En 10216-1 Seamless Steel Tubes For Pressure Purposes
En 10216-1 Seamless Steel Tubes For Pressure Purposes
php)
EN 10216-1
EN 10216-1 Seamless steel tubes for pressure purposes - Technical delivery
conditions - Part 1: Non-alloy steel tubes with specified room temperature
properties.
(en-10216-1-non-alloy-steel-tubes.php)
1.Scope
This European Standard specifies the technical delivery conditions for two qualities TR1 and TR2 of
seamless tubes of circular cross section with specified room temperature properties made of non-alloy
quality steel.
NOTE:Once this standard is published in the Official Journal of the European Union (OJEU) under Directive
97/23/EC, presumption of conformity to the Essential Safety Requirements (ESR) of Directive 97/23/EC is
limited to technical data of materials in this standard and does not presume adequacy of the material to a
specific item of equipment. Consequently, the assessment of the technical data stated in this material
standard against the design requirements of this specific item of equipment to verify that the ESRs of the
Pressure Equipment Directive are satisfied,needs to be done by the designer or manufacturer of the
pressure equipment, taking also into account the subsequent manufacturing processes which may affect
2. Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references,the latest edition of the referenced document (including any amendments) applies.
EN 10020, Definition and classification of grades of steel
EN 10021, General technical delivery conditions for steel products
EN 10220, Seamless and welded steel tubes Dimensions and masses per unit length
CEN/TR 10261, Iron and steel European standards for the determination of chemical composition
EN 10266, Steel tubes, fittings and structural hollow sections Symbols and definitions of terms for use in
product standards
EN ISO 148-1, Metallic materials Charpy pendulum impact test Part 1: Test method (ISO 148-1)
EN ISO 377, Steel and steel products Location and preparation of samples and test pieces for mechanical
EN ISO 2566-1, Steel Conversion of elongation values Part 1: Carbon and low alloy steels(ISO 2566-1)
EN ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature(ISO 6892-
1)
EN ISO 10893-1, Non-destructive testing of steel tubes Part 1:Automated electromagnetic testing of
seamless and welded (except submerged arc-welded) steel tubes for the verification of hydraulic
EN ISO 10893-2, Non-destructive testing of steel tubes Part 2: Automated eddy current testing of
seamless and welded (except submerged arc-welded) steel tubes for the detection of imperfections (ISO
10893-2)
EN ISO 10893-3,Non-destructive testing of steel tubes Part 3: Automated full peripheral flux leakage
testing of seamless and welded (except submerged arc-welded) ferromagnetic steel tubes for the detection
EN ISO 10893-10, Non-destructive testing of steel tubes Part 10: Automated full peripheral ultrasonic
testing of seamless and welded (except submerged arc-welded) steel tubes for the detection of longitudinal
and/or transverse imperfections (ISO 10893-10)
EN ISO 14284,Steel and iron Sampling and preparation of samples for the determination of chemical
4.Symbols
For the purpose of this Part of EN 10216, the symbols given in EN 10266 apply.
plus either:
the steel name in accordance with EN 10027-1;
or:
the indication of the specified minimum yield strength for thickness ≤ 16 mm, expressed in MPa(see Table 5
The following information shall be supplied by the purchaser at the time of enquiry and order:
the dimensions (outside diameter D and wall thickness T) (see Table 7);
the designation of the steel grade in accordance with this Part of EN 10216 (see 5.2).
Options
A number of options are specified in this Part of EN 10216 and these are listed below. In the event that the
purchaser does not indicate a wish to implement any of these options at the time of enquiry and order, the
tubes shall be supplied in accordance with the basic specification (see 6.1).
1) Delivery condition normalized or normalizing-formed for TR1 (see 7.2.2);
2) restriction on copper and tin contents (see Table 2 and Table 3);
10) test unit restriction for tubes with D ≤ 76,1 mm of quality TR2 (see 10.1.1);
11) wall thickness measurement away from the ends (see 11.5);
12) additional marking (see 12.2);
13) protection (see 13).
Example of an order
100 t of seamless tube with an outside diameter of 168.3 mm, a wall thickness of 4,5 mm, in accordance
with EN 10216-1, made of steel grade P235TR2 with a 3.2 inspection certificate in accordance with EN
10204.
The steelmaking process is at the discretion of the manufacturer with the exception that the open hearth
(Siemens-Martin) process shall not be employed unless in combination with a secondary steelmaking or
equivalent to it.
The operating authorization issued by the employer shall be in accordance with a written procedure.
