Additive Manufacturing
Additive Manufacturing
net/publication/334545466
CITATIONS READS
21 23,326
2 authors, including:
SEE PROFILE
All content following this page was uploaded by Solomon Dufera Tolcha on 18 July 2019.
ABSTRACT
Additive manufacturing (AM) is a latest technology that could improve manufacturing process by building up thin
layers of materials from digitized three-dimensional (3D) designs virtually constructed using advanced CAD software.
This technique affords the creation of new types of object with unique material properties. But while AM is widely billed
as ‘the next industrial revolution’, in reality there are still significant hurdles for successful commercialisation of the
technologies. This paper aims to provide a comprehensive review of literature, technologies and manufacturing practices
on modern Additive Manufacturing.
KEYWORDS: Additive Manufacturing (AM), 3D-Printing, Rapid Prototyping (RP), Stereo Lithography (SL)
1. INTRODUCTION
Additive Manufacturing (AM) technology, which is referred as three dimensional printing technology which
produces objects layer-by layer (additively), rather than subtracting similar to a two dimensional printer with the only
difference that a third dimension (z-axis) is added, which is also called the building direction (Reeves, 2009)
Historically, AM technology was used to build conceptual prototypes referring to that process as Rapid
Prototyping (RP), a term which is still often used as a synonym to AM. Those prototypes were meant only to accelerate the
development phase of a product and under no circumstance are comparable to the end product with respect to material,
durability and quality (Feenstra, 2002). Rapid Manufacturing (RM) has evolved through RP due to technological
advancements defined by Rudgley (2001) as “the manufacture of end-use products using additive manufacturing
techniques (solid imaging)”.RM was responsible for approximately 20% of overall AM revenues in 2010, as per
2011Wohlers Report.
A sub-category of RM is Rapid Tooling (RT) whose aim is to create consistent tools which serve traditional
manufacturing procedures (Dimov, 2001). RT has been mostly used to create injection molds but recent developments
enable RT technology to be used for other tooling processes like casting and forging (Levy et al., 2003). RT further
portioned into direct tooling and indirect tooling. In direct tooling moulds are layer manufactured for use, and indirect
tooling, a master model is created and furthermore used to produce a casted mould. According to 2009 Wholers Report,
16% of AM processes were used for direct part production (RM), 21% for functional prototypes (RP) and 23% for tooling
and metal casting patterns (RT) from which approximately 56% and 9% of process preferences were direct metal and
direct polymer tooling respectively (Levy et al., 2003). In AM, object representation is stored in a STL file (stereo
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
90 K. Srinivasulu Reddy & Solomon Dufera
lithography), generated by conventional CAD software or obtained from Magnetic Resonance Imaging, laser scanning,
Computer Tomography (CT) and mathematical modelling software (Reeves, 2009). Afterwards, the STL file is imported
into slicing software in which the three dimensional digital object is sliced into layers and oriented appropriately in order to
define the best possible tool path for the printer which then creates the object via selective placement of material
(Campbell et al., 2011). Furthermore, it is essential to choose the appropriate building direction as it can change
specifications of the object such as lead time, cost and quality. Choosing a direction other than the optimum would lead to
more layers required resulting in increased lead time needed to manufacture the product (Reeves, 2009).
This paper aims to provide a comprehensive review of literature, technologies and manufacturing practices of
Additive Manufacturing and its sub category Rapid Tooling. The paper is organized as follows. In section two the most
widely applied and advanced technological processes of AM are presented. This section is also reviewed the technological
limitations and design restrictions of AM. Section three focuses on the adoption of AM by various industries. Finally, in
section four the possible outcome and the impact of AM technology adoption are discussed.
AM refers to a group of technologies that build physical objects directly from three dimensional CAD data. AM
adds liquid, sheet, wire or powdered materials, layer-by layer, to form component parts with little or no subsequent
processing requirements. This approach provides a number of advantages including near 100% material utilisation, short
lead timesandun-rivalled geometric freedom of design.
The ASTM has defined ‘additive manufacturing’ as a (ASTM international, 2012) : “ process of joining materials
to make objects from 3D models data, usually layer upon layer, as opposed to subtractive methodologies, such as
traditional machining.”
Since the onset of layer based processing for creating 3D components, a number of terms have evolved and as
such various terminology derivations have arisen. In more recent times, this has resulted in some misunderstanding or
misuse of terminology contributing to a ‘weakness’ in its advancement. The innovative nature of the technology and lack
of available standardisation have also contributed to this.
‘Rapid Prototyping’ seems to be the earliest describer and trends to be deemed ‘layer based processing for
creating 3D components in its infancy’. However, considerable progress in the field has taken the technology far beyond
that of ‘prototyping’. 3D printing, a term brought about in the 90s, has been widely used since and has become a wider
spread term for creating layered 3D components, more generally known for low- cost 3D home printing and some of the
larger commercial 3D printing systems. The term ‘Additive Manufacturing’ was later introduced and seems to have taken
the position for describing the technology overall, and more specifically for industrial applications and professional high
end equipment and applications. Figure 1 shows a number of terms for AM.
