CHEMITAC 111
DESCRIPTION
Chemitac 111 is a versatile thermoreactive adhesive that can be used as a primer under other
Chemitac covercoat adhesive for bonding NR, SBR, BR, CR, NBR, HNBR, IIR, CIIR, BIIR, CSM and
EPDM or as a one-coat adhesive for bonding NBR, ACM and solid PU to rigid substrates.
TYPICAL PROPERTIES
Solvents MEK/MIBK
CHEMICAL COMPOSITION
SURFACE PREPARATION
Rev.1 – 28.05.21
1
TECHNICAL DATA SHEET
2. Surface treatment – In order to achieve good adhesion results, the surface must be
either mechanically or chemically treated before the application of the adhesive.
§ Chemical treatment – Phosphatizing, anodizing and KTL coatings are the most
used methods.
§ Mechanical treatment – We recommend grit blasting the surface to a roughness
(Rz) greater than 15 microns. Steel grit should be used for ferrous metals such as
steel and iron; for other nonferrous metals, the use of aluminum oxide is
recommended. Care should be taken to maintain grits clean. Blasting residues
should be removed before the application of the adhesive. Layover time between
blasting and adhesive application should be kept to a minimum in order to avoid
oxidation.
ADHESIVE APPLICATION
Agitation – We recommend stirring Chemitac 111 before the application to avoid settling.
Dilution – We recommend the dilution be always made with MEK or MIBK. Dilution of the
product depends upon the type of application.
Application Layer – The film obtained by applying Chemitac 111 is thin and gray. The layer
thickness should be 3-8 microns.
Drying – Drying time is usually 30-45 minutes at room temperature. If it is necessary to reduce
drying time, we recommend using circulating air at 70ºC for 15 minutes maximum. Check the
purity of drying air to avoid contamination. The adhesive film should be completely dry before
the application of the covercoat adhesive and/or vulcanization.
The application layer and drying time values are to be used as reference. They may deviate based
on processing conditions. For more details and guidance, please contact us at
[email protected].
Layover time – Coated parts can be stored for 30 days before vulcanization in a clean and
moisture-free condition.
CAUTIONARY INFORMATION
Before using this product, please refer to the Safety Data Sheet for safe use and handling
instructions.
Rev.1 – 28.05.21
2
TECHNICAL DATA SHEET
STORAGE
Keep the container tightly closed and away from heat sources. Maximum temperature storage
is 25ºC.