NDT operations shall be authorized by level 3 NDT individual approved by the employer.
NOTE The definition of level 1, 2 and 3 can be found in appropriate standards, e.g. EN ISO 9712 and ISO
11484.
The tubes shall be manufactured by a seamless process. The forming operations and delivery conditions
are shown in Table 1.
8. Requirements
8.1 General
When supplied in a delivery condition indicated in 7.2 and inspected in accordance with Clauses 9, 10 and
11,the tubes shall conform to the requirements of this Part of EN 10216.
In addition, the general technical delivery requirements specified in EN 10021 shall apply.
fact that the behaviour of the steel during and after welding is dependent not only on the steel, but also on
the applied heat treatment and the conditions of preparing for and carrying out the welding.
Steel Steel
name number
P195TR2 1.0108 0,13 0,35 0,70 0,025 0,015 0,30 0,08 0,30 0,02 0,30 0,010 0,
d
P235TR2 1.0255 0,16 0,35 1,20 0,025 0,015 0,30 0,08 0,30 0,02 0,30 0,010 0,
d
P265TR2 1.0259 0,20 0,40 1,40 0,025 0,015 0,30 0,08 0,30 0,02 0,30 0,010 0,
d
a Elements not included in this Table shall not be intentionally added to the steel without the agreement of
the purchaser, except for elements which may be added for finishing the cast. All appropriate measures shall
be taken to prevent the addition of undesirable elements from scrap or other materials used in the
steelmaking process.
b The content of these elements need not be reported unless intentionally added to the cast.
c Option 2: In order to facilitate subsequent forming operation, an agreed maximum copper content lower
than indicated and an agreed specified maximum tin content shall apply.
d This requirement is not applicable provided the steel contains a sufficient amount of other nitrogen binding
Steel grade C Si Mn P S Cr Mo Ni Al Cu Nb T
max. max. max. max. max. b b b tot b b b
max. max max. min. c max. ma
max
Steel Steel
name number
P195TR1 1.0107 0,13 0,35 0,70 0,025 0,020 0,30 0,08 0,30 - 0,30 0,010 0,
d
P235TR1 1.0254 0,16 0,35 1,20 0,025 0,020 0,30 0,08 0,30 - 0,30 0,010 0,
d
P265TR1 1.0258 0,20 0,40 1,40 0,025 0,020 0,30 0,08 0,30 - 0,30 0,010 0,
d
a Elements not included in this table shall not be intentionally added to the steel without the agreement of
the purchaser, except for elements which may be added for finishing the cast. All appropriate measures shall
be taken to prevent the addition of undesirable elements from scrap or other materials used in the
steelmaking process.
b The content of these elements need not be reported unless intentionally added to the cast.
c Option 2:In order to facilitate subsequent forming operation, an agreed maximum copper content lower
than indicated and an agreed specified maximum tin content shall apply.
d These grades do not support the Essential Requirements of the New Approach Directive 97/23/EC.
than or equal to 76, 1 mm this option applies only in combination with Option 11.
Table 4 specifies the permissible deviations of the product analysis from the specified limits on cast analysis
Element Limiting value for the cast Permissible deviation of the product analysis % by mass
analysis in accordance with
Table 2 % by mass
C ≤ 0,20 + 0,02
Si ≤ 0,40 + 0,05
Mn ≤ 1,40 + 0,10
P ≤ 0,025 + 0,005
Al ≥ 0,020 − 0,005
Cr ≤ 0,30 + 0,05
Cu ≤ 0,30 + 0,05
Mo ≤ 0,08 + 0,02
Nb ≤ 0,010 + 0,005
Ni ≤ 0,30 + 0,005
Ti ≤ 0,04 + 0,01
V ≤ 0,02 + 0,01
T≤ 16 < 40 < l t
16 T≤ T≤
40 60
c l = longitudinal t = transverse
d Option 4: In addition to the test in Table 11, longitudinal impact strength shall be verified at - 10 °C.
*1 MPa = 1 N/mm 2
T≤ 16 < T ≤ 40 < T l t
16 40 ≤
60
a For wall thickness greater than 60 mm the mechanical properties are subject to agreement.
b See 11.2.
c l = longitudinal t = transverse
d These grades do not support the Essential Requirements of the New Approach Directive 97/23/EC.
* 1 MPa = 1 N/mm
and,where applicable, the heat treatment employed. Normally the finish and surface condition shall be such
that any surface imperfections requiring dressing can be identified.