Due to the layer based manufacturing, sometimes additive manufactured parts require post conditioning. As a
result of these additional steps, AM can be divided into many categories. From the CAD model to the actual part, AM
technology is separated to eight different steps (Gibson et al, 2010)
AM starts with designing a model with any professional CAD software. The output model has to be a 3D or
surface representation of the actual part. Scanning and reverse engineering equipment could be also be used to generate
this model. (Gibson, Rosen, & Stucker, 2010, p. 4)
STL is the standard file type for the AM machines. Once a CAD model is created it should be saved in STL
format through the CAD software. STL file translates the surface in the CAD model to a mesh of triangles. The number of
the triangles controls the precision of the rounded surfaces. The CAD software allows the user to control the number and
the size of those triangles (Stratasys Ltd., 2015).
The STL file should be transferred to the machine. The file should be verified for its right size and build
orientation. Also if there are multiple parts they should be properly placed so they wouldn’t overlap with other parts.
AM Machine Setup
Machine setup is a crucial step in the process. The parameters should be properly set up to achieve the tolerances
of the manufactured part. Layer thickness, orientation, energy provided, timing and roller speeds can be named as some of
these parameters.
Build Phase
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
92 K. Srinivasulu Reddy & Solomon Dufera
This is step is more of automated process done by the machine. Partial monitoring will be required to ensure there
are no errors and the machine would not run out of material.
Removal
In this phase the machine is done producing the part and the user has to take it out. The user should follow the
safety protocols and proper shut down procedures. This will ensure the safety of the user and the machine.
Once the parts are produced they might need some additional treatment such as curing, sintering and cleaning. At
these stages parts may be weak and they should be handled with care.
Various AM processes have been introduced to the commercial market by industrial companies, including the
Electro Optical Systems (EOS) in Germany, Arcam in Sweden, MCP Tooling Technologies in the UK, and Stratasys, 3D
Systems, Optomec, and Z Corporation in the United States, among others [6]. There are several systems to classify the AM
processes, e.g., the one proposed by the ASTM F42 Committee classifies the AM processes into seven areas [1].
Powder bed fusion (PBF) methods use either a electron beam or laser source to melt and fuse material powder
together. Electron beam melting (EBM), methods require a vacuum but can be used with metals and alloys in the creation
of parts. All PBF processes involve the spreading of the powder material over previous layers. There are different
mechanisms to enable this, including a roller or a blade. A hopper or a reservoir provides fresh material supply. Direct
metal laser sintering (DMLS) is the same as Selective Laser Sintering (SLS), but with the use of metals and not plastics.
This process sinters the powder, layer by layer. Selective Heat Sintering differs from other processes by way of using a
heated thermal print head to fuse powder material and, layers are added with a roller in between fusion of layers as before
(Gibson et al., 2010). Figure 2 bellow shows Powder bed fusion methods
Selective Laser Melting (SLM) Compared to SLS, SLM is often faster (Gibson et al., 2010), but requires the use
of an inert gas, has higher energy costs and typically has a poor energy efficiency of 10 to 20 % (Gibson et al., 2010). The
process uses either a roller or a blade to spread new layers of powder over previous layers. When a blade is sed, it is often
vibrated to encourage a more even distribution of powder (Gibson et al., 2010). A hopper or a reservoir below or aside the
bed provides a fresh material supply.
Selective Heat Sintering (SHS) uses a heated thermal print head to fuse powder material together. As before,
layers are added with a roller in between fusion of layers. The process is used in creating concept prototypes and less so
structural components. The use of a thermal print head and not a laser benefits the process by reducing significantly the
heat and power levels required. Thermoplastics powders are used and as before act as support material. The ‘Blue printer’
is a desktop 3D printer that uses the SHS technology, with a build chamber of 200mm x 160mm x 140mm, print speed of
23mm/hour and a layer thickness of 0.1mm (Blue Printer SHS, 2014).
Direct Metal Laser Sintering (DMLS) uses the same process as SLS, but with the use of metals and not plastic
powders. The process sinters the powder, layer by layer and a range of engineering metals are available.
Electron Beam Melting (EBM) Layers are fused using an electron beam to melt metal powders. Machine
manufacturer Arcam used electromagnetic coils to control the beam and a vacuum pressure of 1×10-5 mba (EBM Arcam,
2014). EBM provides models with very good strength properties due to an even temperature distribution of during fusion
(Chua et al., 2010). The high quality and finish that the process allows for makes it suited to the manufacture of high
standard parts used in aeroplanes and medical applications. The process offers a number of benefits over traditional
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
94 K. Srinivasulu Reddy & Solomon Dufera
methods of implant creation, including hip stem prosthesis (Araguaia, 1995). Compared to CNC machining, using EBM
with titanium and a layer thickness of 0.1mm, can achieve better results, in a faster time and can reduce the cost by up to
35%.
Directed Energy Deposition (DED) is a more complex printing process commonly used to repair or add additional
material to existing components (Gibson et al., 2010), also called as Laser engineered net shaping, directed light
fabrication, direct metal deposition, 3D laser cladding.
A typical DED machine consists of a nozzle mounted on a multi axis arm, which deposits melted material onto
the specified surface, where it solidifies. The process is similar in principle to material extrusion, but the nozzle can move
in multiple directions and is not fixed to a specific axis. The material, which can be deposited from any angle because of 4
and 5 axis machines, is melted upon deposition with electron or laser beam. The process can be used with polymers,
ceramics but is typically used with metals, in the form of either powder or wire. Typical applications include repairing and
maintaining structural parts.
The DED process uses material in wire or powder form. Wire is less accurate due to the nature of a pre-formed
shape but is more material efficient when compared to powder (Gibson et al., 2010). The method of material melting varies
between a laser, an electron beam, and laser beam or 201plasma arc, all within a controlled chamber where the atmosphere
has reduced oxygen levels. With 4 or 5 axis machines, the movement of the feed head will not change the flow rate of
material, compared to fixed, vertical deposition (Gibson et al., 2010).
