Ch21 Fundamentals of Cutting2
Ch21 Fundamentals of Cutting2
Fundamentals of Machining
Two-Dimensional
Cutting Process
Figure 21.3 Schematic illustration of a
two-dimensional cutting process, also
called orthogonal cutting: (a) Orthogonal
cutting with a well-defined shear plane,
also known as the Merchant Model. Note
that the tool shape, depth of cut, to, and the
cutting speed, V, are all independent
variables, (b) Orthogonal cutting without a
well-defined shear plane.
Introduction to cutting
Compare Figs. 20.2 and 20.3,
and note that:
Feed in turning is equivalent to t0
Depth of cut in turning is
equivalent to width of cut
(dimension perpendicular to the
page) in the idealized model.
These relationships can be
visualized by rotating Fig. 20.3
CW by 90o.
Orthogonal cutting
Chip Formation by Shearing
The tool has a rake
angle of , and a
relief (clearance)
angle.
The shearing
process in chip
formation (Fig.
21.4a ) is similar to
the motion of cards
in a deck sliding
against each other.
Figure 21.4 (a) Schematic illustration of the basic mechanism of
chip formation by shearing. (b) Velocity diagram showing angular
relationships among the three speeds in the cutting zone.
Figure - Effect of shear plane angle : (a) higher with a resulting lower shear
plane area; (b) smaller with a corresponding larger shear plane area. Note that
the rake angle is larger in (a), which tends to increase shear angle according to the
Merchant equation
Continuous
Built-up Edge
Serrated or Segmented
Discontinuous
Built-up Edge
(b)
(c)
Figure 21.6 (a) Hardness distribution with a built-up edge in the cutting zone (material, 3115 steel).
Note that some regions in the built-up edge are as much as three times harder than the bulk metal of
the workpiece. (b) Surface finish produced in turning 5130 steel with a built-up edge. (c) Surface
finish on 1018 steel in face milling. Magnifications: 15x. Source: Courtesy of Metcut Research
Associates, Inc.
Chip Breaker
CBs increase the effective rake
angle of the tool and,
consequently, increase the
shear angle.
Chips can also be broken by
changing the tool geometry,
thereby controlling chip flow,
as in the turning operations
shown in Fig. 21.8.
Experience has indicated that
the ideal chip is in the shape of
the letter C or the number 9 and
fits within a 25 mm square
block.
Figure 21.7 (a) Schematic illustration of the action of a chip breaker. Note that the chip
breaker decreases the radius of curvature of the chip and eventually breaks it. (b) Chip
breaker clamped on the rake face of a cutting tool. (c) Grooves in cutting tools acting as
chip breakers. Most cutting toold used now are inserts with built-in chip breaker
features.
Figure 21.8 Chips produced in turning: (a) tightly curled chip; (b) chip hits workpiece and
breaks; (c) continuous chip moving radially away from workpiece; and (d) chip hits tool
shank and breaks off. Source: After G. Boothroyd.
Figure 21.10 (a) Schematic illustration of right-hand cutting tool. The various
angles on these tools and their effects on machining are described in Section
23.3.1 Although these tools traditionally have been produced from solid tool-steel
bars, they have been replaced largely with (b) inserts made of carbides and other
materials of various shapes and sizes.
Cutting Forces
Figure 21.11 (a) Forces acting on a cutting tool during two-dimensional cutting. Note
that the resultant force, R, must be collinear to balance the forces. (b) Force circle to
determine various forces acting in the cutting zone.
(21.11)
TEMPERATURE IN CUTTING
The main sources of heat generation are the primary shear
zone and the tool-chip interface.
If the tool is dull or worn, heat is also generated when the tool
tip rubs against the machined surface.
Cutting temperatures increase with:
1. strength of the workpiece material
2. cutting speed
3. depth of cut
Cutting temperatures decrease with increasing specific heat
and thermal conductivity of workpiece material.
TEMPERATURE IN CUTTING
The mean temperature in turning on a lathe is proportional to the
cutting speed and feed:
Mean temperature Va fb
(21.19)
a and b are constants that depend on tool and workpiece
materials, V is the cutting speed, and f is the feed of the tool.
Tool Material a
Carbide
0.2
0.125
HSS
0.5
0.375
Figure 21.13 Temperatures developed in turning 52100 steel: (a) flank temperature
distribution and (b) tool-ship interface temperature distribution. Source: After B. T.
