CONCRETE MIX DESIGN SUMMARY
Contractor Project : TRIMATRA LIGUNA, PT Doc. No : MD23110102-001
Project : Marketing Galery Ciputat Paradise Req. Date : 7 November 2023
Address : Serua Indah Kec. Ciputat Kota Tangerang Selatan Proc. Date :

Type of Concrete K175

Slump 12 +/-2
Element to be cast STRUCTURE RETAIL

[concrete class definition K] 175 kg/cm2

Cement content ( kg ) 262

Coarse Agg. max 25 mm ( kg ) 1015
Fine Aggregate ( kg ) 426
Fine Aggregate ( kg ) 334
[Admixture] 0.25 - 0.79
Free Water Content ( litres ) 185

W/C Ratio 0.7061

[Admixture] 95 - 302

Total Weight of Cement Content (kg) 262

Note :
1. The batch weight are in kilogram (kg) or liters per cubic meter
2. Yield measurements shall comply with ASTM Standard (C 138 M)
3. All batch weights are in saturated surface dry (SSD) condition
4. Admixture dosage rate :
a. Milliliters (ml) per 100 kg cementitious material
b. Liter per cubic meter
5. Cementitious content may include cement, fly ash or silica fume depending on the requirement/project specification and testing is carried out in accordance
with the relevant ASTM Standard.
6. Dosage of split and fine aggregate to depend on the material characteristics of the above materials (SG, Water Absorption, Fineness modulus) at the time of
supply and also performance at site.
The above mixes will comply with all the current requirements of ACI provided all aspects of sampling preparation and testing carried out in accordance with
current editions of ASTM.

* This document was issued electronically and is therefore valid without signature

1
4
3
2
 PT. Pionirbeton Industri
TECHNICAL DEPARTMENT
Jl. Rawa Sumur IV Blok BB9
Kawasan Industri Pulogadung
CONCRETE MIX DESIGN SUMMARY
Contractor Project : TRIMATRA LIGUNA, PT Doc. No : MD23110102-001
Project : Marketing Galery Ciputat Paradise Req. Date : 7 November 2023
Address : Serua Indah Kec. Ciputat Kota Tangerang Selatan Proc. Date :

Type of Concrete K300

Slump 12 +/-2
Element to be cast STRUCTURE RETAIL

[concrete class definition K] 300 kg/cm2

Cement content ( kg ) 312

Coarse Agg. max 25 mm ( kg ) 1025
Fine Aggregate ( kg ) 423
Fine Aggregate ( kg ) 329
[Admixture] 0.3 - 1.25
[Admixture] 1.59 - 2.5
Free Water Content ( litres ) 165

W/C Ratio 0.5288

[Admixture] 96 - 401
[Admixture] 510 - 801

Total Weight of Cement Content (kg) 312

Note :
1. The batch weight are in kilogram (kg) or liters per cubic meter
2. Yield measurements shall comply with ASTM Standard (C 138 M)
3. All batch weights are in saturated surface dry (SSD) condition
4. Admixture dosage rate :
a. Milliliters (ml) per 100 kg cementitious material
b. Liter per cubic meter
5. Cementitious content may include cement, fly ash or silica fume depending on the requirement/project specification and testing is carried out in accordance
with the relevant ASTM Standard.
6. Dosage of split and fine aggregate to depend on the material characteristics of the above materials (SG, Water Absorption, Fineness modulus) at the time of
supply and also performance at site.
The above mixes will comply with all the current requirements of ACI provided all aspects of sampling preparation and testing carried out in accordance with
current editions of ASTM.

* This document was issued electronically and is therefore valid without signature

2
1
4
3
 PT. Pionirbeton Industri
TECHNICAL DEPARTMENT
Jl. Rawa Sumur IV Blok BB9
Kawasan Industri Pulogadung
CONCRETE MIX DESIGN SUMMARY
Contractor Project : TRIMATRA LIGUNA, PT Doc. No : MD23110102-001
Project : Marketing Galery Ciputat Paradise Req. Date : 7 November 2023
Address : Serua Indah Kec. Ciputat Kota Tangerang Selatan Proc. Date :

Type of Concrete K350

Slump 12 +/-2
Element to be cast STRUCTURE RETAIL

[concrete class definition K] 350 kg/cm2

Cement content ( kg ) 343

Coarse Agg. max 25 mm ( kg ) 1025
Fine Aggregate ( kg ) 408
Fine Aggregate ( kg ) 318
[Admixture] 0.34 - 1.04
[Admixture] 1.78 - 2.61
Free Water Content ( litres ) 165

W/C Ratio 0.4810

[Admixture] 99 - 303
[Admixture] 519 - 761

Total Weight of Cement Content (kg) 343

Note :
1. The batch weight are in kilogram (kg) or liters per cubic meter
2. Yield measurements shall comply with ASTM Standard (C 138 M)
3. All batch weights are in saturated surface dry (SSD) condition
4. Admixture dosage rate :
a. Milliliters (ml) per 100 kg cementitious material
b. Liter per cubic meter
5. Cementitious content may include cement, fly ash or silica fume depending on the requirement/project specification and testing is carried out in accordance
with the relevant ASTM Standard.
6. Dosage of split and fine aggregate to depend on the material characteristics of the above materials (SG, Water Absorption, Fineness modulus) at the time of
supply and also performance at site.
The above mixes will comply with all the current requirements of ACI provided all aspects of sampling preparation and testing carried out in accordance with
current editions of ASTM.

* This document was issued electronically and is therefore valid without signature

3
2
1
4
 PT. Pionirbeton Industri
TECHNICAL DEPARTMENT
Jl. Rawa Sumur IV Blok BB9
Kawasan Industri Pulogadung
CONCRETE MIX DESIGN SUMMARY
Contractor Project : TRIMATRA LIGUNA, PT Doc. No : MD23110102-001
Project : Marketing Galery Ciputat Paradise Req. Date : 7 November 2023
Address : Serua Indah Kec. Ciputat Kota Tangerang Selatan Proc. Date :

Type of Concrete KB0

Slump 12 +/-2
Element to be cast STRUCTURE RETAIL

[concrete class definition K] KB0

Cement content ( kg ) 152

Coarse Agg. max 25 mm ( kg ) 860
Fine Aggregate ( kg ) 51
Fine Aggregate ( kg ) 944
[Admixture] 0.15 - 0.45
Free Water Content ( litres ) 188

W/C Ratio 1.2368

[Admixture] 99 - 296

Total Weight of Cement Content (kg) 152

Note :
1. The batch weight are in kilogram (kg) or liters per cubic meter
2. Yield measurements shall comply with ASTM Standard (C 138 M)
3. All batch weights are in saturated surface dry (SSD) condition
4. Admixture dosage rate :
a. Milliliters (ml) per 100 kg cementitious material
b. Liter per cubic meter
5. Cementitious content may include cement, fly ash or silica fume depending on the requirement/project specification and testing is carried out in accordance
with the relevant ASTM Standard.
6. Dosage of split and fine aggregate to depend on the material characteristics of the above materials (SG, Water Absorption, Fineness modulus) at the time of
supply and also performance at site.
The above mixes will comply with all the current requirements of ACI provided all aspects of sampling preparation and testing carried out in accordance with
current editions of ASTM.

* This document was issued electronically and is therefore valid without signature