Whilst in most cases, it is the arm that moves and the object remains in a fixed position, this can be reversed and a
platform could be moved instead and the arm remain in a fixed position. The choice will depend on the exact application
and object being printed. Material cooling times are very fast, typically between 1000 – 5000 degrees Celsius / second
(Gibson et al., 2010). The cooling time will in turn affect the final grain structure of the deposited material, although the
overlapping of material must also be considered, where the grain structure is changed as the overlapping can cause re-
melting to occur, resulting in a uniform but alternating micro-structure. Typical layer thicknesses of 0.25 mm to 0.5 mm
(Gibson et al., 2010)
Fused deposition modelling (FDM) is a common material extrusion process in which material is drawn through a
nozzle, where it is heated and is then deposited layer by layer. The nozzle can move horizontally and platform moves up
and down vertically after each new layer is deposited. FDM is a commonly used technique used by many inexpensive,
domestic and hobby 3D printers.
The process has many factors that influence the quality of final model but has great potential and viability when
these factors are properly controlled. Whilst FDM is similar to all other 3D printing processes, as it builds layer by layer, it
varies in the fact that material is added through a nozzle under constant pressure and in a continuous stream. This pressure
must be kept steady and at a constant speed to enable accurate results (Gibson et al., 2010). Material layers can be bonded
by the use of chemical agents or temperature control. Material is often added to the machine in spool form as shown in
figure 3.
Advantages of the material extrusion process include use of readily available ABS plastic, which can produce
models with good structural properties, close to final production model. In low volume cases, this can be a more
economical method than using injection moulding. However, the process requires many factors to control in order to
achieve a high quality finish. The nozzle size and shape will affect the final quality of the printed object because nozzle
which deposits material will always have a radius, as it is not possible to make a perfectly square nozzle and this (Chua et
al., 2010). Accuracy and speed of FDM are low when compared to other processes and the quality of the final model is
limited to material nozzle thickness (Krar et al., 2003).
One method of post processing to improve the visual appearance of models is through improving material
transmissivity. Methods have been explored by Ahnet all; include increasing temperature and the use of resin. Experiments
using cyamo acrylate resin, often used to improve the strength of parts, resulted in a 5% increase in transmissivity after 30
seconds and sanding (Ahn, 2004). As with most heat related post processing processes, shrink- age is likely to occur and
must be taken into account if a high tolerance is required.
Vat polymerisation uses a vat of liquid photopolymer resin, out of which the model is constructed layer by layer.
An ultraviolet (UV) light is used to cure or harden the resin where required, whilst a platform moves the object being made
downwards after each new layer is cured.
As the process uses liquid to form objects, there is no structural support from the material during the build phase.
Unlike powder based methods, where support is given from the unbound material. In this case, support structures will often
need to be added. Resins are cured using a process of photo polymerisation (Gibson et al., 2010) or UV light, where the
light is directed across the surface of the resin with the use of motor controlled mirrors (Grenda, 2009). Where the resin
comes in contact with the light, it cures or hardens.
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
96 K. Srinivasulu Reddy & Solomon Dufera
Stereo Lithography (SL) is the first commercialized AM technology using laser technology to achieve the
photo-polymerization of liquid resin which becomes consistent when exposed to the laser (UV light) in order to create
plastic objects (Figure 5). After each layer is completed the platform lowers itself by one layer usually allowing the blade
to refill the liquid resin on the surface of the object (xpress3d, 2012). This technology is still used for RP to create
conceptual polymeric products and for indirect RT to create master patterns for casting processes. Generally, the layer
thickness achieved depends on the model of the machine and ranges between 0.05 mm and 0.15 mm with a roughness of
approximately 35-40 µm Ra (Reeves, 2009). The main advantages of SL are temperature resistance and the creation of
complex structures with very thin walls. The main disadvantage of SL is the necessary support structure to fabricate
objects which consumes additional material and extended production time (Petrovic et al., 2011).
Post Processing: Parts must be removed from the resin and any excess resin fully drained from the vat. Supports
can be removed using a knife or sharp implement. Care must be taken not to contaminate the resin and the appropriate
safety precautions must be taken. Methods for removing resin and supports include the use of an alcohol rinse followed by
a water rinse. The processing may be lengthy as parts may require additional scrubbing to remove material fully. Finally,
parts can be dried naturally or by using an air hose. UV light is often used as well, for a final post cure process to ensure a
high quality object.
The binder jetting process uses two materials; a powder based material and a binder. The binder acts as an
adhesive between powder layers. The binder is usually in liquid form and the build material in powder form. A print head
moves horizontally along the x and y axes of the machine and deposits alternating layers of the build material and the
binding material. After each layer, the object being printed is lowered on its build platform.
Due to the method of binding, the material characteristics are not always suitable for structural parts and despite
the relative speed of printing, additional post processing (see below) can add significant time to the overall process.
As with other powder based manufacturing methods, the object being printed is self-supported within the powder
bed and is removed from the unbound powder once completed. The technology is often referred to as 3DP technology and
is copyrighted under this name.
The binder jetting process allows for colour printing and uses polymers and ceramics and metals. This process is
faster than others and can be further speed up by increasing the number of print head holes that deposit material. The two
material approaches allows for a large number of different binder-powder combinations and various mechanical properties
of the final model to be achieved by changing the ratio and individual properties of the two materials. Therefore, the
process is well suited when the internal material structure needs to be of a specific quality.
