IMMERSION SILVER
Page 1 of 11
Revision: 09.22.08
PRODUCT OVERVIEW
Florida CirTechs Immersion Silver process plates a silver coating on copper. This silver coating is used as a lead-free solderable finish on printed circuit boards. Immersion Silver is a co-planar, dense finish that contains only silver. It is compatible with all assembly fluxes and solder pastes. Our Immersion Silver process consists of an acid cleaner, a peroxide-sulfuric microetch, an acidic pre-dip, the IS150 immersion silver bath, and an optional antitarnish bath called IS175. In the unlikely event that silver tarnish forms, we can provide a cleaner called IS127 that can be used to remove mild silver tarnish. Florida CirTechs Immersion Silver finish has a shelf life greater than 1 year, and is solderable through multiple assembly operations. Immersion silver does not migrate into copper, like immersion tin. As a result, the shelf life of immersion silver is much longer than immersion tin finishes.
Page 2 of 11
Revision: 09.22.08
DI Water Rinses 3x counterflow Pre-Dip for Immersion Silver IS150 Immersion Silver DI Water Rinses 2x counterflow
** Optional ** IS175 Silver Anti-tarnish
WORK FLOW
Hot DI Rinse
NOTES: DI water must be high purity, and be free of halides (e.g. chlorides). If halides are drug into the IS150 bath, then silver will precipitate out, and the silver deposit quality will decrease.
Page 3 of 11
Revision: 09.22.08
EQUIPMENT SPECIFICATIONS
MATERIALS TANKS: RACKS & BASKETS: HEATERS: PUMPS: FILTERS AND HOUSINGS: (Listed in order of preference.) Polypropylene, Polyethylene, or CPVC. Do not use PVC Plastic coated stainless steel; use polypro or Halar (black or green). Do not use PVC. Quartz, Enamel, Teflon, or PTFE Non-metallic centrifugal or magnetic-drive Polypropylene, Polyethylene. Do not use PVC
EQUIPMENT REQUIREMENTS FOR THE ENTIRE LINE 1. 2. 3. Ventilation recommended for each chemical tank. Work-bar agitation recommended for the line to aid in chemical action and rinsing. Do not use air agitation in any step of this process.
EQUIPMENT REQUIREMENTS BY CHEMICAL BATH PC-5012 Acid Cleaner Heated to 110 - 130 F. Circulation pump recommended, but not required. CirEtch 130 Heated to 75 - 85 F. Ventilation is required for this bath.
Immersion Silver Pre-Dip A heater is recommended, but not required. Circulation pump with filtration required. Circulation rate of 3 - 5 turnovers per hour. Filter ratings of 20 micron. Ventilation is required for this bath. IS150 Immersion Silver Heated to 110 - 130 F. Circulation pump with filtration required. Circulation rate of 3 - 5 turnovers per hour. Filter ratings of 20 micron. Ventilation is required for this bath. IS175 Silver Anti-tarnish Heated to 90 - 110 F. Circulation pump recommended, but not required. Water Rinses OPTIONAL Horizontal conveyorized equipment can be used, with immersion, flood bar agitation. All rinses must be De-ionized water and cannot contain halides (e.g. chlorides). Rinse volume turnover of 2 -4 times per hour. The final DI water rinse is heated to 110 130 F, mainly to speed drying.
Page 4 of 11
Revision: 09.22.08
Page 5 of 11
Revision: 09.22.08
If halides are present in the water, then it cannot be used in this process. Contact your local water purification company for recommendations on how to remove halides. Typically this is done by using either DI (deionized) or RO (reverse osmosis) purified water. DI water rinses should be run at flow rates of 2 - 4 volume turnovers per hour to ensure adequate rinsing. Bath Makeup The makeup quantities are shown below for both the Pre-dip and Silver baths. Follow the order given in the table for additions, and mix well after each step. Bath Makeup Step Step 1 Step 2 Pre-dip Silver Bath Add about 75% by volume of DI water* Add about 75% by volume of DI water* Add 1% by volume of nitric acid, Add 2% by volume of nitric acid, reagent grade, 68-70% reagent grade, 68-70% Step 3 Add 2.5% by volume of IS150B Add 5% by volume of IS150B Step 4 Bring tank to level with DI water Add 5% by volume of IS150A Step 5 --Bring tank to level with DI water * It is critical that the water be free of halides. See the test above. All analysis procedures are detailed in section V. below. A summary of the control ranges for each bath are shown in the table below. Component Acid normality IS150B concentration Silver metal Copper metal Pre-Dip 0.2 0.3 N 2.0 2.5 % by vol ----Silver Bath 0.4 0.6 N 4.0 - 5.0 % by vol 1.0 2.0 g/L Below 5.0 g/L (5000 ppm)
Nitric acid, reagent grade, 68% IS150B IS150A Nitric acid, reagent grade, 68% IS150B IS175
IS175 Anti-tarnish
*Analytical procedures and control ranges can be found in the Technical Bulletins for each product.