8.4.1.3 It shall be permissible to dress, only by grinding or machining, surface imperfections provided
that,after doing so, the wall thickness in the dressed area is not less than the specified minimum wall
thickness. All dressed areas shall blend smoothly into the contour of the tube.
8.4.1.4 Surface imperfections which encroach on the specified minimum wall thickness shall be considered
defects and tubes containing these shall be deemed not to conform to this Part of this EN 10216.
8.4.2.1 Leak-tightness
The tubes shall pass a hydrostatic test (see 11.4.1) or electromagnetic test (see 11.4.2) for leak-
tightness.Unless the Option 5 is specified the choice of the test method is at the discretion of the
manufacturer.
Option 5: The test method for verification of leak-tightness in accordance with 11.4.1 or 11.4.2 is specified by
the purchaser.
8.4.2.2 Non-Destructive Testing
Option 6: The tubes of quality TR2 shall pass a non-destructive test for the detection of longitudinal
imperfections in accordance with 11.7. The test method shall be specified by the purchaser
8.5 Straightness
The deviation from straightness, of any tube length L shall not exceed 0,001 5 L. Deviations from
straightness over any one metre length shall not exceed 3 mm.
8.6 Preparation of ends
Tubes with wall thickness ≥ 3,2 mm shall be delivered with square cut ends. The ends shall be free from
excessive burrs.
Option 7: The tubes with wall thickness ≥ 3.2 mm shall be delivered with bevelled ends (see Figure 1). The
bevel shall have an angle α of 30°( +°5,-0°)with a root face C of 1,6 mm ± 0,8 mm, except that for wall
Key
D outside diameter
α bevel angle
Table 7.
Dimensions which are different from those in Table 7 may be agreed.
8.7.2 Mass
For the mass per unit length the provisions of EN 10220 apply.
8.7.3 Lengths
Unless Option 8 is specified the tubes are delivered in random lengths. The delivery range shall be agreed
at the time of enquiry and order.
Option 8: The tubes shall be delivered in exact lengths and the length shall be specified at the time of
enquiry and order. For the tolerances, see 8.7.4.2.l
Dimensions in millimetres
8.7.4 Tolerances
8.7.4.1 Tolerances on diameter and thickness
The diameter and the wall thickness of the tubes shall be within the tolerance limits given in Table 8.
Out-of-roundness is included in the tolerances on outside diameter and eccentricity is included in the
a For outside diameters D ≥ 355,6 mm it is permitted to exceed the upper wall thickness locally by a further
5 % of the wall thickness T
Dimensions in millimetres
9 Inspection
9.1 Types of inspection
Conformity to the requirements of the order, for tubes in accordance with this Part of EN 10216, shall be
verified by:
When an inspection certificate 3.1 is specified, the material manufacturer shall state in the confirmation of
the order whether he is operating according to a “quality-assurance system”, certified by a competent Body
established within the Community, and having undergone a specific assessment for materials.
NOTE See the EU Directive 97/23/EC, Annex I, section 4.3 third paragraph and for further information the
Guidelines of the EU Commission and the Member States for its interpretation (see e.g. Guidelines 7/2 and
7/16).
address of the organization or person who is to carry out the inspection and produce the inspection
document, and it shall be agreed which party shall issue the certificate.
Document 3.1 and 3.2 are to be validated by the manufacturer’s authorized representative.
information:
D01 marking and identification, surface appearance, shape and dimensional properties;
Z validation.
9.2.2.3 For tubes supplied with specific inspection the inspection certificate shall contain the following codes
and information:
D01 marking and identification, surface appearance, shape and dimensional properties;
Z validation.
In addition, for inspection document 3.1 the manufacturer shall state the references to the certificate (see
Non-specific Specific
inspection inspection
Longitudinal impact test at -10 °C (Option 4) One per test unit 8.3.1 and
11.3
10 Sampling
10.1 Frequency of tests
10.1.1 Test unit
Quality TR1: Tubes of the same specified outside diameter and wall thickness, the same steel grade, the
same manufacturing process and, if applicable, the same normalising treatment in a continuous furnace or
Quality TR2: Tubes of the same specified outside diameter and wall thickness, the same steel grade, the
same cast, the same manufacturing process and, if applicable, the same normalising treatment in a
continuous furnace or heat-treated in the same furnace charge in a batch-type furnace. Tubes with specified
outside diameter less than or equal to 76.1 mm need not be separated by cast unless Option 10 is specified.
The number of tubes, in manufacturing lengths, per test unit shall conform to Table 12.