Layers of build material, often in granular and powder form, are held together using the adhesive binder. The print
head deposits the binding material in micro amounts and the powder material is used in creating the majority of the overall
object mass. A heated build chamber can help to speed up the printing process by increasing the viscosity of the materials
(Chua et al., 2010).
Post Processing: The overall process time is extended as it requires the binder to set and the part is often allowed
to cool in the machine to fully solidify to achieve a high quality finish (Gibson et al., 2010). Post processing is often
required to make the part stronger and give the binder-material better mechanical and structural properties (Gibson et al.,
2010).
Material jetting creates objects in a similar method to a two dimensional ink jet printer. Material is jetted onto a
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
98 K. Srinivasulu Reddy & Solomon Dufera
Material is jetted onto the build surface or platform, where it solidifies and the model is built layer by layer.
Material is deposited from a nozzle which moves horizontally across the build platform. Machines vary in complexity and
in their methods of controlling the deposition of material. The material layers are then cured or hardened using ultraviolet
(UV) light.
As material must be deposited in drops, the number of materials available to use is limited. Due to viscous nature
and drop forming nature of polymers and waxes are commonly used materials.
Material Jetting builds objects in a similar method to a two dimensional ink jet printer. Multiple materials can be
used in one process and the material can be changed during the build stage. Material is jetted onto the build platform
surface in droplets, which are formed using an oscillating nozzle. Droplets are then charged and positioned onto the surface
using charged deflection plates. This is a continuous system which allows for a high level of droplet control and
positioning. Droplets which are not used are recycled back into the printing system.
Drop on Demand (DOD) is used to dispense material onto the required surface. Droplets are formed and
positioned into the build surface, in order to build the object being printed, with further droplets added in new layers until
the entire object has been made. The nature of using droplets, limits the number of materials available to use. Because of
viscous nature and ability to form as drops, polymers and waxes are suitable and often used. Viscosity is the main
determinant in the process; there is a need to re-fill the reservoir quickly and this in turn affects print speed. Unlike a
continuous stream of material, droplets are dispensed only when needed, released by a pressure change in the nozzle from
thermal or piezoelectric actuators. Droplets are deposited by thermal actuators at a very fast rate and use a thin film resistor
to form the droplet. Piezoelectric method allows wide range of materials and often considered better option.
Post processing: Support material can be removed using a sodium hydroxide solution or water jet. Due to the
high accuracy of the process technology, the level of post processing required to enhance the properties is limited and the
functional and aesthetic qualities of a part are largely determined during the printing stage. Stratasys polyjet technology
cures the material using UV light and therefore no post curing process is needed.
Sheet lamination processes include ultrasonic additive manufacturing (UAM) and laminated object manufacturing
(LOM). The Ultrasonic Additive Manufacturing process uses sheets or ribbons of metal, which are bound together using
ultrasonic welding. This process does require additional CNC machining and removal of the unbound metal during the
welding process. Laminated object manufacturing (LOM) uses a similar layer by layer approach but uses paper as material
and adhesive instead of welding. Cross hatching method is used during the printing process to allow for easy removal of
post build in LOM process. Laminated objects are often used for aesthetic and visual models and are not suitable for
structural use. UAM uses metals like aluminium, copper, stainless steel and titanium (Ultrasonic Additive Manufacturing
Overview, 2014). UAM uses low temperature and allows for internal geometries to be created. The process can bond
different materials and requires relatively little energy, as the metal is not melted.
Polymers are the most widely used material in AM. Most notably, nylon is the most widely used polymer because
it melts and bonds better than other polymers (Guo, N. & Leu, M.C, 2013)
Metal products can be formed in a “direct” way – by melting metal particles together or an “indirect” way – by
bonding the metal with post-processing. There are many ways and AM methods to form metals through the indirect or
direct way (Ibid)
Ceramics are used in AM processing because of their chemical structures and resistance to high temperatures.
Unfortunately, these materials can be brittle making them difficult to manufacture especially if complex geometries are
involved. Examples of ceramics include alumina, silica and zirconia. Ceramics can be produced through indirect or direct
process (Guo, N. & Leu, M.C, 2013)
Composites are, as their name suggests, materials that are combinations of two or more materials, either naturally
(in nature) or engineered. Composites can be mixed uniformly or no uniformly to make different compounds (Ibid).
Functionally graded materials can be created through AM processing. Guo & Leu (2013) show that, “One
example is a pulley that contains more carbide near the hub and rim to make it harder and more wear resistant and less
carbide in other areas to increase compliance.” (Ibid)
AM technologies started more than twenty years ago but public attention has only focused on it in the latest years,
mainly owing to the publicity around developments in 3D printing (Hype Cycle for 3D Printing, 2014) This is illustrated
by the Gartner Hype Cycle (Hype Cycle for 3D Printing, 2014) (Figure 8) which demonstrates what the expectations are
for technologies to be close to adoption. For instance, up to 2009, AM is not even referenced. Only in 2010, AM appears
for the first time with an estimation of 5-10 years to maturity (Figure 8). In 2013, nevertheless we already see that
industrial applications appear, such as Enterprise 3D Printing already situated on the ‘slope of enlightenment’, almost near
real production. There are also concepts emerging for 3D scanners and consumer 3D printing, estimated to reach in 5-10
year the ‘plateau of productivity’, close to mainstream adoption.