Page 6 of 11
Revision: 09.22.08
Reagent Information The following reagents are required for the IS150B titration. They can be purchased from Sigma-Aldrich at 1-800-558-9160. The catalog number information is shown below. Hexamethylenetetramine solution [CAS# 100-97-0] Makeup: 20% by weight dissolved in DI water Sigma-Aldrich Catalog #: H11300-500G Chromeazurol S indicator [CAS# 1667-99-8] Makeup: 0.1% by weight dissolved in DI water Sigma-Aldrich Catalog #: 199532-25G Copper (II) nitrate hydrate [CAS# 19004-19-4] - 0.01 M Makeup: Dissolve 2.32 grams into 1 liter of 2% by vol. nitric acid Sigma-Aldrich Catalog #: 467855-50G
TYPCIAL BATH OPERATION FOR IMMERSION SILVER PC-5012 Acid Cleaner Copper cleaning action and drag out reduces the concentration of PC-5012. Weekly analysis and addition of PC-5012 concentrate is recommended. CirEtch 130 Microetch rate is controlled by Cir130A concentration. We recommend an etch depth of 10-30 microinches. Sulfuric acid concentration controls the solubility of copper in solution. Cir130W can be added in small amounts to control misting. Bath analysis and additions of sulfuric acid and Cir130A should be performed daily. Pre-Dip for Immersion Silver As the pre-dip is used, the acid normality and IS150B concentrations drop. Additions of nitric acid and IS150B will keep the bath in specifications. Analysis should be performed weekly. Over time, the pre-dip can form a precipitate, which needs to be removed by filtration. The precipitate does not affect bath performance, and is normal. The pre-dip should be discarded and remade when the copper content of the Immersion Silver bath reaches the high limit, as detailed below. IS150 Immersion Silver As the Immersion Silver bath is used; silver, acid normality and IS150B content all drop, and copper content increases. Copper is dissolved as silver is plated. Additions of nitric acid, IS150A and IS150B will keep the bath in specifications. Analysis of the IS150 Immersion Silver bath and additions should be performed daily. When the copper level reaches 5000 ppm (5 g/L), then the Immersion Silver bath should be replaced. The pre-dip should also be replaced at the same time. Over time, the IS150 Immersion Silver bath can form a precipitate, which needs to be removed by filtration. The precipitate does not affect bath performance, and is normal. IS175 Anti-tarnish Anti-tarnish is consumed as the silver is coated with this protective chemical. There is no analysis for the active ingredient. This bath should be dumped and remade when approximately 600 square feet of circuit board area has been processed per gallon. The bath should also be remade if performance decreases.
Page 7 of 11
Revision: 09.22.08
CONTROLLING THE SILVER COATING The immersion silver coating is comprised of pure silver over copper. We recommend maintaining the pure silver layer thickness between 5 and 30 microinches to ensure good solderability through multiple assembly cycles. Silver thickness is best measured by XRF. We recommend the use of a collimator with a diameter that is at least 3x smaller in size than the feature that is being measured. Silver thicknesses on large pads can be much lower than on smaller pads. We recommend taking readings on various pad sizes, and using an average value for the measurement.
SILVER TARNISH It is the nature of silver to tarnish, which appears as a yellow to yellow-brown color. Tarnish can be minimized or prevented by taking certain precautions. These precautions are detailed below. Follow the general handling guidelines above. Ensure that the rinses following the IS150 Immersion Silver bath are filled with clean DI water. Dry the PWBs promptly and completely after immersion silver plating, using a clean dryer. Store the PWBs in a clean and dry environment. Sulfur compounds will cause silver tarnish. Ensure that sulfur containing compounds do not come into contact with the PWBs.
STORAGE It is good practice to store silver plated PWBs as soon as possible after plating. Store silver plated PWBs interleafed with paper, and inside plastic bags. The bags and paper must be sulfur free. Do not use rubber bands. Contaminates in the rubber can cause markings and tarnish on the silver, even through plastic bags. Silver plated PWBs should be stored at room temperature and humidity. REWORK OF THE SILVER FINISH In the event that tarnish forms on the silver surface, mild tarnish can be removed by using our IS127 Cleaner. Heavier tarnish may require more aggressive chemistries. Contact your Florida CirTech representative for details. The process steps for IS127 are shown below. Silver Tarnish Removal 1. Immerse the boards in a working IS127 Cleaner solution.
