68°F 0.090
    Modulus of Elasticity in Tension ksi 15954

    SIZES AVAILABLE
    ROUND RODS 8mm To 100 mm
    HEX 10mm To 60mm
    SQUARE 10mm To 60mm
    FLAT 10mm Min Thickness and max Width 120mm
    BILLETS Up to 200 mm
    INGOTS As per Specification

    Regd. Office & Works:


    217/218 Phase–ll, Okha Rajkot Road, Dared, Jamnagar-361004 INDIA
    Tel.: +91 - 288 – 2730118 Mobile: +91-9328105172
    [email protected] I www.shree-extrusion.com

    You might also like