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
100 K. Srinivasulu Reddy & Solomon Dufera
Figure 8: 2010 and 2013 Gartner Hype Cycles (Hype Cycle for 3D Printing, 2014)
Another information matrix that was released by Tuan Tranpham, from Objet Inc., helps to compare the various
role-players in the AM industry (Materials KTN., 2012). The horizontal axis, from left to right follows the stages of
development from obtaining 3D content to producing the physical part. The vertical axis, from the bottom up shows the
different categories of user-groups for each of the various technologies presented
Applications for parts made by additive manufacturing continue to grow. An industry that was once known for
rapid prototyping has extended its reach to a broader, more diversified range of possibilities.
As applications grow, the users of the technology grow as well. Once relegated to high-tech laboratories at
Fortune 100 companies, AM now is employed by the smallest organizations – and increasingly even by individuals. At
every point along that spectrum are users with new ideas and unique applications. It seems that almost any problem
involving three-dimensional objects can be solved faster and better with the use of AM technology (Neal de Beer, 2013)
The prerequisite for using AM was once a CAD model, but now input can be generated by medical scan data,
entertainment software, as is the case with computer game avatars, and simple drawing and sketching programs. This frees
the average individual from the need to learn complex, technical (and relatively costly) software in order to create 3D
content for additive manufacturing. In addition, users can purchase 3D content online from companies like Shape ways or
download them for free at other companies like Thing verse. Prototyping was among the earliest applications of AM
technologies and remains one of the most powerful tools for product development. As material quality, surface finish, and
dimensional accuracy have improved, AM models have been increasingly used for functional prototyping and for tooling
and metal casting processes (Neal de Beer, 2013)
The Gartner Hype Cycle mainly represents trends to the adoption of a technology. However, AM technologies
have already established themselves in some sectors at the level of real production. A survey conducted by Wohler’s over
100 key AM system manufacturers and service providers (representing over 100,000 users and customers) showed that the
industrial/business machines are the leading sectors using AM technologies (Figure 10). Immediately follows the consumer
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
102 K. Srinivasulu Reddy & Solomon Dufera
products/electronics and motor vehicles sectors. Medical/dental and aerospace sectors are also great users of AM
technologies (Wholers Report, 2014).
The main characteristics of the manufacturing sectors currently using AM technologies for real production
conditions are the following:
a)Consumer Products
Within the consumer market there is a large array of products being manufactured by various AM technologies
including toys, games, home furnishings, fashion items, sports equipment etc. Artists, jewellers and fashion designers are
using AM in a range of ways including to produce one off bespoke pieces (figure 11)
Survey results from Wohlers 2012, showed consumer products/electronics as leading sector and reported that it
had been for the last seven years (Hohlers, 2012). In UK, when combining the creative industries, consumer products and
fashion/ home categories as one generic sector, SIG UK reported that this sector accessed some £2. 5 millions of industry
contribution to lever around £ 7.5 million supports for sector (Materials KTN, 2012).
One of the principles of uses of AM parts in consumer goods industry is to produce prototypes and models.
Although the main use of additive fabrication is making prototypes, technology is developing towards “rapid
manufacturing” which is also called as “direct digital manufacturing” (DDM) by the Society of Manufacturing Engineers.
Industry projection for the future would involve the use of a single machine for the design, prototype, and creation of
finished parts.
b) Electronics
The electronics industry is using AM to print electronic devices and components. Similarities between AM and
direct write technologies can also be made, particularly for the deposition of conductive materials onto conformal surfaces.
Inkjet technology can be used to print passive circuit components such as resistors, capacitors and inductors, as well as
diodes, and circuit interconnections (figure 12)
c) Motor Vehicles
More and more car manufacturers are using the benefits of AM in the production of concept cars. The process
opens a new world of design freedom and allows concept cars to be built faster than with more traditional methods. 3D
models are used for everything from concept creation to production planning, allowing design engineers to speed up and
improve the development process. The automotive industry has historically used AM as an integral tool in the design
process. The fast-paced design cycles in the automotive industry require a rapid prototyping solution that can produce
almost any geometry with a variety of material properties, quickly and cost effectively.
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
104 K. Srinivasulu Reddy & Solomon Dufera
AM techniques have been applied within the medical and dental arena for the creation of assistive, surgical and
prosthetic devices, surgical implants, and scaffolds for tissue engineering. For instance, AM allows complex parts to be
created specifically for the patient direct from a 3D CAD model generated from a patient’s CT or MRI scan. Accurate
patient specific implants produced using the 3D scan data can reduce the removal of healthy bone, eliminate the need for
bone grafting, promote effective planning of implantation/surgery and shorten the time of anaesthesia. There is also the
possibility that the customisation enabled by AM will result in increased implant-life eliminating the need for further
surgery. [ ]
e) Aerospace
AM is an attractive alternative manufacturing route for the aerospace industry, due primarily to its high material
use efficiency and ability to process aerospace grade titanium and nickel alloys. AM is seen as an enabling technology for
light-weighting or topology optimisation, because of its capability to create complex structures. This can have the
additional benefits of improving performance and reducing waste. AM has also been used for testing of complex or
difficult to implement designs, including extensive tests in ‘full engine’ rigs.
