190326quadax Valves Coating Specifications
190326quadax Valves Coating Specifications
müller co-ax ag
Gottfried-Müller-Str. 1
74670 Forchtenberg
Germany
Table of Contents
1 Scope 3
2 Applicable standards 3
3 Preparation 3
4 Covering 4
5 Coating preparation 4
6 Coating 4
7 Protection of non-coated surfaces 4
8 Final inspection 5
1 Scope
These specifications describe the passive corrosion protection through the external coating
of housing elements of QUADAX butterfly valves that do not come into contact with medium.
These specifications do not apply to butterfly valves made of rust-resistant materials that are
not coated in the standard configuration.
2 Applicable standards
Standards
Preparation of steel substrates before application of
paints and related products – Visual assessment of
EN ISO 8501-1,2 ,4 surface cleanliness
Preparation of steel substrates before application of
paints and related products – Surface roughness
EN ISO 8503 characteristics of blast-cleaned steel substrates
Paints and varnishes – Corrosion protection of steel
EN ISO 12944 structures by protective paint systems
Preparation of steel substrates before application of
EN ISO 11124 paints and related products
3 Preparation
‐ All soil and loose particles must be removed from the surfaces to be coated.
4 Covering
The following parts of the valve are coated:
‐ Body (partially)
5 Coating preparation
‐ The parts to be coated must be at least 5° above the dew point
6 Coating
‐ One-component silicone resin varnish (cover coating material) and conventional
atomizing spray are applied to the surface.
‐ The varnish has a single-layer structure and a minimum dry film thickness of
50 µm.
8 Final inspection
‐ A final inspection of the coating of the valves is to be performed on a random-basis.
‐ The total thickness may not be less than 80% of the specified coat thickness at any
point
‐ The total thickness may not exceed 250% of the specified coat thickness at any point
Minimum permissible
-20°C
duration - temperature
Maximum permissible
+500°C
duration - temperature
Maximum temporary
+600°C
permissible temperature
Corrosion class No official corrosion class
Expected duration of
5 years (no liability)
corrosion protection
Materials for coating Ferrous materials such as steel and cast steel