The manufacturing length (e.g. the rolled length after the normalising forming process) may differ from the
delivery length providing there is no additional HT after cutting the manufacturing lengths into individual
lengths.
Option 10: Tubes with specified outside diameter less than or equal to 76,1 mm shall be separated by cast
for quality TR2 .
10.2.2 Location, orientation and preparation of samples and test pieces for mechanical tests
10.2.2.1 General
Samples and test pieces shall be taken at the tube ends and in accordance with the requirements of EN ISO
377.
section and shall be taken in a direction longitudinal to the axis of the tube;
for tubes with an outside diameter D > 219,1 mm the test piece shall either a machined test piece with
circular cross section from an unflattened sample or a strip section and be taken in a direction either
pieces of width less than 10 mm, but not less than 5 mm shall be prepared; the largest obtainable width shall
be used.
Where test pieces at least 5 mm width cannot be obtained, the tubes shall not be subjected to impact
testing.
Unless otherwise specified (see Option 4), the test pieces shall be taken transverse to the tube axis unless
D min , as calculated by the following equation, is greater than the specified outside diameter, in which case
longitudinal test pieces shall be used:
D min = (T-5) + [ 756,25 / (T-5) ] (1)
The test pieces shall be prepared such that the axis of the notch is perpendicular to the surface of the
tube,see Figure 2.
Key
physical or chemical analytical method for the analysis shall be at the discretion of the manufacturer. In
cases of dispute, the method used shall be agreed between manufacturer and purchaser taking into account
CEN/TR 10261.
the upper yield strength (R eH ) or if a yield phenomenon is not present the 0,2 % proof strength (R p0,2 );
11.3.1 The test shall be carried out (but see 10.2.2.3) in accordance with EN ISO 148-1 at 0 °C and, if option
4 is specified, at -10 °C.
11.3.2 The mean value of the three test pieces shall meet the requirements given in Table 5 and Table 6.
One individual value may be below the specified value, provided that it is not less than 70 % of that value.
11.3.3 If the width (W) of the test piece is less than 10 mm, the measured impact energy (KV p ) shall be
where
The calculated impact energy KV c shall conform to the requirements given in 11.3.2.
11.3.4 If the requirements of 11.3.2 are not met, then an additional set of three test pieces may be taken at
the discretion of the manufacturer from the same sample and tested. To consider the test unit as conforming,
after testing the second set, the following conditions shall be satisfied simultaneously:
the average value of the six tests shall be equal to or greater than the specified minimum value;
not more than two of the six individual values may be lower than the specified minimum value;
not more than one of the six individual values may be lower than 70 % of the specified minimum average
value.
11.3.5 The dimensions in millimetres of the test pieces, the measured impact energy values and the
where
P is the test pressure, in bar;
The test pressure shall be held for not less than 5 s for tubes with an outside diameter D less than or equal
to 457 mm and for not less than 10 s for tubes with an outside diameter D greater than 457 mm.
The outside diameter shall be measured at tube ends. For tubes with outside diameter D ≥ 406,4 mm, the
diameter may be measured using a circumference tape.
Unless Option 11 is specified the wall thickness shall be measured at both tube ends.
Option 11: The wall thickness shall be measured away from the tube ends in accordance with an agreed
procedure.
11.6 Visual examination
Tubes shall be visually examined to ensure conformity to the requirements of 8.4.1.
When Option 6 is specified, the tubes of quality TR2 shall be subjected to Non-Destructive testing for the
detection of longitudinal imperfections in accordance with EN ISO 10893-2, EN ISO 10893-3 or EN ISO
10893-10 to acceptance level 3, sub-category C, where applicable.
Regions at the tube ends not automatically tested shall either be subjected to manual/semi-automatic
For retest, sorting and reprocessing the requirements of EN 10021 shall apply.
12 Marking
12.1 Marking to be applied
The marking shall be indelibly marked on each tube at least at one end. For tubes with outside diameter D ≤
51 mm the marking on tubes may be replaced by the marking on a label attached to the bundle or box.
the number of this European Standard and the steel name (see 5.2).
an identification number (e.g. order or item number), which permit the correlation of the product or delivery
Example of marking:
EXAMPLE X – EN 10216-1 - P265TR2 - Y - Z 1 - Z 2
where
Option 12: Additional marking, as agreed upon at the time of the enquiry and order, shall be applied.
13 Protection
The tubes shall be delivered without a temporary protective coating.
Option 13: A temporary protective coating or durable coating and/or lining shall be applied.
(astm-a335-chrome-moly-pipe.php) (astm-a213-alloy-tubes.php)