Although we can already see significant usage of AM in particular sectors, there is still a massive potential to
further enhance its use and even enter new sectors. However, one of the present problems for AM is that many of the
traditional manufacturing sectors are not aware of, or do not fully understand, how they can utilise AM. AM will replace
certain manufacturing methods, but not all of them while it has the added potential to complement many of those it cannot
substitute.
f) Architecture
In the field of architecture, AM is used to produce scaled replica models of buildings and constructions. A
continued challenge in this field of application however exists in scaling down features such as window frames and guard
railings. When scaling down a construction to a size that can be produced using AM, any such features virtually disappear
and need to be reconstructed on the scaled CAD model – which is a time consuming exercise. Below is a selection of
examples where 3D printing was used to construct architecture models.
Additive manufacturing is disruptive in nature and has the potential scope to transform new ideas and
methodologies outside of ‘conventional’ industry norms.
“As comparatively young technology, AM already today raises high expectations. Since AM is NOT just another
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
106 K. Srinivasulu Reddy & Solomon Dufera
technology to replace conventional ones but requires a new thinking in entire business Models, Progress is needed in
various elements of such a chain. Ignoring that and pushing AM too hard into traditional rules at this early stage may
inflict damage on the technology and also ruin market reputation” (Lenz, 2013)
6.1 AM Challenges
The AM value chain can be described in five areas: 1) materials, 2) systems, 3) software, 4) application of design,
and 5) production.37 although all of these areas help in the creation and functioning of AM technologies, the market is
fragmented with only a few key players in each area. Moreover, overall market penetration of AM is not very large (only
about 1%) and the company’s size limit investment in R&D indicates that one player cannot be active in all areas
(Services, Licenses, Training and Seminars, Powder, Application Design, and Software).39
There are several challenges in widespread adoption of AM: (Energetic Inc. (2013), (Opens haw, E. & Cotteleer,
M., 2014) and (Merissa Piazza, 2015)
• Process Control: Feedback control systems and metrics are needed to improve the precision and reliability of the
manufacturing process and to increase throughput while maintaining consistent quality
• Tolerances: Some potential applications would require micron-scale accuracy in printing (Bullinger,2009)
• Finish: The surface finishes of products manufactured using additive technology require further refinement. With
improved geometric accuracy, finishes may impart corrosion and wear resistance or unique sets of desired
properties.
• AM has been used for prototyping for years, but the technology is now being used to directly manufacture
products in small batches (Huang, Y et al, 2015).
• PWC calls the road from using AM for prototyping to direct manufacturing the “long mile.” Most
manufacturers see AM as a tool for prototyping and small batch manufacturing, but not for large production
runs(Price Waterhouse Cooper , 2014)
• Estimates indicate that IP losses due to 3D printing will reach $100 billion by 2018. (Gartner,2015)
• IP is considered a major issue since the marginal cost of 3D printing is significant (Price Waterhouse Cooper,
2013)
• Educational challenges:
• AM is a multidisciplinary area, therefore it is difficult to train the workforce because technologies involve a
variety of disciplines (modelling, physics, metallurgy, and statistics).
• Difficult for one person to have adequate expertise in all areas to understand technology development
One of the biggest challenges to widespread adoption of AM is the small amount of materials (e.g., polymers,
metals, and ceramics) that can be used to fabricate items.46 Every year new materials are advanced in AM, resulting in
better microstructures, and enhanced material tolerability.47 The types of materials used in AM (for more technical
information (see Guo & Leu (2013):
Polymers are the most widely used material in AM. Most notably, nylon is the most widely used polymer because
it melts and bonds better than other polymers (Guo, N. & Leu, M.C, 2013)
Metal products can be formed in a “direct” way – by melting metal particles together or an “indirect” way – by
bonding the metal with post-processing. There are many ways and AM methods to form metals through the indirect or
direct way (Ibid)
Ceramics are used in AM processing because of their chemical structures and resistance to high temperatures.
Unfortunately, these materials can be brittle making them difficult to manufacture especially if complex geometries are
involved. Examples of ceramics include alumina, silica and zirconia. Ceramics can be produced through indirect or direct
process (Guo, N. & Leu, M.C, 2013)
Composites are, as their name suggests, materials that are combinations of two or more materials, either naturally
(in nature) or engineered. Composites can be mixed uniformly or no uniformly to make different compounds (Ibid).
Functionally graded materials can be created through AM processing. Guo & Leu (2013) show that, “One
example is a pulley that contains more carbide near the hub and rim to make it harder and more wear resistant and less
carbide in other areas to increase compliance.” (Ibid)
To better understand and use advanced materials in AM processes, it is suggested that research in the following
areas be conducted: 53
• Develop better tools for micro- and nano- AM to build items atom by atom Develop sustainable materials
Other challenges in AM include understanding the fundamentals of materials, processes, and applications. For
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
108 K. Srinivasulu Reddy & Solomon Dufera
example, some scientists are grappling with the physics behind AM, while others question why certain materials can be
used in AM and not others.
6.2 AM Opportunities
Overall, studies cite three major benefits and opportunities that AM can provide:
• Innovation
AM has been a game changer for rapid prototyping. AM allows companies to change design on the fly in a just a
few hours, as opposed to the traditional method of creating a prototype from wood or metal from machine shops.
AM can contribute to entrepreneurial success because entrepreneurs can have a low cost mechanism to produce a
prototype
6.2.2 Innovation
• AM spurs innovation because it allows users to manufacture complex structures quickly and efficiently (Haung et
al, 2015)
• There is conjecture that 4D printers are being built to incorporate “shape memory fibers” into inks to create
different forms(Price Waterhouse Cooper (2014))
• Price Waterhouse Cooper (PWC) has conducted a survey of manufacturers that shows small firms are keeping
pace with large firms in the adoption of 3D printing.