Page 8 of 11
Revision: 09.22.08
(Read the IS127 technical bulletin for details) 2. Rinse several times using clean DI water 3. Dry completely. It is possible to completely strip and re-plate the silver finish, if necessary. During silver stripping, cosmetic defects can form in the copper which are later translated into the re-plated silver deposit. It is very difficult to clean the copper sufficiently to remove these cosmetic defects. If silver stripping is necessary, then use the following process. Silver Stripping (Permanganate) 1. Immerse the boards in a working permanganate desmear type bath, until the silver is completely removed. An addition of about 5 10% by volume of ammonium hydroxide solution will speed stripping and brighten the copper surface. 2. Rinse several times. 3. Immerse in a working neutralizer bath. 4. Rinse several times. 5. Microetch about 40 60 microinches of copper. More may be required to clean the surface. 6. Rinse several times. 7. Run through an aluminum oxide jet scrub to buff the copper surfaces. 8. Run the boards through the complete immersion silver process to recoat with silver. An alternate silver stripping procedure is shown below. Silver Stripping (Alternate) 1. Run the tarnished silver boards through HASL to coat with solder. 2. Strip the solder using a standard tin/solder strip chemistry. 3. Clean the copper by microetching 40 60 microinches. 4. Run through an aluminum oxide jet scrub to buff the copper surfaces. 5. Run the boards through the complete immersion silver process to recoat with silver.
TROUBLE SHOOTING
Several defects can occur with immersion silver finishes. These defects will be discussed below. TARNISH The most common defect with immersion silver coatings is tarnish, or discoloration of the silver. This was discussed in the handling and storage section above. Some additional potential sources of silver tarnish are listed below. Contaminated rinses after the IS150 immersion silver bath, will cause tarnish. Rinsing with dirty water will cause tarnish. Clean DI water should be used for any rinse after immersion silver plating. Excessively long rinse times, especially in contaminated rinses, can attack silver and discolor it. Rinse times need to be long enough to remove the IS150 chemistry from the board, but not excessively long. Do not rinse for extended periods of time, e.g. longer than 5 minutes. Chemical fumes in the air can cause silver tarnish. Do not store silver coated boards in chemical process areas. Silver is especially susceptible to tarnish from sulfides. Do not store silver coated boards near waste treatment areas. Paper, plastics, and other materials can cause tarnish when in contact with the silver finish. Sulfur in the paper and plastic is known to cause silver tarnish. Ensure that sulfur free paper and plastics are used for board storage. If silver is plated too quickly or if the plating rate is too high, this can result in a porous deposit which can tarnish quickly. This type of tarnish is typically a brown color, which is indicative of
Page 9 of 11
Revision: 09.22.08
oxidation of the copper underneath the silver. Proper maintenance and control of the immersion silver chemistry and process will prevent this type of tarnish. MICROVOIDS Microvoids are small holes that form in a solder joint. These voids typically form near the surface of the pad, where the silver layer used to exist. Microvoids can compromise solder joint strength, making them more susceptible to fracturing The actual cause of microvoids is not well understood. There are several factors that can influence microvoid formation. Thicker silver deposits seem to be more susceptible to microvoids. Organic components that co-deposit in the silver coating have been identified as a possible cause. It is important to maintain the chemical baths within specifications, and run the process according to recommended guidelines. This will help to prevent the possibility of microvoid formation.
EXPOSED COPPER Exposed copper is seen as a red to orange/brown color showing through the silver deposit. This indicates that the silver deposit is porous and did not cover the copper completely. Contamination on the copper surface, from preceding processes can cause exposed copper. Thin solder mask residues can prevent silver plating, allowing copper to show through. Heavy copper oxides, if not completely removed, can inhibit silver plating. Other contamination on the copper surface can have the same effect. Proper solder mask development and final curing is necessary to prevent this problem. Proper pre-cleaning in the immersion silver process is a key to ensure complete coverage. If the pre-dip or immersion silver baths are allowed to go out of specifications, this can cause exposed copper. The pre-dip and immersion silver baths must be chemically maintained with regular frequency. Proper bath maintenance will help prevent exposed copper. Poor agitation in the immersion silver bath can cause exposed copper. Proper agitation in the immersion silver bath will make the silver coverage more uniform. A high plating rate in the silver bath can cause exposed copper. If bath components are accidentally overdosed, or if the bath temperature is too high, then the plating rate will be high. This may allow silver to plate quickly in some areas, while leaving exposed copper in other areas. Proper bath concentrations and temperature must be used to prevent this problem. Excessive rinsing, and rinsing with contaminated water can cause exposed copper. Extended rinse times (> 5 minutes), especially in dirty rinse water can actually cause copper color to show through the silver layer. Clean DI water rinses, and proper rinse times should be used to prevent this problem.
RELATED DOCUMENTS
Here is a list of related documents that are available from Florida CirTech. Technical Bulletins: PC5012 IS127 CirEtch 130 Immersion Silver IS150 Immersion Silver Process Flow Other Materials: Immersion Silver Presentation
Page 10 of 11
Revision: 09.22.08
CONTACTS
Florida CirTech 1309 N. 17th Avenue Greeley, CO 80631 (800) 686-6504 (970) 346-8331 FAX www.floridacirtech.com Manufactures and sells all products for the Immersion Silver processes.