Chao and K. J. Trigger.
Taylor Equation:
VT n C
n x
y
VT
d
f
C
Figure 21.16 Effect of workpiece hardness and microstructure on tool life in turning ductile cast iron. Note
the rapid decrease in tool life (approaching zero) as the cutting speed increases. Tool materials have been
developed that resist high temperatures, such as carbides, ceramics, and cubic boron nitride, as will be
described in Chapter 22.
Tool-life Curves
Figure 21.17 Tool-life curves for a
variety of cutting-tool materials.
The negative inverse of the slope
of these curves is the exponent n
in the Taylor tool-life equation and
C is the cutting speed at T = 1
min, ranging from about 200 to
10,000 ft./min in this figure.
Figure 21.18 (a) Schematic illustration of types of wear observed on various cutting tools. (b)
Schematic illustrations of catastrophic tool failures. A wide range of parameters influence these wear
and failure patterns. Source: Courtesy of V. C. Venkatesh.
Figure 21.19 Relationship between crater-wear rate and average tool-chip interface
temperature: 1) High-speed steel, 2) C-1 carbide, and 3) C-5 carbide (see Table 22.4).
Note how rapidly crater-wear rate increases with an incremental increase in temperature.
Source: After B. T Chao and K. J Trigger.
(a)
(b)
Figure 21.22 Schematic illustration of a dull tool with respect to the depth
of cut in orthogonal machining (exaggerated). Note that the tool has a
positive rake angle, but as the depth of cut decreases, the rake angle
effectively can become negative. The tool then simply rides over the
workpiece (without cutting) and burnishes its surface; this action raises
the workpiece temperature and causes surface residual stresses.
MACHINABLITY
Machinability of a material is defined in terms of 4 factors:
1. SF and SI of the machined part
2. tool life
3. force and power req
4. chip control
Tool life and SF: most important factors in machinability
Machinability ratings
based on a tool life, T = 60min
standard material is AISI 1112 steel (resulfurized), given a
rating of 100
for a tool life of 60 min, this steel should be machined at speed
of 100 ft/min
MACHINABLITY
machinability of steels
Improved by adding lead and sulfur (free machining steels)
Resulfurized & Rephosphorized Steels
S forms manganese sulfide inclusions (2nd phase particles)
Act as stress raisers in the primary shear zone
So chips break up easily and are small
P has 2 major effects:
1. It strengthens ferrite, causing increased hardness, resulting in
better chip formation and SF
2. Increased hardness causes the formation of short chips
MACHINABLITY
leaded steels
High % of lead in steels solidifies at the tip of manganese sulfide
inclusions
in non-resulfurized steels, lead takes the form of dispersed fine
particles
Pb acts as solid lubricant because of low shear strength
When temp is high, Pb melts in front of the tool, acting as a liquid
lubricant
Bismuth and tin are possible substitutes for lead in steel
Calcium-Deoxidized steels
Oxide flakes of Calcium silicates (CaSO) are formed
These flakes reduce strength of secondary shear zone, decreasing
tool-chip interface friction and wear
Temp is reduced, better crater wear
MACHINABLITY
Stainless steels
Austentic steels (300 series) are generally difficult to machine
Chatter can be a problem, need machine tools with high
stiffness
Ferrite steels have good machinability
Martensistic steels are abrasive, tend to form BUE, and require
tool material with high hot hardness and crater wear resistance
Precipitation-hardening steels are strong and abrasive, require
hard and abrasion resistance tool material
MACHINABLITY
Effects of other elements in steel
Al and Si is always harmful because they combine with O to
form aluminium oxide and silicates, which are hard and
abrasive
C and Mn have various effects on machinability, depending on
their composition.
Plain low carbon steels (< 0.15% C) can produce poor SF by
forming BUE
Tool and die steels are very difficult to machine and usually
require annealing prior to machining.
Machinability of most steels is improved by cold working,
which hardens the material and reduces the tendency to form
BUE.
Ni, Cr, Molybdenum, Vn generally reduce machinability
MACHINABLITY
Thermally Assisted Machining
Source of heat is focused to an area just ahead of the cutting
tool
Advantages are:
1. lower cutting forces
2. increased tool life
3. use of inexpensive cutting tool materials
4. higher material removal rates
5. reduced tendency for vibration and chatter
Homework:
Problems: 40, 41, 45, 52
Due date: 23/4/2013
A quiz will be made at the same day.