• Conversation has begun about how universities and industry can collaborate on this technology through
technology transfer, but collaboration seems to be limited to federally funded programs (i.e. SBIR/STTR, NSF)
(Haung et al, 2015)
• SBIR/STTR
There is a significant amount of academic literature of the cost savings attributed to AM. An excellent review of
this literature can be found in Thomas and Gilbert (2014). According to Thomas and Gilbert (2014)
• AM of metal parts, combined with part redesign, can show significant cost savings. The field is starting to
consider the implication of electricity consumption in AM production as a component of the cost savings
(Baumers et al ,2010 and Baumers et al 2011)
A 2013 article by Huang et al examined the societal impact of AM. The positive impacts of AM included:
customizable healthcare products, reduced environmental impact (reduced energy use and reduced material use), simplified
supply-chain. The authors call for more research on the cost savings due to energy reduction since this is a major cost for
manufactures (Haung et al, 2013).
As manufactures can create products on demand with AM, the amount of inventory they need to keep on hand
decreases. Inventory decreases come from the ability to manufacture needed parts on demand. Inventory costs are a
significant portion of manufacturers’ costs. Moreover, in traditional manufacturing if a manufacturer does not have a part
in inventory, they have to order the part and this can delay production. AM can reduce these issues and costs (Walters et al,
2009 and Piazza, et al, 2014). According to Thomas et al Business cost savings can be achieved using AM because it can
reduce the amount of transportation of parts with traditional manufacturing (Thomas et al, 2014). Dollar et al adds that, as
the technology improves, the quality of AM machines will increase, while the cost will go down (Dollar et al, 2013). AM
equipment has followed the digital technology progress model in which more capable and cheaper machines are introduced
each year, following Moore’s Law.
New Markets
There is significant discussion about technology advancements and innovation that takes place with AM, but little
discussion on potential businesses and profits that can be made from this technology.
It is estimated that there are seven areas of revenue streams from this technology (Berger, L, 2013)
• Training and Seminars – training and seminars on AM technology, design, and use
• Powder – sales of metal powder (some AM processes require material in powder form)
Currently, metal powders, used in AM, are up to 30 times more expensive than their bulk counterparts; as the
volume demand for metal powder increases, the price will decrease (Price Waterhouse Cooper, (2013) It is estimated that
over the next few years the rate and speed of building products will increase while powder rates will decrease (Berger,
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
110 K. Srinivasulu Reddy & Solomon Dufera
2013). Some researchers have suggested that examining how AM can fit into the lifecycle costs of components and create
cost advantages is the best way to sell the technology (Lindeman, 2012). AM is also starting to be used in the consumer
market. Products such as home electronics, entertainment components, computer and mobile device parts, shoes and
fashion accessories, and customizable consumer products can use AM to create intricate designs or make it customizable.
REFERENCE
1. Wohlers Report 2014 – 3D Printing and Additive Manufacturing State of the Industry, Annual Worldwide
Progress Report, Wohlers Associates, 2014.
2. Wohlers, T, 2012, Wohlers Report 2012 – Additive Manufacturing and 3D Printing State of the Industry Annual
Worldwide Progress Report, Wohlers Associates Inc., Fort Collins, USA.
4. Materials KTN. (2012). Shaping our National Competency in Additive Manufacturing – A Technology
Innovation Needs Analysis Conducted by the Additive Manufacturing Special Interest Group for the Technology
Strategy Board.
6. Energetic Inc. (2013). Measurement Science Roadmap for Metal-Based Additive Manufacturing: Workshop
Summary Report. National Institute of Standards and Technology.
7. Openshaw, E. & Cotteleer, M. (2014, June 24). 3D Printing: A Powerful Technology, but No Panacea. Financial
Times.
8. Price Waterhouse Cooper. (2013). 3D Printing: A Potential Game Changer for Aerospace and Defence. Gaining
Altitude, 7. Retrieved on March 12, 2015 from www.pwc.com/us/gainingaltitude
9. National Institute of Standard and Technology. 2013. Measurement Science Roadmap for Metal- Based Additive
Manufacturing.
10. Bullinger, H., Technology Guide - Principles, Applications, Trends. Springer, Berlin, 2009.
11. Huang, Y., Leu, M.C.,, Mazmunder, J., & Donmez, A. (2015). Additive Manufacturing: Current Sate, Future
Potential, Gaps, Needs, and Recommendations. Journal of Manufacturing Science and Engineering 137, 014001-
1-014001-10
12. Price Waterhouse Cooper (2014). 3D Printing and the New Shape of Industrial Manufacturing.
13. Gartner: 3D printing to result in $100 billion IP losses per year. (2013, October 14). Retrieved March 26, 2015
fromhttp://www.3ders.org/articles/20131014-gartner-3d-printing-to-result-in-100-billion-iplosses-per year.html
14. Price Waterhouse Cooper. (2013). 3D Printing: A Potential Game Changer for Aerospace and Defense. Gaining
Altitude, 7.
16. Merissa Piazza, 2015 Additive Manufacturing: A Summary of the Literature, Cleveland State University
17. Kruth, J.-P., Leu, M.C., and Nakagawa, T. (2007), “Progress in Additive Manufacturing and Rapid Tooling”,
CIRP Annals - Manufacturing Technology, Vol. 47(2), pp. 525–540.
18. Levy, G.N., Schindel, R, and Kruth, J.P. (2003), “Rapid manufacturing and rapid tooling with layer
manufacturing technologies: state of the art and future perspectives”, CIRP Annals, Vol. 52(2), pp. 589602.
19. Reeves, P. (2009), “Additive Manufacturing – A supply chain wide response to economic uncertainty and
environmental sustainability”, Econolyst Limited, The Silversmiths, Derbyshire, UK.
20. Rudgley, M. (2001), “Rapid Manufacturing – the revolution is beginning”, Proceedings of the uRapid 2001,
Amsterdam, Netherlands
21. Wholers, T. (2011) Wohlers Report 2011: State of Industry, Wholers Associates Inc., USA.
22. Kruth, J.-P., and Schueren, B. V.d. (1997), “Soft and hard rapid tools for polymer and metal casting/moulding”,
Proc. Colloquium EMO Hannover, Werkzeugbau – eine Branche mit Zukunft.
23. Dimov, S.S., Pham, D.T., Lacan, F., and Dotchev, K.D. (2001), “Rapid tooling applications of the selective laser
sintering process”, Assembly Automation, Vol. 21(4), pp.296-302.
24. Thomas, D. S., Gilbert, S. W. (2014, December). Costs and Cost Effectiveness of Additive Manufacturing: A
Literature Review and Discussion. NIST Special Publication 1176. Retrieved on March 31, 2015 from
http://dx.doi.org/10.6028/NIST.SP.1176
25. Baumers, M., C. Tuck, R. Hague, I. Ashcroft, and R. Wildman. 2010. “A Comparative Study of Metallic Additive
Manufacturing Power Consumption.” In 21st Annual International Solid Freeform Fabrication Symposium–An
Additive ManufacturingConference, Austin/TX/USA, 9th–11th August. Austin, TX.
26. Baumers, M., C. Tuck, R. Wildman, I. Ashcroft, and R. Hague. 2011. “Energy Inputs to Additive Manufacturing:
Does Capacity Utilization Matter?” In 22nd Annual International Solid Freeform Fabrication Symposium–An
Additive ManufacturingConference, Austin/TX/USA, 8th–10th August.
27. Huang, S., Liu, P., Mokasdar, A., & Hou, L. (2013). Additive Manufacturing and its Societal Impact: a Literature
Review. The International Journal of Advanced Manufacturing Technology. 67 (5-8), 11911203.
28. Walter, M., Holmstrom, J., Yrjola, H., (2004). Rapid manufacturing and its Impact on Supply Chain
Management. Logistics Research Network Annual Conference, September 9-10, 2004, Dublin, Ireland
29. 26 Piazza, M.C., Hill, E. & Schnoke, M. (2014). Machining Industry: Survey & Focus Groups. Cleveland, OH:
Cleveland State University.
30. Thomas, D. S., Gilbert, S. W. (2014, December). Costs and Cost Effectiveness of Additive Manufacturing: A
Literature Review and Discussion. NIST Special Publication 1176. Retrieved on March 31, 2015 from
http://dx.doi.org/10.6028/NIST.SP.1176
31. Dollar, A. M. (n.d.) Additive Manufacturing: State of the Art and Practical Design Notes. New Haven, CT: Yale
University
Impact Factor (JCC): 1.5429- This article can be downloaded from www.bestjournals.in
112 K. Srinivasulu Reddy & Solomon Dufera
32. Khajavi, S. H., Partanen, J., & Holmstrom, J. (2013). Additive Manufacturing in the Spare Parts Supply Chain.
Computers in Industry. In Press. Retrieved March 10, 2015 from
http://dx.doi.org/10.1016/j.compind.2013.07.008
33. Mack, C. (2015, March 30). The Multiple Lives of Moore’s Law. IEEE Spectrum. Retrieved March 30, 2015 from
http://spectrum.ieee.org/semiconductors/processors/the-multiple-lives-of-moores-law
34. Berger, R. (2013, November). Additive Manufacturing: A Game Changer for the Manufacturing Industry?
Presentation in Munich, Germany.
35. Lindemann, C., Jahnke, U., Moi, M., & Koch, R. (2012). Analyzing Product Lifecycle Costs for a Better
Understanding of CostDrivers in Additive Manufacturing. Paderborn, Germany: Direct Manufacturing Research
Center (DMRC), University of Paderborn.
36. Kendrick, A. (n.d.) 3D Printing: The Next Industrial Revolution? Tolland, CT: Nerac Inc.
37. Price Waterhouse Cooper. (2013). 3D Printing: A Potential Game Changer for Aerospace and Defense. Gaining
Altitude. Issue
38. Bradshaw, B. (2011, May 1). 3-D Printing Provides New Options for Prototyping, Moldmaking. Moldmaking
Technology. Retrieved March 30, 2015 from moldmaking
39. A Spin on Additive Manufacturing. (2013, September 17) Modern Machine Shop. Retrieved March 10,
40. Price Waterhouse Cooper (2014). 3D Printing and the New Shape of Industrial Manufacturing.
41. Huang, Y., Leu, M.C.,, Mazmunder, J., & Donmez, A. (2015). Additive Manufacturing: Current Sate, Future
Potential, Gaps, Needs, and Recommendations. Journal of Manufacturing Science and Engineering 137, 014001-
1-014001-10
42. Price Waterhouse Cooper (2014). 3D Printing and the New Shape of Industrial Manufacturing.
43. Ibid.
44. Huang, Y. & Leu., M.C. (2014, March). Frontiers of Additive Manufacturing Research and Education.